Nitroxide mediated synthesis of low dispersity random copolymers for low‐loss optical waveguides

Candidate materials for low‐loss optical waveguides based on poly(glycidyl methacrylate‐ran‐pentafluostyrene) [P(GMA‐ran‐PFS)] copolymers were synthesized by nitroxide mediated polymerization (NMP) initiated with BlocBuilder^® [N‐(2‐methylpropyl)‐N‐(1‐diethlphosphono‐2,2‐dimethylpropyl)‐O‐(2‐carboxylprop‐2‐yl) hydroxylamine] bearing a succinimidyl ester group (NHS‐BlocBuilder) at 90 °C in 1,4 dioxane. The copolymerizations yielded copolymers with low dispersity M_w/M_n between 1.2 and 1.4. The core structure of single‐mode channel waveguides was fabricated by direct UV lithographic patterning. The copolymers with low M_w/M_n resulted in line width roughness (LWR) of about 0.16 μm, whereas LWR of copolymers with M_w/M_n=3.5 but similar compositions was about 0.5 μm. The improvement in microstructural control allotted by NMP permitted finer pattern replication for copolymers desired for optical waveguides, as suggested for photoresist polymers. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2970–2978     

Cobalt(II) octanoate and cobalt(II) perfluorooctanoate catalyzed atom transfer radical polymerization of styrene in toluene and fluorous media—A versatile route to catalyst recycling and oligomer formation

Cobalt(II) perfluorooctanoate‐catalyzed atom transfer radical polymerization (ATRP) and reverse ATRP were developed to prepare oligostyrenes (M_n < 2500) with low polydispersities M_w/M_n < 1.5. Fluorous biphase catalysis was applied for effective recycling of catalyst and fluorous solvent. The homogeneous polymerization reaction was performed at 90 °C in toluene/cyclohexane/perfluorodecalin mixture (1:1:1) and fluorine‐free solvents. Temperature‐induced phase separation of this fluorous solvent mixture occurred at room temperature and proved to be the key for the very effective separation of the cobalt(II) perfluorooctanoate from the oligostyrene and fluorine‐free solvents. Both the fluorine‐tagged cobalt catalysts and the fluorous media were recycled and reused up to three times without encountering catalyst activity losses. The roles of cobalt catalysts, fluorous media, and monomer/initiator ratio were examined with respect to the polymerization kinetics. Fluorine‐containing and fluorine‐free cobalt(II) octanoate catalyzed controlled styrene oligomerization according to the ATRP mechanism. The molar mass control range was limited in fluorous biphase catalysis most likely because of precipitation of high molar mass polystyrenes in the fluorous reaction medium. To the best of our knowledge, this is the first time temperature‐induced phase separation of fluorous and fluorine‐free solvents has been successfully applied to polymerization processing. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3804–3813, 2005     

Fluorine‐containing vinyl ether polymers: Living cationic polymerization in fluorinated solvents as new media and unique solubility characteristics in organic solvents

Living cationic polymerization of fluorine‐containing vinyl ethers [CH₂?CH? O? C₂H₄? O? C₃H₆? C_nF_2n+1: 5FVE (n = 2), 13FVE (n = 6)] was investigated in various solvents with a CH₃CH(OiBu)OCOCH₃/Et_1.5AlCl_1.5 initiating system in the presence of an added base. 5FVE was polymerized quantitatively in toluene at 0 °C, and the obtained polymers had predetermined molecular weights with narrow molecular weight distributions (M_w/M_n < 1.1). On the other hand, for the polymerization of 13FVE, the product polymers precipitated due to their extremely poor solubility in nonfluorinated organic solvents. Therefore, fluorinated solvents such as hydrochlorofluorocarbons, hydrofluorocarbons, hydrofluoroethers, or α,α,α‐trifluorotoluene, as‐yet uninvestigated for cationic polymerization, were employed. In these solvents, living polymerization was achieved even with 13FVE, yielding well‐defined polymers (M_w/M_n < 1.1, by size exclusion chromatography using a fluorinated solvent as an eluent). The solvents were also shown to be good for living polymerization of isobutyl vinyl ether. The obtained fluorine‐containing polymers underwent temperature‐responsive solubility transitions in organic solvents. Poly(5FVE) showed sensitive upper critical solution temperature (UCST)‐type phase separation behavior in toluene. Copolymers of 13FVE and isobutyl vinyl ether showed UCST‐type phase separation in common organic solvents with different polarities depending on their composition, while a homopolymer of 13FVE was insoluble in all nonfluorinated organic solvents. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis of well‐defined cyclodextrin‐core star polymers

