Dynamic response and energy dissipation characteristics of balsa wood: experiment and analysis

Dynamic response of a cellular sandwich core material, balsa wood, is investigated over its entire density spectrum ranging from 55 to 380 kg/m³. Specimens were compression loaded along the grain direction at a nominal strain rate of 3 × 10³ s⁻¹ using a modified Kolsky (split Hopkinson) bar. The dynamic data are discussed and compared to those of quasi-static experiments reported in a previous study (Mech. Mater. 35 (2003) 523). Results show that while the initial failure stress is very sensitive to the rate of loading, plateau (crushing) stress remains unaffected by the strain rate. As in quasi-static loading, buckling and kink band formation were identified to be two major failure modes in dynamic loading as well. However, the degree of dynamic strength enhancement was observed to be different for these two distinct modes. Kinematics of deformation of the observed failure modes and associated micro-inertial effects are modeled to explain this different behavior. Specific energy dissipation capacity of balsa wood was computed and is found to be comparable with those of fiber-reinforced polymer composites.     

Strength and stiffness of sandwich beams in bending

This investigation is concerned with the experimental versus analytical correlation of the mechanical properties of sandwich-beam specimens. Such sandwich structures are commonly employed in the aircraft industry. Four-point and three-point load tests were conducted on a large number of sandwich-beam specimens, fabricated by using fiber-glass reinforced plastics (both unidirectional and woven-glass cloth) and DTD 685 aluminum alloy for the facings with aluminum honeycomb core and polyurethane foam cores and the indigenously available Araldite as the bonding medium between the core and the facings.The flexural stiffness of the composite sandwich specimens used in this investigation compared favorably with theoretical predictions. The shear stiffness was found to be about 55 percent and 45 percent of the theoretically predicted values for FRP (fiberglass-reinforced-plastic) cloth and FRP unidirectional laminates with aluminum honeycomb core sandwich, respectively. The failure load as determined by experiments was less than the theoretically predicted safe load. There was a loss of strength as well as a steep decrease in the failure load in the case of low density foam core.It was concluded that FRP facing plates with aluminum honeycomb core sandwich structure may be preferred to similar aluminum-alloy facing sandwich construction if high flexural stiffness and shear stiffness properties are required at less cost and weight. Indigenously available Araldite was quite satisfactory for bonding the core to the facings.This investigation has confirmed the importance of experiments in the field of sandwich structures which can effectively replace other conventional uneconomical structural or machine members which are currently in use.     

环氧树脂/泡沫铝一体型复合夹层板压缩及弯曲试验研究

提出了一种环氧树脂/泡沫铝一体型复合夹层板,通过准静态试验以及与纯泡沫铝、传统蒙皮夹层板的对比研究了其破坏过程、破坏形貌、破坏机理及压缩和弯曲力学性能。分别通过压缩应力-应变曲线和弯曲荷载-挠度曲线分析了复合层厚度对压缩及弯曲力学性能的影响,并与传统夹层板的力学性能进行了比较。结果表明,随着夹层板中环氧树脂/泡沫铝复合层厚度增加,其压缩弹性模量和抗压强度增加,弯曲承载力提高。相比传统蒙皮夹层板,由于表层和芯层之间没有明显界面,大大提高了夹芯板的整体性,在受力过程中不会出现表层剥离等现象。     

Compressive response of a sandwich plate containing a cracked diamond-celled lattice

The compressive strength is determined for a sandwich plate containing a centre-cracked core made from an elastic–brittle, diamond-celled lattice. It is assumed that the lattice fails when the major component of principal stress anywhere in the lattice attains the compressive or tensile strength of the solid, or when local buckling intervenes. First, analytical and numerical predictions are given for the unnotched strength of the core and for the compressive fracture toughness of the lattice K_IC. Second, finite element simulations and analytical models are reported for the fracture response of the sandwich plate with cracked core. The active failure mechanism in the cracked core is sensitive to core height, crack length, lattice geometry and material choice; this is illustrated by means of material-property charts.     

Multiobjective optimization for design of multifunctional sandwich panel heat pipes with micro-architected truss cores

A micro-architected multifunctional structure, a sandwich panel heat pipe with a micro-scale truss core and arterial wick, is modeled and optimized. To characterize multiple functionalities, objective equations are formulated for density, compressive modulus, compressive strength, and maximum heat flux. Multiobjective optimization is used to determine the Pareto-optimal design surfaces, which consist of hundreds of individually optimized designs. The Pareto-optimal surfaces for different working fluids (water, ethanol, and perfluoro(methylcyclohexane)) as well as different micro-scale truss core materials (metal, ceramic, and polymer) are determined and compared. Examination of the Pareto fronts allows comparison of the trade-offs between density, compressive stiffness, compressive strength, and maximum heat flux in the design of multifunctional sandwich panel heat pipes with micro-scale truss cores. Heat fluxes up to 3.0 MW/m² are predicted for silicon carbide truss core heat pipes with water as the working fluid.     

