New π‐conjugated polyaryleneethynylenes containing a 1,3,5‐triazine unit in the main chain: Synthesis and optical and electrochemical properties

A series of new π‐conjugated poly(aryleneethynylene)s containing a 1,3,5‐triazine unit in the main chain were synthesized in yields higher than 70% by polycondensation between dibromophenyl‐1,3,5‐triazine monomers and alkyl‐substituted diethynylbenzene (or diethynylfluorene) comonomers with Pd(PPh₃)₄ and CuI as catalysts in the presence of triethylamine. The polymers had a number‐average molecular weight in the range of 5000–10,000 and showed good solubility in common organic solvents. The polymers were photoluminescent both in solutions and in the solid state. X‐ray diffraction patterns of the powders of the polymers revealed that the polymers were semicrystalline. Electrochemically, the polymers appeared to be reversible under reduction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3797–3806, 2006     

1‐(2,6‐dibenzhydryl‐4‐fluorophenylimino)‐2‐aryliminoacenaphthylylnickel halides highly polymerizing ethylene for the polyethylenes with high branches and molecular weights

A series of 1‐(2,6‐dibenzhydryl‐4‐fluorophenylimino)‐ 2‐aryliminoacenaphthylene derivatives ( L1–L5 ) and their halonickel complexes LNiX₂ (X = Br, Ni1–Ni5 ; X = Cl, Ni6–Ni10 ) are synthesized and well characterized. The molecular structures of representative complexes Ni2 and Ni4 are confirmed as the distorted tetrahedron geometry around nickel atom by the single crystal X‐ray diffraction. Upon activation with methylaluminoxane, all nickel complexes show high activities up to 1.49 × 10⁷ g of PE (mol of Ni)^?1 h^?1 toward ethylene polymerization, producing polyethylenes with high branches and molecular weights up to 1.62 × 10⁶ g mol^?1 as well as narrow polydispersity. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1369–1378     

Inclusion complexes of α‐cyclodextrin and (AB)n block copolymers

Cyclodextrins thread onto polymer chains to form inclusion complexes, especially when the polymer is hydrophobic relative to the solvent. Selective threading might occur when the polymer architecture contains both hydrophobic and hydrophilic segments. α‐Cyclodextrin formed crystalline inclusion complexes with (AB)_n microblock copolymers, where the A block was a linear alkyl segment containing a single double bond and the B block was an exact length segment of poly(ethylene oxide). The complexes were isolated and characterized by solution and solid‐state NMR, X‐ray diffraction, differential scanning calorimetry, and thermogravimetric analysis. Each method confirmed complex formation and showed that the physical properties of the complexes were distinct from those of its individual components. The X‐ray data were consistent with known inclusion complexes having a channel or column crystal structure. The stoichiometry of the complex formation, 2.3 α‐cyclodextrin rings per polymer repeat unit, was determined by NMR analysis of the complexes and from an analysis of the inclusion complex yields. The data suggest that the inclusion complex stoichiometry is defined by the increasing insolubility of the polymer–cyclodextrin complex. Solid‐state NMR data were consistent with a preference for threading onto hydrophobic segments of the (AB)_n polymer. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2731–2739, 2001     

Synthesis and characterization of stereoregular AABB‐type polymannaramides

The condensation of D ‐mannaro‐1,4:6,3‐dilactone ( 2 ) with even‐numbered alkylenediamines (C₂, C₆–C₁₂) in a methanol solution and in the presence of triethylamine afforded polymannaramides 3 – 7 , which were isolated directly as white solids with various hydrophobic–hydrophilic characters. Because all the stereocenters in 2 possessed an S configuration, the random polymerization led to optically active, stereoregular polyhydroxypolyamides. The polymers were characterized by elemental analysis and IR, ¹H NMR, and ¹³C NMR spectroscopy. Their number‐average molecular weights were estimated by ¹H NMR spectral integration analysis. Thermal and powder X‐ray diffraction studies revealed that compounds 3 – 7 were poorly crystalline. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1024–1030, 2001     

