A note on Ξc(3055)+ and Ξc(3123)+

The Babar Collaboration announced two new excited charmed baryons Ξ_c(3055)⁺ and Ξ_c(3123)⁺. We study their strong decays assuming they are D-wave states. Some assignments are excluded by comparing our numerical results with the experimental values of the total widths of Ξ_c(3055)⁺ and Ξ_c(3123)⁺. We also suggest some possible decay modes, which will be helpful to     

石墨相C_3N_4压致结构相变研究

将有机物三聚氰胺(C3N6H6)高温热解,得到了石墨相C3N4(g-C3N4)。利用同步辐射X射线衍射和金刚石对顶砧(DAC)高压技术,在室温下对g-C3N4进行了结构变化研究。实验结果表明,在16.57 GPa压力范围内,g-C3N4发生了压致结构相变,在6.6 GPa压力下,晶体结构由原来的石墨相转变为三斜相。使用Birch-Murnagha等温状态方程拟合出了样品的等温状态方程。     

PECVDSi3N4/InP界面特性的研究

本文利用Auger分析技术和C-V测量方法,详细地研究了PECVDSi₃N₄/InP界面特性,Auger能谱分析表明热处理使界面面发生互扩散,同时InP的热分解导致P元素穿过Si₃N₄薄膜到达表面。C-V测量表明Ag/Si₃N₄/InPMIS结构可以实现载流子的堆积、耗尽和反型。     

添加剂Li8SiN4对cBN晶体形貌的影响

 在4.5~5.0 GPa，1 500~1 800 ℃范围内，在Li基复合氮硼化物的催化体系中添加Li₈SiN₄后，得到了具有光泽的棕色透明的cBN单晶。研究了cBN晶体的形貌，结果表明，添加Li₈SiN₄后得到的等积形cBN晶体的百分比明显增多，除部分截角四面体外，多为截角八面体晶体，且棱角尖锐，晶面致密光滑。     

0212型Ca3Cu2O4+δCl2-y化合物高温高压合成与研究

 利用“顶角氧掺杂”机制，即以二价氧部分替代顶角一价氯，用Ag₂O做氧源，在高温高压下制备了单相的Ca₃Cu₂O_4+δCl_2-y样品。X射线衍射分析发现，随着Ag₂O含量的增加，Ca₃Cu₂O_4+δCl_2-y样品的晶格常数a逐渐变小，c逐渐增大，体现了空穴掺杂的本质。进行了电阻率和磁化率测量，没有发现超导性，可能是空穴载流子没有达到合适的浓度所致。     

La2CuO4+δ和La2-xSrxCuO4系统中的电子输运性质

 本文解释了La₂CuO_4+δ（0≤δ≤0.09）和La_2-xSr_xCuO₄（0≤x≤0.3）两种p型系统含铜稀土氧化物中的电阻和Seebeck系数与温度的依赖关系，在室温以上，一氧大气压下的La₂CuO_4+δ系统趋于失氧；在500 K以上，超导样品显示出失氧的一级相变，并且恢复到反铁磁相。在转变温度T₁≈300 K以下，对0<δ<0.05成份的样品，相分离成反铁磁相和超导相；而在T_cρ≈100 K的温度范围内，超导相进一步分离成富空穴和贫空穴畴。在0.04≤δ≤0.09范围内，T_c处的电阻陡降出现了台阶；我们认为，它反映了电子成对的起伏。在La_2-xSr_xCuO₄系统中，对于成分为01≈300 K以上，空穴的运动是弥散的，但是ΔH_m=0；而对于x≥0.22的样品，经历了从平滑到Fermi液态的转变。成份为0c1范围（其中空穴继续以弥散方式运动）是亚稳的，但是，在T_cρ≤150 K范围，出现了电荷起伏。当样品冷却通过T₁时，对于成份为0.15≤x≤0.2的样品，经历了由弥散到强质量增强巡游电子状态的转变；在T_c处，从均匀的修饰电子的正常态凝聚成超导的载流子对。在超导成份样品的正常态中，不寻常的电子-晶格相互作用，可以归结为在CuO₂面上从更离子性的到共价性的Cu:3d_x²-r²─O:P_σ键合的转变；通过这种转变，轨道杂化和Hubbard U参量随Cu─O键长和Cu原子上的外表局域氧化态都产生灵敏的变化。     

PAC investigation of qudropole interaction in nano-soft magnetic material Fe73.5Cu1Nb3Si13.5B9

The quadrupole interaction in nano-soft magnetic material Fe_73.5Cu₁Nb₃Si_13.5B₉ has been studied by perturbed angular correlation using ⁶²Zn probe nuclei from the ISOL radioactive nuclear beam facility at CIAE HI-13 tandem accelerator. Two quadrupole interaction frequencies ω₀₁=440 Mrad/s with a distribution width σ=0 and ω₀₂=90 Mrad/s with a width σ=0.48 are obtained. The fractions of ω₀₁ and ω₀₂ are 38% and 62%, respectively. The measured quadruple interaction parameters indicate that 62% of the implanted ⁶²Zn are located in the grain boundary and 32% in the grain.     