The synthesis of 21‐arm methyl methacrylate (MMA) and styrene star polymers is reported. The copper (I)‐mediated living radical polymerization of MMA was carried out with a cyclodextrin‐core‐based initiator with 21 independent discrete initiation sites: heptakis[2,3,6‐tri‐O‐(2‐bromo‐2‐methylpropionyl]‐β‐cyclodextrin. Living polymerization occurred, providing well‐defined 21‐arm star polymers with predicted molecular weights calculated from the initiator concentration and the consumed monomer as well as low polydispersities [e.g., poly(methyl methacrylate) (PMMA), number‐average molecular weight (M_n) = 55,700, polydispersity index (PDI) = 1.07; M_n = 118,000, PDI = 1.06; polystyrene, M_n = 37,100, PDI = 1.15]. Functional methacrylate monomers containing poly(ethylene glycol), a glucose residue, and a tert‐amine group in the side chain were also polymerized in a similar fashion, leading to hydrophilic star polymers, again with good control over the molecular weight and polydispersity (M_n = 15,000, PDI = 1.03; M_n = 36,500, PDI = 1.14; and M_n = 139,000, PDI = 1.09, respectively). When styrene was used as the monomer, it was difficult to obtain well‐defined polystyrene stars at high molecular weights. This was due to the increased occurrence of side reactions such as star–star coupling and thermal (spontaneous) polymerization; however, low‐polydispersity polymers were achieved at relatively low conversions. Furthermore, a star block copolymer consisting of PMMA and poly(butyl methacrylate) was successfully synthesized with a star PMMA as a macroinitiator (M_n = 104,000, PDI = 1.05). © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2206–2214, 2001     

Synthesis of end‐functionalized poly(methyl methacrylate) by ruthenium‐catalyzed living radical polymerization with functionalized initiators

A series of functionalized 2‐bromoisobutyrates and 2‐chloro‐2‐phenylacetates led to α‐end‐functionalized poly(methyl methacrylate)s in Ru(II)‐catalyzed living radical polymerization; the terminal functions included amine, hydroxyl, and amide. These initiators were effective in the presence of additives such as Al(Oi‐Pr)₃ and n‐Bu₃N. The chlorophenylacetate initiators especially coupled with the amine additive gave polymers with well‐controlled molecular weights (M_w/M_n = 1.2–1.3) and high end functionality (F_n ～ 1.0). © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1937–1944, 2002     

Simultaneous control of the stereospecificity and molecular weight in the ruthenium‐catalyzed living radical polymerization of methyl and 2‐hydroxyethyl methacrylates and sequential synthesis of stereoblock polymers