Regioregular poly[3‐(4‐alkoxyphenyl)thiophene]s

An easy synthetic procedure for soluble poly[3‐(4‐alcoxyphenyl)thiophene]s is reported. The polymers present a high regioregularity degree as determined by both UV–vis spectra and ¹H and ¹³C NMR analysis. Furthermore, X‐ray powder diffraction analysis performed on films of the polymers suggests a π‐stacked packing structure of the macromolecules. Electrical characterization was performed on one of the synthesized polythiophenes on both undoped and doped (with FeCl₃ or iodine) films. The conductivity and charge‐carrier mobility were assessed by current–voltage and field effect measurements. Well‐structured polymer films were obtained simply via spin coating from chloroform solutions and without the need of further processing, unlike other regioregular polythiophenes reported in the literature. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1758–1770, 2007     

Hydrogen‐bonded supramolecular polymers from derivatives of α‐amino‐ε‐caprolactam: A bio‐based material

Hydrogen‐bonded supramolecular polymers were prepared from the derivatives of α‐amino‐ε‐caprolactam (ACL), obtained from a renewable resource. Several self‐complimentary bis‐ or tetra‐caprolactam monomers were synthesized by varying the number of carbons of the spacer between the hydrogen‐bonding end groups. Physical properties of these hydrogen‐bonded polymers were clearly demonstrated by differential scanning colorimetry, solid‐state NMR, and X‐ray powder diffraction analyses. The supramolecular behavior was also supported by fiber formation from the melt for several of these compounds, and stable glassy materials were prepared from the physical mixtures of two different biscaprolactams. The self‐association ability of ACL was also used by incorporating ACL at the chain ends of low‐molecular weight Jeffamine (M_n = 900 g/mol) using urea and amide linkages. The transformation of this liquid oligomer at room temperature into a self‐standing, transparent film clearly showed the improvement in mechanical properties obtained by the introduction of terminal hydrogen‐bonding groups. Finally, the use of monomers with a functionality of four gave rise to network formation either alone or combination with bifunctional monomers. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Studies on the modification of poly(ω‐bromoalkyl‐1‐glycidylether)s with 4′‐methoxybiphenyl‐4‐oxy mesogenic groups

A series of poly[ω‐(4′‐methoxy‐biphenyl‐4‐oxy)alkyl‐1‐glycidylether]s were synthesized by chemically modifying the corresponding poly(ω‐bromoalkyl‐1‐glycidylether)s with the sodium salt of 4‐hydroxy‐4′‐methoxybiphenyl. New high‐molecular‐weight side‐chain liquid‐crystalline polymers were obtained with excellent yields and almost quantitative degrees of modification. They were all insoluble in THF and other common solvents. Characterization by ¹³C NMR confirmed that all the polymers had the expected structure. The liquid crystalline behavior of the polymers was analyzed by DSC and polarized optical microscopy, and mesophase assignments were confirmed by X‐ray diffraction studies. Polymers that had alkyl spacers with n = 2 and 4 were smectic C, those that had spacers with n = 6 and 8 were nematic cybotactic, and those that had longer spacers (n = 10 and 12) were smectic C again. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5998–6006, 2005     

Synthesis and Crystal Structure of [Nd(η6‐1, 3, 5‐C6H3Me3)‐(AlCl4)3](C6H6) and Structural Comparison of Ln(η6‐arene)‐(AlCl4)3

Reaction of Ndcl₃ with AlCl₃ and mesitylene in benzene gives complex [Nd(η⁶‐1, 3, 5‐C₆H₃Me₃)‐(AlCl₄)₃](C₆H₆) (1) which was characterized by elemental analysis, IR spectra, MS and X‐ray diffractions. The X‐ray determination indicates that 1 has a distorted pentagonal bipyramidal geometry and crystallizes in the monoclinic, space group P2₁/n with a = 0.9586(2), b = 1.1717(5), c = 2.8966(7) nm, β = 90.85 (2)°, V = 3.2529 (6) nm³,D_c= 1.573 g/cm³, Z = 4. A comparison of bond parameters for all the reported Ln (η⁶‐Ar) (AlCl₄)₃ complexes indicates that the bond distance of La? C is shortened with the increasing of methyl group on benzene and with the decreasing of radius of lanthanide ions.     

