Oxygen permeability of La2Cu(Co)O4+δ solid solutions

Formation of the La₂Cu_1−xCo_xO_4+δ solid solutions with orthorhombic K₂NiF₄-type structure was found to be in the range of 0≤x≤0.30 at temperatures above 1270 K. Incorporating cobalt into the copper sublattice of lanthanum cuprate leads to increasing oxygen hyperstoichiometry and decreasing electrical conductivity. Thermal expansion coefficients of the La₂Cu_1−xCo_xO_4+δ (x=0.02–0.30) ceramics at 470–1100 K were calculated from the dilatometric data to vary in the range (12.2–13.2)×10⁻⁶ K⁻¹. Studying the dependence of oxygen permeation fluxes through La₂Cu(Co)O_4+δ on the membrane thickness demonstrated that the oxygen transport at the thickness values below 1 mm is limited by both surface exchange rate and bulk ionic conductivity. Oxygen permeability of the La₂Cu_1−xCo_xO_4+δ solid solutions was ascertained to increase with cobalt concentration at x=0.02–0.10 and to decrease with further dopant additions, indicating a participation of interstitial oxygen in the ionic transport.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part I: F-NMR investigation

A ¹⁹F-NMR investigation of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is undertaken as a function of temperature. Several F⁻ ion groups become progressively mobile at the NMR time scale at increasing temperature, the first, (F_i)_pb and (F_n)_pb, are located in the surroundings of Pb²⁺ cations, the second ones, (F_rd)_AI and (F_ra)_Al, in that of Al³⁺ cations. Four types of fluoride ions are distinguished in the ¹⁹F-NMR spectra of rigid lattice at low temperature (T = 175 K) and the distribution of fluoride ions among the four sites is determined by deconvolution of the spectra registered. The sites occupied by the (F_n)_pb anions are identified with the normal anionic sites of the fluorite network, the others with different interstitial sites.     

Intercalation thermodynamics and chemical diffusion of oxygen in the solid solution YBa2Cu3−xCoxO6+δ

The equilibrium oxygen content as a function of the temperature and oxygen pressure was measured for the solid solution YBa₂Cu_3−xCo_xO_6+δ, where x=0, 0.2, 0.4, 0.6, 0.8, by using coulometric titration in the temperature range 600–850°C and oxygen pressures between 10⁻⁵ and 1.0 atm. The change in the partial molar enthalpy and entropy of the intercalated oxygen was determined at different oxygen and cobalt contents. The oxygen chemical diffusion was studied by thermogravimetric relaxation in the oxygen-controlled atmosphere. The thermodynamic data were employed to determine how the chemical diffusion coefficient, the thermodynamic factor and the random-diffusion coefficient depend on oxygen content in specimens with different cobalt concentration. The oxygen intercalation thermodynamics and diffusivity results provide evidence of ordering phenomena on a microscopic scale in the basal plane of the tetragonal solid solution YBa₂Cu_3−xCo_xO_6+δ. A model for the oxygen diffusion is suggested to explain the large difference between the random and tracer diffusion coefficients in YBa₂Cu₃O_6+δ     

Material design of new lithium ionic conductor, thio-LISICON, in the Li2S–P2S5 system

A new lithium ionic conductor of the thio-LISICON (LIthium SuperIonic CONductor) family was found in the binary Li₂S–P₂S₅ system; the new solid solution with the composition range 0.0≤x≤0.27 in Li_3+5xP_1−xS₄ was synthesized at 700 °C and characterized by X-ray diffraction measurements. Its electrical and electrochemical properties were studied by ac impedance and cyclic voltammetry measurements, respectively. The solid solution member at x=0.065 in Li_3+5xP_1−xS₄ showed the highest conductivity value of 1.5×10⁻⁴ S cm⁻¹ at 27 °C with negligible electronic conductivity and the activation energy of 22 kJ mol⁻¹ which is characteristic of high ionic conduction state. The extra lithium ions in Li₃PS₄ created by partial substitution of P⁵⁺ for Li⁺ led to the large increase in ionic conductivity. In the solid solution range examined, the minimum conductivity was obtained for the compositions, Li₃PS₄ (x=0.0 in Li_3+5xP_1−xS₄) and Li₄P_0.8S₄ (x=0.2 in Li_3+5xP_1−xS₄); this conductivity behavior is similar to other thio-LISICON family with the general formula, Li_xM_1−yM_y′S₄ (M=Si, Ge, and M′=P, Al, Zn, Ga, Sb). Conduction mechanism and the material design concepts are discussed based on the conduction behavior and the structure considerations.     