The stereospecific living radical polymerizations of methyl methacrylate (MMA) and 2‐hydroxyethyl methacrylate (HEMA) were achieved with a combination of ruthenium‐catalyzed living radical and solvent‐mediated stereospecific radical polymerizations. Among a series of ruthenium complexes [RuCl₂(PPh₃)₃, Ru(Ind)Cl(PPh₃)₂, and RuCp*Cl(PPh₃)₂], Cp*–ruthenium afforded poly(methyl methacrylate) with highly controlled molecular weights [weight‐average molecular weight/number‐average molecular weight (M_w/M_n) = 1.08] and high syndiotacticity (r = 88%) in a fluoroalcohol such as (CF₃)₂C(Ph)OH at 0 °C. On the other hand, a hydroxy‐functionalized monomer, HEMA, was polymerized with RuCp*Cl(PPh₃)₂ in N,N‐dimethylformamide and N,N‐dimethylacetamide (DMA) to give syndiotactic polymers (r = 87–88%) with controlled molecular weights (M_w/M_n = 1.12–1.16). This was the first example of the syndiospecific living radical polymerization of HEMA. A fluoroalcohol [(CF₃)₂C(Ph)OH], which induced the syndiospecific radical polymerization of MMA, reduced the syndiospecificity in the HEMA polymerization to result in more or less atactic polymers (mm/mr/rr = 7.2/40.9/51.9%) with controlled molecular weights in the presence of RuCp*Cl(PPh₃)₂ at 80 °C. A successive living radical polymerization of HEMA in two solvents, first DMA followed by (CF₃)₂C(Ph)OH, resulted in stereoblock poly(2‐hydroxyethyl methacrylate) with syndiotactic–atactic segments. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3609–3615, 2006     

Novel catalyst system of MCl2/FeCl3·6H2O/PPh3 (M = Ni,Co, or Mn) for the atom transfer radical polymerization of methyl methacrylate

MCl₂ (M = Ni, Co, Sn, or Mn) and PPh₃ together acted as a catalyst for the radical polymerization of methyl methacrylate (MMA) in the presence of ethyl 2‐bromoisobutyrate as an initiator. The four systems all led to conventional radical polymerizations, which yielded polymers with a weight‐average molecular weight/number‐average molecular weight (M_w/M_n) ratio greater than 2.0 and became well controlled when a certain amount of FeCl₃·6H₂O was added. The polymerizations of MMA catalyzed by these four FeCl₃‐modified catalyst systems provided well‐defined polymers with low polydispersities (M_w/M_n < 1.28). © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2625–2631, 2005     

Synthesis of well‐defined AB20‐type star polymers with cyclodextrin‐core by combination of NMP and ATRP

The synthesis of an AB₂₀‐type heteroarm star polymer consisting of a polystyrene arm and 20‐arms of poly(methyl methacrylate) or poly(tert‐butyl acrylate) was carried out using the combination of nitroxide‐mediated polymerization (NMP) and atom transfer radical polymerization (ATRP). The NMP of styrene was carried out using mono‐6‐[4‐(1′‐(2″,2″,6″,6″‐tetramethyl‐1″‐piperidinyloxy)‐ethyl)benzamido]‐β‐cyclodextrin peracetate ( 1 ) to afford end‐functionalized polystyrene with an acetylated β‐cyclodextrin (β‐CyD) unit (prepolymer 2 ) with a number‐average molecular weight (M_n) of 11700 and a polydispersity (M_w/M_n) of 1.17. After deacetylation of prepolymer 2 , the resulting polymer was reacted with 2‐bromoisobutyric anhydride to give end‐functionalized polystyrene with 20(2‐bromoisobutyrol)s β‐CyD, macroinitiator 4 . The copper (I)‐mediated ATRP of methyl methacrylate (MMA) and tert‐butyl acrylate (tBA) was carried out using macroinitiator 4 . The resulting polymers were isolated by SEC fractionation to produce AB₂₀‐type star polymers with a β‐CyD‐core, 5 . The well‐defined structure of 5 with weight‐average molecular weight (M_w)s of 13,500–65,300 and M_w/M_n's of 1.26–1.28 was demonstrated by SEC and light scattering measurements. The arm polymers were separated from 5 by destruction with 28 wt % sodium methoxide in order to analyze the details of their characteristic structure. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4271–4279, 2005     

Synthesis and photophysical properties of soluble low‐bandgap thienothiophene polymers with various alkyl side‐chain lengths

