Size,composition and optical properties of copper nanoparticles prepared by laser ablation in liquids

Colloidal copper nanoparticles were prepared by pulsed Nd:YAG laser ablation in water and acetone. Size and optical properties of the nanoparticles were characterized by transmission electron microscopy and UV–visible spectrophotometry, respectively. The copper particles were rather spherical and their mean diameter in water was 30 nm, whereas in acetone much smaller particles were produced with an average diameter of 3 nm. Optical extinction immediately after the ablation showed surface plasmon resonance peaks at 626 and 575 nm for the colloidal copper in water and acetone, respectively. Time evaluation showed a blue shift of the optical extinction maximum, which is related to the change of the particle size distribution. Copper nanoparticles in acetone are yellowish and stable even after 10 months. In water, the color of the blue-green solution was changed to brown-black and the nanoparticles precipitated completely after two weeks, which is assigned to oxidation of copper nanoparticles into copper oxide (II) as was confirmed by the electron diffraction pattern and optical absorption measurements. We conclude that the ablation of bulk copper in water and acetone is a physical and flexible method for synthesis of stable colloidal copper and oxidized copper nanoparticles. PACS 42.62.-b; 81.07.-b; 61.46.+w     

Synthesis and characterization of spherical and narrow size distribution indium oxide nanoparticles

This work reports the synthesis of indium oxide nanoparticles and their thermal, structural, microstructural and optical characterization. The preparation method is based on a surfactant-free room temperature soft chemistry route. Spherical indium oxide nanoparticles (about 8 nm in diameter) were obtained after thermal treatment of gels at 400 °C for 2 h, as shown by X-ray diffraction experiments and nitrogen adsorption measurements. Transmission electron microscopy observations confirm the single-crystalline nature of the produced nanoparticles. The photoluminescence emission spectrum at room temperature shows a broad peak with onset at approximately 315 nm as a result of quantum size effect as revealed by small-angle X-ray scattering.     

Optical diagnostics of physicochemical properties of NiO/Al2O3 nanocomposites upon exposure to different gases and heat

We have studied nanostructural and optical properties of composites of nanostructured nickel oxide films on a substrate from porous aluminum oxide NiO/Al₂O₃ in the UV, visible, and IR spectral ranges on exposure of composites to different gases, vacuum, and heat. We have found that, upon irradiation of NiO/Al₂O₃ composites by laser radiation at a wavelength of 633 nm, they demonstrate a high sensitivity to carbon monoxide CO in the range of the excitonic absorption of nickel oxide. We assume that an increase in the transmission coefficient of the composite in the excitonic absorption band is determined by luminescence that is caused by the oxidation reaction of carbon monoxide. The sensitivity of composites to CO is enhanced with decreasing the size of NiO nanoparticles and after evacuation. The values of the diffuse reflection coefficient at the laser radiation wavelength of 633 nm correlate with the size of nickel oxide nanoparticles. Spectral changes in the range of the fundamental absorption band of NiO that occur in the IR range and in diffuse reflection spectra are related to the appearance of carbon-containing compounds in the composite exposed to CO.     

Nanoparticles size modifications during femtosecond laser ablation of nickel in vacuum

Nanoparticles were synthesized by irradiating a nickel target with femtosecond laser pulses in high vacuum, and subsequently analyzed. The proof-of-principle experiments aim to modify the size characteristics of the produced nanoparticles. For nickel it is found that: (i) ultraviolet laser pulses lead to a remarkable change in the nanoparticles size distribution with respect to visible laser pulses; (ii) irradiation of the femtosecond pulses induced ablation plume with a second, delayed ultraviolet laser pulse can change the size characteristics of the produced nanoparticles.     

