基于二级结构TiO_2纳米晶光阳极的高效染料敏化太阳能电池

本文报道了一种新型的二级结构TiO2纳米晶(nano-TiO2)光阳极的简单制备方法及其在高效染料敏化太阳能电池中的应用.通过添加适量TiCl4异丙醇溶液到传统nano-TiO2浆料中,可生成微米级nano-TiO2聚集体.该二级结构能有效提高光阳极光谱吸收和散射性能及电子传输和收集效率.基于这种结构光阳极的染料敏化太阳能电池光电性能有显著提高.在光阳极中将6μm厚传统nano-TiO2膜用相同厚度nano-TiO2聚集体替换,电池光电转换效率由5.03%提高到7.30%.进一步增加nano-TiO2聚集体的厚度能制备出更高光电转换效率的电池.     

静电喷雾法制备高效染料敏化太阳能电池的二氧化钛光阳极

TiO2光阳极膜是染料敏化太阳能电池（DSSC）的核心部件之一,它对电池的光电转换效率起决定性作用．TiO2电极一般采用刮涂法和丝网印刷法制备．近3年,通过静电喷雾制备光阳极的方法得到国内外学者的关注．静电喷雾制备光阳极会受到多种因素的影响,如电压、流速、悬浮液浓度、喷雾距离以及喷雾时间等．但这些因素对成膜和DSSC器件性能的影响却没有得到全面的研究或者报道．本文使用静电喷雾法制备了多孔TiO2纳米膜,并研究了以其为电极的电池器件特性．经过超声充分分散的稳定TiO2乙醇悬浮液在高电压下喷雾到导电玻璃上成膜．通过改变电喷雾距离,得到了具有不同形貌的TiO：光阳极膜,并解释了其形成的机理及其对电池性能的影响．研究还表明,光阳极膜的TiC14处理能够很好地改善电池性能．通过优化,基于流速为0．8mL／h、电喷雾距离和时间分别为2．2cm和8min条件下制备的光阳极,结合TiC14处理,组装的电池在模拟太阳光源AM1．5G下光电转化效率达6．24％．     

TiO2/SnO2复合空心球在染料敏化太阳能电池中的应用

采用模板辅助法制备了SnO2/TiO2复合空心球,样品直径为1.5~4.0μm,比表面积达到了92.9 m^2·g^-1,复合空心球表现出优越的光散射性能.以这种复合空心球作为染料敏化太阳能电池的光阳极,电池的光电转换效率可达到7.72%,高于SnO2微米球(2.70%)和TiO2微米球(6.26%).此外,以锐钛矿型TiO2纳米晶作为底层,SnO2/TiO2复合空心球作为光散射层制备的双层结构光阳极,电池光电转换效率进一步提升至8.43%.     

Addition of TiO2 nanowires in different polymorphs for dye-sensitized solar cells

TiO₂ (B) and TiO₂ anatase nanowires were prepared at 150 °C for 120 h by a hydrothermal method followed by calcination in air at 400 °C for 2 h and at 700 °C for 2 h for TiO₂ (B) and TiO₂ anatase, respectively. Although dye-sensitized solar cells (DSC) with fully nanowire electrodes showed a rather low light-to-electricity conversion efficiency of 1.33 % for TiO₂ (B) and 2.42% for TiO₂ anatase, 10 wt % nanowire-dispersed electrodes in a P-25 TiO₂-nanoparticle matrix demonstrated improved efficiency of 6.17 % for TiO₂ (B) and 6.53% for TiO₂ anatase, these exceeding that of pure P-25 electrodes in this work (η=5.59%). The dominant mechanisms of the improvement at 10 wt% for the two different polymorphs are thought to be different, i.e., a light-scattering and film-thickness increment for the TiO₂ (B) system, whereas there is an improved conduction path through the matrix for the TiO₂ anatase system.      

Polypyrrole-cobalt-carbon nanocomposites as efficient counter electrode materials for dye-sensitized solar cells

In this work, we demonstrate a new kind of Pt-free counter electrode for dye-sensitized solar cells(DSCs). Polypyrrole-cobalt-carbon(PPY-Co-C) nanocomposites, with the advantages of low cost and simple preparation, show favorable catalytic activity in promoting tri-iodide reduction. The DSC composed of the PPY-Co-C nanocomposite electrode exhibits an acceptable energy conversion efficiency of 6.01%, a considerable short-circuit photocurrent of 15.33 mA cm-2, and a low charge-transfer resistance of 1.5 Ω cm2. The overall performance of PPY-Co-C is superior to the carbon counterparts and comparable with the platinum reference, rendering them efficient and promising counter electrode materials for DSCs.     

