Formation of PPy/Ta2O5/Ta structure by electropolymerization

Electropolymerization of pyrrole on tantalum (Ta) electrodes was carried out in buffer solutions (0.04 M phosphoric acid, 0.04 M acetic acid, 0.04 M boric acid and 0.2 M sodium hydroxide) containing 0.1 M sodium ptoluenesulfonate (TsONa) under galvanostatic conditions and it was found that a polypyrrole (PPy) and a tantalum oxide (Ta₂O₅) layer are formed on a Ta electrode by an electrochemical oxidation process. The conditions of this simultaneous formation were studied in respect to current density (i_d), pyrrole concentration ([Py]), pH and the amount of electricity. Under certain conditions ([Py] = 0.25 M, pH = 1.8, i_d = 10–20 mA cm^?2, the amount of electricity = 1 C), 6–8 μm thick PPy films were efficiently formed on homogeneous 30–50 nm thick Ta₂O₅ layers. The PPy film showed a high electrical conductivity (110 s cm^?1), adhered well and covered the Ta₂O₅ layer. The resulting PPy/Ta₂O₅/Ta system is therefore proved to have excellent properties as a capacitor.     

Ta2O5/Si薄膜界面结构及光催化活性

利用溶胶-凝胶法和旋转镀膜法在单晶Si(110)基底上制备了Ta2O5光催化剂薄膜. 薄膜颗粒的晶粒度和大小随着热处理温度的升高而增加. 利用扫描俄歇电子能谱(AES)的表面成分分析、深度剖析和线形分析技术研究了热处理温度对Ta2O5/Si 样品膜层和基底的界面化学状态和相互作用的影响规律. 研究表明, 在700 ℃以下热处理时, Ta2O5/Si薄膜界面处以扩散作用为主;在800 ℃高温热处理时,在界面扩散的同时也引发界面反应, 生成了SiO2物种, 界面扩散和界面反应会对薄膜和基底元素的化学价态发生影响. 在紫外光下降解水杨酸的光催化活性的研究表明, 在600 ℃下焙烧制备的Ta2O5/Si薄膜具有与TiO2/Si薄膜相当的光催化活性.     

Adsorption of transition metal atoms on the NiO(100) surface and on NiO/Ag(100) thin films

We have studied the adsorption of Au, Pd, and Pt atoms on the NiO(100) surface and on NiO/Ag(100) thin films using plane wave DFT+U calculations. The scope of this work is to compare the adsorption properties of NiO, a reducible transition metal oxide, with those of MgO, a simple binary oxide with the same crystal structure and similar lattice parameter. At the same time, we are interested in the adsorption characteristics of NiO ultra-thin films (three atomic layers) deposited on Ag(100) single crystals. Also in this case the scope is to compare NiO/Ag(100) with the corresponding MgO/Ag(100) films which show unusual properties for the case of Au adsorption. The results show that the transition metal atoms bind in a similar way on NiO(100) and NiO/Ag(100) films, with Pt, Pd, and Au forming bonds of decreasing strength in this order. No charging effects occur for Au adsorbed on NiO/Ag(100) films, at variance with MgO/Ag(100). The reasons are analyzed in terms of work function of the metal/oxide interface. Possible ways to modify this property by growing alternate layers of MgO and NiO are discussed.     

Capacitance and photocurrent study of electronic properties of anodic oxide films on Nb and Ta. Evaluation of the ionized donor concentration profile in Nb2O5 film

Electronic properties of electrochemically formed oxide films on Nb were studied by photocurrent and differential capacitance measurements in 0.025 M KH₂PO₄+0.025 M Na₂HPO₄ electrolyte, pH 6.9. Oxide films of n-type conductivity were formed galvanostatically for final potentials ranging from 4 to 230 V. Measurements were performed in two potential regions, which correspond to formation of a depleted layer of variable thickness at relatively low potentials, and to complete depletion of oxide films of electronic charge carriers at higher potentials. In the first potential region the behavior of both capacitance and photocurrent, was governed by a build up of a depleted layer of potential dependent thickness. In the second, high potential, region, which extends up to the oxide film formation potential, the photocurrent and capacitance of oxide films in most features followed the trends typical of dielectric films containing defects and traps. The photocurrent and capacitance measurements on presumably dielectric oxide films formed on Ta were staged for comparison. The capacitance–potential measurements performed in the first potential region enabled us to construct the ionized donor concentration profile across the Nb₂O₅ film width. The limitations on the use of the C–E profiling method for electrochemically formed oxide layers are considered.     