Silver nanoparticles produced by PLD in vacuum: role of the laser wavelength used

In this work we report the results of investigation of silver (Ag) nanoparticles prepared on a silica substrate by laser ablation. Our attention was focused on the mean diameter, size distribution and optical absorption properties of nanoparticles prepared in vacuum by using different laser wavelengths. The fundamental wavelength and the second, third, and fourth harmonics of a nanosecond Nd:YAG laser were used for nanoparticles fabrication. The corresponding values of the laser fluence for each wavelength were: 0.6 J/cm² at 266 nm, 0.8 J/cm² at 355 nm, 2.8 J/cm² at 532 nm, and 2 J/cm² at 1064 nm. The Ag nanoparticles produced have mean diameters in the range from 2 nm to 12 nm as the nanoparticles’ size decreases with the decrease of the wavelength used. The presence of the Ag nanoparticles was also evidenced by the appearance of a strong optical absorption band in the measured UV-VIS spectra associated with surface plasmon resonance (SPR). A redshift and widening of the absorption peak were observed as the laser wavelength was increased. Some additional investigations were performed in order to clarify the structure of the Ag nanoparticles.     

Effect of surrounding gas temperature on the morphological evolution of TiO2 nanoparticles generated by laser ablation in tubular furnace

Titanium oxide nanoparticles are synthesized by laser ablation of Ti target in oxygen atmosphere under well-controlled temperature profiles in a tubular furnace. The size and the shape of generated nanoparticles are varied by changing the temperature of furnace. The mobility-based size distributions of generated air-borne nanoparticles are measured using a scanning mobility particle sizer, and the size distributions of primary particles are analyzed by a scanning electron microscope. When the particles are generated by laser ablation at the room temperature, the particles are agglomerates in gas phase with the average mobility diameter of 117 nm and the mean diameter of primary particles of 11 nm. The primary particle diameter increases from 11 to 24 nm by raising the furnace temperature up to 800 °C. Since the mass of Ti vapor ablated from a target is found to be constant regardless of the furnace temperature, this particle growth may be attributed to the reduction in nuclei number as a result of mild quenching at higher temperatures. As the temperature reaches higher than 1,000 °C, the mobility diameter suddenly drops and the primary particle diameter increases due to sintering, and at 1,200 °C the mobility diameter coincides with the primary particle diameter. Since the laser oven method offers an independent control of vapor concentration and the temperature of surrounding atmosphere, it is an effective tool to study the formation process of nanoparticles from primary particles with a given size.     

Laser ablation of microparticles for nanostructure generation

The process of laser ablation of microparticles has been shown to generate nanoparticles from microparticles; but the generation of nanoparticle networks from microparticles has never been reported before. We report a unique approach for the generation of nanoparticle networks through ablation of microparticles. Using this approach, two samples containing microparticles of lead oxide (Pb₃O₄) and nickel oxide (NiO), respectively, were ablated under ambient conditions using a femtosecond laser operating in the MHz repetition rate regime. Nanoparticle networks with particle diameter ranging from 60 to 90 nm were obtained by ablation of microparticles without use of any specialized equipment, catalysts or external stimulants. The formation of finer nanoparticle networks has been explained by considering the low pressure region created by the shockwave, causing rapid condensation of microparticles into finer nanoparticles. A comparison between the nanostructures generated by ablating microparticle and those by ablating bulk substrate was carried out; and a considerable reduction in size and narrowed size distribution was observed. Our nanostructure fabrication technique will be a unique process for nanoparticle network generation from a vast array of materials.     

氧化铜纳米粒子的制备及其SERS特性

采用激光刻蚀法在水溶液中制备了氧化铜纳米粒子,刻蚀完成后将氧化铜胶体沉积在铝片上形成一层氧化铜岛膜.所得纳米粒子的紫外—可见吸收峰在280 nm处,表明所得为氧化铜.原子力显微镜观察表明所制得的纳米粒子具有椭圆状结构,长轴约为30～50 nm,厚度约为8 nm.扫描电镜图片显示氧化铜粒子沉积在铝基底后形成了大小在0.5...     

