Long‐term stability of an ambient self‐curable latex based on colloidal dispersions in water of two reactive polymers

An ambient self‐curable latex (ASCL) was prepared via the blending of colloidal dispersions in water of a chloromethylstyrene‐functionalized copolymer and a tertiary‐amine‐functionalized copolymer. Upon casting and drying under ambient conditions, the ASCL could generate crosslinked continuous polymer films. The crosslinking occurred via the Menschutkin reaction (quaternization) between the two types of functional groups. Because this reaction was reversible at high temperatures, the films could be decrosslinked and hence were self‐curable. The prepared ASCL exhibited excellent colloidal and chemical stability during long‐term storage: no significant changes in the colloidal properties, such as the particle size, electrophoretic mobility, and crosslinking reactivity, were observed after 48 months of storage. The electrophoretic measurements indicated that the electrostatic repulsion between the negatively charged particles of the ASCL was responsible for the excellent stability. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2598–2605, 2005     

Emulsion procedures for thermally reversible covalent crosslinking of polymers

Quaternization and dequaternization of tertiary amine compounds were employed to obtain thermally reversible ionene networks from aqueous colloidal polymer dispersions prepared via emulsion polymerization. Chlorine‐functionalized polymers prepared via the emulsion copolymerization of styrene (St), butylacrylate (BA), or both with chloromethylstyrene, and amino‐functionalized polymers prepared via the emulsion copolymerization of St, BA, or both with 2‐(dimethylamino)ethylacrylate or 4‐vinylpyridine, were reacted without polymer separation, with a ditertiaryamine crosslinker and a dihalide crosslinker, respectively, to obtain crosslinked polymers. Crosslinked polymers were also obtained via the reaction of a chlorine‐functionalized polymer dispersion with an amino‐functionalized polymer dispersion or via the drying of the polymer blend prepared from the two kinds of dispersions. Reactive solubility experiments, flowability investigations (by thermocompression at ca. 215 °C), IR, and ¹H NMR analyses of the obtained crosslinked polymers indicated that the generated ionene bridges dequaternized on heating and requaternized on cooling. In comparison with solution crosslinking, no organic solvent was employed, and simple procedures were required for the preparation of the thermally reversible covalent crosslinked polymers. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 4373–4384, 2000     

Toughening of nylon‐6 with epoxy‐functionalized acrylonitrile‐butadiene‐styrene copolymer

Glycidyl methacrylate (GMA) functionalized acrylonitrile‐butadiene‐styrene (ABS) copolymers have been prepared via an emulsion polymerization process. The epoxy‐functionalized ABS (e‐ABS) particles were used to toughen nylon‐6. Molau tests and FTIR results showed the reactions between nylon‐6 and e‐ABS have taken place. Scanning electron microscopy (SEM) displayed the compatibilization reaction between epoxy groups of e‐ABS and nylon‐6 chain ends (amine or carboxyl groups), which improve disperse morphology of e‐ABS in the nylon‐6 matrix. The presence of only a small amount of GMA (1 wt %) within the e‐ABS copolymer was sufficient to induce a pronounced improvement of the impact strength of nylon‐6 blends; whereas further increase of the GMA contents in e‐ABS resulted in lower impact strength because of the crosslinking reaction between nylon‐6 and e‐ABS, resulting in agglomeration of the ABS particles. SEM results showed shear yielding of the nylon‐6 matrix and cavitation of rubber particles were the major toughening mechanisms. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2170–2180, 2005     

Surface functionalization of polymer latex particles. I. Catalytic oxidation of poly(methylstyrene) latex particles in the presence of an anionic surfactant