We report the facile synthesis and characterization of a class of thienothiophene polymers with various lengths of alkyl side chains. A series of 2‐alkylthieno[3,4‐b]thiophene monomers (Ttx) have been synthesized in a two‐step protocol in an overall yield of 28–37%. Poly(2‐alkylthieno[3,4‐b]thiophenes) (PTtx, alkyl: pentyl, hexyl, heptyl, octyl, and tridecyl) were synthesized by oxidative polymerization with FeCl₃ or via Grignard metathesis (GRIM) polymerization methods. The polymers are readily soluble in common organic solvents. The polymers synthesized by GRIM polymerization method (PTtx‐G) have narrower molecular weight distribution (?) with lower molecular weight (M_n) than those synthesized by oxidative polymerization (PTtx‐O). The band structures of the polymers with various lengths of alkyl side chains were investigated by UV–vis spectroscopy, cyclic voltammetry, and ultraviolet photoelectron spectroscopy. These low‐bandgap polymers are good candidates for organic transistors, organic light‐emitting diodes, and organic photovoltaic cells. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis and polymerization of N‐(4‐tetrahydropyranyl‐oxyphenyl)maleimide

N‐(4‐Tetrahydropyranyl‐oxy‐phenyl)maleimide (THPMI) was prepared and polymerized by radical or anionic initiators. THPMI could be polymerized by 2,2′‐azobis(isobutyronitrile) (AIBN) and potassium tert‐butoxide. Radical polymers (poly(THPMI)r) were obtained in 15–50% yields for AIBN in THF at 65°C after 2–5 h. The yield of anionic polymers (poly(THPMI)a) obtained from potassium tert‐butoxide in THF at 0°C after 20 h was 91%. The molecular weights of poly(THPMI)r and poly(THPMI)a were M_n = 2750–3300 (M_w/M_n = 1.2–3.3) and M_n = 11300 (M_w/M_n = 6.0), respectively. The difference in molecular weights of the polymers was due to the differences in the termination mechanism of polymerization and the solubility of these polymers in THF. The thermal decomposition temperatures were 205 and 365°C. The first decomposition step was based on elimination of the tetrahydropyranyl group from the poly(THPMI). Positive image patterns were obtained by chemical amplification of positive photoresist composed of poly(THPMI) and 4‐morpholinophenyl diazonium trifluoromethanesulfonate used as an acid generator. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 341–347, 1999     

N,N,N′,N′,N″‐penta(methyl acrylate)diethylenetriamine: A novel ligand for atom transfer radical polymerization of methyl methacrylate

A novel ligand, N,N,N′,N′,N″‐penta (methyl acrylate) diethylenetriamine (MA₅‐DETA), was synthesized by the reaction of diethylenetriamine with methyl acrylate in almost quantitive yield. The polymerizations of methyl methacrylate with MA₅‐DETA as the ligand and α,α‐dichlorotoluene (DCT) and ethyl 2‐bromoisobutyrate (2‐EBiB) as the initiators, respectively, under different conditions were examined. The polymerization with CuCl/MA₅‐DETA/DCT was closely controlled in bulk and gave polymers with quite narrow molecular weight distributions (M_w/M_n's) of 1.16–1.29. The polymerization with the system CuBr/MA₅‐DETA/EBiB in bulk gave high activity. However, the system was not well controlled and gave the polymers with M_w/M_n = 1.35–1.53. The solution polymerization in anisole with CuBr/MA₅‐DETA/EBiB showed a better‐controlled nature. Moreover, the addition of CuBr₂ into the aforementioned system can further improve its controllability. The M_w/M_n's of the resulting polymers ranged from 1.11 to 1.21. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1963–1969, 2004     

Stimuli‐responsive cationic terpolymers by RAFT polymerization: Synthesis,characterization, and protein interaction studies