Epitaxial growth of AlN films on single-crystalline Ta substrates

We have demonstrated the first epitaxial growth of AlN films on single-crystalline Ta substrates by the use of a low-temperature growth technique based on pulsed laser deposition (PLD). Although previous AlN films grown on Ta(100) and (111) substrates have exhibited quite poor crystallinity, an epitaxial AlN(0001) film with an in-plane epitaxial relationship of AlN[112¯0]//Ta[001] has been obtained on a Ta(110) substrate at a growth temperature of 450 °C. We found that the full-width at half-maximum values for the crystal orientation distribution in the tilt and twist directions of the AlN film were 0.37° and 0.41°, respectively. Grazing-incidence X-ray reflection (GIXR) and X-ray photoelectron spectroscopy (XPS) measurements have revealed that the AlN/Ta heterointerface is quite abrupt, and that its abruptness remains unchanged even after annealing at 1000 °C.     

Magnetron formation of Ni/YSZ anodes of solid oxide fuel cells

Physico-chemical and structural properties of nanocomposite NiO/ZrO₂:Y₂O₃ (NiO/YSZ) films applied using the reactive magnetron deposition technique are studied for application as anodes of solid oxide fuel cells. The effect of oxygen consumption and magnetron power on the discharge parameters is determined to find the optimum conditions of reactive deposition. The conditions for deposition of NiO/YSZ films, under which the deposition rate is maximum (12 μm/h), are found and the volume content of Ni is within the range of 40–50%. Ni-YSZ films reduced in a hydrogen atmosphere at the temperature of 800°C have a nanoporous structure. However, massive nickel agglomerates are formed in the course of reduction on the film surface; their amount grows at an increase in Ni content in the film. Solid oxide fuel cells with YSZ supporting electrolyte and a LaSrMnO₃ cathode are manufactured to study electrochemical properties of NiO/YSZ films. It is shown that fuel cells with a nanocomposite NiO/YSZ anode applied using a magnetron sputtering technique have the maximum power density twice higher than in the case of fuel cells with an anode formed using the high-temperature sintering technique owing to a more developed gas-anode-electrolyte three-phase boundary.     

Amperometric Hydrogen Peroxide Biosensor Based on the Immobilization of Horseradish Peroxidase (HRP) on the Layer‐by‐Layer Assembly Films of Gold Colloidal Nanoparticles and Toluidine Blue

The precursor film was first formed on the Au electrode surface based on the self‐assembly of L ‐cysteine and the adsorption of gold colloidal nanoparticles (nano‐Au). Layer‐by‐layer (LBL) assembly films of toluidine blue (TB) and nano‐Au were fabricated by alternately immersing the electrode with precursor film into the solution of toluidine blue and gold colloid. Cyclic voltammetry (CV) and quartz crystal microbalance (QCM) were adopted to monitor the regular growth of {TB/Au} bilayer films. The successful assembly of {TB/Au}_n films brings a new strategy for electrochemical devices to construct layer‐by‐layer assembly films of nanomaterials and low molecular weight materials. In this article, {TB/Au}_n films were used as model films to fabricate a mediated H₂O₂ biosensor based on horseradish peroxidase, which responded rapidly to H₂O₂ in the linear range from 1.5×10^?7 mol/L to 8.6×10^?3 mol/L with a detection limit of 7.0×10^?8 mol/L. Morphologies of the final assembly films were characterized with scanning probe microscopy (SPM).     

Molecular electrodes at the exposed edge of metal/insulator/metal trilayer structures

Producing reliable electrical contacts of molecular dimensions has been a critical challenge in the field of molecule-based electronics. Conventional thin film deposition and photolithography techniques have been utilized to construct novel nanometer-sized electrodes on the exposed vertical plane on the edge of a thin film multilayer structure (metal/insulator/metal). Via thiol surface attachment to metal leads, an array of paramagnetic, cyanide-bridged octametal complexes, [(pzTp)FeIII(CN)3]4[NiII(L)]4[O3SCF3]4 (1) [(pzTp) = tetra(pyrazol-1-yl)borate; L = 1-S(acetyl)tris(pyrazolyl)decane], were covalently linked onto the electrodes forming a dominant conduction pathway. A series of molecule-based devices were fabricated using Ni, NiFe, Ta, and Au as metal electrodes separated by insulating Al2O3 spacers, followed by treatment with 1. A series of control experiments were also performed to demonstrate that the conduction path was through tethered metal clusters. The molecular current was analyzed via the Simmons tunnel model, and calculations are consistent with electron tunneling through the alkane ethers to the central metal core. With a Ni/Al2O3/Au molecular electrode, the tether binding was found to be reversible to the top Au layer, allowing for a new class of chemical detection based on the steric bulk of coordinating analytes to disconnect the molecular current path. Simple and economical photolithography/liftoff/self-assembly fabrication techniques afford robust molecular junctions with high reproducibility (>90%) and long operational lifetimes (>1 year).     