A facile synthesis of functionalized poly[3(4)-methylstyrene] (PMS) latex particles containing aldehyde and carboxylic acid groups was achieved via an emulsion polymerization of 3(4)-methylstyrene in the presence of sodium dodecyl sulfonate, followed by an in-situ oxidation catalyzed by copper(II) chloride and t-butyl hydroperoxide (t-BuOOH) in the presence of t-butyl alcohol (t-BuOH). The structure of the anionic surfactant, metal catalyst, organic solvent, oxidant, and their concentrations strongly affected the rate of oxidation and the stability of the emulsion. The average size of the polymer latex particles was found to increase after oxidation, and the polymer was slightly crosslinked. A free-radical mechanism is proposed involving metal-catalyzed decomposition of t-BuOOH and benzylic oxidation. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 1863–1872, 1997     

The effect of different stabilizers on the formation of self‐assembled porous film via the breath‐figure technique

The Breath‐Figure technique was employed to imprint honeycomb structures in the polymer films via the condensation of water vapor on the surface of an evaporating polymer solution. Generally, the condensed water droplets can be stabilized by an end‐functional polymer or by particles added to the polymer solution. In this study, we carried out a systematic experiment on the effect of different stabilizers on the porous honeycomb structure under identical physical conditions. The end‐functional polymer produced a large area of regular spherical bubbles, whereas adding particles to the polymer solution leads to smaller arrays of the flattened bottom bubbles. The separation length between pores was larger for polymer/particle sample than that of the end‐functional polymer films. In the regular area of polymer/particle film many bubbles were not decorated by particles. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 49: 1430–1436, 2011     

In‐line monitoring of immiscible polymer blends in a rheometer with a fiber‐optics‐assisted fluorescence detection system

In‐line studies of the initial stages of shear‐induced coalescence in two‐phase polymer blends were carried out with a home‐built device combining a cone and plate rheometer and a fiber‐optic‐assisted fluorescence detection system. A blend of 90 wt % poly(2‐ethylhexyl methacrylate) (PEHMA) and 10 wt % poly(butyl methacrylate) (PBMA) was prepared by the casting of films onto a solid substrate from mixed aqueous latex dispersions of the two polymers. The dispersions were prepared via emulsion polymerization under conditions in which both components were formed as spherical particles with a very narrow size distribution. By using a 14:1 particle ratio of PEHMA to PBMA, we obtained films in which 120‐nm PBMA particles were surrounded by a PEHMA matrix. The blend contained phenanthrene‐labeled PBMA particles and anthracene‐labeled PBMA particles in a ratio of 4:1, whereas the PEHMA matrix polymer was unlabeled. We monitored the anthracene‐to‐phenanthrene fluorescence intensity ratio (I₄₇₀/I₃₆₀) as a measure of direct nonradiative energy transfer from phenanthrene to anthracene, whereas the blend was sheared at different shear rates and temperatures. Under no‐shear conditions, the results of in‐line experiments were in good agreement with the results of off‐line measurements of energy transfer by conventional techniques. In blends under shear, the two sets of experiments, in‐line and off‐line, did not agree with each other. The cause of this disagreement was associated with normal forces in the blend under shear that affected the optical path length and the relative intensities of the fluorescence signals of the phenanthrene and anthracene groups in the blend. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2302–2316, 2001     

Synthesis of a thermoresponsive shell‐crosslinked 3‐layer onion‐like polymer particle with a hyperbranched polyglycerol core

A novel thermoresponsive shell crosslinked three‐layer onion‐like polymer particles were prepared using hyperbranched polyglycerol (PG) as parents compound, the periphery hydroxyl groups of PG were transformed into trithiocarbonates (? SC(S)S? ) first; then, it was used as chain transfer agent to prepare star‐like block copolymer of N‐isopropyl acrylamide (NIPA) and N,N‐dimethylaminoethyl acrylate (DMA) in sequence via reversible addition fragmentation chain transfer (RAFT) process. Thus, a three‐layer polymer, PG? [SC(S)S? (DMA)? b? (NIPA)]_n, was obtained. The middle layer of poly(DMA) was then crosslinked with 1,8‐diiodoctane, and the resulting onion‐like three‐layer polymer showed a lower critical solution temperature (LCST) in water because of the outer layer of poly(NIPA). The LCST value only slightly depended on the crosslinking degree. Finally, the ? SC(S)S? were transformed into thiols by sequential treating with sodium borohydride and formic acid; thus, the core molecule was chemically detached from the crosslinked shell and a novel shell crosslinked polymer particle was obtained. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5652–5660, 2005     

