Surface modification of poly(propylene carbonate) by oxygen ion implantation

Poly(propylene carbonate) (PPC) was implanted by oxygen ion with energy of 40 keV. The influence of experimental parameters was investigated by varying ion fluence from 1 × 10¹² to 1 × 10¹⁵ ions/cm². XPS, SEM, surface roughness, wettability, hardness, and modulus were employed to investigate structure and properties of the as-implanted PPC samples. Eight chemical groups, i.e., carbon, CH, COC, CO, OCO, CO, , and groups were observed on surfaces of the as-implanted samples. The species and relative intensities of the chemical groups changed with increasing ion fluence. SEM images displayed that irradiation damage was related strongly with ion fluence. Both surface-recovering and shrunken behavior were observed on surface of the PPC sample implanted with fluence of 1 × 10¹⁵ ions/cm². As increasing ion fluence, the surface roughness of the as-implanted PPC samples increased firstly, reached the maximum value of 159 nm, and finally decreased down the minimum value. The water droplet contact angle of the as-implanted PPC samples changed gradually with fluence, and reached the minimum value of 70° with fluence of 1 × 10¹⁵ ions/cm². The hardness and modulus of the as-implanted PPC samples increased with increasing ion fluence, and reached their corresponding maximum values with fluence of 1 × 10¹⁵ ions/cm². The experimental results revealed that oxygen ion fluence closely affected surface chemical group, morphology, surface roughness, wettability, and mechanical properties of the as-implanted PPC samples.     

Carbon monoxide adsorption on Pd-deposited Cu(1 1 0) surface: Infrared reflection absorption and temperature programmed desorption studies

We investigated carbon monoxide (CO) adsorption and desorption behaviors on 0.1-nm-, 0.15-nm-, and 0.3-nm-thick-Pd-deposited Cu(1 1 0) surfaces using infrared reflection absorption (IRRAS) and temperature-programmed desorption (TPD) spectroscopic methods. CO was exposed to the 0.1-nm-thick-Pd/Cu(1 1 0) surface at the substrate temperature of 90 K. The IR band attributable to CO bonded to Cu atoms emerged at 2092 cm⁻¹: the band was located at 2100 cm⁻¹ at saturation coverage, with a shoulder at 2110 cm⁻¹. In addition to these bands, weak absorptions attributable to the PdCO bonds appeared at 2050 and 1960 cm⁻¹. With increasing Pd thickness, the Pd related-bands became increasingly prominent. Particularly at the early stage of exposure, the band at 2115 cm⁻¹ became visible. The band at 2117 cm⁻¹ dominated the spectra all through the exposures for the 0.3-nm-thick-Pd surface. The TPD spectra of the surfaces showed two remarkable features at around 220-250 and 320-390 K, ascribable ,respectively, to CuCO and PdCO. The desorption peaks shifted to higher temperatures with increasing Pd thickness. Based on the TPD and IRRAS results, we discuss the adsorption-desorption behaviors of CO on the Pd/Cu(1 1 0) surfaces.     

Asymmetric surface modification of poly(ethylene terephthalate) film by CF4 plasma immersion

Poly(ethylene terephthalate) (PET) films were treated with CF₄ plasma immersion. The samples were processed at different RF powers and treatment time. The surface modification of PET films was evaluated by water contact angle (CA), X-ray photoelectron spectroscopy (XPS) and atomic force microscope (AFM). Decrease in contact angle of both sides of PET films was observed under mild treatment conditions. However, as raising treatment power and/or time, the change in contact angle between the two sides of PET films was different. The relatively hydrophobic and hydrophilic surfaces were being in situ formed on the two sides of PET films, respectively. And the extreme values of water contact angle reached 108.63 and 7.56°, respectively. XPS analyses revealed that there was a substantial incorporation of fluorine and/or oxygen atoms in both side surfaces. The relative chemical composition of the C (ls) spectra's showed the incorporation of non-polar fluorine-based functionalities (i.e. CFCF_n, CF₂ or CF₃ groups) and polar oxygen-based functionalities (i.e. COOH or OH groups) in the surfaces. Correlation between the plasma parameters and the surface modification of PET films is also discussed.     