Oxygen nonstoichiometry and phase transitions of the neodymium-rich Nd1+xBa2−xCu3Oz solid solution

On the basis of chemical, thermal analysis and Cu K-edge X-ray absorption measurements, oxygen content in the Nd_1+xBa_2−xCu₃O_z solid solution was determined between 1000°C in air and 400°C in oxygen for x=0.05–0.9 compositions. It has been observed that the oxygen nonstoichiometry Δz of the Nd_1+xBa_2−xCu₃O_7+x/2−Δz solid solution decreases 2–2.5 times for a large substitution (Δz≈0.3–0.33 for x=0.9), despite of the acclaimed higher total oxygen content. The difference in nonstoichiometry is explained by a higher average value of the copper oxidation state (ACV), which is vital for the solid solution with large x even at elevated temperatures (ACV≈2–2.05 for x>0.3 at 1000°C, PO₂=0.21 atm). On the contrary, the ACV after complete oxygenation is almost constant (about 2.25–2.3) for the whole series. The x-dependence of the oxygen content is not monotonous and structural phase transitions can be observed at x=0.3 and x=0.6, as confirmed by the X-ray diffraction and the Raman scattering spectroscopy. The first well-known transition is connected with the oxygen disorder due to the Nd substitution for Ba at random Ba-sites. In the present work, it is proved by the apical oxygen mode broadening in Raman spectra. Ordering of the Nd and Ba atoms with a subsequent orthorhombic distortion of the lattice may occur even at 1000°C in air due to the second transformation at x≈0.6. The invariable orthorhombicity of the Nd-rich solid solution with x>0.6 is not caused by the oxygen absorption as in the x=0.05 case. Existence of high- and low-temperature orthorhombic modifications of this solid solution has been observed for the first time. Finally, a tentative 3D (z–x–T) diagram is suggested for the Nd_1+xBa_2−xCu₃O_z solid solution up to 1000°C in air, including the new x=0.6–0.9 region.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Infrared spectra and transport properties of Li-doped La214 system

The microstructure, charge transport and phonon vibration of polycrystalline samples of Li-doped La214 system have been studied by X-ray diffraction, resistivity and transmission infrared (IR) spectra. It is found that the doping of Li in La₂Cu_1−xLi_xO_y (0x0.5) and La_1.85+xSr_0.15−xCu_1−xLi_xO_y shows different effects on the crystal structure and resistivity. The change of resistivity with Li doping can be interpreted based on the variation of carrier concentration and impurity scattering. The shift of two IR vibration modes around 512 and 683 cm⁻¹, which are referred to the vibrations of apical oxygen and planar oxygen, is analyzed in detail. The change of the intensity for the mode around 683 cm⁻¹ is interpreted in terms of the screened effect of charge carrier in CuO₂ plane. The relation among crystal microstructure, carrier concentration, transport properties and phonon vibration is analyzed and discussed based on the experiment results.     