Modular synthesis of functional polymer nanoparticles from a versatile platform based on poly(pentafluorophenylmethacrylate)

Control of functionalities in polymer nanoparticles (PNPs) is important for their application. Thus, there is an interest for well‐defined nanoparticle platforms to which desired functions could readily, and in modular fashion, be imparted. Herein, we report an amine‐reactive PNP platform for the modular synthesis of functional PNPs from poly(pentafluorophenylmethacrylate) (poly(PFPMA)) through a simple substitution/nanoprecipitation/photo‐crosslinking strategy. Substitution of amine containing coumarin into poly(PFPMA) allows for the achievement of structural stability of nanoprecipitated particles through photo‐crosslinking after nanoprecipitation, making it possible to carry out subsequent chemical transformations in organic solvents if needed. We demonstrate that various small molecules and an amine‐terminated polymer could be used to modify the crosslinked PNPs to endow them with various functions including fluorescence and responsiveness to temperature changes. The functional PNPs were characterized with variable temperature dynamic light scattering (DLS), UV–vis, and photoluminescence (PL) spectroscopy, and transmission electron microscopy (TEM). © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1895–1901     

Dispersion copolymerization of 2‐ethylhexyl methacrylate and vinylbenzyl chloride and functional group conversions in a fluorinated solvent using microwave heating

Conventional and microwave heating were compared for free radical dispersion polymerizations of crosslinked copolymers of 2‐ethylhexyl methacrylate, vinylbenzyl chloride (VBC), and fluoroalkyl methacryate monomers in the solvent nonafluorobutyl ethyl ether, and for the functional conversion of the VBC units of the copolymer particles with trimethylamine to quaternary ammonium chloride units. By conventional heating, all polymerizations produced foamy coagulated products consisting of primary spherical particles 1–2 μm in diameter. Microwave heating using poly(1H,1H‐dihydroperfluorooctyl acrylate) as a stabilizer gave faster polymerization and stable dispersions of discrete 1 μm particles. Microwave heating also gave faster reactions of the copolymers with trimethylamine to produce quaternary ammonium chloride functionalized colloidal particles. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3813–3819, 2008     

Nanostructured latexes made by a sequential multistage emulsion polymerization

A series of linear and lightly crosslinked nanostructured latices was prepared by a sequential multistage semicontinuous emulsion polymerization process alternating styrene (S) and n‐butyl acrylate (BA) monomer feeds five times, that is ten stages, and vice versa, along with several control latices. Transmission electron micrographs of the RuO₄‐stained cross sections of nanostructured and copolymer latex particles and films showed that their particle morphologies were not very different from each other, but the nanostructured latex particles were transformed into a nanocomposite film containing both polystyrene (PS) and poly(n‐butyl acrylate) (PBA) nanodomains interconnected by their diffuse polymer mixtures (i.e. interlayers). The thermal mechanical behaviors of the nanostructured latex films showed broad but single T_gs slightly higher than those of their counterpart copolymer films. These single T_gs indicated that their major component phases were the diffuse interlayers and that they behaved like pseudopolymer alloys. The minimum film formation temperatures of nanostructured latices capped with PBA and PS, respectively, were 15 °C lower than and equal to those of their counterpart copolymer latices, but their T_gs were about 10 °C higher. Consequently, nanostructured latices enabled us to combine good film formation with high strengths for adhesives and coatings applications. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2826–2836, 2006     

