溶胶-凝胶法制备YAl3(BO3)4粉末

使用溶胶-凝胶法、XRD与SEM等方法,研究了YAl3(BO3)4的合成参数.相对于固相合成YAl3(BO3)4需要温度1200 ℃才能形成纯相,溶胶-凝胶法当灼烧温度为900 ℃时,YAl3(BO3)4主相已经形成,当温度升至1100 ℃,可制得纯相,其粒径大约为1 μm.但其中存在晶粒大小不均问题,需进一步研究.     

溶胶-凝胶法合成KGd(WO4)2:Eu3+红色荧光粉及其发光性质的研究

采用溶胶-凝胶法合成KGd(WO4)2:Eu3+红色荧光粉.该荧光粉的性质通过X射线粉末衍射、扫描电子显微镜、激发谱、发射谱以及荧光衰减曲线来表征.KGd(WO4)2:Eu3+的激发谱主要由中心大约在270nm处的宽谱峰以及一系列由Eu3+离子f-f电子能级跃迁导致的锐线峰组成,在近紫外区有一个最强的激发峰在395nm.正好与紫外InGaN发光二极管(LED)芯片发射波长匹配.在395nm激发下,可以观察到最佳掺杂量为40%(原子分数)的KGd(WO4)2:Eu3+在614nm处产生强烈的红光.发光特性表明,KGd(WO4)2:Eu3+荧光粉可能潜在成为近紫外发光二极管(LEDs)用的红色荧光粉.     

溶胶-凝胶法制备稀土无机发光材料及其发光性能的研究

报道了用溶胶-凝胶法制备可用于光转换农膜的稀土无机发光材料, 用荧光分光光度计研究了其发光性能, 并对实验过程中影响样品发光性能的各种因素(体系pH值、反应温度、不同稀土组合)进行了探讨, 得到了优化的实验条件.当控制体系pH=9, 反应温度50 ℃, Eu3+/Y3+ 值为50/50时, 所得样品的发光性能较好.     

溶胶-凝胶法制备稀土铽配合物掺杂的发光薄膜

采用溶胶－凝胶法原位制备了稀土配合物掺杂的发光薄膜，薄膜透明均一。结果表明用原位合成法，可以将难溶性稀土羧酸类配合物有效地掺杂到溶胶基质中，荧光光谱分析表明，所得到的薄膜材料在紫外激发下发射出铽离子的特征发射线。     

Ca_2Y_8(SiO_4)_6O_2∶RE(RE=Eu,Tb)发光薄膜的制备及发光性能的研究

采用溶胶 凝胶法制备了稀土离子掺杂 (Eu3 ,Tb3 )的氧磷灰石三元稀土硅酸盐Ca2 Y8(SiO4 ) 6 O2 发光薄膜。通过X射线衍射 (XRD) ,红外光谱 (IR) ,扫描电镜 (SEM)等方法对薄膜的组成、结构、颗粒尺寸、形貌及厚度进行了研究 ,通过发光光谱对薄膜的发光性质进行了分析。XRD结果表明 70 0℃时薄膜尚处于非晶态 ,80 0℃时已开始有Ca2 Y8(SiO4 ) 6 O2 的物相形成 ,10 0 0℃时结晶已完全。这一点和红外光谱的结果相符。发光光谱测试表明Ca2 Y8(SiO4 ) 6 O2 ∶Eu3 薄膜显示了很强的红光发射 ,并以Eu3 的5D0 -7F2 (616nm)超灵敏跃迁为最强一组。Ca2 Y8(SiO4 ) 6 O2 ∶Tb3 的发射光谱由蓝光发射和绿光发射两部分组成 ,前者对应于5D3-7FJ,后者对应于5D4 -7FJ(J =6,5 ,4,3 ) ,且以5D4 -7F5(5 44nm)绿光发射为最强。     

