稀土Tb3+掺杂纳米ZnO的发光性质

ZnO是一种优良的直接宽带隙半导体发光材料(Eg=3.4 eV),具有优异的晶格、光学和电学性质,稀土离子掺杂浓度和热处理温度对ZnO∶Re3 纳米晶发光强度、峰位变化等光学性质具有重要影响.利用溶胶-凝胶法(Sol-Gel),在不同退火温度下,制备了不同浓度的ZnO∶Tb3 纳米晶.室温下,测量了样品的X射线衍射谱(XRD)、光致发光谱(PL)和激发谱(PLE).观察到纳米ZnO基质在520 nm附近宽的绿光可见发射和稀土Tb3 在485,544,584和620 nm附近的特征发射.通过ZnO基质可见发射强度和稀土Tb3 特征发射强度随Tb3 掺杂浓度、退火温度的变化关系,获得了5D4→7F5跃迁的绿色主发射峰最强的样品制备工艺参数,其退火温度为600℃、掺杂浓度为4 at%;给出了稀土Tb3 的激发态5D4→7F6(485 nm),5D4→7F5(544 nm)和5D4→7F4(584 nm)的发射机制;证实了稀土Tb3 与纳米ZnO基质之间存在双向能量传递.     

ZnO∶Tb3+纳米晶的制备及发光性质研究

利用溶胶-凝胶法（Sol-Gel）制备了不同浓度的ZnO∶Tb3+纳米晶，测量了样品的光致发光谱(PL)和激发谱(PLE).在ZnO宽的可见发射背景上，观察到样品在485 nm、544 nm、584 nm和620 nm附近出现了稀土Tb3+的特征发射.给出了ZnO∶Tb3+纳米晶光致发光的峰值强度随掺Tb3+浓度的变化关系，分析了稀土Tb3+的激发态5D4→7F6、5D4→7F5和5D4→7F4的发射机制，证实了稀土Tb3+的特征发射来源于稀土离子内部4f电子的f-f跃迁和ZnO基质与稀土Tb3+离子之间能量传递.     

ZnO:Tb纳米晶的协同发光现象

用光致发光的方法研究了掺铽的ZnO纳米晶这种新型掺杂纳米晶体系,观察到了其中的协同发光现象,指出ZnO纳米基质与掺入其中的铽中心之间存在有效的能量传递.该能量传递对稀土铽离子的特征发光起决定性的作用. 关键词： 光致发光 掺杂 纳米晶     

Photoluminescence of ZnO and Mn-Doped ZnO Polycrystalline Films Prepared by Plasma Enhanced Chemical Vapour Deposition

ZnO and Mn-doped ZnO polycrystalline films are prepared by plasma enhanced chemical vapour deposition at low temperature （220℃）, and room-temperature photoluminescence of the films is systematically investigated. Analysis from x-ray diffraction reveals that a11 the prepared films exhibit the wurtzite structure of ZnO, and Mndoping does not induce the second phase in the films. X-ray photoelectron spectroscopy confirms the existence of Mn^2＋ ions in the films rather than metalic Mn or Mn^4＋ ions. The emission efficiency of the ZnO film is found to be dependent strongly on the post-treatment and to degrade with increasing temperature either in air or in nitrogen ambient. However, the enhancement of near band edge （NBE） emission is observed after hydrogenation in ammonia plasma, companied with more defect-related emission. Furthermore, the position of NBE shifts towards to high-energy legion with increasing Mn-doped concentration due to Mn incorporation into ZnO lattice.     

1.54 μm emission mechanism of Er-doped zinc oxide thin films

Zinc oxide (ZnO) and Er-doped zinc oxide (ZnO:Er) thin films were formed by pulsed laser deposition, and characterized by photoluminescence (PL) and X-ray diffraction (XRD) in order to clarify the 1.54 μm emission mechanism in the ZnO:Er films. Er ions were excited indirectly by the 325 nm line of a He-Cd laser, and the comparison of the ultraviolet to infrared PL data of ZnO and ZnO:Er films showed that the 1.54 μm emission of Er³⁺ in ZnO:Er film appears at the expense of the band edge emission and the defect emission of ZnO. The crystallinity of the films was varied with the substrate temperature and post-annealing, and it was found that the intensity of the 1.54 μm emission is strongly related with the crystallinity of the films. There are three processes leading to the 1.54 μm emission; absorption of excitation energy by the ZnO host, energy transfer from ZnO to Er ions, and radiative relaxation inside Er ions, and it is suggested that the crystallinity plays an important role in the first two processes.     