Phase equilibria at low oxygen partial pressure in the Y---Ba---Cu---O system

The phase equilibria around YBa₂Cu₃O_7−x (123) and YBa₂Cu₄O₈ (124) phases at low oxygen partial pressure (1 atm) were investigated by X-ray diffraction and thermal analysis. The coexistence of 123 and 124 phase was confirmed under 1 atm oxygen pressure. By using the high temperature X-ray diffraction method, the univariant reaction YBa₂Cu₃O_7−x+Cu₂OY₂BaCu₂O₂+O₂ was identified. The oxygen partial pressure dependence of several univariant reactions has been investigated and the existence of two invariant reactions of L+O₂YBa₂Cu₃O_7−x+ BaCuO₂+CuO+Cu₂O and L+Y₂BaCuO₅+O₂YBa₂Cu₃O_7−x+CuO+Cu₂O was deduced to occur at 1103 K under 0.0032 atm O₂ and at 1143 K under 0.0085 atm O₂, respectively.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Structure, oxygen stoichiometry and electrical conductivity in the system Sr-Ce-Co-O

Mixed oxides in the system S-Ce-Co-O were prepared by solid state reaction and by freeze-drying of precursor compounds followed by thermal treatment. Two types of perovskite oxides exist in the system: Solid solutions of the type Sr_{1 − y}Ce_yCoO_{3 − x} and mixed oxides of the type (1 − y)SrCeO₃ − ySrCoO_{3 − x}. Microstructures and phase compositions were determined by electron microscopy and X-ray diffraction. SrCoO_{3 − x} forms a solid solution of ceria on the A-site in the strontium cobaltite lattice up to 0.15 mol Ce. This solid solution corresponds to the high-temperature structure of pure SrCoO_{3 − x} and is characterized by high oxygen exchange and electrical conductivity. The oxygen deficiency x was measured by solid electrolyte coulometry. The oxygen deficiency of solid solutions Sr_{1 − y}Ce_yCoO_{3 − x} increases with temperature and decreases with pO₂ in the ambient atmosphere and with increasing Ce dopant concentration. The pO₂-T-x diagram of the solid solution was determined. The T, pO₂ and dopant concentration dependencies of electrical conductivity were measured by a four-point d.c. technique. By Ce doping strontium cobaltite becomes a stabilized high-conductive material (maximum conductivity: 500 S cm⁻¹ at 400 °C, E_a = 0.025 eV, p-type). Above this temperature the T-coefficient of the conductivity changes from positive (semiconducting) to negative values.     

Determination of different oxygen transport mechanisms and measurement of the oxygen ion conductivity of Y1Ba2Cu3O7−x

By undertaking AC electrochemical impedance experiments on yttria stabilised zirconia electrolytes with polished Y₁Ba₂Cu₃O_7−x electrodes, the activation energy for oxygen ion transport within the bulk of Y₁Ba₂Cu₃O_7−x, in air, over the temperature range 823 K–1043 K, was determined to be 1.50 ± 0.05 eV. At 1000 K the oxygen ionic conductivity was calculated to be around one order of magnitude lower than that in yttria stabilised zirconia. Typical calculated values were σ=5×10⁻⁵ (ω cm)⁻¹ and 6×10⁻³ (ω cm)⁻¹ at the respective temperatures 823 K and 1043 K. By employing a similar cell but with Y₁Ba₂Cu₃O_7−x paste electrodes, oxygen transfer between the Y₁Ba₂Cu₃O_7−x and the electrolyte was found to occur via a surface diffusional processes. Over the temperature range 873 K–1098 K, in air, the activation energy for in-diffusion at the surface was found to be 1.4±0.1 eV and that for out-diffusion at the surface to be 1.76±0.05 eV.     