Y2O3∶Eu3+发光薄膜的溶胶-凝胶法制备、表征及图案化

采用Pechini溶胶-凝胶法制备了纳米级Y2O3∶Eu3+发光薄膜, 同时, 通过软石印技术得到了条纹宽度为5～60 μm的Y2O3∶Eu3+图案化发光薄膜. 通过X射线衍射 (XRD)、付里叶变换-红外光谱 (FT-IR)、原子力显微镜(AFM), 光致发光(PL)光谱及寿命等方法对得到的发光薄膜进行了表征. XRD结果表明500 ℃时薄膜开始结晶, 900 ℃已结晶完全, 得到了立方相的产物. 图案化的条纹在烧结的过程中发生了明显的收缩(50%). Y2O3基质向掺杂的稀土离子Eu3+发生了有效的能量传递, 使得Eu3+显示出5D0-7FJ(J=0, 1, 2, 3, 4)特征发射. 寿命和光致发光光谱的研究表明, 发光强度随着温度的升高而增强.     

溶胶-凝胶工艺制备发光薄膜研究进展

本文综述了通过深胶－凝胶工艺制备发光薄膜的基本过程、薄膜的表征方法、发光薄膜的当前发展及应用情况。依据组成特点,对溶胶－凝胶法制备的发光薄膜乾地了分类阐述,并预言了今后该法制备发光薄膜的发展趋势。     

YAG∶Eu~(3+)、Bi~(3+)的溶胶-凝胶法合成及其结构和发光性能

溶胶－凝胶法以其各组分混合均匀性好、反应温度低、节省能源等诸多优点而引起了人们极大兴趣［１，２］．近年来，利用该法研制玻璃和陶瓷等无机材料的报道越来越多［３，４］．但研制稀土固体发光材料的报道则较少．钇铝石榴石Ｙ３Ａｌ５Ｏ１２（ＹＡＧ）是一种很好的基...     

CaWO4-YNbO4固溶体的Pechini溶胶-凝胶法合成及其发光性能

利用Pechini溶胶-凝胶法成功地合成了一系列CaWO4 - YNbO4固溶体Ca1-xYxW1-xNbxO4(1),其结构和性能经XRD,IR,SEM,PL等表征.结果表明,在NbO43-的掺杂量(x)为25％,于800℃焙烧2h的条件下合成的1最佳.W-O电荷迁移跃迁随着x的增加发生明显的蓝移,其荧光强度降低.     

Tb4O7纯度对Tb3Al5O12发光性质的影响

采用溶胶－凝胶法用不同纯度的Tb4O7在非还原气氛下合成了Tb3Al5O12，并研究了最佳合成条件，电子能谱以及发光性质，结果表明：Tb3Al5O12最佳合成时间应不超过3h，最佳合成温度不超过900℃，提高Tb4O7的纯度，Tb3Al5O12中Tb^3 的发光明显增强。     

Spectral Parameters of Nd^3＋ inthe Nd^3＋：GdMgB5O10 Crystal

1 INTRODUCTION With the development of diode-pumped solid-statelasers, the search of more efficient materials for diode-pumped solid-state lasers is becoming more and moreimportant. The good laser materials should have thefeatures of large absorption coefficient and large ab-sorption line widths, as well as large emission crosssection at the emission wavelength. In the past years,a number of Nd3 -doped crystals, such as Nd3 :YVO4 , Nd3 :YAG[2], Nd3 :KLW[3] and Nd3 : [1]YAP…     

Ce3+和Tb3+掺杂的稀土硼酸盐玻璃的发光性质

报道Ｃｅ＾３＋和Ｔｂ＾３＋掺杂的硼酸盐玻璃的合成及该系列玻璃的激发和发射光谱性质。在紫外光激发下,玻璃中的Ｃｅ＾３＋发射蓝紫光,Ｔｂ＾３＋发射有特征的绿光,在Ｃｅ＾３＋和Ｔｂ＾３＋共掺杂的体系中,可观察到Ｃｅ＾３＋强烈敏化Ｔｂ＾３＋发光的现象。分析表明,Ｃｅ＾３＋和Ｔｂ＾３＋之间存在辐射能量传递稿铲无辐射能量传递。     

Preparation and Characterization of Novel Luminescent Sol-Gel Films Containing a RE3+ Carboxylic Acid Complex

