Na_2Ge_2Se_5电子结构和光学性质的第一性原理研究

Na_2Ge_2Se_5是一种优异的红外非线性晶体材料.采用基于第一性原理的密度泛函理论赝势平面波方法对Na_2Ge_2Se_5进行结构优化,并以此为基础计算研究了Na_2Ge_2Se_5的电子结构和光学性质.结果表明:Na2Ge2Se5是宽禁带间接带隙半导体,价带至导带的电子跃迁主要来自于Ge和Se的48,4p态;Na对光学性质的贡献较小,Ge和Se之间的相互耦合作用决定了Na_2Ge_2Se_5的光学性质;该晶体在紫外区有强烈的反射和吸收,静态折射率为2.133,双折射率值适中,为0.145.理论计算结果表明,Na_2Ge_2Se_5是一种性能优良的红外非线性光学晶体材料.     

Optical characterization of amorphous Ga50Se45S5 films

The transmission spectra of thermally evaporated Ga₅₀Se₄₅S₅ films were measured over the wavelength range 300–900 nm. A simple method, suggested by Swanepoel, was used for the determination of the optical constants and thickness of the films. Increasing the thickness of the film beyond 450 nm does not affect the optical constants. The dependence of the absorption coefficient on the photon energy (hν) at the edge of the absorption band is well described by the relation hν=β(hν−E_opt)² with an optical gap equals 2.4 eV. A good fit of the experimental points with Tauc relation indicates that non-direct transition is the most probable mechanism responsible for the photon absorption inside the investigated film.     

Ge20Sb15Se65薄膜的热致光学特性变化研究

采用磁控溅射法制备了Ge₂₀Sb₁₅Se₆₅薄膜, 研究热处理温度(150—400 ℃)对薄膜光学特性的影响. 通过分光光度计、X射线衍射仪、显微拉曼光谱仪对热处理前后薄膜样品 的光学特性和微观结构进行了表征, 并根据Swanepoel方法以及Tauc公式分别计算了薄膜折射率色散曲线和光学带隙等参数. 结果表明当退火温度(T_a)小于薄膜的玻璃转化温度(T_g)时,薄膜的光学带隙(E_g^opt)随着退火温度的增加由1.845 eV上升至1.932 eV, 而折射率由2.61降至2.54; 当退火温度大于薄膜的玻璃转化温度时,薄膜的光学带隙随退火温度的增加由1.932 eV降至1.822 eV, 折射率则由2.54增至2.71. 最后利用Mott和Davis提出的非晶材料由非晶到晶态的结构转变模型对结果进行了解释, 并通过薄膜XRD和Raman光谱进一步验证了结构变化是薄膜热致变化的重要原因. 关键词： 20Sb₁₅Se₆₅薄膜')" href="#">Ge₂₀Sb₁₅Se₆₅薄膜 热处理 光学带隙 折射率     

Growth mechanism and characterisation of chemically grown Sb doped Bi2Se3 thin films

The synthesis of combinatorial Bi_2−xSb_xSe₃ thin films by arrested precipitation technique (APT) using triethanolamine-bismuth, triethanolamine-antimony and sodium selenosulphite as sources of Bi³⁺, Sb³⁺ and Se²⁻, respectively is investigated on commercial glass substrates. The growth mechanism of film formation, composition and surface morphology of the as deposited films were studied as a function of preparative parameters and bath composition. The films were monophasic, polycrystalline and covered the surface of the substrate completely. Energy dispersive X-ray analysis gave coherent elemental composition indicating single phase BiSbSe₃ was made. The good results obtained for Bi_2−xSb_xSe₃ thin films revealed that arrested precipitation technique is best suited for the deposition of large area thin films on conducting/nonconducting substrates to produce materials for device applications.     