Elastoplastic buckling and post-buckling analysis of sandwich columns

Sandwich structures are widely used in many industrial applications thanks to their interesting compromise between lightweight and high mechanical properties. This compromise is realized thanks to the presence of different parts in the composite material, namely the skins which are particularly thin and stiff relative to the homogeneous core material and possibly core reinforcements. Owing to these geometric and material features, sandwich structures are subject to global but also local buckling phenomena which are mainly responsible for their collapse. The buckling analysis of sandwich materials is therefore an important issue for their mechanical design. In this respect, this paper is devoted to the theoretical study of the local/global buckling and post-buckling behavior of sandwich columns under axial compression. Only symmetric sandwich materials are considered with homogeneous and isotropic core/skin layers. First, the buckling problem is analytically addressed, by solving the so-called bifurcation equation in a 3D framework. The bifurcation analysis is performed using an hybrid model (the two faces are represented by Euler–Bernoulli beams, whereas the core material is considered as a 2D continuous solid), considering both an elastic and elastoplastic core material. Closed-form expressions are derived for the critical loadings and the associated bifurcation modes. Then, the post-buckling response is numerically investigated using a 2D finite element bespoke program, including finite plasticity, arc-length methods and branch-switching procedures. The numerical computations enable us to validate the previous analytical solutions and describe several kinds of post-critical responses up to advanced states, depending on geometric and material parameters. In most cases, secondary bifurcations occur during the post-critical stage. These secondary modes are mainly due to the modal interaction phenomenon and give rise to unstable post-buckled solutions which lead to final collapse.     

Analytical modeling and finite element simulation of the plastic collapse of sandwich beams with pin-reinforced foam cores

Analytical predictions are presented for the plastic collapse strength of lightweight sandwich beams having pin-reinforced foam cores that are loaded in 3-point bending. Both polymer and aluminum foam cores are considered, whilst the facesheet and the pins are made of either composite or metal. Four different failure modes are account for: metal facesheet yield or composite facesheet microbuckling, facesheet wrinkling, plastic shear of the core, and facesheet indentation beneath the loading rollers. A micromechanics-based model is developed and combined with the homogenization approach to calculate the effective properties of pin-reinforced foam cores. To calculate the elastic buckling strength of pin reinforcements, the pin-reinforced foam core is treated as assemblies of simply supported columns resting upon an elastic foundation. Minimum mass design of the sandwich is then obtained as a function of the prescribed structural load index, subjected to the constraint that none of the above failure modes occurs. Collapse mechanism maps are constructed and compared with the failure maps of foam-cored sandwich beams without pin reinforcements. Finite element simulations are carried out to verify the analytical model and to study the performance and failure mechanisms of the sandwich subject to loading types other than 3-point bending. The results demonstrate that the weaker the foam is, the more optimal the pin-reinforced foam core becomes, and that sandwich beams with pin-reinforced polymer foam cores are structurally more efficient than foam- or truss-cored sandwich beams.     

Imperfection sensitivity of axially compressed stringer reinforced cylindrical sandwich panels

This paper presents some numerical results of the effects of several nondimensional parameters on the buckling and initial post buckling behaviors of shallow sandwich panels under axial compression. Results are presented that show these effects due to transverse shearing resistance of the core material, different face-sheet thicknesses, and different core thicknesses. Further effects on the buckling and initial postbuckling behaviors of sandwich panels are presented due to the torsional resistance of longitudinal edge stiffeners.The results show that the range of flatness parameter, δ/d, for which sandwich panels remain imperfection-insensitive increases with increases in transverse shearing resistance of the core material and with larger core thicknesses. These results also indicate that this range of δ/d is smallest when the face-sheet thicknesses are equal. Finally, as in the case of homogeneous panels, torsional resistance of the longitudinal edge stiffeners has the effect of making the sandwich panel less imperfection-sensitive.     