RE³⁺ (Eu³⁺, Tb³⁺) complexes with carboxylic acid (salicylic acid and benzoic acid) were introduced into the sol, which was prepared by the hydrolysis of tetraethoxysilane (TEOS). A sol-gel luminescent thin film (SG-LTF) was then prepared by dispersing the sol onto a silica substrate by a spin coating method. Multi-layer luminescent thin films were prepared by repeating the same process. The luminescent spectra, fluorescence lifetime and thermal stability of the SG-LTFs were investigated. For the reason of comparison polyvinylbutyral (PVB) was added into a N,N-dimethylformamide (DMF) solution in which the comparative RE³⁺ carboxylic acid complexes were previously dissolved to form the DMF/PVB solution and the PVB luminescent thin film (PVB-LTF) was prepared. The results show that a broad excitation band indicates the formation of RE complexes in the solid SG-LTFs. RE ions, which are restrained in the silica matrix, present longer lifetimes and higher thermal stability than that in the PVB-LTF containing the corresponding pure complexes. The different doping concentration of RE (III) complexes in the SG-LTFs and the different change of the emission intensities with the heat treatment temperature in the sol-gel thin film and the sol-gel bulk gel were also discussed in this paper.     

绿色荧光粉Ba2-xB2O5:xTb3+的制备及发光性能研究

采用高温固相法合成了Ba2-xB2O5:xTb3+绿色荧光粉。XRD图谱表明合成物质为纯相的Ba2B2O5晶体。该样品在256 nm(4f8→4f75d1)处有最强激发;有4个发射峰,分别位于489 nm(5D4→7F6),545 nm(5D4→7F5),585 nm(5D4→7F4)和622 nm(5D4→7F3);其中在545 nm处有最强发射。随着Tb3+掺杂浓度的不同,激发峰与发射峰的强度先增大后减小,当x=0.7时最佳。研究了电荷补偿剂Na+对发光性能的影响,样品的发射光谱强度随Na+掺杂浓度的增大而增大,当掺杂浓度达到或超过Tb3+浓度后发射光谱强度下降。     

TiO2-SiO2溶胶体系中Eu3+荧光性质的研究

溶胶-凝胶法制备了掺稀土Eu3 的TiO2-SiO2杂化体系,发现随着Ti/Si摩尔比的增加,Eu3 特征发射峰的强度增强,荧光寿命延长,表明TiO2的加入能够有效降低Eu3 的团聚;同时,Eu3 发射光谱中5D0→7F2与5D0→7F1的荧光强度比值R也随着TiO2浓度的增加而增大,显示了Eu3 -O2--Ti4 键的形成。研究了Eu3 掺杂浓度的改变对Eu3 荧光强度和R值的影响。     

Fe3O4@YF3:Eu3+双功能复合颗粒的制备与性能研究

采用直接沉淀法合成了Fe3 O4@ YF3:Eu3核壳结构磁性-荧光性双功能纳米复合颗粒,对其结构和性能进行了表征.XRD分析表明,得到了结晶良好的尖晶石型Fe3 O4纳米晶和正交相的YF3纳米晶.TEM照片表明,双功能复合颗粒具有明显的核壳结构.构成核的Fe3 O4纳米颗粒尺寸在40 ～80nm之间.Fe3 O4@ YF3:Eu3+核壳结构复合纳米颗粒的尺寸约为100 ～250 nm,壳层YF3:Eu3+厚度介于20 ～30 nm之间.EDS分析表明样品由Y,F,Eu,O和Fe元素组成.荧光光谱和磁性测试结果表明,复合颗粒同时具有良好的发光性和较强的磁性,使其在生物医学领域具有潜在的应用.     

Preparation and Luminescence Properties of the Ternary Europium Complex Incorporated into an Inorganic/Polymer Matrix by a Sol-Gel Method

Ternary europium complexes with thenoyltrifluoroacetone (TTA) and phenanthroline (phen) were incorporated into SiO₂/polymer matrix by a sol-gel method. The gels exhibit the characteristic emission bands of europium ion. In addition, Eu³⁺ presents a longer fluorescence lifetime in gel than in the corresponding pure complex powder. Concentration effects on the luminescence intensity were investigated. The reasons that are responsible for above results are also discussed in the context.     

SrMgB6O11:