Electrochemical Surface Plasmon Resonance Spectroscopy at Bilayered Silver/Gold Films

Bilayered silver/gold films (gold deposited on top of the silver film) were used as substrates for electrochemical surface plasmon resonance spectroscopy (EC-SPR). EC-SPR responses of electrochemical deposition/stripping of copper and redox-induced conformation changes of cytochrome c immobilized onto self-assembled monolayers preformed at these substrates were measured. Influence of the Ag layer thickness and the double-layer capacitance on the EC-SPR behavior was investigated. The results demonstrated that the bilayered Ag/Au metal films produce a sharper SPR dip profile than pure Au films and retain the high chemical stability of Au films. Contrary to the result by the Fresnel calculation that predicts a greater fraction of Ag in the bilayered film should result in a greater signal-to-noise ratio, the EC-SPR sensitivity is dependent on both the Ag/Au thickness ratio and the chemical modification of the surface. Factors affecting the overall SPR sensitivity at the bilayered films, such as the film morphology, potential-induced excess surface charges, and the adsorbate layer were investigated. Forming a compact adsorbate layer at the bilayered film diminishes the effect of potential-induce excess surface charges on the SPR signal and improves the overall EC-SPR sensitivity. For the case of redox-induced conformation changes of cytochrome c, the SPR signal obtained at the bilayered silver/gold film is 2.7 times as high as that at a pure gold film.     

Formation of NiO/YSZ functional anode layers of solid oxide fuel cells by magnetron sputtering

The decrease in the polarization resistance of the anode of solid-oxide fuel cells (SOFCs) due to the formation of an additional NiO/(ZrO₂ + 10 mol % Y₂O₃) (YSZ) functional layer was studied. NiO/YSZ films with different NiO contents were deposited by reactive magnetron sputtering of Ni and Zr–Y targets. The elemental and phase composition of the films was adjusted by regulating oxygen flow rate during the sputtering. The resulting films were studied by scanning electron microscopy and X-ray diffractometry. Comparative tests of planar SOFCs with a NiO/YSZ anode support, NiO/YSZ functional nanostructured anode layer, YSZ electrolyte, and La_0.6Sr_0.4Co_0.2Fe_0.8O₃/Ce_0.9Gd_0.1O₂ (LSCF/CGO) cathode were performed. It was shown that the formation of a NiO/YSZ functional nanostructured anode leads to a 15–25% increase in the maximum power density of fuel cells in the working temperature range 500–800°C. The NiO/YSZ nanostructured anode layers lead not only to a reduction of the polarization resistance of the anode, but also to the formation of denser electrolyte films during subsequent magnetron sputtering of electrolyte.     

SEM and AES depth profile studies of thin titanium and titanium oxide films covered by nanoscale evaporated Au layers

Thin titanium and titanium oxide films, both covered by ultra-thin gold layers, have been compared with titanium films after analysis, using a combination of SEM and AES. The Ti films were prepared under UHV conditions by evaporation on a glass substrate. The Ti oxide layers were prepared in situ by precisely controlled oxygen sorption at 298 K on Ti film. Both Ti and Ti oxide films were then covered in situ by a very thin Au layer. Analysis was performed in a separate system after long-term exposure of the films to air. SEM analysis revealed a much smaller size grain on the Au coated Ti films than on Ti films not coated with a Au layer. The thin gold layers covering the Ti surface prevent an extensive air interaction with Ti film. The analysis of the features of the Ti Auger spectra during the sputter profile measurements allow to characterise the chemical nature of Ti-oxide formed in Ti/Au interface region. Received: 7 September 1998 / Revised: 14 January 1999 / Accepted: 2 February 1999     

XPS study of the oxidation of nanosize Ni/Si(100) films

The XPS (X-ray photoelectron spectroscopy) study of nickel oxide nanolayers obtained by magnetron sputtering of the metal and its subsequent oxidation in air at different temperatures (400°C and 1000°C) was performed. Silicon(100) was used as a substrate. Surface of the initial Ni/Si structure was shown to contain not only Ni metal, but also the NiO oxide. Annealing at 400°C results in a complete oxidation of the metal film. At a high-temperature annealing (1000°C), nickel interacts both with oxygen and silicon substrate to form NiSi silicide and a composite Ni-Si-O phase in transition layer. Electronconductivity of NiO films is determined by intercrystallite barriers. Activation energies of film electroconductivity in model gases (O₂, Ar, H₂) were found.     