Nitroxide‐mediated radical polymerization of 2‐(dimethylamino)ethyl acrylate and its sequential block copolymerization with styrene and N‐butyl acrylate

Nitroxide‐mediated radical polymerization (NMRP) of 2‐(dimethylamino)ethyl acrylate (DMAEA) was carried out at 100–120 °C, initiated by MONAMS, an alkoxyamine based on N‐tert‐butyl‐N‐(1‐diethyl phosphono‐2,2‐dimethylpropyl)nitroxide, SG1. Controlled polymerization can be achieved by the addition of free SG1 (the initial molar ratio of SG1 to MONAMS ranged from 0.06 to 0.12), giving a linear first‐order kinetic plot up to 55–70% conversion depending on the reaction conditions. The molecular weights show a near linear increase with conversion; however, they deviate to some extent with theoretical values. SG1‐mediated polymerization of DMAEA at 112 °C is also controlled in organic solvents (N,N‐dimethylformide, anisole, xylene). Polymerization rate increases with increasing solvent polarity. Chain transfer to polymer produces ～1 mol % branches in bulk and 1.2–1.9 mol % in organic solvents, typical of those for acrylates. From poly(styrene) (pS) and poly(n‐butyl acrylate) (pBA) macroinitiators, amphiphilic di‐ and triblock copolymers p(S‐b‐DMAEA), p(DMAEA‐b‐S‐b‐DMAEA), p(BA‐b‐DMAEA), and p(DMAEA‐b‐BA‐b‐DMAEA) were synthesized via NMRP at 110 °C. Polymers were characterized by GPC, NMR, surface tension measurements, and DSC. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 414–426, 2006     

Polymer coating of carboxylic acid functionalized multiwalled carbon nanotubes via reversible addition‐fragmentation chain transfer mediated emulsion polymerization

In this work, successful polymer coating of COOH‐functionalized multiwalled carbon nanotubes (MWCNTs) via reversible addition fragmentation chain transfer (RAFT) mediated emulsion polymerization is reported. The method used amphiphilic macro‐RAFT copolymers as stabilizers for MWCNT dispersions, followed by their subsequent coating with poly(methyl methacrylate‐co‐butyl acrylate). Poly(allylamine hydrochloride) was initially used to change the charge on the surface of the MWCNTs to facilitate adsorption of negatively charged macro‐RAFT copolymer onto their surface via electrostatic interactions. After polymerization, the resultant latex was found to contain uniform polymer‐coated MWCNTs where polymer layer thickness could be controlled by the amount of monomer fed into the reaction. The polymer‐coated MWCNTs were demonstrated to be dispersible in both polar and nonpolar solvents. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Self-compatibilization of polymer blends prepared via functionalized concentrated emulsion polymerization

Two “functionalized” concentrated emulsions in water were prepared separately, one from a weakly polymerized mixture of styrene (S) and a small amount of acrylic acid (AA) and the other from a mixture of butyl acrylate (or butyl methacrylate) and a small amount of glycidyl methacrylate (GMA). After the two concentrated emulsions were polymerized partially, they were mixed and subjected to complete polymerization. During the latter polymerization, reactions between the carboxyl groups of the AA moieties of the S/AA copolymer and the glycidyl groups of the GMA-containing copolymer occurred, and copolymers and crosslinked structures were generated that constituted the compatibilizers of the system. The blend materials thus obtained possessed excellent toughness compared to those without functional groups. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 4233–4240, 1999     

Synthesis,surface properties,and morphologies of poly[methyl(3,3,3‐trifluoropropyl)siloxane]‐b‐polystyrene‐b‐poly(tert‐butyl acrylate) triblock copolymers by a combination of anionic ROP and ATRP