一种高效染料敏化太阳电池电解质添加剂

报道了一种新型染料敏化太阳电池电解质添加剂——N-十六烷基吡啶碘(N-CPI).往电解质中添加0.02MN-CPI,能同时提高染料敏化太阳电池(DSSC)的短路电流和开路电压,光电转换效率也由4.429%提高到6.535%,增幅高达47.55%,由此可见,N-CPI是一种高效电解质添加剂.N-CPI这种功能来源于其双极性基团的特殊分子结构,这种结构使N-CPI在电解质中如表面活性剂那样形成有序分布,影响I-/I3-的扩散和氧化还原性能,进而影响DSSC的光电性能.     

双层结构CeO2光阳极在染料敏化太阳能电池中的应用

利用水热法合成核壳结构Au@SiO₂@CeO₂纳米微球,制备了一系列双层结构复合光阳极并应用于染料敏化太阳能电池(DSSC)。研究表明：当CeO₂纳米微球和核壳结构Au@SiO₂@CeO₂纳米微球应用于DSSC光阳极散射层时,电池的光电转化效率有了显著提高。相对于纯 TiO₂ (P25)光阳极,P25/CeO₂纳米球光阳极电池的 DSSC 光电性能提高了 15.3%,P25/Au@SiO₂@CeO₂纳米球光阳极电池的光电性能提高了27.9%。DSSC光电性能的提高主要归因于2个方面：一方面,Au纳米粒子的表面等离子体共振效应有效提高了光阳极薄膜的光散射效应。另一方面,CeO₂具有较高的染料负载能力,核壳球形结构具有较高的比表面积,增强了光的散射效应,提高了电子传输能力。     

双层结构CeO2光阳极在染料敏化太阳能电池中的应用

利用水热法合成核壳结构Au@SiO₂@CeO₂纳米微球,制备了一系列双层结构复合光阳极并应用于染料敏化太阳能电池(DSSC)。研究表明：当CeO₂纳米微球和核壳结构Au@SiO₂@CeO₂纳米微球应用于DSSC光阳极散射层时,电池的光电转化效率有了显著提高。相对于纯TiO₂(P25)光阳极,P25/CeO₂纳米球光阳极电池的DSSC光电性能提高了15.3%,P25/Au@SiO₂@CeO₂纳米球光阳极电池的光电性能提高了27.9%。DSSC光电性能的提高主要归因于2个方面：一方面,Au纳米粒子的表面等离子体共振效应有效提高了光阳极薄膜的光散射效应。另一方面,CeO₂具有较高的染料负载能力,核壳球形结构具有较高的比表面积,增强了光的散射效应,提高了电子传输能力。     

Synthesis of nano-TiO2 assisted by diethylene glycol for use in high efficiency dye-sensitized solar cells

The performance of dye-sensitized solar cells(DSSCs) consisting of anatase TiO_2 nanoparticles that were synthesized via a hydrothermal method was studied.The synthesized TiO_2 nanoparticles were characterized by X-ray diffraction(XRD),nitrogen sorption analysis,scanning electron microscopy(SEM),high resolution transmission electron microscopy(HRTEM),and UV-vis spectroscopy.Then the J-Vcurve,electrochemical impedance spectroscopy(EIS),and open-circuit voltage decay(OCVD) measurement were applied to evaluate the photovoltaic performance of DSSCs.Compared with the commercial TiO_2nanoparticles(P25),the synthesized-TiO_2 nanoparticles showed better performance.By adding diethylene glycol(DEG) before the hydrothermal process,the synthesized TiO_2 nanoparticles(hereafter referred to as TiO_2-DEG particles) shows narrower size distribution,larger specific surface area,higher crystallinity,and less surface defects than TiO_2(DEG free) particles.The analysis of photovoltaic properties of DSSCs based on TiO_2-DEG particles showed that the recombination of electron-hole pairs was decreased and the trapping of carries in grain boundaries restrained.It was believed that the photoelectrode fabricated with the as-prepared TiO_2 nanoparticles improved the loading amount of dye sensitizers(N719).and enhanced the photocurrent of the DSSCs.As a result,the TiO_2-DEG particle based cells achieved a photo-to-electricity conversion efficiency(η) of 7.90%,which is higher than 7.53%for the cell based on TiO2(DEG free) and 6.59%for the one fabricated with P25.     

Plasma-based preparation of polyaniline/graphene and polypyrrole/graphene composites for dye-sensitized solar cells as counter electrodes

This study presents the preparation of graphene (GR) nanocomposites with polyaniline (PANI) and polypyrrole (PPy) through the fast, versatile and environmentally friendly process of radio frequency (RF)-plasma polymerization. Morphological characterization of the nanocomposites is performed using scanning electron microscopy (SEM) and shows that the PANI and PPy conducting polymers coated the GR surface. The surface properties of the GR nanocomposites are determined using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). The prepared GR nanocomposites are then used as counter electrodes in dye-sensitized solar cells (DSSCs). The conversion cell efficiencies for iodine-doped DSSC samples are found to be 0.086%, 5.41%, and 5.60% for I₂-PANI, I₂-PANI-GR and I₂-PPy-GR, respectively, while the corresponding undoped samples reaches power conversion efficiencies of 3.82%, 1.30%, and 0.077% for PPy-GR, PANI-GR and PANI, respectively. The incident photon-to-current efficiency (IPCE) of iodine-doped composite-based DSSCs is significantly enhanced.     