Salicylaldiminato nickel(II) catalysts with 5‐halo‐3‐methoxy groups for ethylene polymerization

Two neutral salicylaldiminato methyl pyridine nickel(II) complexes were synthesized and evaluated for ethylene polymerization. Each catalyst bears a methoxy group in the 3‐position and a halogen atom in the 5‐position of the salicyl ligand, chlorine in case of catalyst 3a and bromine in 3b . Molecular structures of the catalysts were obtained by X‐ray crystallography. The resulting polymerization activities, for example, indicated by a maximum turnover frequency of 4,870 mol ethylene/(mol Ni × h) for 1‐h runs obtained with 3a , were higher than those of similar catalysts at comparable conditions reported in the literature. Catalyst 3a was slightly more active than catalyst 3b . The polymers are branched as measured by ¹H NMR and ¹³C NMR. This was also reflected in the melting temperatures between 76 and 113 °C obtained by differential scanning calorimetry. By using gel permeation chromatography measurements, it was determined that the M_w of the polymers ranges between about 5,400 and 21,600 g/mol. In particular, the effect of the polymerization temperature on the catalyst activity, degree of branching, and molecular weight properties has been described. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Rigid‐rod polyamides and polyimides prepared from 4,3″‐diamino‐2′,6′‐di(2‐naphthyl)‐p‐terphenyl and 2′,6′,3‴,5‴‐tetra(2‐naphthyl)‐4,4″‐diamino‐p‐quinquephenyl

A series of rigid‐rod polyamides and polyimides containing p‐terphenyl or p‐quinquephenyl moieties in backbone as well as naphthyl pendent groups were synthesized from two new aromatic diamines. The polymers were characterized by inherent viscosity, elemental analysis, FT‐IR, ¹H‐NMR, ¹³C‐NMR, X‐ray, differential scanning calorimetry (DSC), thermomechanical analysis (TMA), thermal gravimetric analysis (TGA), isothermal gravimetric analysis, and moisture absorption. All polymers were amorphous and displayed T_g values at 304–337°C. Polyamides dissolved upon heating in polar aprotic solvents containing LiCl as well as CCl₃COOH, whereas polyimides were partially soluble in these solvents. No weight loss was observed up to 377–422°C in N₂ and 355–397°C in air. The anaerobic char yields were 57–69% at 800°C. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 15–24, 1999     

π‐conjugated polymers having diaza[12]annulene rings and aminopenta‐2,4‐dienylidene groups generated by the ring opening of pyridinium rings

Reactions of N‐(2,4‐dinitrophenyl)pyridinium chloride with 2,5‐dimethyl‐1,4‐phenylenediamine in 1:2, 1:1.5, 1:1, and 2:1 molar ratios caused the ring opening of the pyridinium ring and thereby yielded polymers ( P1 – P4 ) consisting of 5‐(2,5‐dimethyl‐1,4‐phenylene)penta‐2,4‐dienylideneammonium chloride (unit A) and N‐2,5‐dimethyl‐1,4‐phenylene diaza[12]annulenium dichloride (unit B). The ¹H NMR spectra suggested that the composition ratios of unit A to unit B in P1 – P4 were 0.98:0.02, 0.94:0.06, 0.81:0.19, and 0.79:0.21, respectively. P1 – P4 showed an absorption maximum (λ_max) at a longer wavelength than the monomers because of the expansion of the π‐conjugation system. Films of P3 and P4 showed λ_max at a considerably longer wavelength than those in solution, and this was attributable to the ordered structures of the polymers in the solid state. Powder X‐ray diffraction analysis supported the ordered structures of P3 and P4 . Pellets molded from P3 and P4 exhibited a metallic luster, whereas those from P1 and P2 did not show such a luster. Cyclic voltammetry measurements indicated that P1 – P4 were electrochemically active in films. The thermal stability of the polymers depended on the composition ratios of unit A to unit B. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1507–1514, 2007     