Photoemission oscillation in epitaxially grown van der Waals β-In2Se3/WS2 heterobilayer bubbles

Thin films of millimeter-scale continuous monolayer WS₂ have been grown on SiO₂/Si substrate, followed by the deposition of β-In₂Se₃ crystals on monolayer WS₂ to prepare In₂Se₃/WS₂ van de Waals heterostructures by a two-step chemical vapor deposition (CVD) method. After the growth of In₂Se₃ at elevated temperatures, high densities of In₂Se₃/WS₂ heterostructure bubbles with monolayer to multilayer β-In₂Se₃ crystals atop are observed. Fluorescence of the resultant β-In₂Se₃/WS₂ heterostructure is greatly enhanced in intensity upon the formation of bubbles, which are evidenced by the Newton's rings in optical image owing to constructive and destructive interference. In photoluminescence (PL) mapping images of monolayer β-In₂Se₃/monolayer WS₂ heterobilayer bubble, significant oscillatory behavior of emission intensity is demonstrated due to constructive and destructive interference. However, oscillatory behaviors of peak position are also observed and come from a local heating effect induced by an excitation laser beam. The oscillatory mechanism of PL is further verified by changing the exterior pressure of bubbles placed in a home-made vacuum chamber. In addition, redshifted in peak position and broadening in peak width are observed due to strain effect during decreasing the exterior pressure of bubbles.     

First-principles calculations of nitrogen-doped antimony triselenide: A prospective material for solar cells and infrared optoelectronic devices

This study is focused on calculation of the electronic structure and optical properties of non-metal doped Sb2Se3 using the first-principles method. One and two N atoms are introduced to Sb and Se sites in a Sb₂Se₃ crystal. When one and two N atoms are introduced into the Sb₂Se₃ lattice at Sb sites, the electronic structure shows that the doping significantly modifies the bandgap of Sb₂Se₃ from 1.11 eV to 0.787 and 0.685 eV, respectively. When N atoms are introduced to Se sites, the material shows a metallic behavior. The static dielectric constants ε1(0) for Sb₁₆Se₂₄, Sb₁₅N₁Se₂₄, Sb₁₄N₂Se₂₄, Sb₁₆Se₂₃N₁, and Sb₁₆Se₂₂N₂ are 14.84, 15.54, 15.02, 18.9, and 39.29, respectively. The calculated values of the refractive index n(0) for Sb₁₆Se₂₄, Sb₁₅N₁Se₂₄, Sb₁₄N₂Se₂₄, Sb₁₆Se₂₃N₁, and Sb₁₆Se₂₂N₂ are 3.83, 3.92, 3.86, 4.33, and 6.21, respectively. The optical absorbance and optical conductivity curves of the crystal for N-doping at Sb sites show a significant redshift towards the short-wave infrared spectral region as compared to N-doping at Se sites. The modulation of the static refractive index and static dielectric constant is mainly dependent on the doping level. The optical properties and bandgap narrowing effect suggest that the N-doped Sb₂Se₃is a promising new semiconductor and can be a replacement for GaSb due to its very similar bandgap and low cost.     

Photoconductivity in the ordered vacancy compound CuIn5Se8

Thin films of the ordered vacancy compound CuIn₅Se₈ are deposited on glass substrates by multisource co-evaporation method and photoconductivity measurements are done on the films at various temperatures from 10 up to 300 K. The two photoactive bands that are identified in the spectral response spectra of CuIn₅Se₈ thin films at all measured temperatures are attributed to photoactive transitions between acceptor V_Cu to donor In_Cu and valence band to conduction band transitions respectively. From the spectra, a shift in band-to-band gap from 1.36 to 1.3 eV is observed with a temperature variation from 10 to 300 K. The non-exponential long-term decay observed in the transient photoconductivity spectra suggests a deep level trap-emptying process to be associated with the decay process and the decay constants are calculated by the differential life-time concept. From the steady state photocurrent analysis, a reduction in intergrain potential barrier on illumination has been noted as one reason for increase in conductivity on illumination. X-ray photoelectron spectroscopy analysis has been done to determine the binding energies of Cu, In and Se in the compound.     

