The influence of titanium dioxide phase composition on dyes photocatalysis

A comparative study of TiO₂ powders prepared by sol–gel methods is presented. Titanium tetraisopropoxide was used as the precursor for the sol–gel processes. The effects of the annealing treatment on phase, crystallite size, porosity and photodegradation of dyes (methyl orange and methylene blue) were studied. The phase structure, microstructure and surface properties of the films were characterized by using X-ray diffraction (XRD) and Atomic Force Microscopy (AFM). The X-ray diffraction was used for crystal phase identification, for the accurate estimation of the anatase–rutile ratio and for the crystallite size evaluation of each polymorph in the samples. It was found that the only TiO₂ anatase phase of the synthesized TiO₂ develops below 500 °C, between 600 and 800 °C the anatase coexist with rutile and above 800 °C only the rutile phase was found in the samples. Attention has been paid not only to crystal structures, but also to the porosity, the particle size and the photocatalytic properties. However, the annealing temperature was found to have significant influence on the photocatalytic properties. Different TiO₂ doctor blade thin films were obtained mixing the sol gel powder (100% anatase) and TiO₂ Aldrich with TiO₂ Degussa P25. The surfactant (Triton X100 or sodium dodecyl sulfate) affects the packing density of the particles during deposition and the photocatalytic degradation efficiency of the dyes. The photocatalytic degradation kinetics of methyl orange and methylene blue using TiO₂ thin film were investigated.     

Thermal and hydrothermal stability of flame hydrolytically synthesized SiO2/TiO2 mixed oxides

The phase stability of the two TiO₂ modifications (anatase and rutile) in fumed SiO₂/TiO₂ nano-composites (0–24.8 wt-% silica) under thermal and hydrothermal conditions was investigated by X-ray powder diffraction, transmission electron microscopy (TEM) and gas adsorption methods (BET). The results show that the phase transformation from anatase to rutile type of structure and the growth of anatase crystallites are significantly retarded by mixing small amounts of SiO₂ into TiO₂, while the specific surface area is maintained. The SiO₂/TiO₂-composites reveal a remarkable shift in the anatase to rutile transformation temperature from approx. 500 °C (pure TiO₂) to approx. 1000 °C (samples with SiO₂ contents of more than 10%). The rate of phase transformation from anatase to rutile is enhanced under hydrothermal conditions compared to conventional thermal treatment, e.g. pure titania (AEROXIDE^® TiO₂ P25) annealed under hydrothermal conditions (100 g/m³ absolute humidity, 4 h at 600 °C) had a rutile content of 85%, while the same specimens annealed in absence of humidity contained only 46% rutile. However, the difference in rate of phase transformation became less pronounced when the silica content in SiO₂/TiO₂-composites was further increased.TEM results showed that the surface of the anatase crystallites was covered with silica. This averts coalescence of anatase crystallites and keeps them under a critical size during the annealing process. When the crystal domains grew larger, a rapid conversion to rutile took place. The critical size of anatase crystallites for the phase transformation was estimated to be 15–20 nm.     

Preparation of nanocrystalline TiO<Subscript>2</Subscript> powders for photocatalytic oxidation of phenol

Nanocrystalline TiO₂ powders in the anatase, rutile, and mixed phases prepared by hydrolysis of TiCl₄ solution were of ultrafine size (<7.2 nm) with high specific surface areas in the range 167 to 388 m²/g. In the photocatalytic degradation of phenol as model reaction, the photocatalytic properties of TiO₂ nanoparticles were evaluated by use of UV–vis absorption spectroscopy and total organic carbon (TOC) content. The synthetic mixed-phase TiO₂ powder calcined at 400 °C had higher activity than pure anatase or rutile; it degraded more than 90% phenol to CO₂ (evaluated by TOC) after irradiation with near UV light for 90 min at a catalyst loading of 0.4 g/L. The TOC results indicated that rutile TiO₂ crystallites of particle size 7.2 nm resulted in much better photocatalytic performance than particles of larger size. This result suggested that some intermediates, not determined by UV–vis absorption spectroscopy, existed in the solution after the photocatalytic process over the rutile TiO₂ photocatalysts of larger crystallite size.     

