La2O3弥散强化的扩散渗铝涂层的氧化行为研究

复合镀Ｎｉ－Ｌａ２Ｏ３扩散渗铝制备的Ｌａ２Ｏ３弥散强化的ＮｉＡｌ型复合涂层，在１２７３Ｋ氧化２０ｈ，比单镀镍渗铝的ＮｉＡｌ型涂层的氧化增重速率低；扫描电镜研究表明，ＮｉＡｌ型涂层掺入Ｌａ２Ｏ３质点后，表面氧化物层形貌明显改观；高分辨电子显微镜观测复合涂层氧化物层的精细结构，发现纳米级的Ｌａ２Ｏ３颗粒（１０～４０ｎｍ）掺入α－Ａｌ２Ｏ３氧化物层。Ｌａ２Ｏ３质点通过影响氧化层的显微结构而改变氧化膜生长     

La和Bi对乙炔与甲酸甲酯加氢酯化合成丙烯酸甲酯的镍基催化剂性能的影响(英文)

在２２０℃和５０－６０大气压条件下,利用固定床对ＮｉＯ／ＳｉＯ２、ＮｉＯ／Ａｌ２Ｏ３、ＮｉＯ－Ｌａ２Ｏ３／Ａｌ２Ｏ３和ＮｉＯ－Ｂｉ２Ｏ３／Ａｌ２Ｏ３催化剂上的乙炔与甲酸甲酯加氢酯化合成丙烯酸甲酯进行了研究。镍基催化剂对乙炔的加氢酯化合成丙烯酸甲酯具有很好的活性。用浸透法制备的Ｍｏ／ＳｉＯ２催化剂的活性和丙烯酸甲酯的选择性均比离子交换法差。ＮｉＯ／Ａｌ２Ｏ３催化剂用Ｌａ或Ｂｉ改性后,其催化活性大大提高。ＸＰＳ、ＸＲＤ和ＴＰＲ结果表明,当催化剂用Ｌａ或Ｂｉ改性后,ＮｉＯ的晶粒明显减小,催化剂表面的Ｎｉ／Ａｌ原子比增大,催化剂的第二个还原峰温大大降低。     

Ni-Cu-Al2O3催化剂的活性相及作用机理

对新鲜和７００℃反应过的Ｎｉ－Ａｌ和Ｎｉ－Ｃｕ－Ａｌ催化剂的ＸＲＤ、ＸＰＳ表征结果表明，新鲜ＮｉＯ－Ａｌ２Ｏ３催化剂体相中的ＮｉＯ，ＮｉＡｌ２Ｏ４经７００℃反应后转变成金属Ｎｉ，同时表面的镍物种由单一的ＮｉＡｌ２Ｏ４变为ＮｉＡｌ２Ｏ４，ＮｉＯ和金属Ｎｉ的混合物，经反应后ＮｉＯ－ＣｕＯ－Ａｌ２Ｏ３催化剂体相和表相中的ＮｉＡｌ２Ｏ４，ＣｕＡｌ２Ｏ４均转变成为Ｎｉ－Ｃｕ合金，这是此催化剂对甲烷部分氧化反     

添加碱金属对甲烷与空气制合成气催化剂性能的影响(英文)

考察了添加在镍基催化剂中的碱金属助剂对甲烷与空气制合成气的催化反应性能的影响。并用ＴＰＯ、ＴＰＲ、ＣＯ_２程序升温脱附（ＴＰＤ）、ＸＰＳ及ＣＯ脉冲色谱对催化剂进行了表征。实验结果表明,碱金属助剂对降低催化剂结炭有一定作用;催化剂抗积炭顺序为; Ｎｉ－Ｋ２Ｏ／ＣａＯ／Ａｌ２Ｏ３＞Ｎｉ－Ｌｉ２Ｏ／ＣａＯ－Ａｌ２Ｏ３＞Ｎｉ－Ｎａ２Ｏ／ＣａＯ－Ａｌ２Ｏ３＞Ｎｉ／ＣａＯ／Ａｌ２Ｏ３。在实验中,我们发现碱金属的添加使催化剂的Ｎｉ晶粒变大和吸附ＣＯ_２的能力增强,结合能发生不同程度的变化。这些实验结果从不同方面解释了碱金属助剂对催化剂活性和抗积炭性的影响。实验结果表明Ｎｉ－Ｌｉ２Ｏ／ＣａＯ－Ａｌ２Ｏ３具有较好的活性和抗积炭性。     