新型硒化锑材料及其光伏器件研究进展

硒化锑(Sb₂Se₃)是一种二元单相化合物, 原料储量大、毒性低、价格便宜; 同时其禁带宽度合适(～1.15 eV), 吸光系数大(>10⁵ cm^-1), 长晶温度低, 非常适合制作新型低成本低毒的薄膜太阳能电池, 理论光电转换效率可达30%以上. 目前文献报道的Sb₂Se₃薄膜太阳能电池效率已达3.7%, 初步证明了Sb₂Se₃材料在薄膜太阳能电池应用方面的巨大潜力. 本文综述了近年来Sb₂Se₃太阳能电池的研究进展, 着重介绍了Sb₂Se₃的材料特性和薄膜制备及相关理论研究, 阐述了不同结构电池器件的研究进展, 并对其发展趋势进行了展望.     

P to Se cross polarization in β-P4Se3

Cross polarization from ³¹P to ⁷⁷Se is demonstrated in β-P₄Se₃. This material, an inorganic glass, is readily synthesized from the elements and serves as a convenient sample for setting the Hartmann-Hahn condition.     

Composition and thermal-induced effects on the optical constants of Ge20Se80−xBix thin films

 The effects of composition and thermal annealing near crystallization temperature, T_c on the optical and structural properties of Ge₂₀Se_80−xBi_x (x=0, 2.5, 5 and 7.5 at%) was investigated. The influence of incorporation Bi content in Ge₂₀Se_80−xBi_x system results in a gradual decrease in the indirect optical gap from 1.89 to 1.44 eV, this behavior can be explained as increased tailing. On annealing, the optical band gap E_g decreases gradually for the crystallized films while the refractive index increases, this behavior can be attributed to transformation from amorphous to crystalline and was explained in the light of dangling bond model. The refractive index n of as-prepared and annealed films has been analyzed according to the Wwmple–DiDominico single oscillator model and the values of E_o and E_d were determined. The effect of annealing on the nature and degree of crystallization has been investigated by studying the structure using transmission electron microscope, X-ray diffraction and scanning electron microscope.     

不同Sb含量p-SnO2薄膜的制备和特性

采用化学气相沉积方法, 利用Sb₂O₃/SnO作为源材料, 在蓝宝石衬底上制备出不同Sb掺杂量的SnO₂薄膜, 并在此基础上制作出p-SnO₂:Sb/n-SnO₂同质p-n 结器件. 研究表明, 随着Sb含量的增加, 样品表面变得平滑, 晶粒尺寸逐渐增大, 且晶体质量有所改善, 发现少量Sb的掺入可以起到表面活化剂的作用. Hall测量结果证实适量Sb的掺杂可以使SnO₂呈现p型导电特性, 当Sb₂O₃/SnO的质量比为1:5时, 其电学参数为最佳值. 此外, p-SnO₂:Sb/n-SnO₂同质p-n结器件展现出良好的整流特性, 其正向开启电压为3.4 V.     

H2S硫化CuInSe2生成CuIn(SxSe1-x)2薄膜的XRD及Raman分析

将CuInSe₂薄膜在H₂S与Ar的混合气体中硫化是制备CuIn(S_xSe_1-x)₂薄膜的一种常用方法。硫化所用到的CuInSe₂薄膜是用溶剂热法生成的CuInSe₂纳米颗粒旋涂而成。不同于其他真空条件下制备CuInSe₂薄膜的方法.溶剂热法的优点是其相对简单的制备工艺和较低廉的成本。对硫化过程进行研究后发现,硫化温度和时间直接影响CuIn(S_xSe_1-x)₂薄膜的质量,诸如薄膜成分、结晶度、均匀性和带隙宽度都可以通过改变这些实验条件来进行控制。     

Synthesis and physical behaviour of In2S3 films

In₂S₃ layers have been grown by close-spaced evaporation of pre-synthesized In₂S₃ powder from its constituent elements. The layers were deposited on glass substrates at temperatures in the range, 200–350 °C. The effect of substrate temperature on composition, structure, morphology, electrical and optical properties of the as-grown indium sulfide films has been studied. The synthesized powder exhibited cubic structure with a grain size of 63.92 nm and S/In ratio of 1.01. The films grown at 200 °C were amorphous in nature while its crystallinity increased with the increase of substrate temperature to 300 °C. The films exhibited pure tetragonal β-In₂S₃ phase at the substrate temperature of 350 °C. The surface morphological analysis revealed that the films grown at 300 °C had an average roughness of 1.43 nm. These films showed a S/In ratio of 0.98 and a lower electrical resistivity of 1.28 × 10³ Ω cm. The optical band gap was found to be direct and the layers grown at 300 °C showed a higher optical transmittance of 78% and an energy band gap of 2.49 eV.     