Shaped crystal growth and scintillating properties of Yb:(Gd,Lu)3Ga5O12 solid solutions

Shaped single crystals of (Lu_xGd_1−x)₃Ga₅O₁₂ (0.0x1.0) and (Yb_0.05Lu_xGd_0.95−x)₃Ga₅O₁₂ (0.0x0.9) were grown by the modified micro-pulling-down method. Continuous solid solutions with garnet structure and a linear compositional dependency of crystal lattice parameter in the system Yb:(Gd,Lu)₃Ga₅O₁₂ are formed. Measured optical absorption spectra of the samples show 4f–4f transitions related to Gd³⁺ ion at 275 and 310 nm, and also an onset of charge transfer transitions from oxygen ligands to Gd³⁺ or Yb³⁺ cations below 240 nm. A complete absence of Yb³⁺ charge transfer luminescence under X-ray excitation in any of the investigated samples was explained by the overlapping of charge transfer absorption of Yb³⁺ by that of Gd³⁺ ions. For specific composition of Lu_1.5Gd_1.5Ga₅O₁₂ an intense defect-host lattice-related emission, which achieve of about 40% integrated intensity compared with Bi₄Ge₃O₁₂, was found.     

Synthesis and investigation of the complex copper oxides Bi2Sr2R2−xCexCu2O10+δ (R=rare earth)

Bi-2222 phases were prepared by solid state reactions and were studied using X-ray diffraction, chemical and EDS-analysis. Compounds with composition Bi₂Sr₂R_1.33Ce_0.67Cu₂O_10+δ were obtained for R=Pr, Nd, Sm-Er. The phases Bi₂Sr₂Cu₂O_10+δ with similar structure but without Ce were prepared for R = Pr, Sm-Dy. For Bi₂Sr₂Eu_2−xCe_xCu₂O_10+δ the solubility limit was determined and the effect of treatment under different oxygen pressures was investigated. Weak diamagnetic signals (<3%) were detected for some of these samples.     

Effects of cation- or oxide ion-defect on conductivities of apatite-type La–Ge–O system ceramics

A series of apatite-type La–Ge–O ceramics were prepared and their cation-defect at the 4f+6h sites and oxide ion-defect at 2a site were investigated. In La_xGe₆O_12+1.5x ceramics of x=6–12, the higher conductivities were obtained in the region of apatite composition, La_x(GeO₄)₆O_1.5x−12 (x=8–9.33), and the highest conductivity was achieved for La₉(GeO₄)₆O_1.5 (x=9), where the number of cation (La³⁺) occupying the 4f+6h sites is 9 and the number of oxide ion occupying the 2a site is 1.5. The ceramics with cation- and oxide ion-defects were La_9−0.66xSr_x(GeO₄)₆O_1.5 (x=0–1), La_9−1.33xZr_x(GeO₄)₆O_1.5 (x=0–1), La_9−xSr_x(GeO₄)₆O_1.5−0.5x (x=0–3), La_9−xZr_x(GeO₄)₆O_1.5+0.5x (x=0–1), La_x(GeO₄)_3x−21(AsO₄)_27−3xO_1.5 (x=0–3), La_x(GeO₄)_33−3x(AlO₄)_3x−27O_1.5 (x=0–3), La₉(GeO₄)_6−x (AlO₄)_xO_1.5−0.5x (x=0–3), La₉(GeO₄)_6−x(AsO₄)_xO_1.5+0.5x (x=0–1), La_9.33−xSr_x(GeO₄)₆O_2−0.5x (x=0–1.2) and La_x(GeO₄)_4.5(AlO₄)_1.5O_1.5x−12.75 (x=8.8–9.83), which were prepared by the partial substitution of La³⁺and GeO₄⁴⁻of the basic apatite La₉(GeO₄)₆O_1.5 with Sr²⁺ or Zr⁴⁺ and AlO₄⁵⁻ or AsO₄³⁻. Such substitutions lowered the conductivity of La₉(GeO₄)₆O_1.5. These results were discussed by the electrostatic interaction between Sr²⁺, Zr⁴⁺, AlO₄⁵⁻ or AsO₄³⁻ and oxide ion as a conductive species.     