The effect of ball-milling on the thermal behavior of anatase-doped hematite ceramic system

High energy ball-milling methods were employed in the synthesis of anatase-doped hematite xTiO₂(a) · (1−x)α-Fe₂O₃ (x = 0.1, 0.5, and 0.9) ceramic system. The thermal behavior of as obtained ceramic system was characterized by simultaneous DSC–TG. The pure anatase phase was found to be stable below 800 °C, but there is a 10.36% mass loss due to the water content. Two exothermic peaks on DSC curves of pure anatase indicate the different crystallization rates. The pure hematite partially decomposed upon heating under argon atmosphere. Ball-milling has a strong effect on the thermal behaviors of both anatase and hematite phases. For x = 0.1 and 0.5, there is gradual Ti substitution of Fe in hematite lattice, and the decomposition of hematite is enhanced due to the smaller particle size after ball-milling. The crystallization of hematite was suppressed as the enthalpy values decreased due to the anatase-hematite solid–solid interaction. For x = 0.9, most of the anatase phase converted to rutile phase after long milling time. The thermal behavior of xTiO₂(a) · (1−x)α-Fe₂O₃ showed smaller enthalpy value of the hematite transformation to magnetite and anatase crystallization due to the small fraction of hematite phase in the system and hematite–anatase interaction, while the mass loss upon heating increased as a function of milling time due to more water content absorbed by the smaller particle size.     

Effect of annealing temperatures and of high content of the iron ion (Fe<Superscript>3+</Superscript>)-doping on transition anatase–rutile phase of nanocrystalline TiO<Subscript>2</Subscript> thin films prepared by sol–gel spin coating

Titanium dioxide doped with iron (III) was prepared by sol–gel Spin Coating method. The phase structures, morphologies, particle size of the doped TiO₂ have been characterized by X-ray diffraction (XRD), Raman spectroscopy, atomic force microscopy (AFM) and ultraviolet–visible (UV–Vis) spectrophotometer. The XRD and Raman results show that the 10% Fe³⁺-doped TiO₂ thin films crystallize in anatase phase between 600 and 800 °C, and into the anatase–rutile phase at 1,000 °C, and further into the rutile phase when the content of Fe³⁺ increases (20%). The grain size calculated from XRD patterns shows that the crystallinity of the obtained anatase particles increased from 39.4 to 43.4 nm as the temperature of annealing increase, whereas the size of rutile crystallites increases, with increasing Fe³⁺ concentrations from 36.9 to 38.1 nm. The AFM surface morphology results confirmed that the particle size increases by increasing the annealing temperature and also with an increasing of Fe³⁺ content. The optical band gap (E _g) of the films was determined by the UV–Vis spectrophotometer. We have found that the optical band gap decreased with an increasing of annealing temperatures and also with an increasing of Fe³⁺ content.     

DSC investigation of nanocrystalline TiO<Subscript>2</Subscript> powder

The aim of the article is to investigate the influence of particle size on titanium dioxide phase transformations. Nanocrystalline titanium dioxide powder was obtained through a hydrothermal procedure in an aqueous media at high pressure (in the range 25–100 atm) and low temperature (≤200 °C). The as-prepared samples were characterized with respect to their composition by ICP (inductive coupled plasma), structure and morphology by XRD (X-ray diffraction), and TEM (transmission electron microscopy), thermal behavior by TG (thermogravimetry) coupled with DSC (differential scanning calorimetry). Thermal behavior of nanostructured TiO₂ was compared with three commercial TiO₂ samples. The sequence of brookite–anatase–rutile phase transformation in TiO₂ samples was investigated. The heat capacity of anatase and rutile in a large temperature range are reported.     