Pulsed laser ablation of borax target in vacuum and hydrogen DC glow discharges

The aim of our experiment was to produce a material with BH bonds for applications in hydrogen storage and generation. By using KrF excimer laser (λ = 248 nm) ablation of borax (Na₂B₄O₇) target, thin films were deposited on KBr and silicon substrates. Ablation was performed both in vacuum and in hydrogen atmosphere. DC glow discharge technique was utilized to enhance hydrogen gas ionization. Experiments were performed using laser fluence from 5 to 20 J/cm². Films were deposited under gas pressure of 1 × 10⁻⁵ to 5 × 10⁻² mbar and substrate temperatures of 130-450 °C. Scanning electron microscopy analysis of films showed presence of circular particulates. Film thickness, roughness and particulates number increased with increase in laser fluence. Energy dispersive X-ray spectroscopy analysis shows that sodium content in the particulates is higher than in the target. This effect is discussed in terms of atomic arrangements (both at surface and bulk) in systems where ionic and covalent bonds are present and by looking at the increased surface/bulk ratio of the particulates with respect to the deposited films. The Fourier transform infrared spectroscopy measurements showed presence of BO stretching and BOB bending bonds. Possible reasons for absence of BH bonds are attributed to binding enthalpy of the competing molecules.     

Influence of nitrogen ion implantation fluences on surface structure and tribological properties of SiC ceramics in water-lubrication

Nitrogen ions were implanted into SiC ceramics by using ion implantation technology (N⁺-SiC). The surface structure and chemical bonds of N⁺-SiC ceramics were determined by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), and their nanohardness was measured by nanoindenter. The friction and wear properties of the N⁺-SiC/SiC tribo-pairs were investigated and compared with those of SiC/SiC tribo-pairs in water using ball-on-disk tribo-meters. The wear tracks on the N⁺-SiC ceramics were observed by non-contact surface profilometer and scanning electron microscope (SEM) and their wear volumes were determined by non-contact surface profilometer. The results show that the N⁺-SiC ceramics were mainly composed of SiC and SiCN phase and SiN, CC, CN and CN bonds were formed in the implantation layer. The highest hardness of 22.3 GPa was obtained as the N⁺-SiC ceramics implanted at 50 keV and 1 × 10¹⁷ ions/cm². With an increase in nitrogen ion fluence, the running-in period of N⁺-SiC/SiC tribo-pairs decreased, and the mean stable friction coefficient decreased from 0.049 to 0.024. The N⁺-SiC ceramics implanted at 50 keV and 5 × 10¹⁷ ions/cm² exhibited the excellent tribological properties in water. In comparison of SiC/SiC ceramic tribo-pairs, the lower friction coefficient and lower wear rate for the N⁺-SiC/SiC tribo-pairs were acquired.     

Near infrared spectroscopy of organic acids: comparing OH and CH oscillator frequencies and intensities

This work investigates the vibrational spectroscopy of a series of organic acids, CH₃(CH₂)_nCOOH (n = 1-5), previously unobserved in the IR and near-IR (2000-15 000 cm⁻¹). The work obtains frequencies and relative intensities for all OH and CH stretching transitions. Comparison of the frequencies and intensities of CH and OH stretching transitions reveal interesting trends in acid chain length that are discussed. Literature values for acetic acid (CH₃COOH) and formic acid (HCOOH) are used to gain a broader understanding for the spectroscopy of the organic acids CH₃(CH₂)_nCOOH. The observation of several combination bands involving the CH and OH stretching vibrations and possible rotational isomer and hot band transitions are reported.     