Nanoparticles of nickel oxide: growth and organization on zinc-substituted anionic clay matrix by one-pot route at room temperature

A room temperature nanocarving strategy is developed for the fabrication of nanoparticles of nickel oxide on zinc-substituted anionic clay matrix (Ni/ZnLDH). It is based on the growth and organization of nanoparticles of nickel oxide which occur during the structural reconstruction of the layered structure of the anionic clay in NiSO₄ aqueous solution. No organic compounds are used during the fabrication. The described material was characterized by X-ray diffraction (XRD), IR spectroscopy (FTIR), transmission electron microscopy (TEM), field-emission scanning electron microscopy (FESEM), energy dispersive X-ray (EDX) spectroscopy, and X-ray photoelectron spectroscopy (XPS). Results show that the nickel-clay nanoarchitecture consists of small nanoparticles of nickel oxide (average size 7 nm) deposited on the larger nanoparticles (average size 90 nm) of zinc-substituted clay. The optical properties of the new nickel-zinc formulation are studied by UV–Vis.     

Third-order nonlinearity of nickel oxide nanoparticles in toluene

We report measurements of the nonlinear refractive index, n(2), of nickel oxide nanoparticles (NPs) in toluene at 532 nm. The measurements were performed using the Z-scan technique with 80 ps laser pulses at 7 Hz. Large values of n(2) in the range of 10(-13)-10(-12) cm(2)/W were measured, and negligible two-photon absorption coefficient was estimated for colloids having NP filling fractions in the range of 10(-8)-10(-7).     

Preparation of nanosized metal (oxides) by gas phase hydrolysis using mesoporous materials as nanoreactors

Immobilized nanosized metal (oxides) on carbonaceous carriers were prepared by hydrolysis under mild conditions by using the carrier pores as a kind of nanoreactor. Metal alkoxide vapor was adsorbed on the carrier and then formed the product upon exposure to water vapor. With this facile method, Titania, Vanadia, Rhodium (oxide), and Platinum (oxide) nanostructures were prepared at high yields, high loadings, and good dispersion in the carrier material. High number concentrations of spheroidal nanoparticles of uniform size (diameter ca. 5 nm) were obtained from less reactive precursors, whereas with highly reactive precursors, such nanoparticles occurred only after subsequent calcination. Nanoparticles appeared to be the thermodynamically stable form of the metal (oxide) produced in the pores. Highly reactive precursors formed metastable seeds, which nucleated and restructured into nanoparticles upon subsequent exposure to heat. The presented method allows for preparation of metal (oxide) nanostructures and effective control of their size and shape.     

Effect of laser fluence on the size of copper oxide nanoparticles produced by the ablation of Cu target in double distilled water

Copper oxide nanoparticles produced in double distilled water at room temperature by laser ablation of the Cu target have been investigated using TEM, SEM, AFM, X-ray diffraction, photo-spectrometry and PIXE. Q-switched Nd:YAG laser operating at 1064 nm with a pulse duration of 5–6 ns was used to conduct the experiments in the fluence range of 5.73–9.87 J/cm². In each experiment, 12,000 laser pulses were used to ablate the target placed in double distilled water. Different diagnostic techniques reveal that the nanoparticles have a size between 2–55 nm and their mean size as well as the width of particle distribution increases with the laser fluence. Since no surface active material (surfactant) was added to water, the nanoparticles aggregated and settled down at the bottom of the container within a week. In addition to stable Cu₂O, the XRD spectrum also shows the presence of suboxide Cu₆₄O in the colloidal solution of nanoparticles produced in the present study.     

Ex vivo assessment of polyol coated-iron oxide nanoparticles for MRI diagnosis applications: toxicological and MRI contrast enhancement effects

