甲烷氧化偶联锂/氧化镁催化剂和纳米催化剂

The Li/MgO catalyst and nanocatalyst were prepared by the incipient wetness impregnation and sol-gel method, respectively. The catalytic performance of the Li/MgO catalyst and nanocatalyst on oxidative coupling of methane was compared. The catalysts prepared in two ways were characterized by X-ray powder diffraction, Brunauer-Emmett-Teller surface and transmission electron microscope. The catalyst was tested at temperature of 973-1073 K with constant total pressure of 101 kPa. Experimental results showed that Li/MgO nanocatalyst in the oxidative coupling of methane would result in higher conversion of methane, higher selectivity, and higher yield of main products (ethane and ethylene) compared to ordinary catalyst. The results show the improved influence of nanoscale Li/MgO catalyst performance on oxidative coupling of methane.     

Pt/ZnO催化剂的电导研究

鉴于Pt/TiO_2等负载型过渡金属催化剂经500℃高温氢处理后有一系列特殊的化学行为和物理性质的变化(称为金属担体强相互作用或SMSI),因此研究负载型催化剂在氢中或其他气氛中的电导性质具有重要意义.用电导法曾检验出在不同温度下氢处理的Pt/TiO_2中有晶间氢和结构氢.本文测定了Pt/ZnO催化剂在室温和高温(≥300℃)下氢处理时的电导.发现在室温下Pt/ZnO暴露于H_2中,电导率瞬间增加6个数量级,经抽空或用N_2置换氢后,电导基本上回到原来值,表明在室温下,氢在Pt/ZnO上可发生氢     

Co-Cu/SiO2催化剂的表征

用溶胶-凝胶法制备了Co-Cu/SiO2系列的担载型催化剂,采用SBET、TPR、XRD、O2滴定等技术对该催化剂进行了研究,并考察了催化剂在F-T合成反应中的催化性能.结果表明,样品的SBET较大,Co和Cu组分均很好分散;Cu2+的加入使得Co更易于被氢气还原,Co是经由Co3+→Co2+→Co0的还原过程,Cu的还原为Cu2+→Cu0;Cu2+的引入使得样品中钴的还原度增大,对F-T合成的催化性能有了一定的改善.     

PEMFC催化剂的研究：自制Pt/C电催化剂的性质

研究了一种用于质子交换膜燃料电池(PEMFC)的自制Pt/C电催化剂(标记为THYT-1)的物理化学和电化学性质.将THYT-1电催化剂与E-TEK公司的同类电催化剂的组成、形态及电催化性能进行了比较.单电池测试结果显示, THYT-1的电催化性能优于E-TEK电催化剂. CV测试结果表明CO在这两种电催化剂上的电氧化性能相近；TEM分析表明两种催化剂上Pt晶粒在炭载体上呈均匀分布，平均粒径均为2～3 nm； XPS和XRD测试结果表明两种催化剂中Pt主要以金属态存在.这些数据表明THYT-1催化剂的物理化学性质与E-TEK公司的相类似.     

Pd/Ce/Al/蜂窝陶瓷催化剂制备方法的研究

本文应用溶胶－凝胶技术对蜂窝陶瓷表面进行涂层,然后负载活性组分,以CO氧化作模型反应,考察了催化剂干燥方法,浸涂原液类型以及助剂CeO2对汽车尾气净化催化剂活性的影响,并应用TPR、XPS等手段对其进行表征,由催化剂活性测试结果表明,干燥方法对催化剂活性影响不大,加入分散剂的氧化铝溶胶作浸渍原液的催化活性最高,同时活性评价实验结果还表明,加入CeO2作助剂的催化剂的活性明显提高,这可能是由于PdO与CeO2之间发生的协同效应所致,XPS谱图结果显示,CeO2与PdO之间存在协同作用,且Pd处于较高的氧化状态,这可能起因于从Pd到Ce的电子转移作用,Ce处于较低的还原状态,导致Ce-O键结合强度的降低。H2－TPR表征结果同样证实了PdO与CeO2之间存在协同效应,CeO2的引入,促进了PdO的还原,而PdO的存在降低了CeO2表面氧的还原温度,同时此现象也支持了XPS结论。     

催化剂浆液制备条件对Pt/C催化剂电化学性能的影响

研究了催化剂浆液分散时间和分散剂等制备条件对Pt/C催化剂电化学活性的影响.结果表明,催化剂浆液的超声振荡时间和分散剂对Pt/C催化剂性能影响很大.当超声分散10 min时,对应的电化学性能最好;低于10 min时,催化剂的分散不够完全,性能较差;超声分散时间过长,则由于浆液温度升高使得样品颗粒团聚长大,导致Pt/C电...     