Ammonia adsorption and decomposition on silica supported Rh nanoparticles observed by in situ attenuated total reflection infrared spectroscopy

Attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) is applied to study NH₃, adsorbed from the gas phase, and its decomposition products, i.e. NH_x species, on Rh nanoparticles, produced by spincoating from a RhCl₃ solution in water followed by reduction. A silicon ATR crystal with a hydroxilated SiO₂ layer acts as the support for the nanoparticles. Upon exposure to NH₃ in the vacuum chamber, NH₃ adsorbed to both silica and Rh is detected (sensitivity ∼5 × 10⁻⁵ absorbance units). Interaction of the NH₃ with the silica OH groups is observed around ∼2840 cm⁻¹ in combination with peaks showing the disappearance of unperturbed OH vibrations between 3500 and 3700 cm⁻¹. In addition, NH bend vibrations at 1634 cm⁻¹ and NH stretch vibrations at 3065 and 3197 cm⁻¹ are observed for substrate temperatures between 20 and 100 °C. The latter two correspond to NH on Rh, as verified with a sample without Rh, and probably correspond to undecomposed NH₃. Moreover, they remain after evacuation, suggesting strongly bound species. For a substrate temperature of 75 and 100 °C, additional NH stretch peaks at 3354 and 3283 cm⁻¹ are observed, possibly due to NH₂ intermediates, indicating NH₃ decomposition. It is shown that ATR-FTIR can contribute to the sensitive detection of adsorption and decomposition of gaseous species on realistic planar model catalysts.     

UV assisted oxidation and nitridation of hafnia based thin films for alternate gate dielectric applications

The synergistic effects of NH₃ ambient and ultraviolet illumination on the dielectric properties of hafnia based gate dielectrics are reported in this paper. The films were processed at relatively low temperatures (∼400 °C) by pulsed laser ablation and UV oxidation technique. UV illumination and the NH₃ ambient created a thin and a denser interfacial layer (at the film-Si interface) comprised of HfSiON bonding. As a result of the interfacial layer modification, a leakage current density lower than 10⁻⁴ A/cm² and a dielectric constant of ∼21.7 were extracted from the best samples processed in NH₃ and under UV illumination. The nitrogen doped HfO₂ also exhibited a thinner interfacial layer (∼12 Å) in comparison to the films processed without NH₃ ambient.     

Hydrophobic and physical properties of the ambient pressure dried silica aerogels with sodium silicate precursor using various surface modification agents

The experimental results on the synthesis and physical properties of the ambient pressure dried hydrophobic silica aerogels in the presence of various surface modification (silylating) agents are presented. The silica aerogels were prepared with 1.12 specific gravity ion exchanged sodium silicate solution, 1N ammonium hydroxide, solvent exchanged with ethanol and hexane, and surface modification with 20% silylating agent in hexane followed by drying the modified gel up to 200 °C. The molar ratio of sodium silicate, water, ammonium hydroxide and silylating agent was kept at 1:45:4.3 × 10⁻²:5, respectively. The physical properties of the aerogels such as density, % of porosity, pore volume, thermal conductivity and contact angle measurements were studied by using various mono, di and tri alkyl or aryl silylating agents (SAs). The tri alkyl silylating agents produced low % of volume shrinkage (2%), low density (0.06 g/cm³), low refractive index (1.011), more pore volume (16.15cm³/g), high percentage of porosity (96.9%) and hydrophobic (contact angle >150°) silica aerogels. It was found from the Fourier transform infrared spectroscopic (FTIR) studies of the aerogels that the intensity of the bands related to the SiC and CH are more and the SiOH and OH are less with the tri than mono and di alkyl SAs. It was found from the TGA-DTA studies of the aerogels with increase in temperature above 325 °C, the % of weight decrease in TGA and exothermic peak in DTA are more with tri than the mono and di alkyl SAs. The SEM studies of the aerogels showed the large pore and particle sizes in the silica network with the tri alkyl SAs. The % of optical transmission of the aerogels is less with the tri alkyl SAs than the mono and di alkyl SAs. It was found from the contact angle and water adsorption studies that the hydrophobicity of the silica aerogel is more with tri alkyl than the di and mono alkyl silylating agents.     