高压固相反应法合成具有理想Ruddlesden-Popper结构的Ca4Mn3O10层状化合物

 采用高压下的固相反应方法,成功地合成了具有空间群I4/mmm的理想三层结构化合物Ca₄Mn₃O₁₀。用电子显微学方法对此结构进行了研究,并提出了近似的结构模型。基于提出的模型,进行了电子衍射图和高分辨像的模拟,并与实验结果进行了比较。     

用同步辐射和高温DAC装置研究Fe2SiO4的γ→α相变动力学过程

 通过对γ-Fe₂SiO₄样品在常压和温度分别为894、926、948和993 K时转变为α相的实验的具体描述，介绍了采用同步辐射和高温DAC装置及高压高温原位X光衍射技术进行高温高压相变动力学过程研究的一般方法。     

低阈值高效率新型晶体Nd:Sr5(PO4)3F腔内倍频研究

采用氙灯泵浦新型晶体Nd:Sr₅(PO₄)₃F,以KTP晶体腔内倍频,实现了该晶体0.5295μm绿光激光BDN染料片调Q运转。测量了输出绿光激光的特性及不同腔长和染料片小信号透过率情况下的输出能量及脉冲宽度,给出了染料片调Q腔内倍频的耦合波方程组,数值求解该方程组,所得的理论数据与实验结果较好地相符。     

不同压制压力下NiFe2O4纳米固体的ESR研究

 以反滴共沉定法制备了NiFe₂O₄纳米微粉，并在不同压力下将其压制成纳成米固体，然后用XRD谱和ESR谱研究了NiFe₂O₄纳米固体结构和界百状态随压制压力的变化。实验结果表明，NiFe₂O₄纳米固体的结构在高压下没有明显的变化，但其ESR谱的共振线宽和g因子值随着压力升高均表示出先逐渐增大至最大值，然手缓慢下降的规律。这种变化可以归因于纳米固体内部界面离子间的磁相互作用在压力的下所发生和变化。这引起实验结果境示，对于NiFe₂O₄纳米固体而言，最佳的成型压力是4.5 GPa，在此压力下，NiFe₂O₄纳米粒子既可以被压制成致密的纳米固体，又能够保留下它们的纳米结构和纳米性质。     

高温高压下SrB4O7：Eu2+玻璃的晶化

 利用X射线衍射和Eu²⁺发射光谱方法研究了非晶玻璃SrB₄O₇在高温高压下的晶化。结果表明：在5.0 GPa压力下，200 ℃仍为玻璃态，只有几个强度极低的小峰，表明有晶化的迹象；600 ℃时已基本晶化，但为SrB₄O₇正交相与SrB₄O₇高压立方相二相共存；当温度提高到1 000 ℃时，晶化成了近单相的与常压SrB₄O₇粉末晶体相同的正交结构。伴随晶化度的加强，Eu²⁺发射强度增强，与Ｘ射线衍射结果相一致。     

A method of detecting capture γ-rays in a strong pulsed radiation field

We present a technology for diagnosing the D－T fusion process by detecting capture γ-rays. This technology provides an alternative route to diagnosing the D－T reaction process when a great deal of heavy Z materials surrounds the D－T region. A very important aspect of this paper is to focus on the methods of shielding low-energy γ-rays whose radiation intensity is 10⁶ times higher than that of the capture γ-rays. Another aspect is about how to distinguish signal from noise. The result of a 50/1 signal-to-noise ratio indicates that the designed double-magnetic spectrograph is very successful for diagnosing the D－T fusion reaction process.     