Ni／Al2O3上甲烷二氧化碳氧气转化制备合成气的研究

在固定床流动反应装置上，从活性组分的负载量，载体的焙烧温度、反应温度，空速等几个方面考察了Ｎｉ／Ａｌ２Ｏ３催化剂对ＣＨ４－ＣＯ２－Ｏ２转化制备合成气的催化活性，发现采用１１００℃焙烧的γ－Ａｌ２Ｏ３载体制备的镍负载量为９．１７ｗ％的Ｎｉ／Ａｌ２Ｏ３催化剂。     

天然气和二氧化碳转化制合成气的研究 Ⅴ．甲烷脱氢积炭反应特征

采用ＴＧ、ＸＲＤ、ＳＥＭ、ＥＤＡＸ和脉冲色谱技术，研究了Ｎｉ／Ａｌ２Ｏ３和Ｎｉ／ＡＲＭ催化剂的甲烷脱氢积炭反应特征。结果指出，甲烷脱氢反应的积炭行为与催化剂上镍的分散状态有关。Ｎｉ－２催化剂上Ｎｉ的分散度小，晶粒大，甲烷脱氢形成的炭丝较长，主要以石墨型炭游离存在：而Ｎｉ／ＡＲＭ催化剂上Ｎｉ的分散度大，镍晶粒小，甲烷脱氢形成的炭丝较短，主要覆盖在催化剂活性中心表面。甲烷脱氢主要产生无定型炭和石墨型炭，其中无定型炭可以被ＣＯ２部分消除。在催化剂制备时，通过提高镍在催化剂表面的分散度，减小镍的晶粒大小，不仅可以提高催化剂的活性，而且可以提高ＣＯ２对积炭的消炭性能。     

EFFECTS OF ALKALI AND RARE EATTH METAL OXIDES ON THE THERMAL STABILITY AND THE CARBON DEPOSITION OVER A NiO/Al_2O_3 CATALYST

采用固定床流动反应装置、ＣＯ吸附、ＴＧ、ＴＰＯ、ＸＰＳ和ＸＲＤ等手段考察了ＮｉＯ／Ａｌ２Ｏ３和ＬｉＮｉＬａＯ／Ａｌ２Ｏ３催化剂上的甲烷部分氧化反应。实验结果表明，ＬｉＮｉＬａＯ／Ａｌ２Ｏ３对甲烷部分氧化反应具有较高的反应活性。锂和镧的添加不仅改善了活性组分镍的分散度，而且提高了ＮｉＯ／Ａｌ２Ｏ３的抗积碳能力和热稳定性     