Microwave and high resolution infrared spectra of vinyl chloride, ab initio anharmonic force field and equilibrium structure

The quadratic, cubic, and semi-diagonal quartic force field of vinyl chloride has been calculated at the MP2 level of theory employing a basis set of triple-ζ quality. The spectroscopic constants derived from this force field are compared with the experimental values. To make this comparison more complete, the rotational constants of the lowest excited state, v₉ = 1 at 395 cm⁻¹ have been determined by microwave spectroscopy and the ν₁₂ band (around 618 cm⁻¹) has been investigated by high-resolution infrared Fourier transform spectroscopy. The equilibrium structure has been derived from experimental ground state rotational constants and ab initio rovibrational interaction parameters. This semi-experimental structure is in excellent agreement with the ab initio structure calculated at the CCSD(T) level of theory using a basis set of quintuple-ζ quality and a core correlation correction. The experimental mass-dependent r_m structures are also determined and their accuracy is discussed. The recommended equilibrium geometry is: r (CC) = 1.3262(10), r (CCl) = 1.7263(10), r (CH_g) = 1.0784(10), r (CH_c) = 1.0795(10), r (CH_t) = 1.0797(10), ∠(CCCl) = 122.77(10)°, ∠(CCH_g) = 123.86(10)°, ∠(CCH_c) = 121.80(10)°, ∠(CCH_t) = 119.29(10)°.     

Ab initio studies of electronic spectra of the linear aluminum-bearing carbon chains AlC2nH (n = 1-5)

Geometries and stabilities of the linear aluminum-bearing carbon chains AlC_2nH (n = 1-5) in their ground states have been explored by the DFT-B3LYP and RCCSD(T) methods. Structures of the X¹Σ⁺ and 1¹Π electronic states have also been optimized by the CASSCF approach. The studies indicate that these species have single-triple bond alternate pattern, AlCCCC?CCH, and the electronic excitation from X¹Σ⁺ to 1¹Π leads to the shortening of the AlC bonds. The vertical excitation energies of the 1¹Π ← X¹Σ⁺ and 2¹Π ← X¹Σ⁺ transitions for AlC_2nH (n = 1-5) have been investigated by the CASPT2, EOM-CCSD, and TD-B3LYP levels of theory with the cc-pVTZ basis set, respectively. CASPT2-predicted 1¹Π ← X¹Σ⁺ transition energies are 3.57, 3.44, 3.33, 3.26, and 3.21 eV, respectively. For AlC₂H, our estimate agrees very well with the experimental value of 3.57 eV. In addition, the AlC bond dissociation energies and the exponential-decay curves for these vertical excitation energies are also discussed.     

Influence of thermal treatment of low dielectric constant SiOC(H) films using MTES/O2 deposited by PECVD

Low dielectric constant SiOC(H) films are deposited on p-type Si(100) substrates by plasma enhanced chemical vapor deposition (PECVD) using methyltriethoxysilane (MTES, C₇H₁₈O₃Si) and oxygen gas as precursors. The SiOC(H) films are deposited at room temperature, 100, 200, 300 and 400 °C and then annealed at 100, 200, 300 and 400 °C temperatures for 30 min in vacuum. The influence of deposition temperature and annealing on SiOC(H) films are investigated. Film thickness and refractive index are measured by field emission scanning electron microscopy and ellipsometry, respectively. Chemical bonding characteristics of as-deposited and annealed films are investigated by Fourier transform infrared (FTIR) spectroscopy in the absorbance mode. As more carbon atoms are incorporated into the SiOC(H) films, both film density and refractive index are decreased due to nano pore structure of the film. In the SiOC(H) film, CH₃ group as an end group is introduced into OSiO network, thereby reducing the density to decrease the dielectric constant thereof. The dielectric constant of SiOC(H) film is evaluated by C-V measurements using metal-insulator-semiconductor (MIS), Al/SiOC(H)/p-Si structure and it is found to be as low as 2.2 for annealed samples deposited at 400 °C.     