A series of well‐defined poly[methyl(3,3,3‐trifluoropropyl)siloxane]‐b‐polystyrene‐b‐poly(tert‐butyl acrylate) (PMTFPS‐b‐PS‐b‐PtBA) triblock copolymers were prepared by a combination of anionic ring‐opening polymerization of 1,3,5‐trimethyl‐1,3,5‐tris(3′,3′,3′‐trifluoropropyl)cyclotrisiloxane (F₃), and atom transfer radical polymerization (ATRP) of styrene (St) and tert‐butyl acrylate (tBA), using the obtained α‐bromoisobutyryl‐terminal PMTFPS (PMTFPS‐Br) as the macroinitiators. The ATRP of St from PMTFPS‐Br, as well as the ATRP of tBA from the obtained PMTFPS‐b‐PS‐Br macroinitiators, has typical characteristic of controlled/living polymerization. The results of contact angle measurements for the films of PMTFPS‐b‐PS‐b‐PtBA triblock copolymers demonstrate that the compositions have an effect on the wetting behavior of the copolymer films. For the copolymer films with different compositions, there may be different macroscale or nanoscale structures on the outmost layer of the copolymer surfaces. The films with high content of PtBA blocks exhibit almost no ordered microstructures on the outmost layer of the copolymer surfaces, even though they have microphase‐separated structures in bulk. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Dendrimers in thiol‐ene crosslinked networks and the effect of subsequent generations on thermoset properties

A series of well‐defined allyl‐ether functionalized polyester dendrimers has been synthesized via the divergent approach using traditional esterification reactions. Two commercially available trifunctional thiols, trimethylolpropane tri(3‐mercaptopropanoate) (TRIS) and ethoxylated trimethylolpropane tri(3‐mercaptopropanoate) (ETTMP), were incorporated with the dendrimers into the thiol‐ene polymer networks. The thiol‐ene reactions were conducted at room temperature and cured by UV light without the addition of photoinitiatior. Highly crosslinked films were obtained and characterized with respect to mechanical (DMA) and thermal (DSC and TGA) properties. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 589–601, 2009     

New preparative procedure for photoluminescent metallopolymers having a biphenyl‐2,2′‐diyl iridium(III) unit bound to a phosphine copolymer ligand

We first prepared polymer‐bound photoluminescent iridium complexes bearing a cyclometalated 2,2′‐biphenylene ligand via an easy procedure in which the metallopolymer was synthesized by the reaction of a metal precursor with a polymer ligand. The iridium compound, [Ir(cod)(biph)Cl]₂ (where cod and biph are 1,5‐cyclooctadiene and biphenyl‐2,2′‐diyl, respectively), was used as the iridium material, and a copolymer built by the radical copolymerization of 4‐styryldiphenylphosphine and methyl methacrylate was employed as the polymer ligand. The obtained metallopolymers were highly crosslinked by iridium atoms forming P? Ir? P bonds. The content of the iridium was experimentally clarified to be in the range of 0.06–0.6 mmol/g of the polymer. Photoluminescence of the iridium polymer in the solid state was observed at 597 nm when the polymer was irradiated at 350 nm. As the Ir content in the copolymer increased to 0.2 mmol/g, the intensity of the luminescence also increased, but more iridium content decreased the intensity. Furthermore, the intensity of the photoluminescence in these photoluminescent polymers depended on the molecular weight of the copolymer ligands. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4204–4213, 2006     

Heterograft copolymers via double click reactions using one‐pot technique

The double click reactions (Cu catalyzed Huisgen and Diels–Alder reactions) were used as a new strategy for the preparation of well‐defined heterograft copolymers in one‐pot technique. The synthetic strategy to the various stages of this work is outlined: (i) preparing random copolymers of styrene (St) and p‐chloromethylstyrene (CMS) (which is a functionalizable monomer) via nitroxide mediated radical polymerization (NMP); (ii) attachment of anthracene functionality to the preformed copolymer by the o‐etherification procedure and then conversion of the remaining ? CH₂Cl into azide functionality; (iii) by using double click reactions in one‐pot technique, maleimide end‐functionalized poly(methyl methacrylate) (PMMA‐MI) via atom transfer radical polymerization (ATRP) of MMA and alkyne end‐functionalized poly (ethylene glycol) (PEG‐alkyne) were introduced onto the copolymer bearing pendant anthryl and azide moieties. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 6969–6977, 2008     