天然气和二氧化碳转化制合成气的研究Ⅵ Ni／Al_2O_3催化剂再生的疏活机理

采用γ－Ａｌ_２Ｏ_３为载体，以硝酸镍、硝酸镁和稀土硝酸盐为原料，按常规浸渍法制备镍负载型催化剂，其中Ｎｉ含量为９．１７％，助剂ＲＥ_２Ｏ_３和Ｍｇ含量分别为５．１８％和１．８０％，该催化剂简称为Ｎ－５－ＲＭ。催化反应评价采用双套管石英反应器，在多功能固定床流动反应装置上进行，以天然气和二氧化碳转化为探针反应，采用连续反应法评价催化剂性能。以反应尾气中合成气摩尔百分数表征催化剂活性。采用理光Ｄ／ｍａｘ－ｒ－Ｂ型Ｘ射线衍射仪测定催化剂晶相。实验发现，催化剂长期使用失活的主要原因是由于活性中心Ｎｉ￣０与载体Ａｌ_２Ｏ_３间形成难还原的ＮｉＡｌ_２Ｏ_４物种，以及活性中心Ｎｉ￣０聚集形成晶相，从而降低了催化剂表面活性中心数。ＴＰＲ结果指出，ＮｉＡｌ_２Ｏ_４物种在高温下通氢气可以得到充分还原。然而，此时催化剂活性仍明显低于新鲜催化剂活性。ＸＲＤ结果表明，此时催化剂存在很强的Ｎｉ￣０衍射峰，说明尽管高温还原已使形成ＮｉＡｌ_２Ｏ_４的Ｎｉ￣（２＋）还原为Ｎｉ￣０，但高温还原又进一步使活性Ｎｉ￣０聚集成晶相，因而降低了催化剂表面活性中心数。这说明，对ＮｉＡｌ_２Ｏ_４的活化仅通过常规高温还原是不够的。２０％过氧化氢水溶液（以下简称     

CH4,CO2和O2制合成气反应中载体对Ni催化剂抗氧化性能的影响

在ＣＨ４、ＣＯ２ 催化氧化制合成气反应中, Ｎｉ／Ａｌ２Ｏ３ 催化剂在高温下生成ＮｉＡｌ２Ｏ４ 尖晶石,是导致催化剂失活的一个重要因素． 通过向载体（Ａｌ２Ｏ３）中添加各种氧化物, 使得催化剂的抗氧化性能得到改善． 并运用ＴＰＲ、ＸＲＤ对催化剂进行表征, 发现催化剂的抗氧化性顺序为： Ｎｉ／ＣａＯ－Ａｌ２Ｏ３ ＞ Ｎｉ／ＭｇＯ－Ａｌ２Ｏ３ ＞ Ｎｉ／ＣｅＯ２－Ａｌ２Ｏ３ ＞ Ｎｉ／Ｌａ２Ｏ３－Ａｌ２Ｏ３ ＞ Ｎｉ／Ｙ２Ｏ３－Ａｌ２Ｏ３ ＞ Ｎｉ／ＴｉＯ２－Ａｌ２Ｏ３＞ Ｎｉ／Ａｌ２Ｏ３＞ Ｎｉ／Ｆｅ２Ｏ３－Ａｌ２Ｏ３．     

甲烷部分氧化制合成气Ⅱ．镍系催化剂的反应性能

主要用第四周期金属元素的氧化物与Ａｌ２Ｏ３的复合氧化物催化剂上甲烷氧化的结果证实了催化剂设计中的预测：（１）催化剂首先应能解离活化甲烷，（２）催化剂要能较快地活化Ｏ２分子．只有同时满足这两个条件，催化剂才可能有较好的甲烷部分氧化活性．第四周期元素中只有镍具有这样的性质．Ｃｕ，Ｍｎ，Ｃｒ，Ｌａ，Ｃａ，Ｚｎ等氧化物的添加可明显提高Ｎｉ－Ａｌ２Ｏ３催化剂的甲烷部分氧化性能，其中Ｃｕ的助催化性能最好．催化剂ＮｉＯ－ＣｕＯ－Ａｌ２Ｏ３，ＮｉＯ－ＭｎＯ－Ａｌ２Ｏ３，ＮｉＯ－Ｃｒ２Ｏ３－Ａｌ２Ｏ３的反应活性和选择性顺序，与金属Ｃｕ，Ｍｎ，Ｃｒ上ＣＯ和Ｈ２脱附的顺序是一致的     