Nano-Sized NiO Immobilized on Au/CNT for Benzyl Alcohol Oxidation: Influences of Hybrid Structure and Interface

Tiny gold nanoparticles were successfully anchored on carbon nanotubes (CNT) with NiO decoration by a two-step synthesis. Characterizations suggested that Ni species in an oxidative state preferred to be highly dispersed on CNT. During the synthesis, in situ reduction by NaBH₄ and thermal treatment in oxidation atmosphere were consequently carried out, causing the formation of Au-Ni-O_x interfaces and bimetal hybrid structure depending on the Ni/Au atomic ratios. With an appropriate Ni/Au atomic ratio of 8:1, Ni atoms migrated into the sub-layers of Au particles and induced the lattice contraction of Au particles, whilst a higher Ni/Au atomic ratio led to the accumulation of NiO fractions surrounding Au particles. Both contributed to the well-defined Au-Ni-O_x interface and accelerated reaction rates. Nickel species acted as structure promoters with essential Au-Ni-O_x hybrid structure as well as the active oxygen supplier, accounting for the enhanced activity for benzyl alcohol oxidation. However, the over-layer of unsaturated gold sites easily occured under a high Ni/Au ratio, resulting in a lower reaction rate. With an Au/Ni atomic ratio of 8:1, the specific rate of AuNi₈/CNT reached 185 μmol/g/s at only 50 °C in O₂ at ordinary pressure.     

NiFe_2O_4/NiO纳米复合材料的制备及电催化水氧化性能

以镍铁水滑石为单一前驱体,通过高温焙烧制备了NiFe_2O_4/NiO纳米复合材料,对该纳米复合材料在碱性介质中电催化水的氧化性能进行了研究.结果表明,相比于化学共沉淀法制备的单独NiFe_2O_4、NiO及其物理混合物NiFe_2O_4+NiO,NiFe_2O_4/NiO纳米复合材料具有更高的电催化水氧化活性和更好的循环稳定性.电流密度为10 m A/cm2时过电位仅为364 m V.     

Efficient and Stable MoS2/CdSe/NiO Photocathode for Photoelectrochemical Hydrogen Generation from Water

A novel CdSe/NiO heteroarchitecture was designed, prepared, and used as a photocathode for hydrogen generation from water. The composite films were structurally, optically, and photoelectrochemically characterized. The deposition of CdSe on the NiO film enhanced light harvesting in the visible‐light region and photoelectrochemical properties. Moreover, the CdSe/NiO photoelectrode showed superior stability both in nitrogen‐saturated and air‐saturated neutral environments. The CdSe/NiO photoelectrode after MoS₂ modification retained the stability of the CdSe/NiO electrode and exhibited higher photocatalytic and photoelectrochemical performances than the unmodified CdSe/NiO electrode. In pH 6 buffer solution, an average hydrogen‐evolution rate of 0.52 μmol h^?1 cm^?2 at ?0.131 V (versus reversible hydrogen electrode, RHE) was achieved on a MoS₂/CdSe/NiO photocathode, with almost 100 % faradaic efficiency.     

Nickel foam-supported porous NiO/polyaniline film as anode for lithium ion batteries

Nickel foam-supported porous NiO film was prepared by a chemical bath deposition technique, and the NiO/polyaniline (PANI) film was obtained by depositing the PANI layer on the surface of the NiO film. The NiO film was constructed by NiO nanoflakes, and after the deposition of PANI, these nanoflakes were coated by PANI. As an anode for lithium ion batteries, the NiO/PANI film exhibits weaker polarization as compared to the NiO film. The specific capacity after 50 cycles for NiO/PANI film is 520 mAh g⁻¹ at 1 C, higher than that of NiO film (440 mAh g⁻¹). The improvement of these properties is attributed to the enhanced electrical conduction and film stability of the electrode with PANI.     