Vinyl‐terminated side‐chain liquid‐crystalline polyethers containing mesogenic benzylideneaniline moieties

The synthesis of two vinyl‐terminated side‐chain liquid‐crystalline polyethers containing benzylideneaniline moieties as mesogenic cores was approached in two different ways: by chemically modifying poly(epichlorohydrin) with suitable mesogenic acids or by polymerizing analogous glycidyl ester or glycidyl ether derivatives. In all the conditions tested, the first approach led to materials in which the imine group was hydrolyzed. The second approach led to the desired polymers PG2a and PG2b , but only from the glycidyl ether derivatives and when the initiator was the system that combined polyiminophosphazene base t‐Bu‐P₄ and 3,5‐di‐t‐butylphenol. These polymers were chemically characterized by IR and ¹H and ¹³C NMR spectroscopies. The estimated degrees of polymerization ranged from 30 to 36. The liquid crystalline behavior of the synthesized polymers was studied by differential scanning calorimetry, polarized optical microscopy (POM) and X‐ray diffraction. Both polymers behave like liquid crystals and exhibited a single mesophase, which was recognized as a smectic C mesophase, probably with a bilayer arrangement, i.e., a smectic C₂ mesophase. The crosslinking of both polymers was performed with dicumyl peroxide as initiator, which led to liquid crystalline thermosets. POM and X‐ray diffraction confirmed that the mesophase organization mantained on the crosslinked materials. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1877–1889, 2006     

Anomalous thermochromic transition of poly(di‐n‐octylsilane)

The thermochromic behavior of poly(di‐n‐octylsilane) {[Si(C₈H₁₇)₂]_n; PDOS} was studied by ultraviolet (UV) absorption, differential scanning calorimetry, and X‐ray diffraction measurements. The structure of PDOS in the low‐temperature phase strongly depended on not only the temperature but also the rate of cooling, that is, the thermal history. Temperature‐dependent UV absorption spectra were highly dependent on thermal hysteresis. Cooled rapidly (10 K/min), PDOS showed two absorption peaks at 3.32 and 3.51 eV in low‐temperature‐ordered phases, whereas a single absorption peak at 3.32 eV became predominant with slow cooling (0.3 K/min). The appearance of the two peaks at low temperatures suggested that a mixture of different conformations was introduced by rapid cooling. A fiber diffraction pattern measured at 240 K after rapid cooling also showed evidence of the existence of novel conformation. A temperature‐dependent powder X‐ray diffraction pattern changed significantly between 270 and 280 K. Rapid cooling reduced the intensity of the X‐ray diffraction peak in this temperature region. This intensity change was explained by the conformational mixture in the polymer. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 1085–1092, 2001     

Synthesis and properties of alternating copolyamide‐imides based on 2,6‐bis(4‐aminophenoxy)naphthalene and comparison with its related isomeric polymers

A series of novel polyamide‐imides III containing 2,6‐bis(phenoxy)naphthalene units were synthesized by 2,6‐bis(4‐aminophenoxy)naphthalene and various bis(trimellitimide)s in N‐methyl‐2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents through direct polycondensation. The polymers were obtained in quantitative yield with inherent viscosities up to 1.53 dL/g. Most of the polymers showed good solubility in NMP, N,N‐dimethylacetamide, N,N‐dimethylformamide, and dimethyl sulfoxide and could be solution‐cast into transparent, flexible, and tough films. The films had tensile strengths of 84–111 MPa, elongations at break of 8–33%, and initial moduli of 2.2–2.8 GPa. Wide‐angle X‐ray diffraction revealed that most polymers III were amorphous. The glass‐transition temperatures of some of the polymers could be determined by differential scanning calorimetry traces, recorded at 247–290 °C. The polyamide‐imides exhibited excellent thermal stabilities and had 10% weight loss at temperatures in the range of 501–575 °C under nitrogen atmosphere. They left more than 57% residue even at 800 °C in nitrogen. A comparative study of some corresponding polyamide‐imides is also presented. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2591–2601, 2001     