新型固定床Raney Ni制备过程中晶相结构的转化

以拟薄水铝石制备粘结剂，加入镍铝合金粉和田菁粉捏合、成型，在空气中高温焙烧，然后用苛性碱溶液充分浸取，制备出可应用于固定床加氢的活性Raney Ni催化剂。采用XRD和TG-DTA分析了催化剂制备过程中晶相结构的转化，结果表明，成型合金焙烧过程中，富铝合金相（如Al₃Ni-Al和Al₃Ni）逐渐转变为贫铝合金相（如Al₃Ni₂和AlNi），释放出的金属铝依次发生氧化，同时抑制金属镍的氧化；在高于1 123～1 133K焙烧时金属铝氧化生成α-Al₂O₃，使催化剂获得较高的颗粒强度。苯加氢活性评价结果表明，该新型固定床Raney Ni催化剂活性高于负载型镍催化剂，也高于参照专利方法制备的有机聚合物粘结的同类型催化剂，并且具有较好的低温加氢活性。     

新型Raney-Ni制备过程中的XRD,SEM和EDAX研究

采用急冷法及预处理制备Raney-Ni原始合金,以XRD,SEM和EDAX手段研究了其活化过程.此方法制备的Raney-Ni原始合金与传统方法制备的相比,晶粒变小,Ni₂Al₃相增多,从而使其具有中心为大量Ni₂Al₃,外围为少量NiAl3包裹的独特结构,使活化始终以铝向表面迁移为控制步骤,活化后残留较多的Ni₂Al₃相,催化剂中活性Ni均匀分布在残留的Ni₂Al₃上.     

Ni的引入对Pd/Al2O3催化甲烷燃烧性能的影响

采用浸渍法制备了Ni掺杂的Pd/Al2O3催化剂,考察了其低浓度甲烷催化燃烧活性和水热稳定性.结果表明,随着Ni的引入及其含量的增加,Pd/Al2O3催化剂性能明显提高,Ni含量至20%时,在0.4%CH4,4%H2O和空气平衡的原料气组成,80000h-1空速和600oC条件下反应150h后,CH4转化率仍能保持在97.5%以上.X射线衍射、H2程序升温还原、NH3程序升温脱附和透射电镜等结果表明,NiAl2O4晶相的形成改善了载体酸性和活性组分的分散度,从而提高了催化剂性能.     

EFFECTS OF RARE EARTH OXIDES ON PERFORMANCES OF Ni/Al_2O_3 CATALYSTS FOR METHANE STEAM REFORMING REACTION

The Catalytic performances for methane steam reforming reaction ofNi/Al_2O_3(commercial), Ni/Al_2O_3 (developed surface )and Ni/Al_2O_3-R_xO_y (R israre earth oxide) Catalysts were investigated by means of X-ray diffraction,TG, SEM/ X-ray analysis, pulse gas chromatography,BET and Mercuryporsiniter techniques. The distribution of rear earth oxides on the supports,themetal-support (additives) interaction and the influence of rare earth oxideadditives on the dispersion of active components,catulytic activities,variationof nickel crystallites size,CO chemisorption,formation of NiAl_2O_4 as well asthe reducibility of the catalysts were examined.The presence of rare earthoxides in the Ni/Al_2O_3 (developed surface) results in great improvement ofstubility through suppressing the growth of Ni crystallites,the oxidation of themetallic Ni and the formation of NiAl_2O_4. The effect of heavy rare earth oxidesis more distinct than that of the light ones.Strong metal support interaction(SMSI) exists in Ni/Al_2O_3- R     

Ni-Zr-Al基非晶合金催化剂的苯加氢催化性能

 利用快速凝固技术制备了Ni23.3Zr6.7Al64Cu2.3Ce3.7非晶态合金,用碱洗抽Al的方法进行活化,制成了Ni-Zr基非晶态合金催化剂(A＞50 m2/g), 并考察了其对苯加氢反应的催化性能. 结果发现,这种新型催化材料的比活性高出常规Raney Ni催化剂约375%. 反应动力学分析表明,苯加氢反应级数对氢基本上表现为一级,表观反应活化能约为31.2 kJ/mol, 并推导出苯加氢反应的动力学方程.     