Ag/AgCl/GO可见光催化剂的制备及其性能

采用微乳液法成功制备了AgCl/GO复合可见光催化剂,利用XRD、TEM、FT-IR、UV-vis对复合光催化剂进行了表征.以甲基橙为目标污染物,考察AgCl/GO可见光催化降解活性.研究结果显示AgCl粒子实际上是以Ag/AgCl纳米结构形式较好地负载在石墨烯表面上.在甲基橙为20 mg·L~(-1),催化剂为0.05g的条件下,可见光照射100min后甲基橙的降解率达到91%以上.     

Ni-MoOx催化剂上的庚烷异构化

在常压固定床流动体系中研究了Ni-MoOx催化剂对正庚烷异构化反应的催化性能.将质量分数为2%～5%的Ni掺杂于MoO3中可有效地缩短催化剂的还原活化时间,并较大幅度地提高催化剂的比活性.Ni-MoOx催化剂上的正庚烷异构化的反应活化能为35.3kJ/mol,显著低于MoOx催化剂上的活化能(49.3kJ/mol),仅为双功能分子筛催化剂的1/3～1/4.     

硅酸盐修饰Ni/海泡石催化剂的制备

Under the hydrothermal condition, the surface of sepiolite was restored with silicate and Ni was precipitated on the restored sepiolite by precipitating-reducing method. The surface of the samples was characterized by SEM, BET and XRD. The catalytic ability was examined by hydrogenation of toluene in gas phase over the silicate restored Ni/sepiolite catalyst. The experimental results show that distribution of Ni over the surface of the sample was even with bare aggregation and can be controlled, the ability of anti-aging of this catalyst was about ten times higher than that prepared by impregnation method at the same reactive condition.     

CuO-BaO/SiO2催化剂的结构表征

以XRD、XPS和EXAFS手段对CuO－BaO／Sic2催化剂及其还原态的结构进行了研究．结果表明，在CuO－BaO／SiO2体系中铜和钡都是以氧化态的形式存在，超细SiO2载体对所负载的CuO的结构有影响．随着样品负载量的逐渐降低，Cu－O和Cu－Cu睡的健长和配位数逐渐征小，而且低载量样品的健长和配位数减小的幅度最大．在总负载量＞13．39％的样品中，CuO以晶相的形式存在；总负载量＜13．39％的样品中，CUO呈现单层分布的高分出状态．还原态样品中钢以本价铜的形式存在，随负载量的降低，还原态Cu－Cu健的镇长和配位数也分别呈现出逐渐减小的趋势．还原态中心铜原子在催化剂表面的分布状态基本上保持了氧化态催化剂中CuO物相的分市状态．     

NixB/沸石催化剂的分散性和反应性

用晶内形成法制备了Ni_xB/沸石催化剂,用饱和氢化学吸附法结合TEM方法考察了负载金属的分散性,并研究了其己环烷脱氢反应性。结果表明,Ni_xB/沸石样品上负载金属的分散性高,金属粒径分布也相对集中;金属负载量、载体结构和性质以及Ni_xB的制备条件对负载金属的分散性有明显影响。Ni_xB/沸石样品呈现较好的环己烷脱氢反应性。     

Pt/ZnO催化剂的光电子能谱研究

用XPS和XAES(X光激发歇电子能谱)研究了Pt/ZnO催化剂的金属与担体间的相互作用。X射线照射、真空加热、尤其是不同温度下的H_2处理都能不同程度地使 ZnO还原,而担载Pt原子簇的存在明显地促进了ZnO的还原;实验结果表明:由H_2处理引起的Pt与ZnO间的相互作用在较宽温度范围内经历两个不同的阶段:低温氢处理(室温和 150℃)使Pt4f电子结合能产生负化学位移,表明电荷从部分还原的担体转移给了担载的金属Pt原子;而高温(300℃)则引起担载金属与担体间界面原子重排,只有经过400℃空气氧化才会破坏这种作用,使体系恢复到初始状态。     

Cu/ZnO/Al2O3/ZrO2催化剂上乙醇脱氢合成乙酸乙酯Ⅱ.催化剂的表征

采用ＸＲＤ，ＴＰＲ和ＴＰＤ／ＴＰＳＲ方法研究了ＣｕＯ／ＺｎＯ／Ａｌ２Ｏ３／ＺｒＯ２（及还原态）催化剂的物相结构，还原状况，酸碱性质及吸附状况，并与其它催化剂作了比较，ＸＲＤ结果表明，此催化剂在还原臆有以晶相存在的ＣｕＯ，还原后以铜晶形式存在，而Ａｌ２Ｏ３，ＺｎＯ，ＺｒＯ２在还原前后均以无定形形式存在，ＴＰＲ实验发现，共沉淀法制备的铜基催化剂只有一个耗氢峰，对应ＣｕＯ的一种分布状态，且催化剂中ＺｒＯ     

Na-W-Mn/SiO2催化剂表面甲烷脉冲反应Ⅰ.单组分Na/、W/、Mn/SiO2催化剂

制备了单组分Na/、 W/、 Mn/SiO2催化剂, 在ITD(Ion Trap Detector)装置上进行了催化剂表面晶格氧脱附前后的甲烷恒温脉冲反应(CH4-CTPR). 研究结果表明, Na/SiO2表面晶格氧具有一定的C2烃选择性, 并能强烈抑制CO2的生成; W/SiO2表面晶格氧对C2烃的选择性较差, 但对COx具有高的选择性; Mn/SiO2表面的晶格氧对C2H4和CO具有高选择性, 而较深部位的晶格氧则对C2H6和CO2具有高的选择性.     