Partially nanowire-structured TiO2 electrode for dye-sensitized solar cells

Partially nanowire-structured TiO₂ was prepared by a hydrothermal processing followed by calcination in air. The hydrogen titanate powder as-synthesized was calcined at 300 °C for 4 h to obtain the partially nanowire-structured TiO₂. A dye-sensitized solar cell (DSC) with a film thickness of 5.6 μm, fabricated using the partially nanowire-structured TiO₂ showed better performance than using a fully nanowire-structured TiO₂ or a conventional equi-axed TiO₂ nanopowder. The short-circuit current density (J_SC), the open-circuit voltage (V_OC), the fill factor (FF) and the overall efficiency (η) are 11.9 mA/cm², 0.754 V, 0.673 and 6.01 %, respectively. The effects of one-dimensional nanostructure and electron expressway concept are discussed.     

Enhancement of the efficiency of dye-sensitized solar cell with multi-wall carbon nanotubes/polythiophene composite counter electrodes prepared by electrodeposition

For the purpose of increasing the energy conversion efficiency of dye-sensitized solar cells (DSSCs), multi-wall carbon nanotube (MWCNT)/polythiophene (PTh) composite film counter electrode has been fabricated by electrophoresis and cyclic voltammetry (CV) in sequence. The morphology and chemical structure have been characterized by transmission electron microscopy (TEM), scanning electron microscope (SEM), and Raman spectroscopy respectively. The overall energy conversion efficiency of the DSSC employing the MWCNT/PTh composite film has reached 4.72%, which is close to that of the DSSC with a platinum (Pt) counter electrode (5.68%). Compared with a standard DSSC with MWCNT counter electrode whose efficiency is 2.68%, the energy conversion efficiency has been increased by 76.12% for the DSSC with MWCNT/PTh counter electrode. These results indicate that the composite film with high conductivity, high active surface area, and good catalytic properties for I₃⁻ reduction can potentially be used as the counter electrode in a high-performance DSSC.     

Controllable hydrothermal synthesis of nanocrystal TiO2 particles and their use in dye-sensitized solar cells

A simple method for the controllable hydrothermal synthesis of nanocrystalline anatase TiO2(nc-TiO2) particles involving the selection of suitable organic alkali peptizing agents is reported.A dye-sensitized solar cell(DSSC) with square-like nc-TiO2 particles with side lengths about 8-13 nm-prepared using tetraethylammonium hydroxide(TEAOH)-in the photoelectrode showed higher photovoltaic performance than two other DSSCs with square-like nc-TiO2 particles with side lengths about 7-10 nm-prepared using tetrabutylammonium hydroxide-or elongated nc-TiO2 particles with lengths about 18-35 nm and width about 10 18 nm-prepared using tetramethylammonium hydroxide(TMAOH)-in the photoelectrodes.When a scattering layer prepared from sub-micron size spheres or cone-like nc-TiO2 particles-synthesized using a higher concentration of TMAOH-was added on top of the photoelectrode fabricated from nc-TiO2 synthesized with TEAOH,the energy conversion efficiency of the DSSC was markedly increased from 6.77% to 8.18%.     

两步电泳沉积制备TiO2光阳极用于高效染料敏化太阳能电池

采用不同沉积电压制备TiO₂光阳极,研究电压对薄膜沉积速率、厚度和形貌的影响。通过台阶仪、光学照片、扫描电子显微镜（SEM）、电化学交流阻抗谱、开路电压衰减曲线对光阳极和电池进行系统表征,并测试了染料敏化太阳能电池器件的电流密度-电压（J-V）曲线,计算其光电转换效率。结果表明,提高沉积电压时,光阳极薄膜的沉积速率加快,膜厚也增加,但是电压过高时,薄膜会有裂缝和覆盖不全的问题,这会对电池的效率造成负面影响。综合考虑低沉积电压条件下薄膜均匀无裂缝和高沉积电压条件下沉积速率快的优点,采用先30 V电压、后60 V电压的电泳沉积方式来制备光阳极,结果呈现协同效果,既降低了制备时间又得到高质量的薄膜,在无其他修饰的情况下,电池的光电转换效率可以达到7.29%。     