Synthesis and ionic conductivity of new layered perovskite compound, Ag2La2Ti3O10

A new layered perovskite compound, Ag₂La₂Ti₃O₁₀, was synthesized by an ion-exchange reaction of M₂La₂Ti₃O₁₀ (M = Na,K) with a AgNO₃ molten salt. The crystal structure and the ionic conductivity of the ion-exchanged compound were investigated. The ionic conductivities attributed to the interlayer silver ions were observed at high temperatures. The ionic conductivity of Ag₂La₂Ti₃O₁₀ was much higher than that of Na₂La₂Ti₃O₁₀, while the interlayer sodium ions in Na₂La₂Ti₃O₁₀ and silver ions in Ag₂La₂Ti₃O₁₀ have almost the same rock-salt type coordination. The higher conductivity of Ag₂La₂Ti₃O₁₀ is probably due to the higher polarizability of silver ions.     

半导体材料AAl2C4(A=Zn, Cd, Hg; C=S, Se)的电子结构和光学性质

采用基于密度泛函理论的第一性原理方法, 对具有缺陷型黄铜矿结构的半导体材料A^ⅡAl₂C₄^Ⅵ(A=Zn, Cd, Hg; C =S, Se)的构型和电子结构进行研究, 并系统考察了各晶体的光学性质. 对于线性光学性质, 五种晶体在红外区和部分可见光区具有良好的透光性能, 其中HgAl₂S₄和HgAl₂Se₄晶体具有适中的双折射率. 在非线性光学性质方面, 该类晶体倍频效应较强, 理论预测得到的二阶静态倍频系数均较大(>20 pm/V). 体系的倍频效应主要来源于价带顶附近以S/Se 价p轨道为主要成分的能带向含有较多Al/Hg 价p成分的空带之间的跃迁. 通过与已商业化的AgGaC₂晶体光学性质的对比, 结果表明HgAl₂S₄和HgAl₂Se₄是一类性能优良的红外非线性光学晶体材料.     

Bi4Se3薄膜的声子结构及电声子相互作用的第一性原理研究

基于密度泛函微扰理论,运用第一性原理研究两种终结面的Bi₄Se₃薄膜的声子结构和电-声子相互作用.结果表明两种终结面的Bi₄Se₃薄膜体系都是动力学稳定的. Bi₄Se₃薄膜中插入的Bi₂双原子层与Bi₂Se₃五原子层的声子投影态密度并不完全匹配,这会阻碍部分声子的输运,降低热导,从而有利于提高材料的热电性能.另外,两种终结面的Bi₄Se₃薄膜的电-声子耦合系数都不太大（约0.278）,有利于制备基于室温工作的电子学器件.     

Ionic diffusion and local hopping in copper chalcohalide glasses measured using Cu tracer and I-Mössbauer spectroscopy

For the first time, ⁶⁴Cu tracer measurements of ionic diffusion were performed for several copper-rich glass compositions in the CuI---As₂Se₃, CuI---SbI₃---As₂Se₃, CuI---PbI₂---As₂Se₃, CuI---PbI₂---SbI₃---As₂Se₃ and Cu₂Se---As₂Se₃ systems. In accordance with previous a.c. impedance results and Wagner d.c. polarization measurements, it was found that pure Cu⁺ ion-conducting glasses (50CuI---17PbI₂---33As₂Se₃ and 50CuI---20PbI₂---10SbI₃---20As₂Se₃) exhibit the highest copper tracer diffusion coefficients, D_Cu, and the lowest diffusion activation energies. The values of D_Cu at room temperature are higher by 4.5–5.5 orders of magnitude than those in an As₂Se₃ glass. The Haven ratio, H_R, is found to be 0.52–0.61 (ternary glass) and 0.93–1.00 (quaternary glass). Short-range diffusional displacements of the iodide ions induced by the hopping Cu⁺ ions are also detected in the CuI---PbI₂---SbI₃---As₂Se₃ glassy system using ¹²⁹I-Mössbauer spectroscopy in the temperature range of 4.2 to 305 K. The activation energy of local hopping, E_h ≈ 0.31 eV, is very similar to that of bulk ionic conductivity (0.37 eV) and copper diffusion (≈ 0.33 eV). In contrast to CuI-based vitreous alloys, 50Cu₂Se---50As₂Se₃ glass exhibits D_Cu that are two to five orders of magnitude lower, and the copper ion transport number, t_Cu⁺, is between 10⁻³ and 10⁻⁴ in the temperature range 140–170 °C.     