The controlled synthesis and characterization of a range of stimuli responsive cationic terpolymers containing varying amounts of N‐isopropylacrylamide (NIPAM), 3‐(methylacryloylamino)propyl trimethylammonium chloride (MAPTAC), and poly(ethylene glycol)monomethyl methacrylate (PEGMA) is presented. The terpolymers were synthesized using reversible addition‐fragmentation chain transfer (RAFT) polymerization. Compositions of the terpolymers determined using ¹H NMR were in close agreement to the theoretical values determined from the monomer feed ratios. GPC‐MALLS was used to analyze the molecular weight characteristics of the polymers, which were found to have low polydispersities (M_w/M_n 1.1–1.4). The phase transitions were studied as a function of PEGMA and NIPAM content using temperature controlled ¹H NMR and turbidity measurements (UV‐Vis). The relationship between thermal stability and the comonomer ratio of the polymers was measured using thermogravimetric analysis (TGA). Protein interaction studies were performed to determine the suitability of the polymers for biological applications. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4021–4029, 2008     

Synthesis and radical polymerization of methacrylate endowed with bicyclobis(γ‐butyrolactone) moiety through methylene linker

A series of methacrylates bearing bicyclobis(γ‐butyrolactone) (BBL) moiety were synthesized and radically polymerized to afford the corresponding poly(methacrylate)s bearing BBL moiety in the side chain, with expecting that the high polarity and rigidity of BBL would be inherited by the polymers. The resulting polymers were soluble in polar aprotic solvents such as dimethyl sulfoxide and N,N‐dimethylformamide because of the high polarity of the BBL moiety. The glass transition temperatures (T_g) of the polymers depended on the length of methylene linker that tethered the methacrylate and BBL moieties, making the use of shorter linkers lead to higher T_gs. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2462–2468     

Polymer grafting onto polyurethane backbone via Diels–Alder reaction

The aliphatic polyurethane with pendant anthracene moieties (PU‐anthracene) was prepared from polycondensation of anthracen‐9‐yl methyl 3‐hydroxy‐2‐(hydroxymethyl)‐2‐methylpropanoate (anthracene diol), 1 with hexamethylenediisocyanate in the presence of dibutyltindilaurate in CH₂Cl₂ at room temperature for 10 days. Thereafter, the PU‐anthracene (M_n,GPC = 12,900 g/mol, M_w/M_n = 1.87, relative to PS standards) was clicked with a linear α‐furan protected‐maleimide terminated‐poly(methyl methacrylate) (PMMA‐MI) (M_n,GPC = 2500 g/mol, M_w/M_n = 1.33), or ‐poly(ethylene glycol) (PEG‐MI) (M_n,GPC = 550 g/mol, M_w/M_n = 1.09), to result in well‐defined PU‐graft copolymers, PU‐g‐PMMA (M_n,GPC = 23800 g/mol, M_w/M_n = 1.65, relative to PS standards) or PU‐g‐PEG (M_n,GPC = 11,600 g/mol, M_w/M_n = 1.45, relative to PS standards) using Diels–Alder reaction in dioxane/toluene at 105 °C. The Diels–Alder grafting efficiencies were found to be over 93–99% using UV spectroscopy. Moreover, the structural analyses and the thermal transitions of all copolymers were determined via ¹H NMR and DSC, respectively. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 521–527     

Construction of PIB‐b‐PDEAEMA well‐defined amphiphilic diblock copolymers via sequential living carbocationic and RAFT polymerization

A series of well‐defined amphiphilic diblock copolymers consisting of hydrophobic polyisobutylene (PIB) and hydrophilic poly(2‐(diethylamino)ethyl methacrylate) (PDEAEMA) segments was synthesized via the combination of living carbocationic polymerization and reversible addition fragmentation chain transfer (RAFT) polymerization. Living carbocationic polymerization of isobutylene followed by end‐capping with 1,3‐butadiene was first performed at ?70 °C to give a well‐defined allyl‐Cl‐terminated PIB with a low polydispersity (M_w/M_n =1.29). This end‐functionalized PIB was further converted to a macromolecular chain transfer agent for mediating RAFT block copolymerization of 2‐(diethylamino)ethyl methacrylate at 60 °C in tetrahydrofuran to afford the target well‐defined PIB‐b‐PDEAEMA diblock copolymers with narrow molecular weight distributions (M_w/M_n ≤1.22). The self‐assembly behavior of these amphiphilic diblock copolymers in aqueous media was investigated by fluorescence spectroscopy and transmission electron microscope, and furthermore, their pH‐responsive behavior was studied by UV‐vis and dynamic light scattering. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1478–1486     