铝面板厚度对Nomex蜂窝夹层结构冲击后弯曲性能影响的试验研究

通过低速冲击试验和四点弯曲试验,研究了铝面板厚度对Nomex蜂窝夹层结构抗冲击能力和剩余强度的影响。结果表明:在冲击荷载作用下,面板发生变形的区域大小随面板厚度增加而变大,当面板厚度大于0.5mm时,变形区域直径趋于稳定;无论试件是否受到过冲击,在弯曲载荷作用下,0.2mm厚面板发生芯格内屈曲失稳,而其他厚度面板均发生格间失稳;对无冲击损伤的结构,0.2mm厚面板弯曲强度显著低于其他厚度面板;对含冲击损伤的结构,0.2mm厚面板的剩余强度百分比最高。     

Theoretical analysis of the deformation of SMP sandwich beam in flexure

Shape memory polymers (SMPs) can have a large frozen strain but with a very small recovery stiffness in comparison with shape memory metals or ceramics. To provide more deployable stresses for the application of actuators, sandwich beams consisting of a SMP core and two thin metallic skins were considered. The packaging behaviors of two types of SMP sandwich beams, aluminum/SMP/aluminum and steel/SMP/steel, were discussed. Due to the high compliance of SMP core on packaging condition that the testing temperature is above the activation temperature of the material, buckling and post-buckling are the essential deformation mechanisms of SMP sandwich beams under bending. Theoretical solutions were derived in studying such non-linear behaviors, including the initiation of critical buckling, post-buckling response, and final failure modes. Systematic parameter’s analyses, e.g., buckling half-wavelength, amplitude, location of the neutral-strain surface in different packaging curvatures, were also presented.     

泡沫铝夹芯梁四点弯曲性能试验研究

通过准静态四点弯曲试验对泡沫铝夹芯梁的弯曲力学性能进行了测试,研究了它的破坏过程、破坏形态和典型荷载-位移曲线,分析了芯层厚度和面层厚度等参数对其弯曲力学性能的影响。结果表明,泡沫铝夹芯梁四点弯曲破坏过程历经三个阶段,呈现三种失效模式:整体弯曲破坏、局部屈曲破坏以及整体屈曲破坏;芯层厚度和面层厚度对夹芯梁的弯曲承载力和吸能效果有明显影响;在本试验参数范围内,芯层厚度为25mm,面层厚度为0.4mm时,夹芯梁具有最优弯曲力学性能。     

多孔金属夹层板在冲击载荷作用下的动态响应

借助两种有限元软件ABAQUS和LS_DYNA, 模拟和分析了两种厚度不同的泡沫铝合金夹层板(三明治板)、方孔蜂窝形夹层板和波纹形夹层板在冲击载荷下的动态响应. 4种夹层板的单位面积密度相同,冲击载荷分别用泡沫铝子弹与不锈钢子弹模拟. 讨论了泡沫金属夹层板和格构式夹层板在不同冲击载荷作用下的变形机制,重点在于对夹层板的吸能特性及板内各部分吸能变化规律的探讨.研究结果表明: 在泡沫子弹冲击下,夹层板主要是通过自身变形来消耗子弹动能,并转化为自身内能. 厚度为22\,mm的泡沫金属夹层板吸收能量最多,底面变形最小,是结构性能最优的夹层板;在刚性子弹高速冲击穿透过程中,格构式夹层板的吸能性能比单位面积密度相同的泡沫金属夹层板的吸能性能更好. 波纹形夹层板的能量吸收能力在4种板中最高.      

泡沫夹层在抗爆复合结构中作用的实验研究

首先对夹芯泡沫材料的力学性能、动态响应和性能特性进行了简单探讨,然后通过钢筋混凝土、泡沫夹层、钢板混凝土复合结构的抗爆实验,对夹芯泡沫材料的主要特点及其在复合结构中的作用机理进行了研究.结果表明:泡沫夹层对爆炸冲击波具有很好的衰减作用,且这种衰减作用随输入压力的增大而增大.这种特性可使爆炸产生的相对集中的局部压力转化为...     

轻质金属点阵夹层板热屈曲临界温度分析

本文针对均匀温度场下四边简支和四边固支金属点阵夹层板的临界热屈曲温度进行了求解和参数影响分析。将点阵夹芯等效为均匀连续体,并且将夹层板的剪切刚度近似为点阵夹芯的抗剪切刚度,忽略夹芯的抗弯刚度且认为夹层板主要由面板来提供抗弯刚度。对于无法获得解析解的四边固支条件,通过对未知变量进行双傅里叶展开的方法求解了Ressiner夹层板模型的临界屈曲温度,理论分析结果与有限元计算结果吻合良好。进一步分析了不同边界条件、点阵胞元构型、点阵材料相对密度、面板厚度等对临界屈曲温度的影响规律。     