Polyol synthesis is a promising method to obtain directly pharmaceutical grade colloidal dispersion of superparamagnetic iron oxide nanoparticles (SPIONs). Here, we study the biocompatibility and performance as T2-MRI contrast agents (CAs) of high quality magnetic colloidal dispersions (average hydrodynamic aggregate diameter of 16-27 nm) consisting of polyol-synthesized SPIONs (5 nm in mean particle size) coated with triethylene glycol (TEG) chains (TEG-SPIONs), which were subsequently functionalized to carboxyl-terminated meso-2-3-dimercaptosuccinic acid (DMSA) coated-iron oxide nanoparticles (DMSA-SPIONs). Standard MTT assays on HeLa, U87MG, and HepG2 cells revealed that colloidal dispersions of TEG-coated iron oxide nanoparticles did not induce any loss of cell viability after 3 days incubation with dose concentrations below 50 μg Fe/ml. However, after these nanoparticles were functionalized with DMSA molecules, an increase on their cytotoxicity was observed, so that particles bearing free terminal carboxyl groups on their surface were not cytotoxic only at low concentrations (<10 μg Fe/ml). Moreover, cell uptake assays on HeLa and U87MG and hemolysis tests have demonstrated that TEG-SPIONs and DMSA-SPIONs were well internalized by the cells and did not induce any adverse effect on the red blood cells at the tested concentrations. Finally, in vitro relaxivity measurements and post mortem MRI studies in mice indicated that both types of coated-iron oxide nanoparticles produced higher negative T2-MRI contrast enhancement than that measured for a similar commercial T2-MRI CAs consisting in dextran-coated ultra-small iron oxide nanoparticles (Ferumoxtran-10). In conclusion, the above attributes make both types of as synthesized coated-iron oxide nanoparticles, but especially DMSA-SPIONs, promising candidates as T2-MRI CAs for nanoparticle-enhanced MRI diagnosis applications.     

Characterization of optical and nonlinear optical properties of silver nanoparticles prepared by laser ablation in various liquids

The optical, structural, and nonlinear optical properties of silver nanoparticles prepared by laser ablation in various liquids were investigated at 397.5, 532, and 795 nm. The TEM and spectral measurements have shown temporal dynamics of size distribution of Ag nanoparticles in solutions. The thermal-induced self-defocusing dominated in the case of high pulse repetition rate as well as in the case of nanosecond pulses. In the case of low pulse repetition rate, the self-focusing (γ = 3 × 10⁻¹³ cm² W⁻¹) and saturated absorption (β = −1.5 × 10⁻⁹ cm W⁻¹) of picosecond and femtosecond radiation were observed in these colloidal solutions. The nonlinear susceptibility of Ag nanoparticles ablated in water was measured to be 5 × 10⁻⁸ esu (at λ = 397.5 nm).     

Properties of pulsed laser deposited nanocomposite NiO:Au thin films for gas sensing applications

Nanocomposite thin films formed by gold nanoparticles embedded in a nickel oxide matrix have been synthesized by a new variation of the pulsed laser deposition technique. Two actively synchronized laser sources, a KrF excimer laser at 248 nm and an Nd:YAG laser at 355 nm, were used for the simultaneous ablation of nickel and gold targets in oxygen ambient. The structural, morphological, and electrical properties of the obtained nanocomposite films were investigated in relation to the fluence of the laser irradiating the gold target. The nanocomposite thin films were tested as electrochemical hydrogen sensors. It was found that the addition of the gold nanoparticles increased the sensor sensitivity significantly.     

Ni nanoparticles fabricated by laser ablation in water

Nickel nanoparticles were fabricated by ablating a bulk Ni target with pulsed 337-nm laser radiation in distilled water. Transmission electron microscope images of the removed material show spherical particles with two size scales: tens of nm and hundreds of nm. Phase explosion and Rayleigh–Plateau hydrodynamic instability are suggested as being responsible for this distribution. An X-ray diffraction pattern of the ablated material demonstrates the presence of both nickel and nickel oxide.     