The effect of annealing temperatures on surface properties,hydroxyapatite growth and cell behaviors of TiO2 nanotubes

Well‐ordered TiO₂ nanotubes were prepared by the electrochemical anodization of titanium in an ethylene glycol electrolyte containing 1 wt% NH₄F and 10 wt% H₂O at 20 V for 20 min, followed by annealing. The surface morphology and crystal structure of the samples were examined as a function of the annealing temperature by field emission scanning electron microscopy (FE‐SEM) and X‐ray diffraction (XRD), respectively. Crystallization of the nanotubes to the anatase phase occurred at 450 °C, while rutile formation was observed at 600 °C. Disintegration of the nanotubes was observed at 600 °C and the structure vanished completely at 750 °C. Electrochemical corrosion studies showed that the annealed nanotubes exhibited higher corrosion resistance than the as‐formed nanotubes. The growth of hydroxyapatite on the different TiO₂ nanotubes was also investigated by soaking them in simulated body fluid (SBF). The results indicated that the tubes annealed to a mixture of anatase and rutile was clearly more efficient than that in their amorphous or plain anatase state. The in vitro cell response in terms of cell morphology and proliferation was evaluated using osteoblast cells. The highest cell activity was observed on the TiO₂ nanotubes annealed at 600 °C. Copyright © 2010 John Wiley & Sons, Ltd.     

Improved efficiency of TiO2 nanotubes in dye sensitized solar cells by decoration with TiO2 nanoparticles

In the present work we investigate the effect of TiCl₄ treatments on the photoconversion efficiency of TiO₂ arrays used in dye sensitized solar cell. The results clearly show that by an appropriate treatment the decoration of the TiO₂ nanotube arrays with TiO₂ nanocrystallites of a typical size of 3 nm can be achieved. These particles can be converted to mixture of anatase and rutile phase by annealing in air. This decoration of the TiO₂ nanotubes leads to a significantly higher specific dye loading and, for certain annealing treatments, to a doubling of the solar cell efficiency (in our case from 1.9% to 3.8% of AM 1.5 conditions) can be achieved.     

Preparation of nanocrystalline anatase TiO2 using basic sol-gel method

Nanocrystalline titanium dioxide particles with anatase structure and high thermal stability have been synthesized using the basic sol-gel method. The particle size and morphology were refined under hydrothermal conditions in the presence of different concentrations of tetramethylammonium hydroxide (TMAH) at 210°C and 230°C. XRD and TEM analysis showed that the TiO₂ particles obtained were homogeneous and monodispersive at low contents of TMAH. All intense peaks, clearly observed in the XRD patterns, were assigned to the anatase phase and no rutile phase was observed. At high contents of TMAH, nanoscale small (10–30 nm) and larger (>100 nm) TiO₂ particles were one-pot synthesized. The nanocrystalline TiO₂ particles synthesized by this method have good thermal stability. With the sintering temperature of up to 650°C, all the XRD peaks maintained good agreement with the anatase reference data.     

Effect of calcination temperature on the microstructure of porous TiO<Subscript>2</Subscript> film

To obtain porous TiO₂ film, the precursor sol was prepared by hydrolysis of Ti isopropoxide and then complexed with trehalose dihydrate. The porous TiO₂ film was fabricated by the dip-coating technique on glass substrates using this solution. The TiO₂ film was calcined at 500 °C. The maximum thickness of the film from one-run dip-coating was ca. 740 nm. The film was composed of nanosized particle and pores. The porosity of the TiO₂ film was increased by addition of trehalose dihydrate to the sol. The porous TiO₂ films were calcined at different temperatures. The effects of calcination temperature on the microstructure of the porous TiO₂ film were investigated. The porous film prepared from sol containing trehalose still kept the porous structure after calcination at 950 °C. The phase transition temperature of the film from anatase to rutile was shifted from 650 to 700 °C by addition of trehalose to the sol.     

TiO2 nanotubes as recyclable catalyst for efficient photocatalytic degradation of indigo carmine dye

TiO₂ nanotubes have been synthesized in a hydrothermal system. The nanotubes were characterized by scanning electronic microscopy (SEM), FT-Raman spectroscopy and surface charge density by surface area analyzer. These nanocatalysts were applied to photocatalyse indigo carmine dye degradation. Photodegradation ability of TiO₂ nanotubes was compared to TiO₂ anatase photoactivity. Indigo carmine dye was completely degraded at 60 and 110 min of reaction catalysed by TiO₂ nanotubes and TiO₂ anatase, respectively. TiO₂ nanotubes presented high photodegradation activity at pH 2 and TiO₂ anatase at pH 4. TiO₂ nanotubes were easily recycled whereas the reuse of TiO₂ anatase was not effective. Nanotubes maintained 90% of activity after 10 catalytic cycles and TiO₂ anatase presented only 10% of its activity after 10 cycles.     