过渡金属与F共掺杂ZnO薄膜结构及磁、光特性

采用溶胶-凝胶法在玻璃衬底上制备了过渡金属元素与F共掺杂Zn_0.98-xTM_xF_0.02O (TM_x=Cu_0.02, Ni_0.01, Mn_0.05, Fe_0.02, Co_0.05)薄膜, 进而利用X射线衍射仪、扫描电子显微镜、紫外-可见透过谱、光致发光及振动样品磁强计等研究了薄膜的表面形貌、微结构、禁带宽度及光致发光(PL)和室温磁学特性. 研究表明: 掺杂离子都以替位的方式进入了ZnO晶格, 掺杂不会破坏ZnO的纤锌矿结构. 其中Zn_0.93Co_0.05F_0.02O薄膜样品的颗粒尺寸最大, 薄膜的结晶度最好且c轴择优取向明显; Zn_0.93Mn_0.05F_0.02O薄膜样品的颗粒尺寸最小, 薄膜结晶度最差且无明显的c轴择优取; Cu, Ni, Fe与F共掺杂样品的颗粒尺寸大小几乎相同. TM掺杂样品均表现出很高的透过率, 同时掺杂后的薄膜样品的禁带宽度都有不同程度的红移. PL谱观察到Zn_0.98-xTM_xF_0.02O薄膜的发射峰主要由较强的紫外发射峰和较弱的蓝光发射峰组成. Zn_0.93Mn_0.05F_0.02O薄膜样品的紫外发光峰最弱, 蓝光发射最强, 饱和磁化强度最大; 与之相反的是Zn_0.96Cu_0.02F_0.02O薄膜, 其紫外发光峰最强, 蓝光发射最弱, 饱和磁化强度最小. 结合微结构和光学性质对Zn_0.98-xTM_xF_0.02O薄膜的磁学性质进行了讨论.     

Ti/TiO_2包覆ZnO:Tb纳米纤维的光学性质

用电纺丝方法制备了ZnO:Tb纳米纤维.用X-射线衍射、Raman光谱对其形貌做了表征.结果显示,ZnO:Tb纳米纤维为六方纤锌矿结构,Tb掺杂对ZnO的结晶性有影响.利用表面等离激元,通过对纳米纤维表面包覆金属Ti和TiO_2,比较了其光致发光谱,得到在325 nm激发下ZnO:Tb纳米纤维中稀土发光效率低的原因是ZnO和Tb之间不能进行有效的能量传递;包覆TiO_2后能提高稀土发光效率.     

Ce3+,Tb3+氟化物磷光体的发光性质比较

采用溶液反应和固相反应分别合成了Ｋ３ＡｌＦ６基质化合物及ＫＢＦ４：Ｃｅ,Ｔｂ和Ｋ３ＡｌＦ６：Ｃｅ,Ｔｂ等磷光体,研究了它们的光谱特性,并与ＫＡｌＦ４：Ｃｅ,Ｔｂ、ＣａＦ２：Ｔｂ和ＡｌＦ３：Ｃｅ,Ｔｂ等磷光体的发光特性进行了比较。结果发现,ＣａＦ２：Ｃｅ,Ｔｂ、ＡｌＦ３：Ｃｅ,Ｔｂ、ＫＢＦ４：Ｃｅ,Ｔｂ和Ｋ３ＡｌＦ６：Ｃｅ,Ｔｂ等磷光体中Ｃｅ＾３＋对Ｔｂ＾３＋的能量传递不能有效进行,有时Ｔｂ＾３＋起     

Characterization and ammonia sensing properties of pure and?modified ZnO films

Zinc oxide (ZnO) films have been prepared by thermal oxidation of pre-deposited zinc films on the glass substrate kept at room temperature. These films were surface modified by dipping them into an aqueous solution (0.1 M) of lithium chloride (LiCl) and aluminium chloride (AlCl₃) followed by firing at 500°C. Based on X-ray diffraction results it is observed that modification of pure ZnO by lithium and aluminium precursor results a change in the lattice parameters. Li and Al ions appear to enhance the a-axis orientation and c-axis orientation of pure ZnO films, respectively. Field emission scanning electron micrographs of lithium-modified ZnO film indicate the presence of nanoneedles, while nanorods are observed in case of aluminium-modified ZnO film. The electrical resistance measurements of modified ZnO films also show variation in resistance as compared to pure ZnO film. Pure and Al-modified films of ZnO are sensitive to ammonia at room temperature, while Al-modified ZnO film is found to be more sensitive with 99% of response at 250 ppm.     