Size-tuneable synthesis of nickel nanoparticles

A facile method is described for synthesising nickel nanoparticles via the thermal decomposition of an organometallic precursor in the presence of excess n-trioctylphosphine as a capping ligand. For the first time, alkylamines with different chain lengths were employed as size-limiting agents in this synthesis. A direct correlation is demonstrated between the size of the alkylamine ligands used and the mean diameter of the nickel nanoparticles obtained. The use of bulky oleylamine as a size-limiting agent over a reaction period of 30 min led to the growth of nickel nanoparticles with a mean diameter of 2.8 ± 0.9 nm. The employment of less bulky N,N-dimethylhexadecylamine groups led to the growth of nickel nanoparticles with a mean diameter of 4.4 ± 0.9 nm. By increasing the reaction time from 30 to 240 min, while employing oleylamine as the size-limiting agent, the mean diameter of the nickel nanoparticles was increased from 2.8 ± 0.9 to 5.1 ± 0.7 nm. Decreasing the amount of capping ligand present in the reaction system allowed further growth of the nickel nanoparticles to 17.8 ± 1.3 nm. The size, structure and morphology of the nanoparticles synthesised were characterised by transmission electron microscopy and powder X-ray diffraction; while magnetic measurements indicated that the particles were superparamagnetic in nature.     

Electrical and magnetic properties of polyaniline/Fe3O4 nanostructures

We report on electrical and magnetic properties of polyaniline (PANI) nanotubes (150 nm in diameter) and PANI/Fe₃O₄ nanowires (140 nm in diameter) containing Fe₃O₄ nanoparticles with a typical size of 12 nm. These systems were prepared by a template-free method. The conductivity of the nanostructures is 10⁻¹–10⁻² S/cm; and the temperature dependent resistivity follows a ln ρT^−1/2 law. The composites (6 and 20 wt% of Fe₃O₄) show a large negative magnetoresistance compared with that of pure PANI nanotubes and a considerably lower saturated magnetization (M_s=3.45 emu/g at 300 K and 4.21 emu/g at 4 K) compared with the values measured from bulk magnetite (M_s=84 emu/g) and pure Fe₃O₄ nanoparticles (M_s=65 emu/g). AC magnetic susceptibility was also measured. It is found that the peak position of the AC susceptibility of the nanocomposites shifts to a higher temperature (>245 K) compared with that of pure Fe₃O₄ nanoparticles (190–200 K). These results suggest that interactions between the polymer matrix and nanoparticles take place in these nanocomposites.     

Pulsed-laser generation of gold nanoparticles with on-line surface plasmon resonance detection

Size of nanoparticles is an important parameter for their applications. The real-time monitoring is required for reliable and reproducible production of nanoparticles with controllable size. We present results of our research on development of the system for the online nanoparticle characterization during their production by a laser. The laser ablation chamber which allows measurements of surface plasmon resonance spectra during the nanoparticle generation process has been designed and fabricated. The online characterization system was tested by producing and modification of gold nanoparticles. Nanoparticles were generated by nanosecond-laser (wavelength 1064 nm) ablation of gold target in deionized water, and optimal conditions for the highest nanoparticle productivity were estimated. The mean diameter of nanoparticles was determined using their absorption spectra measured in the real-time during the ablation experiments and from the TEM images analysis, and it varied from 20 to 45 nm. The mismatch between nanoparticle diameters, estimated using these two methods, is due to the polydispersity of the generated nanoparticles. The further experiments of laser-induced modification of colloidal gold nanoparticles were carried out using second harmonic (wavelength 532 nm) of nanosecond Nd:YAG laser and alteration in nanoparticle size were acquired by the online measurement system.     

Optical properties of sol-gel fabricated Ni/SiO2 glass nanocomposites

Nickel nanoparticles were grown in silica glass by annealing of the sol-gel prepared silicate matrices doped with nickel nitrate. TEM characterization of Ni/SiO₂ glass proves the formation of isolated spherical nickel nanoparticles with mean sizes 6.7 and 20 nm depending on annealing conditions. The absorption and photoluminescence spectra of Ni/SiO₂ glasses were measured. In the absorption spectra, we observed the band related to the surface plasmon resonance (SPR) in Ni nanoparticles. The broadening of SPR was observed with decrease of Ni nanoparticle size. The width of the surface plasmon band decreases 1.5 times at the lowering of temperature from 293 to 2 K because of strong electron-phonon interaction. The spectra proved the creation of nickel oxide NiO clusters and Ni²⁺ ions in silica glass as well.