Chemical reaction of sputtered Cu film with PI modified by low energy reactive atomic beam

Polyimide (PMDA-ODA) surface was irradiated by low energy reactive atomic beam with energy 160-180 eV to enhance the adhesion with metal Cu film. O₂⁺ and N₂⁺ ions were irradiated at the fluence from 5 × 10¹⁵ to 1 × 10¹⁸ cm⁻². Wetting angle 78° of distilled deionized (DI) water for bare PI was greatly reduced down to 2-4° after critical ion flounce, and the surface energy was increased from 37 to 81.2 erg/cm. From the analysis of O 1s core-level XPS spectra, such improvement seemed to result from the increment of hydrophilic carbonyl oxygen content on modified PI surface. To see more carefully correlation of the peel strength with interfacial reaction between Cu and PI, flexible copper clad laminate with Cu (9 μm)/Cu (200 nm) on modified PI substrate (25 μm) was fabricated by successive sputtering and electroplating. Firstly, peel strength was measured by using t-test and it was largely increased from 0.2 to 0.5 kgf/cm for Ar⁺ only irradiated PI to 0.72-0.8 kgf/cm for O₂⁺ or N₂O⁺ irradiated PI. Chemical reaction at the interface was reasoned by analyzing C 1s, O 1s, N 1s, and Cu 2p core-level X-ray photoelectron spectroscopy over the as-cleaved Cu-side and PI side surface through depth profiling. From the C 1s spectra of cleaved Cu-side, by the electron transfer from Cu to carbonyl oxygen, carbonyl carbon atom became less positive and as a result shifted to lower binding energy not reaching the binding energy of C₂ and C₃. The binding energy shift of the peak C₄ as small as 1.7 eV indicates that carbonyl oxygen atoms were not completely broken. From the analysis of the O 1s spectra, it was found that new peak at 530.5 eV (O₃) was occurred and the increased area of the peak O₃ was almost the same with reduced area of the peak carbonyl oxygen peak O₁. Since there was no change in the relative intensity of ether oxygen (O₂) to carbonyl oxygen (O₁), and thus O₃ was believed to result from Cu oxide formation via a local bonding of Cu with carbonyl oxygen atoms. Moreover, from X-ray induced Auger emission spectra Cu LMM which was very sensitive to chemical bonding, Cu oxide or CuOC complex formation instead of CuNO complex was clearly identified by the observation of the peak at 570 eV at higher 2 eV than that of metal Cu. In conclusion, when Cu atoms were sputtered on modified PI by low energy ion beam irradiation, it can be suggested that two Cu atoms locally reacted with carbonyl oxygen in PMDA units and formed Cu⁺O⁻C complex linkage without being broken from carbon atoms and thus the chemically bound Cu was in the form of Cu₂O.     

Hydration of acetic acid and acetate ion in water studied by 1D-RISM theory

Structural and thermodynamic aspects of the hydration of acetic acid (CH₃COOH) and acetate ion (CH₃COO⁻) were studied with the 1D-RISM integral equation method. It was found that the average number of water molecules in the hydrophobic hydration shell of the CH₃ group is 8.9 for acetic acid and 10 for acetate. The average number of H-bonds formed by the COOH group is 2.5, whereas that of COO⁻ is 6, indicating that deprotonation of acetic acid leads to increased H-bonding of water molecules with the carboxylate moiety. This step involves significant reorientation of water molecules surrounding the carboxylic group. The hydration free energies and the aqueous ionization constant calculated with the set of semi-empirical corrections are in reasonable agreement with available experimental results.     