Structural and chemical characterisation of titanium deuteride films covered by nanoscale evaporated palladium layers

Thin titanium deuteride (TiD_y) films, covered by an ultra-thin palladium layer, have been compared with the corresponding titanium and palladium films using a combination of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The TiD_y layers were prepared under ultra-high vacuum (UHV) conditions by precisely controlled deuterium sorption at 298 K on a Ti film evaporated onto a Si(100) substrate. Both Ti and TiD_y films were then covered in situ by a nanoscale Pd layer. It was found that a 10- to 12-nm-thick Pd layer protects the TiD_y films efficiently against extensive air interaction. The morphology of both the surface and bulk Pd/TiD_y (Ti) films have been observed using SEM and cross-sectional TEM analysis, respectively. A polycrystalline bulk morphology in both Ti and TiD_y films accompanied by a fine-grained Pd surface was observed. High-magnification cross-sectional TEM images reveal the TiD_y film to be plastically deformed leading to an increase in the roughness of the top Pd layer. Complex structures, including Moiré patterns, have been identified within the Pd/TiD_y interface. The chemical nature of this interface has been analysed after partial sputtering of the Pd top layer using XPS. Besides TiD_y and Pd, TiO and PdO were found to be the main chemical species in the interface region of the Pd/TiH_y film. The XPS valence-band spectra of the Pd/TiD_y interface reveal electronic features characteristic of a Pd–Ti bimetallic structure.     

Structure of Nb/Ta layered ternary tellurides containing first row transition metal atoms

A summary of research on the structure of Nb/Ta layered tellurides in the past period is reported. 14 compounds, which have been structurally characterized by X-ray diffraction work, are presented according to their structural features. The first two compounds, Nb2CrTe4 and Nb2Cu1.48Te4, are characterized in that the ternary atoms are inserted in the different layers from the Nb atoms. While in the other compounds, both kinds of metal atoms are inserted in the same layer. The six compounds with formula M2M'2Te4(M = Nb/Ta; M' = Ni, Co, Fe) are characterized in that their structure can be described as construction by using cluster units "M2M'2Te10" as building blocks. in the two metal-rich compounds, TaCo2Te2 and TaNi2Te2, Ta atom has a distorted mono-capped pentagonal prism configuration. The structure of TaFeTe3, TaNTe3 and NbNi2.34Te3 can be described as building by the arrangement of double octahedral chains (DOC), in this con-nection, a selenide Ta2Ni2Se5 is also included by using the second type of     

Boosting Hydrogen Evolution at Visible Light Wavelengths by Using a Photocathode with Modal Strong Coupling between Plasmons and a Fabry-Pérot Nanocavity

Hot-hole injection from plasmonic metal nanoparticles to the valence band of p-type semiconductors and reduction by hot electrons should be improved for efficient and tuneable reduction to obtain beneficial chemical compounds. We employed the concept of modal strong coupling between plasmons and a Fabry-Pérot (FP) nanocavity to enhance the hot-hole injection efficiency. We fabricated a photocathode composed of gold nanoparticles (Au−NPs), p-type nickel oxide (NiO), and a platinum film (Pt film) (ANP). The ANP structure absorbs visible light over a broad wavelength range from 500 nm to 850 nm via hybrid modes based on the modal strong coupling between the plasmons of Au−NPs and the FP nanocavity of NiO on a Pt film. All wavelength regions of the hybrid modes of the modal strong coupling system promoted hot-hole injection from the Au−NPs to NiO and proton/water reduction by hot electrons. The incident photon-to-current efficiency based on H₂ evolution through water/proton reduction by hot electrons reached 0.2 % at 650 nm and 0.04 % at 800 nm.     

Fabrication of YBCO/CeO2/YBCO multilayer films through an all chemical solution deposition approach

In this paper, the growth characteristics and superconducting properties of YBCO/CeO₂/YBCO multilayer films derived from an all chemical solution deposition process layer by layer are investigated. X-ray diffraction results show that the c-axis epitaxial growth feature of the bottom YBa₂Cu₃O_7-δ (YBCO) film was perfectly inherited. Alternating epitaxial growth of YBCO/CeO₂/YBCO multilayer films was confirmed by high resolution transmission electron microscopy in combination with selected area electron diffraction, which will lay the groundwork for preparation of SIS-type Josephson junctions. In addition, nanosized BaCeO₃ particle rather than BaCeO₃ transition layer was observed in the interface between YBCO and CeO₂. The superconductivity measurement results show that the proposal method gives better superconducting properties only for high magnetic field and at low magnetic field it deteriorates the superconducting properties.