Influence of Nd substitution on the superconducting properties of ceramics in the 2212 system Bi2−wPbwSr2−xCa1−yNdx+yCu2O8+z

In the system Bi_2−wPb_wSr_2−xCa_1−yNd_x+yCu₂O_8+z different fractions of Nd are substituted on either Sr of Ca sites in order to introduce intrinsic insulating pinning centres. It is shown that a Nd concentration around x or y = 0.2 is likewise favourable with an average Nd---Nd distance in the range of the coherence length in the a, b-plane. However, clear evidence of flux pinning is only present for charge compensation with Pb²⁺. A simultaneous substitution of the Bi-based 2212 superconductor with moderate amounts of Nd³⁺ and Pb²⁺ improves the superconducting properties by strengthening the flux pinning forces.     

Preparation, characterization and oxide ion conductivity in U-substituted Bi4V2O11

A Bi₂V_{1 − x − y}U_xBi_yO_{5.5 + 0.5x − y} solid solution derived from Bi₄V₂O₁₁ has been prepared and characterized with x up to 0.125 for y = 0. Partial substitution of U⁶⁺ for V⁵⁺ in Bi₄V₂O₁₁ leads to the stabilization at room temperature of the high-oxide ion conducting γ-phase, in contrast with other M⁶⁺ dopants which stabilize the β-phase. The lower conductivity in U substituted system compared with BICUVOX.10 is attributed to its higher activation energy. Conductivity values and activation energies of the U substituted phases compare well with Bi₂UO₆.     

Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Relationship between electronic and crystal structure in Cu–Ni–Co–Mn–O spinels: Part B: Binding energy anomaly in Cu photoemission spectrum

In very rare circumstances, X-ray photoemission spectra of copper in spinel oxides exhibit a “negative binding energy shift”. The origin of such an anomalous XPS chemical shift was investigated. A metastable Ni_0.48Co_0.24Cu_0.6+xMn_1.68−xO₄ (0 < x < 0.6) spinel was fabricated at 600 °C using a low-temperature solution technique. The binding energy of the 2p_3/2 level of copper (930.8 eV) is found 1.9 eV lower than that of Cu⁰ (932.7 eV). XPS and EXAFS studies revealed that the post-thermal annealing between 600 and 800 °C undergoes an irreversible cubic-to-tetragonal phase transformation through oxidation–reduction reaction Cu¹⁺ + Mn⁴⁺  Cu²⁺ + Mn³⁺, and only tetrahedral Cu¹⁺ species in the cubic spinel shows this anomalous chemical shift. The negative shift of the core levels was correlated to an equal shift of the Cu 3d valence band levels. XPS valence bands from the samples annealed at different temperatures were compared to DOS calculations. The DOS computations were performed with FEFF-8.1 code using experimental crystal parameters established by the EXAFS analysis. It was found that the tetrahedral Cu¹⁺ in the 600 °C annealed sample exhibits localization of the 3d orbitals showing behavior characteristic to zinc. The completely filled and isolated 3d electron shell appears as a false valence band edge in the XPS spectrum. The position of the Cu 3d, and other core levels, is established by oxygen pinning the Cu valence band levels and by the fixed value of the p–d gap characteristic to the tetrahedral copper environment in this spinel.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Effect of Hg addition on synthesis of Bi-based superconductors

We have investigated the effect of Hg addition on the superconducting properties of BiSrCaCuO system. Polycrystalline samples with nominal composition Bi₂Sr_2−xHg_xCa₁Cu₂O_y and Bi₂Sr_2−xHg_xCa₂Cu₃O_y (x=0.3) were synthesized and used to investigate the phase evolution by XRD, superconducting behaviour by R–T measurement and the structural grain boundary effects by SEM. From these measurements, it has been noticed that the phases obtained with both types of compositions are the same as Bi2212 but the T_c values are different. With additional annealing, T_{c zero} values were raised from 60 to 72 K in Bi₂Sr_2−xHg_xCa₁Cu₂O_y and 64 to 92 K in Bi₂Sr_2−xHg_xCa₂Cu₃O_y. Also, an improved grain boundary linkage has been observed by SEM for the 92 K sample.