Aromatic poly(1,3,4‐oxadiazole)s and poly(amide‐1,3,4‐oxadiazole)s containing ether sulfone linkages

Polyhydrazides and poly(amide‐hydrazide)s were prepared from two ether‐sulfone‐dicarboxylic acids, 4,4′‐[sulfonylbis(1,4‐phenylene)dioxy]dibenzoic acid and 4,4′‐[sulfonylbis(2,6‐dimethyl‐1,4‐phenylene)dioxy]dibenzoic acid, or their diacyl chlorides with terephthalic dihydrazide, isophthalic dihydrazide, and p‐aminobenzhydrazide via a phosphorylation reaction or a low‐temperature solution polycondensation. All the hydrazide polymers were found to be amorphous according to X‐ray diffraction analysis. They were readily soluble in polar organic solvents such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylacetamide and could afford colorless, flexible, and tough films with good mechanical strengths via solvent casting. These hydrazide polymers exhibited glass‐transition temperatures of 149–207 °C and could be thermally cyclodehydrated into the corresponding oxadiazole polymers in the solid state at elevated temperatures. Although the oxadiazole polymers showed a significantly decreased solubility with respect to their hydrazide prepolymers, some oxadiazole polymers were still organosoluble. The thermally converted oxadiazole polymers had glass‐transition temperatures of 217–255 °C and softening temperatures of 215–268 °C and did not show significant weight loss before 400 °C in nitrogen or air. For a comparative study, related sulfonyl polymers without the ether groups were also synthesized from 4,4′‐sulfonyldibenzoic acid and the hydrazide monomers by the same synthetic routes. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2271–2286, 2001     

Stereospecific and molecular weight‐controlled polymerization of 1,3‐butadiene with Co(acac)3‐MAO catalyst

The polymerization of butadiene (Bd) with Co(acac)₃ in combination with methylaluminoxane (MAO) was investigated. The polymerization of Bd with Co(acac)₃‐MAO catalysts proceeded to give cis‐1,4 polymers (94 – 97%) bearing high molecular weights (40 × 10⁴) with relatively narrow molecular weight distributions (M_w's/M_n's). The molecular weight of the polymers increased linearly with the polymer yield, and the line passed through an original point. The polydispersities of the polymers kept almost constant during reaction time. This indicates that the microstructure and molecular weight of the polymers can be controlled in the polymerization of Bd with the Co(acac)₃‐MAO catalyst. The effects of reaction temperature, Bd concentration, and the MAO/Co molar ratio on the cis‐1,4 microstructure and high molecular weight polymer in the polymerization of Bd with Co(acac)₃‐MAO catalyst were observed. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2793–2798, 2001     

Air‐tolerantly surface‐initiated AGET ATRP mediated by iron catalyst from silica nanoparticles

Well‐defined polymer‐nanoparticle hybrids were prepared by a newly reported method: atom transfer radical polymerization using activators generated by electron transfer (AGET ATRP) mediated by iron catalyst. The kinetics of the surface‐initiated AGET ATRP of methyl methacrylate from the silica nanoparticles, which was mediated by FeCl₃/triphenylphosphine as a catalyst complex, ascorbic acid as a reducing agent, N,N‐dimethylformamide as the solvent in the presence of a “sacrificial” (free) initiator, was studied. Both the free and grafted polymers were grown in a control manner. The chemical composition of the nanocomposites was characterized by Fourier transform infrared spectroscopy, X‐ray photoelectron spectroscopy, and ¹H nuclear magnetic resonance spectroscopy. Thermogravimetric analysis was used to estimate the content of the grafted organic compound, and transmission electron micrographs was used to observe the core‐shell structure of the hybrid nanoparticles. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2006–2015, 2010     

Structure and morphology of the aliphatic polyester poly(δ‐valerolactone) in solution‐grown,chain‐folded lamellar crystals