稀土焦绿石化合物R2Fe4/3W2/3O7的高温高压稳定性研究和X射线相分析

 本文利用X射线粉末衍射和位敏探测技术，研究了R₂Fe_4/3W_2/3O₇（R=Er、Yb、Dy）化合物经高温高压处理后的变化情况。在3.7 GPa，1 200 ℃条件下，六方相R₂Fe_4/3W_2/3O₇化合物按两种方式分解，而直接由R₂O₃，Fe₂O₃和WO₃原料出发，经上述同样的高温高压条件合成所得的产物与六方相高温高压分解产物相同，均为R₂WO₆、RFeO₃、WO₃和Fe₂O₃的多相聚合物。同时给出了R₂Fe_4/3W_2/3O₇六方相高温高压下的稳定区范围。     

压力及高压增氧对La2-xSmxCuO4结构及输运性质的影响

 对常压、高压、高压增氧条件下合成的La_2-xSm_xCuO₄（0≤x≤2.0）结构进行了研究。常压合成样品清晰地反应出样品由T→T+T′→T′相的变化，其中，T相：0相似文献   

高氧压合成产物La2CuO4+δ的相变研究

 本文采用超高氧压2.3 GPa合成方法，得到超导相含量大于30%的超导化合物La₂CuO_4+δ所采用的压力是目前所见报导中对La₂CuO₄化合物施加的最高氧压。湿化学方法测量给出过量氧含量δ=0.05±0.01，而TGA（氮气中）给出δ=0.143。高氧压合成产物经在空气中、不同温度下加热，然后淬火到室温，结果发现超导体在200~300 ℃的加热处理中存在着一个一级相变。经此相变后，超导体转变成反铁磁半导体。TGA及DSC证实了此相变的存在。该相变前后所联系的氧含量变化恰好为湿化学方法给出的结果，这部分与超导电性存在联系的过量氧，实际上引起了Cu²⁺向Cu^(2+2δ)+的转变。该结果强有力地排除了所谓“超氧化物”引起超导电性的可能性。     

常压烧结和高压合成Nd2-xCexCuO4的结构特征与导电性质

 本文在常压高温和高压高温条件下合成出了Nd_2-xCe_xCuO₄（x=0~0.20）系列样品，对比研究了两种不同条件下合成产物的结构特征与室温至液氮温区的导电性质。测试分析结果表明，高温高压（1.7 GPa，800 ℃，10 min）合成的样品与常压高温（1 000 ℃，10 h）烧结的样品具有相同的四方结构，但晶格常数随掺杂量变化有所不同，高压合成产物的c轴随掺杂量基本不变，而常压烧结样品c轴随掺杂量增加呈下降趋势。两种条件合成的样品在液氮温区均呈现出不同程度的半导体特征，经过一次高温淬火后处理后，高压样品的导电性质明显优于常压样品。实验结果表明，高压可以降低固相反应的合成温度，缩短反应时间，特别是高压的还原作用有利于产物导电性质的改善。     

Developments in accelerator mass spectrometry (AMS) method for 182Hf

The present detection limit for ¹⁸²Hf at CIAE HI-13 AMS systems could not satisfy various applications (e. g. detection of a nearby supernovae signal). Therefore, techniques were developed in this work to improve the AMS measurement of ¹⁸²Hf mainly on building a new injector and using a method that based on solid-phase reaction for the preparation of HfF₄ samples from HfO₂. The experimental results show that mass resolution of the injector can reached 630, and the F^－/O－ and beam current of ¹⁸⁰HfF₅^－ for HfF₄ samples produced by dry method is about 2—3 times and 1.5 times of that by previously method, respectively.     

Effects of Single Vacancy on Electronic and Optical Properties for γ-Si3N4

基于密度泛函理论的广义梯度近似方法研究了中性单点缺陷γ-Si₃N₄的能量、电子结构和光学性质. N缺陷的结合能和形成能比Si(8)和Si(4)位的都低,显示γ-Si₃N₄中N缺陷更易形成. 分析了各种缺陷情况下相应的态密度. Si缺陷能形成p型半导体,N缺陷使材料形成间接带隙的n型半导体. Si缺陷情况下,物质有相对大的静态介电常数,在可见光区和红外区,吸收和反射得到显著改善,但是N缺陷却没什么影响.     

含硼条形金刚石的生成与成因探讨

 在1 470 ℃、5.9 GPa的高温高压条件下，由Fe₅₅Ni₂₉Co₁₆+B₄C体系合成出了十分规则的条形金刚石，这在人工合成金刚石实验中是少见的。并与Ni₇₀Mn₂₅Co₅+B₄C体系中的情形作了比较，探讨了条形金刚石的形成原因，其分析为获得实用性的条形金刚石提供了可能的途径。