The influence of concentration of doping elements on anatase–rutile transformation at the synthesis of rutile pigments (Ti,Cr,Nb)O2 and their pigmentary properties

An analysis of the effects of dopants concentration and different starting titanium compounds on the anatase to rutile phase transformation at the synthesis of rutile pigments Ti_1?3xCr_xNb_2xO_2±δ is presented in this study. The main goal was to analyze reaction mixtures for x = 0.05 (previous study) and 0.30 by simultaneous TG–DTA analysis and to determine the temperature of anatase–rutile transition. For x = 0.05, initial temperatures 760–830 °C are needful for a formation of rutile structure. The temperature is the lowest for the hydrated Na₂Ti₄O₉ paste (760 °C) and similar for other starting compounds of titanium. But for x = 0.30, the anatase–rutile transition begins at higher temperatures 910–1,030 °C because of high-Nb content, which is the inhibitor of this modification change. In addition, we found the influence of calcination temperatures (850, 900, 950, 1000, 1050, 1100, and 1150 °C) on color properties and particle size distribution of these materials prepared from anatase TiO₂ and with x = 0.30. Selected pigments were also analyzed by X-ray powder diffraction.     

Synthesis of nanosized TiO2/SiO2 particles using microwave processes and their photocatalytic activity on the decomposition of orange II

The nanosized titania and TiO₂/SiO₂ particles were prepared by the microwave-hydrothermal method. The effect of physical properties TTIP/TEOS ratio and calcination temperature has been investigated. The major phase of the pure TiO₂ particle is of the anatase structure, and a rutile peak was observed above 800°C. In TiO₂/SiO₂ particles, however, no significant rutile phase was observed, although the calcination temperature was 900°C. No peaks for the silica crystal phase were observed at either silica/titania ratio. The crystallite size of TiO₂/SiO₂ particles decreases as compared to pure TiO₂ at high calcination temperatures. The TiO₂/SiO₂ particles show higher activity on the photocatalytic decomposition of orange II as compared to pure TiO₂ particles.     

Electronic Structure and Size of TiO2 Nanoparticles of Controlled Size Prepared by Aerosol Methods

Summary.  A complete characterization of nanostructures has to deal both with electronic structure and dimensions. Here we present the characterization of TiO₂ nanoparticles of controlled size prepared by aerosol methods. The electronic structure of these nanoparticles was probed by X-ray absorption spectroscopy (XAS), the particle size by atomic force microscopy (AFM). XAS spectra show that the particles crystallize in the anatase phase upon heating at 500°C, whereas further annealing at 700°C give crystallites of 70% anatase and 30% rutile phases. Raising the temperature to 900°C results in a complete transformation of the particles to rutile. AFM images reveal that the mean size of the anatase particles formed upon heating at 500°C is 30 nm, whereas for the rutile particles formed upon annealing at 900°C 90 nm were found. The results obtained by these techniques agree with XRD data. Received October 5, 2001. Accepted (revised) December 6, 2001     

水热法合成掺杂铁离子的小管径TiO2纳米管

碳纳米管这种一维结构的新材料的发现为物理、化学、材料科学和纳米科学开辟了全新的研究领域.近年来,非碳无机类富勒烯(Inorganic Fullerenelike,简称IF)纳米管也受到人们的广泛关注.     