聚氨酯/钢夹芯结构爆炸载荷下动力学响应的数值模拟

聚氨酯泡沫具有良好的缓冲和吸能性能,以硬质聚氨酯泡沫作为芯体,钢作为面板的夹芯结构在工程中用途广泛。为了研究聚氨酯/钢夹芯结构在爆炸载荷作用下的抗爆性能,利用Ansys/Autodyn非线性有限元程序对聚氨酯/钢夹芯结构在爆炸载荷作用下的动力学响应进行数值模拟分析,并与相同面密度的钢板进行对比。结果表明,加入聚氨酯芯体后,结构的吸收能量为相同面密度钢板的1.49倍,整体结构的抗爆性能得到很大的提高。     

Exact analytical solutions for the local and global buckling of sandwich beam-columns under various loadings

Sandwich structures are widely used in many industrial applications, due to the attractive combination of a lightweight and strong mechanical properties. This compromise is realized thanks to the presence of different parts in the composite material, namely the skins and possibly core reinforcements or thin-walled core structure which are both thin/slender and stiff relative to the other parts, namely the homogeneous core material, if any. The buckling phenomenon thus becomes mainly responsible for the final collapse of such sandwiches. In this paper, classical sandwich beam-columns (with homogeneous core materials) are considered and elastic buckling analyses are performed in order to derive the critical values and the associated bifurcation modes under various loadings (compression and pure bending). The two faces are represented by Euler–Bernoulli beams, whereas the core material is considered as a 2D continuous solid. A set of partial differential equations is first obtained from a general bifurcation analysis, using the above assumptions. Original closed-form analytical solutions of the critical loading and mode of a sandwich beam-column are then derived for various loading conditions. Finally, the proposed analytical formulae are validated using 2D linearized buckling finite element computations, and parametric analyses are performed.     

Dynamic crushing of sandwich panels with prismatic lattice cores

The dynamic out-of-plane compressive response of stainless steel corrugated and Y-frame sandwich cores have been investigated for impact velocities ranging from quasi-static to 200 ms⁻¹. Laboratory-scale sandwich cores of relative density 2.5% were manufactured and the stresses on the front and rear faces of the dynamically compressed sandwich cores were measured using a direct impact Kolsky bar. Direct observational evidence is provided for micro-inertial stabilisation of both topologies against elastic buckling at impact velocities below 30 ms⁻¹. At higher impact velocities, plastic waves within the core members result in the front face stresses increasing with increasing velocity while the rear face stresses remain approximately constant. While the finite element calculations predict the rear face stresses and dynamic deformation modes to reasonable accuracy, the relatively slow response time of the measurement apparatus results in poor agreement between the measured and predicted front face stresses. The finite element calculations also demonstrate that material strain-rate effects have a negligible effect upon the dynamic compressive response of laboratory-scale and full-scale sandwich cores.     

夹层梁总体屈曲及皱曲的有限元计算

皱曲是夹层结构的一种短波屈曲模式,通常发生于夹心较厚或夹心刚度较低的情况。由于模型规模的限制,在常规有限元建模时通常将夹层板模拟为二维板单元,这种方法忽略了面板和夹心在厚度方向上的相互作用,无法计算出皱曲模式。针对上述问题,本文首先介绍了一个计算夹层结构总体屈曲和皱曲的统一理论,并将此理论的计算结果作为理论解。为了同时...     

夹芯板结构局部压入力学响应研究

利用材料试验机(MTS)实验研究了复合材料面板、闭孔泡沫铝芯层夹芯板结构在准静态压入时的变形和破坏特征。实验结果表明,夹芯板的破坏主要集中在压头作用的局部区域内;同时,根据最小势能原理建立了泡沫铝夹芯板在半球形压头作用下的压入力学响应理论预测模型。通过引入无量纲参数分析了夹芯板压入载荷-位移响应,并在不同面板厚度、芯层厚度和芯层相对密度情况下,对夹芯板压入响应理论解的有效性和适用性进行了讨论。     

Experimental and Numerical Investigation of Free Vibrations of Composite Sandwich Beams with Curvature and Debonds

In this paper experimental and numerical results concerning the dynamic response of composite sandwich beams with curvature and debonds are reported. Sandwich beams made of carbon/epoxy face sheets and polyurethane foam core material were manufactured with four different radii of curvature and debonds between the top and bottom interface of face sheet and foam core. Dynamic response was obtained using the impulse frequency response technique under clamped-clamped boundary condition. Experimental results were compared with numerical finite element model results. A combined experimental and numerical FE approach was used to determine the material properties of the skin and foam core materials based on modal vibration and static flexure tests. Results indicate that the fundamental frequency increases with increasing curvature angle, however, for higher frequencies; the natural frequencies are not significantly affected. Also, it is found that face/core debond causes reduction of the natural frequencies due to stiffness degradation.