两步电泳沉积制备TiO2光阳极用于高效染料敏化太阳能电池

采用不同沉积电压制备TiO₂光阳极,研究电压对薄膜沉积速率、厚度和形貌的影响。通过台阶仪、光学照片、扫描电子显微镜(SEM)、电化学交流阻抗谱、开路电压衰减曲线对光阳极和电池进行系统表征,并测试了染料敏化太阳能电池器件的电流密度-电压(J-V)曲线,计算其光电转换效率。结果表明,提高沉积电压时,光阳极薄膜的沉积速率加快,膜厚也增加,但是电压过高时,薄膜会有裂缝和覆盖不全的问题,这会对电池的效率造成负面影响。综合考虑低沉积电压条件下薄膜均匀无裂缝和高沉积电压条件下沉积速率快的优点,采用先30 V电压、后60 V电压的电泳沉积方式来制备光阳极,结果呈现协同效果,既降低了制备时间又得到高质量的薄膜,在无其他修饰的情况下,电池的光电转换效率可以达到7.29%。     

向列相液晶4-氰基-4'-庚基联苯和4-氰基-4'-戊基联苯在准固态染料敏化太阳电池中的应用

将两种向列相液晶,4-氰基-4'-庚基联苯和4-氰基-4'-戊基联苯,引入到染料敏化太阳电池(DSC)用偏氟乙烯-六氟乙烯共聚物基准固态电解质中,以期提高DSC的光电转化效率.研究了液晶的引入对电解质中I-/I3-的氧化还原行为、DSC中TiO2/电解质界面的暗反应以及DSC光伏性能的影响.结果表明,尽管液晶的引入会降低电解质中I-/I3-的传输并且使得DSC中暗反应加快,但是DSC的短路电流密度却显著地提高,使DSC的光电转化效率增加.这可能是由于液晶的引入改善了DSC中的界面接触以及增加染料的光吸收引起的.     

Composite electrolytes based on poly(ethylene oxide) and binary ionic liquids for dye-sensitized solar cells

The sunlight is the largest single available source of clean and renewable energy to ensure human society’s sustainable development. Owing to their low production cost and high energy conversion efficiency, dye-sensitized solar cells (DSSCs) have been regarded as good alternatives to conventional photovoltaic devices. Herein, a series of composite electrolytes based on poly(ethylene oxide) (PEO) and the binary ionic liquids 1-propyl-3-methy-imidazolium iodide ([PMIm]I) and 1-ethyl-3-methylimidazolium thiocyanate ([EMIm][SCN]) were prepared and then applied to fabricate six DSSCs. The composite electrolytes were characterized by fourier transform infrared spectroscopy (FTIS), X-ray diffraction (XRD), and electrochemical impedance spectra (EIS). It was shown that the addition of binary ionic liquids would reduce the degree of crystallinity of PEO, thus improving the ionic conductivities of the electrolytes by about 2 orders of magnitude. Investigation on the photovoltaic performances of these DSSCs showed that the fill factor (FF) could reach up to 0.67 and energy conversion efficiency (η) could reach up to 4.04% under AM 1.5 full sunlight (100 mW/cm2).     

Influence of light scattering particles in the TiO2 photoelectrode for solid-state dye-sensitized solar cell

A TiO₂ film was modified by adding light scattering particles and applied to an anode electrode in solid-state dye-sensitized solar cells (DSSCs). The TiO₂ films with 10 wt% (vs. TiO₂ weight) light scattering particles showed enhanced performance (28%), compared with nanocrystalline TiO₂ films, which were used as the controls. In particular, the photocurrent density (J_sc) reached approximately 12.6 mA/cm² under a one-sun condition. This was attributed to the light scattering effect and decrease in internal resistance through the macroporous structure with a minor loss of electron transport. However, in the case of a larger concentration of light scattering particles (>10 wt%), there was a decrease in the efficiency of DSSCs, which resulted from the decreased surface area and degraded electron transport and charge recombination properties, as confirmed by the measurement of stepped light-induced photocurrent and photovoltage transients. Furthermore, the diffusion properties and kinetics of the composite polymer electrolyte with the nanoporous and macroporous TiO₂ films were compared and evaluated from the electrochemical impedance spectra.     

三苯胺类染料敏化太阳能电池能量转化效率的全息定量构效关系研究

研究构建了三苯胺类化合物分子结构与相应染料敏化太阳能电池能量转化效率(PCE)之间的全息定量构效关系(HQSAR)模型。当fragment distinction、fragment size、hologram length和principal components分别为“C、DA”、“4-7”、“199”和“6”时,可以获得最优HQSAR模型。采用外部测试集验证和留一交叉验证对所建立模型进行检验,外部测试集验证中CCC和 Q2F3分别为0.933和0.892,留一交叉验证中其q2cv和r2分别为0.791和0.902,表明所建立模型具有较好的拟合效果和预测能力。通过所建立HQSAR模型的分子贡献图可知,环戊并二噻吩基团的存在有利于提高PCE值,长烷基链的存在可能降低PCE值。