Linear optical characterization of chalcogenide glasses

A simple experimental method is used to obtain the evolution of both the refractive index and the linear absorption coefficient as a function of the optical wavelength in the near infrared range (from 900 up to 1700 nm with 10 nm resolution). Several chalcogenide glasses (As₂S₃, As₂Se₃, GeSe₄) are tested and the corresponding Cauchy coefficients are determined. Comparison of our results shows a good agreement with values available in the literature at some wavelength. Application of this method is used to estimate Cauchy coefficients of Ge₁₀As₁₀Se₈₀ for the first time to our best knowledge.     

Picosecond nonlinear optical response of Ba0.5Sr0.5TiO3 thin films fabricated by pulsed laser deposition

Well-crystallized Ba_0.5Sr_0.5TiO₃ thin films with good surface morphology were prepared on MgO(1 0 0) substrates by pulsed laser deposition technique at a deposition temperature of 800 °C under the oxygen pressure of 2 × 10⁻³ Pa. X-ray diffraction and atomic force microscopy were used to characterize the films. The full width at half maximum of the (0 0 2) Ba_0.5Sr_0.5TiO₃ rocking curve and the root-mean-square surface roughness within the 5 μm × 5 μm area were 0.542° and 0.555 nm, respectively. The nonlinear optical properties of the films were determined by a single beam Z-scan method at a wavelength of 532 nm with laser duration of 55 ps. The results show that Ba_0.5Sr_0.5TiO₃ thin films exhibit a fast third-order nonlinear optical response with the nonlinear refractive index and nonlinear absorption coefficient being n₂ = 5.04 × 10⁻⁶ cm²/kW and β = 3.59 × 10⁻⁶ (m/W), respectively.     

Sol–gel preparation and characterisation of dense proton conducting Sr3CaZr0.5Ta1.5O8.75 thin films

Dense proton conducting Sr₃CaZr_0.5Ta_1.5O_8.75 films (1.25 μm, with grain size in the 200–400 nm range) were deposited, using the sol–gel method, on Al₂O₃–8%Y₂O₃-stabilised ZrO₂ plates. The obtained gels were characterised by differential and thermogravimetric thermal analysis (DTA–TGA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results of a study of the structural and electrical properties of Sr₃CaZr_0.5Ta_1.5O_8.75 films deposited on the mentioned substrates are presented herein. The structural data for the gels and films were compared with those obtained for the same material prepared by solid state synthesis. Electrical properties of the sandwich-type structure were investigated by AC impedance conductivity measurements at different temperatures, in both dry and wet 5% H₂/Ar atmospheres. A careful analysis of the impedance spectra for this complex structure was performed, using a model with a series of five electrical circuits, having resistance and capacitance coupled in parallel. The specific responses observed in the impedance spectra were assigned to the corresponding substrate and layer contributions. A significant improvement, by an order of magnitude, in the electrode response was observed in the presence of the interleaving Sr₃CaZr_0.5Ta_1.5O_8.75 proton conducting layer, between the electrode and electrolyte. This enhancement is lost at temperatures above that at which the Sr₃CaZr_0.5Ta_1.5O_8.75 dehydrates and its protonic conductivity diminishes. Considering the structural and electrical characterisation results, these Sr₃CaZr_0.5Ta_1.5O_8.75 sol–gel derived films have a potential use for proton conducting electrolyte or intermediate layer in fuel cells.