UV‐induced crosslinking of ring opening metathesis block copolymer micelles

Statistical and amphiphilic block copolymers bearing cinnamoyl groups were prepared by ring opening metathesis polymerization (ROMP). The UV‐induced [2 + 2] cycloaddition reaction of polymer bound cinnamic acid groups was studied in polymer thin films as well as in block copolymer micelles. In both cases, exposure to UV‐light for 10 min led to a crosslinking conversion of about 60%, as determined by FT‐IR spectroscopy and UV–vis absorption measurements. Time based IR‐spectroscopy revealed a maximum conversion of 78% reached after an irradiation time of about 16 min. For micelles obtained from polymers bearing 5 mol % or more cinnamoyl groups, the crosslinking reaction proceeded smoothly, yielding in crosslinked particles which were stable in a non‐selective solvent (CHCl₃). Diameters determined by dynamic light scattering in the selective solvent (MeOH) were similar for both, non‐crosslinked and crosslinked micelles, whereas diameters of crosslinked micelles in the non‐selective solvent (CHCl₃) were significantly larger compared to MeOH samples. This strategy of direct self assembly of block‐copolymers in a selective solvent followed by “clean” crosslinking, without the need for additional crosslinking reagents or crosslinking initiators, provides a straight forward approach toward ROMP‐based polymeric nano‐particles. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2402–2413, 2008     

Polymer coating of graphene oxide via reversible addition–fragmentation chain transfer mediated emulsion polymerization

This work describes a versatile method to encapsulate graphene oxide (GO) with polymers using reversible addition‐fragmentation chain transfer (RAFT) mediated emulsion polymerization. A living low molecular weight anionic macro‐RAFT statistical copolymer of sodium styrene sulfonate, acrylic acid, and butyl acrylate (BA) was synthesized using 2‐{[(butylsulfanyl)carbonothioyl] sulfanyl} propanoic acid as the chain transfer agent. GO was dispersed in water by pretreating the surface with poly(allylamine hydrochloride) (PAH), before being stabilized by the addition of the anionic macro‐RAFT copolymer. PAH was used to facilitate the adsorption of the macro‐RAFT copolymer to the GO surface via electrostatic attraction between opposite charges. The dispersed GO sheets were encapsulated with polymer by the free radical emulsion polymerization of methyl methacrylate and BA under starved fed conditions. The polymer shells encapsulating the GO sheets were formed by the chain extension of the adsorbed living macro‐RAFT copolymer. TEM, SEM, FTIR, and AFM were used to confirm the presence of the polymer layer on the surface of the GO. The thickness of the polymer coating can be adjusted by controlling the amount of monomer fed into the system. Partial polymer coatings of the GO could be achieved by varying the amount of PAH. The encapsulated GO was found to be easily dispersed in both aqueous and organic solvents over a range of polarities. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1413–1421     

Carbosilane/carbosiloxane‐based ADMET homopolymers and copolymers possessing latent reactivity

Reactive methoxy‐functionalized carbosilane and carbosiloxane dienes can be either homopolymerized or copolymerized via acyclic diene metathesis (ADMET) polycondensation chemistry to produce reactive materials with mechanical behavior dependent on the molar ratios of the comonomers. The methoxy‐functional group within the polycarbosilane repeat unit remains inert during the metathesis polymerization and can be triggered subsequently with water to generate crosslinks between polymer chains. In this way, linear, thermoplastic copolymers can be prepared with ADMET chemistry and converted into crosslinked, thermoset copolymers upon exposure to moisture. Crosslinked films containing 5–10% of the crosslinked hard segment are soft and flexible materials. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1544–1550, 2000