Hyperbranched polymers as scaffolds for multifunctional reversible addition–fragmentation chain‐transfer agents: A route to polystyrene‐core‐polyesters and polystyrene‐block‐poly(butyl acrylate)‐core‐polyesters

Polydisperse hyperbranched polyesters were modified for use as novel multifunctional reversible addition–fragmentation chain‐transfer (RAFT) agents. The polyester‐core‐based RAFT agents were subsequently employed to synthesize star polymers of n‐butyl acrylate and styrene with low polydispersity (polydispersity index < 1.3) in a living free‐radical process. Although the polyester‐core‐based RAFT agent mediated polymerization of n‐butyl acrylate displayed a linear evolution of the number‐average molecular weight (M_n) up to high monomer conversions (>70%) and molecular weights [M_n > 140,000 g mol^?1, linear poly(methyl methacrylate) equivalents)], the corresponding styrene‐based system reached a maximum molecular weight at low conversions (≈30%, M_n = 45,500 g mol^?1, linear polystyrene equivalents). The resulting star polymers were subsequently used as platforms for the preparation of star block copolymers of styrene and n‐butyl acrylate with a polyester core with low polydispersities (polydispersity index < 1.25). The generated polystyrene‐based star polymers were successfully cast into highly regular honeycomb‐structured microarrays. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3847–3861, 2003     

Ruthenium‐catalyzed fast living radical polymerization of methyl methacrylate: The R?Cl/Ru(Ind)Cl(PPh3)2/n‐Bu2NH initiating system

A fast living radical polymerization of methyl methacrylate (MMA) proceeded with the (MMA)₂? Cl/Ru(Ind)Cl(PPh₃)₂ initiating system in the presence of n‐Bu₂NH as an additive [where (MMA)₂? Cl is dimethyl 2‐chloro‐2,4,4‐trimethyl glutarate]. The polymerization reached 94% conversion in 5 h to give polymers with controlled number‐average molecular weights (M_n's) in direct proportion to the monomer conversion and narrow molecular weight distributions [MWDs; weight‐average molecular weight/number‐average molecular weight (M_w/M_n) ≤ 1.2]. A poly(methyl methacrylate) with a high molecular weight (M_n ～ 10⁵) and narrow MWD (M_w/M_n ≤ 1.2) was obtained with the system within 10 h. A similarly fast but slightly slower living radical polymerization was possible with n‐Bu₃N, whereas n‐BuNH₂ resulted in a very fast (93% conversion in 2.5 h) and uncontrolled polymerization. These added amines increased the catalytic activity through some interaction such as coordination to the ruthenium center. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 617–623, 2002; DOI 10.1002/pola.10148     

The influence of comonomer (2‐hydroxyethyl acrylate) and keto group on photocrosslinking property of arylidene polymers