Low temperature catalytic performance of nanosized TiNiO for oxidative dehydrogenation of propane to propene

Nanosized TiNiO catalysts prepared by a modified sol-gel method have been investigated in the oxidative dehydrogenation of propane (ODP) to propene. At 300 °C the yield to propene of 12.1% was obtained on 9.1 wt.% TiNiO catalyst with the selectivity of 43%. The continued variety of lattice parameter and variation of chemical value of nickel and titanium ion on the surface indicates that there are strong interactions of TiO₂ and NiO. The decreased low temperature oxygen desorption and the weaker reducibility seems to be responsible for the decreased activity and enhanced selectivity of propane oxidative dehydrogenation over TiNiO catalysts.     

An XPS study of pulsed plasma polymerised allyl alcohol film growth on polyurethane

The growth of highly functionalised poly allyl alcohol films by pulsed plasma polymerisation of CH₂CHCH₂OH on biomedical grade polyurethane has been followed by X-ray photoelectron spectroscopy (XPS) and contact angle measurements. Film thickness is observed to increase approximately linearly with plasma modification time, suggesting a layer-by-layer growth mode of poly allyl alcohol. Water contact angle measurements reveal the change in the surface free energy of wetting decreases linearly with plasma modification up to the monolayer point after which a constant limiting value of −24 mJ m⁻² was attained. Films prepared at 20 W plasma power with a duty cycle of 10 μs:500 μs exhibit a high degree of hydroxyl (OH) retention with minimal fragmentation of the monomer observed. Increasing the plasma power up to 125 W is found to improve OH retention at the expense of ether formation generating films close to the monomer stoichiometry. Duty cycle plays an important role in controlling both film composition and thickness, with longer off times increasing OH retention, while longer on times enhance allyl alcohol film growth.     

Configuration dependence of photon stimulated ion desorption from methyl ester compounds induced by core excitation

Photon stimulated ion desorption (PSID) from methyl ester terminated self-assembled monolayer (MHDA-SAM, HS(CH₂)₁₅COOCH₃) and methyl mercaptoacetate (MA, HSCH₂COOCH₃) on Ag has been investigated using soft X-ray in the C and O K-edge regions. In MHDA-SAM on Ag, site-selective ion desorption has been clearly observed at resonant core excitations of C_1s, O_1s(OCH₃) → σ^∗(OCH₃) and O_1s(OCH₃) → σ^∗(COCH₃). Ion intensity in MA on Ag is obviously reduced for (n = 1-3) at C_1s, O_1s(OCH₃) → σ^∗(OCH₃) excitations, and no site-selective reaction at O_1s(OCH₃) → σ^∗(COCH₃) excitations has been observed. These reactions may be influenced by configurational difference of reactive sites. It is suggested that surface effects on the selective reaction due to positioning methyl ester group near the surface plays an important role.     

Rapid synthesis of water-glass based aerogels by in situ surface modification of the hydrogels

The objective of the present research was to reduce the processing time of water-glass based aerogels synthesized via an ambient pressure drying. For this purpose we employed a co-precursor method for the surface modification in hydrogels using trimethylchlorosilane (TMCS) and hexamethyldisilazane (HMDS). The surface modification resulted in the displacement of pore water from the hydrogels and thereby absolutely avoiding the time-consuming solvent exchange step. The attachment of trymethylsilyl (Si(CH₃)₃) groups to the silica surface was confirmed by the presence of SiCH₃ peaks at 2900, 1400, 1255 and 845 cm⁻¹ in the Fourier Transform Infrared (FTIR) spectra. The differential thermal analysis (DTA) revealed that the aerogels maintain their hydrophobic behavior up to a maximum temperature of 500 °C above which they become hydrophilic. The physical and textural properties of the silica aerogels have been reported and the results have been discussed by taking into account the surface modification and the amounts of the pore water displaced out from the hydrogels.