Preparation and Characterization of Peroxo Titanic Acid Solution Using TiCl3

The peroxo titanic acid solution was successfully prepared using titanium trichloride as a precursor. The basic properties of the TiO₂ film prepared by the solution were investigated in view of phase change, bandgap energy, crystalline size etc. The film displayed amorphous TiO₂ at room temperature, anatase above 281°C and a mixture of anatase and rutile at 990°C. The crystalline size increases with annealing temperatures, while the bandgap energies decrease due to the quantum size effect and the formation of rutile phase which has low bandgap energy. As a result of TG-DTA, it was found that annealing treatment at 990°C for 2 h formed a mixture of anatase and rutile through three steps: (1) the removal of physically adsorbed water (2) the decomposition of peroxo group (3) amorphous-anatase or anatase-rutile phase transformation.     

Preparation of TiO2 Powder by Modified Two-Stage Hydrolysis

Nano-sized TiO₂ powders were synthesized by modified hydrolysis reaction using two-stage treatments of acid/base catalyst. Using an acidic catalyst, the primary particle size of assynthesized TiO₂ was smaller than using basic catalyst, but rutile ratio and the particle size were increased after heat treatment due to the dense packing of particles. However, in the synthesized TiO₂ powder using a basic catalyst persist the anatase phase and a loosely aggregation of particle after heat treatment. It was found that the catalyst used in the first stage determines the primary particle size. However the phase, the packing density and degree of dispersion of TiO₂ powder were determined by the secondly applied catalyst. Therefore, the addition sequence of catalysts is the most important key to prepare fine powders for photocatalytic use and solar cell. In this study, an acid treatment followed by a base is suggested as best route to obtaining fine size and distribution of particles and high content of anatase phase.     

Morphological and phase evolution of TiO2 nanocrystals prepared from peroxotitanate complex aqueous solution: Influence of acetic acid

Nanosized anatase and rutile TiO₂ having different shape, phase and size have been prepared from aqueous solutions of peroxo titanium complex starting from titanium(IV) isopropoxide (TTIP), acetic acid and hydrogen peroxide (H₂O₂) in water/isopropanol media by a facile sol-gel process. The TiO₂ nanocrystals are characterized by powder X-ray diffraction (XRD), Raman spectroscopy, FT-IR spectroscopy, TEM, high resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED) techniques. The influence of pH and the sequence of addition of reaction contents on the phase and morphology of TiO₂ are studied. The reasons for the observation of only anatase and/or mixture of anatase and rutile are given.     

Preparation of TiO<Subscript>2</Subscript> nanofibers immobilized on quartz substrate by electrospinning for photocatalytic degradation of ranitidine

The photocatalytic activity of TiO₂ nanofibers immobilized on quartz substrates was investigated by evaluating the decomposition of organic pollutants. TiO₂ nanofibers were synthesized by electrospinning the Ti-precursor/polymer mixture solution, followed by hot-pressing for enhancing the adhesion of TiO₂-nanofiber films to the substrates. TiO₂ started to crystalize in the anatase form at 500 °C and reached the optimal photocatalytic anatase/rutile phase ratio of 70:30 at a calcination temperature of 600 °C. The TiO₂-nanofiber film was demonstrated to be an efficient photocatalyst by ranitidine decomposition under UV illumination and was proven to have a comparable photocatalytic activity with the well-known Degussa P25 nanoparticulate photocatalyst and excellent recyclability during 10 cycles of photocatalytic operation, indicating no loss of TiO₂ nanofibers during photocatalytic operations.     

Effect of silicon dioxide on the formation of the phase composition and pore structure of titanium dioxide with the anatase structure

The formation of the structure of titanium dioxide modified with silicon dioxide, which was introduced as tetraethyl orthosilicate, was studied. It was found that the formation of the nanocrystalline structure of TiO₂ occurred upon the modification of titanium dioxide with silicon dioxide. This nanocrystalline structure of TiO₂ was formed by highly dispersed anatase particles of size 6–10 nm stabilized by silicon oxide layers, which were formed upon the decomposition of tetraethyl orthosilicate. An increase in the modifier concentration resulted in a deceleration of the growth of anatase particles and an increase in the temperature of the phase transition of anatase to rutile. It was found that the anatase phase in the samples containing 5–15 wt % SiO₂ was stable up to 1000°C. The stabilization of highly dispersed anatase particles facilitated the retention of the developed fine-pore structure of xerogels with a pore diameter of 4 nm up to 900°C.