溶胶-凝胶法制备ZnO薄膜及其光致发光性质

利用溶胶-凝胶法在石英衬底上制备了ZnO薄膜,通过测量样品的透射谱、X射线衍射谱、扫描电子显微镜(SEM)图像和光致发光谱研究了其结构特征和发光性质.结果表明:在衍射角2θ=34.32°处出现了对应(002)晶面的强衍射峰,ZnO膜呈多晶状态,具有六角纤矿晶体结构和良好的C轴择优取向,薄膜中颗粒的平均粒径为56nm;光致发光呈多发光峰状,有中心波长为378nm的紫带,520nm绿带,446nm附近的蓝带以及发现未见报道过的绿带以后中心波长为586nm和570nm两个弱发射峰.实验结果表明,制备的ZnO薄膜具有发光特性,但内部与深能级发射相关的结构缺陷浓度还是较高,样品中两个低能量光致发光应来源于晶粒间界的缺陷能级,多缺陷能级导致了多发射峰的光致发光谱.     

ZnS:TbF3,ErF3,HoF3ACTFEL的亮度与跃迁几率的关系

测量了低浓度下ZnS:TbF3,ErF3和ZnS:TbF3,HoF3交流电致发光薄膜(ACTFEL)中的Tb3+,Er3+,HO3+主要发射峰的相对积分强度,并与Tb3+,Er3+,Ho3+主要发射能级的辐射跃迁几率及高浓度时的发光特性进行了比较,发现稀土氟化物掺杂的ZnS薄膜电致发光(ACTFEL)的最大亮度,不完全取决于稀土离予本身的辐射跃迁几率,而主要取决于稀土离子主要发射能级激发态的运动。本文首次给出了Tb3+离子在ZnS中的强度参数Ω2=3.2×10-19cm2,Ω4=1.6×10-19cm2,Ω6=2.6×10-19cm2,并应用这组Ωλ参数估算了Tb3+离子的交叉弛豫(cross-relaxation)几率。     

Ca2SnO4∶Tb3+绿色荧光粉的制备及光致发光研究

采用高温固相法合成了Ca2 SnO4∶Tb3+绿色荧光粉.利用X射线衍射分析了Ca2 SnO4∶Tb3+物相的形成.测量了Ca2 SnO4∶Tb3+的激发和发射光谱,激发光谱由一个宽激发峰组成,研究了Tb3+浓度对样品激发光谱的影响,结果显示,随Tb3+浓度增大,宽带激发峰发生了红移.发射光谱由四个主要发射峰组成,峰值...     

水热法制备LaF3:Ce,Tb纳米荧光粉及发光性质研究

利用水热法制备了LaF3∶Ce,Tb纳米荧光粉,分别用XRD,TEM和发光光谱等测试手段对粉末的物相、形貌、发光性质进行了研究.XRD和TEM结果表明:所得的纳米荧光粉粒度均匀、结晶完好,呈规则的六边形形状,颗粒平均尺寸为30 nm,掺人Ce3 和Tb3 ,杂质后晶格结构没有变化.发光光谱的测试表明:Ce3 呈现其宽带发射;Tb3 呈现其特征绿色发射,最强峰位于544 nm处.Ce3 的掺入有效敏化了Tb3 的发光,通过进一步光谱分析证实了在LaF3∶Ce,Tb体系中存在Ce3 →Tb3 的能量传递过程.当Ce3 和Tb3 掺杂摩尔浓度分别为35 mol%和5 mol%时具有最强荧光发射.制备的样品无需煅烧即可获得比体相材料高2倍的荧光,也高于优化条件下煅烧样品的荧光.     