Characterization and Catalytic Properties of a Rapidly Quenched Ni-RE-P-AL Catalyst

IntroductionAmorphous.alloy has been found to have superior catalytic properties["']. However, asan applied catalyst, its small surface area and low thermal stability during the catalytic processare the encountered problems usually.In the previous study, we found that addition of a small amount of rare earth element effectively stabilized the amorphous phase in a Ni--P alloyL'~'j, and the surface area of the amorphous Ni--RE--P alloy could be greatly enlarged by introducing Al into the Ni-…     

低水碳比条件下 Ni/CeO2/Al2O3催化剂上液化石油气的预重整

采用硝酸盐溶液共浸渍薄水铝石制备了不同Ni含量的Ni/CeO2/Al2O3催化剂,并采用X射线衍射、N2物理吸附和程序升温还原等手段对其进行了表征.结果表明,Ni和CeO2物种之间存在较强的相瓦作用,CeO2的加入有利于NiAl2O4还原成金属Ni,而金属Ni又促进了CeO2还原并与Al2O3反应形成CeAlO3.详细...     

Ni-Fe-Al-O双金属催化剂在生物质基2-羟基四氢吡喃还原胺化合成5-氨基-1-戊醇中的性能研究北大核心CSCD

采用共沉淀法制备了不同Fe/Ni摩尔比(0、0.125、0.25、0.5和0.75)的Al_(2)O_(3)负载型NiFe单、双金属催化剂,并考察了它们在生物糠醛衍生2-羟基四氢吡喃(2-HTHP)还原胺化合成高附加值5-氨基戊醇反应中的催化性能.研究发现当Fe/Ni摩尔比为0.25时表现出最高的5-氨基戊醇收率(在80℃和2 MPa优化条件下达90%).利用N_(2)吸脱附、X射线衍射(XRD)、氢气程序升温还原(H_(2)-TPR)、透射电镜(TEM)等技术对催化剂进行了表征,结果表明适量Fe的掺入可以提高催化剂的分散性和还原性,同时在还原活化催化剂中形成Ni-Fe合金相,继而使相应催化剂表现出更优异的催化活性.通过固定床对比考察了催化剂的稳定性,NiFe(0.25)-Al-O双金属催化剂表现出明显优于NiFe(0)-Al-O单金属催化剂的稳定性,运行120 h前者只有微弱失活而后者显著失活.对比反应后催化剂表征发现,金属Fe的修饰可以有效抑制金属活性颗粒的烧结和流失,从而显著提高其反应稳定性.     

Effect of CeO2 on the catalytic performance of Ni/Al2O3 for autothermal reforming of methane

The effect of promoter Ce on the catalytic performance of Ni/Al2O3 catalyst for autothermal reforming of methane to hydrogen was investigated. The catalysts were characterized by X-ray diffraction （XRD）, temperature-programmed reduction （TPR）, and X-ray photoelectron spectroscopy （XPS）. The results indicated that the catalytic performance of the catalysts was improved with the addition of Ce. Ni/Ce30Al70Oδ showed the highest CH4 conversion in operation temperatures ranging from 650 ℃ to 850 ℃. At the same time, the decrease in H2/CO ratio with increasing reaction temperature was consistent with the fact that water-gas shift reaction was thermodynamically unfavorable at higher temperatures. The XRD result indicated that adding Ce to Ni/Al2O3 catalyst prevented the formation of NiAl2O4 and facilitated the formation of NiO. The formation of NiO increased the number of active sites, resulting in higher activity. Comparing the TPR profiles of Ni/Ce30Al70Oδ with Ni/Al2O3, it could be clearly observed that with the addition of Ce, the total reduction peak areas in the middle and low temperatures increased. It was most probably that the addition of Ce inhibited the stronger interaction between Ni and Al2O3 to form the phase of NiAl2O4, and favored the formation of the strong interaction between NiO species and CeO2. Therefore, the addition of Ce to the Ni/Al2O3 catalyst increased the active surface that promoted the activity of the catalyst.