醇脱氢制酯Cu/Zn/Al/Zr催化剂的表征

醇脱氢制酯Ｃｕ／Ｚｎ／Ａｌ／Ｚｒ催化剂的表征温涛潘伟雄孙旭辉（清华大学化学系Ｃ１国家重点实验室，北京１０００８４）关键词Ｃｕ／Ｚｎ／Ａｌ／Ｚｒ催化剂，乙醇，乙酸乙酯，脱氢，表征分类号Ｏ６４３／ＴＱ４２自Ｅｌｉｏｔｔ等［１］报道在Ｃｕ／Ｚｎ／Ａｌ催化...     

沉淀剂对AU/ZnO催化剂CO氧化性能及催化剂结构的影响

在25 C和进料中含水条件下,考察了由Na2CO3,(NH4)2CO3,NaOH和NH4OH等4种沉淀剂制备的Au/ZnO催化剂上CO氧化活性和稳定性.结果表明,沉淀剂影响Au/ZnO催化剂的前体组成、金粒子和ZnO粒子大小、比表面积及CO氧化性能.由NH4OH制备的Au/ZnO催化剂活性和稳定性较差,CO转化率只有15%;由其它3种沉淀剂制备的Au/ZnO催化剂的CO氧化活性和稳定性明显改善,可至少连续反应1 100 h,且保持CO完全氧化,其中Na2CO3是最佳沉淀剂.在反应过程中反应气氛可引起金粒子的聚集及在催化剂表面生成新的碱式碳酸锌物相.催化剂的稳定性与金粒子长大速度和碳酸根累积量有关.     

甲醇氧化PtSnCo/C阳极催化剂

通过乙二醇液相分步还原法制备了金属质量分数为20%的PtSn/C二元及PtSnCo/C三元催化剂.采用X射线衍射(XRD)光谱法、能量散射谱(EDS)对催化剂进行了表征;通过阳极线性伏安扫描法(LSV)、连续循环伏安法(CV)、预吸附单层CO溶出法研究了其电化学性质.结果表明,PtSnCo/C三元催化剂较商业化JM-PtRu/C催化剂具有更好的氧化甲醇催化活性.循环伏安扫描100圈后发现,PtSn/C二元催化剂的甲醇氧化峰电流快速衰减到其初始氧化峰电流的11%左右,而PtSnCo/C三元催化剂仅衰减到其初始值的50%左右,这表明PtSnCo/C三元催化剂具有更好的化学稳定性.在PtSnCo/C催化剂上,甲醇氧化起始电位比直接吸附CO后的CO阳极溶出电位负,意味着甲醇在PtSnCo/C催化剂上氧化的中间产物不是CO,而是比CO更为活泼且易于氧化的中间物种.     

合成甲醇的催化剂Rh-ZnO/MWNTs的研究

研究新型的由多壁碳纳米管(MWNTs)负载的， ZnO助催的铑基甲醇合成催化剂. 当铑含量达到4％(w)时，催化剂具有较高的比表面积(99.6 m2•g－1), 催化剂的反应活化能为68.8 kJ•mol－1.在563 K, 1 MPa下，催化剂的最高催化活性和甲醇选择性分别为411.4 mg/gcat.•h和96.7％. TEM、TPR和TPD等表征结果显示，碳纳米管能增加Rh在催化剂表面的分散度，提高催化剂的还原温度并能增加氢物种的吸附量，这些结果将有助于更好地了解催化剂中各组分间的协同作用和催化活性中心本质.     

Pt-Ce/KL和Pt/CeKL沸石重整催化剂的研究

ＳＴＵＤＹＯＦＰｔ┐Ｃｅ／ＫＬＡＮＤＰｔ／ＣｅＫＬＺＥＯＬＩＴＥＲＥＦＯＲＭＩＮＧＣＡＴＡＬＹＳＴＳＬｕＷｅｉｑｉ，ＬｉＦｅｎｇｙｉ（ＩｎｓｔｉｔｕｔｅｏｆＡｐｐｌｉｅｄＣｈｅｍｉｓｔｒｙ，ＮａｎｃｈａｎｇＵｎｉｖｅｒｓｉｔｙ，Ｎａｎｃｈａｎｇ３３０...