Difference in magnetic properties between Co-doped ZnO powder and thin film

This paper reports that the Zn掺钴;氧化锌粉末;氧化锌薄膜;磁性差异;晶体取向ZnO, Co-doped, crystalline orientation, magnetismProject supported by the Shanghai Nanotechnology Promotion Center (Grant No~0452nm071).2006-09-152006-11-29This paper reports that the Zn0.95Co0.05O polycrystalline powder and thin film were prepared by sol-gel technique under the similar preparation conditions. The former does not show typical ferromagnetic behaviour, while the latter exhibits obvious ferromagnetic properties at 5 K and room temperature. The UV-vis spectra and x-ray absorption spectra show that Co2＋ ions are homogeneously incorporated into ZnO lattice without forming secondary phases.The distinct difference between film and powder sample is the c-axis （002） preferential orientation indicated by the x-ray diffraction pattern and field emission scanning electron microscopy measurement, which may be the reason why Zn0.95Co0.05O film shows ferromagnetic behaviour.     

两步化学沉积法制备ZnO薄膜及其场发射特性

在低温常压条件下,以ITO玻璃为衬底,采用电化学法与湿化学法结合的两步化学沉积法制备了团簇状ZnO薄膜。利用XRD,SEM分析了薄膜结构和表面形貌,并采用二极管结构在高真空条件下对薄膜进行了场发射性能测试。稳定发射后,开启电场为3.0 V/μm。当电场为5.8 V/μm时,电流密度为583.3 μA/cm²。研究表明:两步化学沉积法低温制备ZnO薄膜是可行的,且该薄膜具有良好的场发射性能。     

铕掺杂纳米氧化锌晶体结构和荧光光谱的研究

以醋酸锌、氧化铕、氢氧化钠为主要原材料,利用共沉淀法制备ZnO∶Eu3+纳米晶体.在X射线衍射谱中,只观察到氧化锌的峰,没有观察到氧化铕的特征峰.比较了ZnO和ZnO∶Eu3+拉曼光谱,在ZnO∶Eu3+样品拉曼光谱中观察到新的局部振动模.这些现象表明铕离子已经进入氧化锌晶格中.SEM形貌显示Eu3+离子掺入使ZnO晶...     

下转换材料β-NaYF4:Tb3+,Yb3+的水热法合成和发光性质研究

利用水热法合成了粉末发光材NaYF4:Tb3+,Yb3+分别用X射线衍射(XRD),光致发光谱(PL)和激发谱(PLE)测试了合成材料的物相结构和发光性质.研究结果表明:合成的NaYF4:Tb3+,Yb3+抖材料为六方相的品体,无立方相的.改变Tb3+和Yb3+的掺杂浓度后品格结构没有变化,说明离子Tb3+和Yb3+取...     

乙酸类稀土配合物/聚丙烯酰胺的合成及其发光性能

以小分子乙酸和乙酸铵为配体,合成了水溶性乙酸类稀土配合物NH4REAc(RE为Tb或Eu)。将该类配合物与水溶性丙烯酰胺单体通过水溶液聚合,得到了透明的聚丙烯酰胺光致发光材料(NH4REAc/PAM)。着重研究了配合物和聚合物发光性能。结果表明,NH4REAc配合物和NH4REAc/PAM聚合物均能发射很强的稀土Tb3+或Eu3+离子特征荧光;NH4TbAc和NH4TbAc/PAM中的Tb3+离子5D4→7F5均有较长的荧光寿命,形成聚合物后表观荧光寿命有所增加,但量子效率η却有所降低。     

溶胶-凝胶法纳米ZnO薄膜的绿光发射

利用溶胶-凝胶法制备了纳米ZnO薄膜,室温下测量了样品的光致发光谱(PL)和X射线衍射谱(XRD),观测到中心波长在523 nm附近的绿色荧光发射,研究了纳米ZnO薄膜的绿光发射机制,证实了纳米ZnO薄膜绿光可见发射带来自氧空位(Vo)形成的浅施主能级和锌空位(Vzn)形成的浅受主能级之间的复合。     

ZnO-Si不同退火条件对生长ZnSe薄膜的影响

研究了作为缓冲层的ZnO薄膜在不同的退火时间、退火温度下退火对Si衬底上生长ZnSe膜质量的影响。当溅射有ZnO膜的Si(111)衬底的退火条件变化时，从X射线衍射谱（XRD）和光致发光谱（PL）中可见，ZnSe(111)膜的晶体质量有较大的变化。变温的PL谱表明，Si衬底上生长的具有ZnO缓冲层的ZnSe膜的近带边发射峰起源于自由激子发射。