Poly(δ‐valerolactone) (PVL) crystals in the form of chain‐folded lamellae were prepared by isothermal crystallization from a 2‐methylbutane‐2‐ol solution. Wide‐angle and small‐angle X‐ray diffraction data, obtained from PVL lamellae sedimented to form oriented mats, were supplemented with morphological and structural data from electron microscopy, both imaging and diffraction. The diffraction signals index on an orthorhombic unit cell with the parameters a = 0.747 ± 0.002 nm, b = 0.502 ± 0.002 nm, and c (chain axis) = 0.742 ± 0.002 nm. Similar unit cell parameters were obtained from crystals grown from 1‐octanol and also from drawn melt‐pressed films. The evidence supports a model containing two antiparallel chain segments in the unit cell. The c value of 0.742 nm is appropriate for an all‐trans or onefold helical backbone conformation for the straight stems. Possible slight perturbations at the ester units from the all‐trans backbone conformation are discussed. Computerized modeling was used to optimize the adjacent‐reentry folded structure. The setting angles, with respect to the a axis, are ±58° for the corner and center chains. The lamellae are 7.26 ± 0.05 nm thick, and the chains run orthogonal to the lamellar surface. The chains fold in the diagonal (110) and (11¯0) planes in an alternating fashion. The X‐ray diffraction data suggest that a proportion of adjacent paired antiparallel entities, or hairpin units, are c‐axis‐sheared, and a relationship to the results obtained from drawn films is discussed. A brief comparison is also made with related polymer structures. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2622–2634, 2001     

Preparation of novel poly(ethylene oxide‐co‐glycidol)‐graft‐poly(ε‐caprolactone) copolymers and inclusion complexation of the grafted chains with α‐cyclodextrin

A well‐defined comblike copolymer of poly(ethylene oxide‐co‐glycidol) [(poly(EO‐co‐Gly)] as the main chain and poly(ε‐caprolactone) (PCL) as the side chain was successfully prepared by the combination of anionic polymerization and ring‐opening polymerization. The glycidol was protected by ethyl vinyl ether to form 2,3‐epoxypropyl‐1‐ethoxyethyl ether (EPEE) first, and then ethylene oxide was copolymerized with EPEE by an anionic mechanism. The EPEE segments of the copolymer were deprotected by formic acid, and the glycidol segments of the copolymers were recovered after saponification. Poly(EO‐co‐Gly) with multihydroxyls was used further to initiate the ring‐opening polymerization of ε‐caprolactone in the presence of stannous octoate. When the grafted copolymer was mixed with α‐cyclodextrin, crystalline inclusion complexes (ICs) were formed, and the intermediate and final products, poly(ethylene oxide‐co‐glycidol)‐graft‐poly(ε‐caprolactone) and ICs, were characterized with gel permeation chromatography, NMR, differential scanning calorimetry, X‐ray diffraction, and thermogravimetric analysis in detail. The obtained ICs had a channel‐type crystalline structure, and the ratio of ε‐caprolactone units to α‐cyclodextrin for the ICs was higher than 1:1. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3684–3691, 2006     

Differential scanning calorimetry,small‐angle X‐ray scattering,and wide‐angle X‐ray scattering on homogeneous and heterogeneous ethylene‐α‐copolymers

The objective of this work was to use both X‐ray and differential scanning calorimetry techniques in a comparative study of the lamellar and crystalline structures of heterogeneous and homogeneous ethylene‐α‐copolymers. The samples differed in the comonomer type (1‐butene, 1‐hexene, 1‐octene, and hexadecene), comonomer content, and catalyst used in the polymerizations. Step crystallizations were performed with differential scanning calorimetry, and the crystallinity and lamellar thicknesses of the different crystal populations were determined. Wide‐angle X‐ray scattering was used to determine crystallinities, average sizes of the crystallites, and dimensions of the orthorhombic unit cell. The average thickness, separation of the lamellae, and volume fractions of the crystalline phase were determined by small‐angle X‐ray scattering (SAXS). The results revealed that at densities below 900 kg/m³, polymers were organized as poorly organized crystal bundles. The lamellar distances were smaller and the lamellar thickness distributions were narrower for the homogeneous ethylene copolymers than for the heterogeneous ones. Step‐crystallization experiments by SAXS demonstrated that the long period increased after annealing. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 1860–1875, 2001