Two types of arylidene compounds were synthesized by reacting p‐hydroxybenzaldehyde with acetone [1,5‐bis(4‐hydroxyphenyl)penta‐1,4‐dien‐3‐one] (PBHP) and cyclohexanone [2,6‐bis(4‐hydroxybenzylidene)cyclohexanone] (HBC). 1,4‐Pentadien‐3‐one‐1‐p‐hydroxyphenyl‐5‐p‐phenyl methacrylate (PHPPMA) and 4‐{[‐3‐(4‐hydroxybenzylidene)‐2‐oxocyclohexylidene]methyl}phenyl acrylate (HBA) were prepared by reacting PBHP and HBC with methacryloyl chloride and acryloyl chloride in the presence of triethylamine, respectively. Copolymerization of different feed compositions of PHPPMA and HBA with 2‐hydroxyethyl acrylate (HEA) was carried out using a free‐radical solution polymerization technique in ethyl methyl ketone (MEK) using benzoyl peroxide (BPO). All the monomer and polymers were characterized by IR and NMR (¹H/¹³C) spectroscopic techniques. The reactivity ratio of the monomers were obtained using Fineman–Ross (FR), Kelen–Tudos (KT), and extended Kelen–Tudos (exKT) methods. The photocrosslinking properties of the polymers were done using a UV absorption spectroscopy technique. Homopolymers of both the arylidene polymers shows similar trend towards the rate of photocrosslinking. The rate of photocrosslinking was enhanced when the cyclohexanone based arylidene monomer was copolymerized with HEA. Thermal stability and molecular weights (M_w and M_n) of the polymers were determined. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3433–3444, 2004     

Fluorinated vinyl ether homopolymers and copolymers: Living cationic polymerization and temperature‐induced solubility transitions in various organic solvents including perfluoro solvents

Partially fluorinated poly(vinyl ether)s with C₄F₉ and C₆F₁₂H groups in the side chain were synthesized via living cationic polymerization in the presence of an added base in a fluorine‐containing solvent, dichloropentafluoropropanes. For comparison, the polymerization of vinyl ether monomers with C₂F₅ and C₆F₁₃ groups and nonfluorinated monomers were also carried out. The characterization of the product polymers using size exclusion chromatography with a fluorinated solvent as an eluent indicated that all polymers had narrow molecular weight distributions (M_w/M_n ～ 1.1). Interestingly, the moderately fluorinated polymers with C₄F₉ exhibited upper critical solution temperature‐type phase separation in various organic solvents with wide‐ranging polarities, whereas highly fluorinated polymers with C₆F₁₃ are insoluble in nonfluorinated solvents. Polymers with C₄F₉ groups exhibited temperature dependent solubility transitions not only in common organic solvents (e.g., toluene, chloroform, tetrahydrofuran, and acetone) but also in perfluoro solvents [e.g., perfluoro(methylcyclohexane) and perfluorodecalin]. On the other hand, the solubility of polymers with C₆F₁₂H showed completely different from that of polymers with C₆F₁₃, despite their similar fluorine content. In addition, various types of fluorinated block copolymers were prepared in a living manner. The block copolymers with a thermosensitive fluorinated segment underwent temperature‐induced micellization and sol–gel transition in various organic solvents. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis of traditional and ionic polymethacrylates by anion catalyzed group transfer polymerization

The hydrophobic ionic liquid 1‐butyl‐1‐methylpyrrolidinium bis(trifluoromethylsulfonyl)imide was successfully used as solvent in group transfer polymerization of traditional methacrylates (methyl methacrylate, n‐butyl methacrylate, and benzyl methacrylate) and of ionic liquid methacrylates (ILMAs). This demonstrates that this ionic liquid makes reaction conditions, which do not require the use of ultra‐dried solvents. The ILMAs were N‐[2‐(methacryloyloxy)ethyl]‐N,N‐dimethyl‐N‐alkylammonium bis(trifluoromethylsulfonyl)imides bearing methyl, ethyl, propyl, butyl, or hexyl substituents. Increasing size of the alkyl substituent at the cation results in decreasing glass transition temperature in case of both ionic liquid methacrylates and polymers derived of them. Furthermore, the glass transition temperature is significantly higher for these polymers compared with the ionic liquid methacrylates, and the effect of glass transition temperature reduction with increasing size of the alkyl substituent is stronger for the polymers. A mechanism was proposed explaining the catalytic function of the ionic liquid used as solvent for polymerization. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2849–2859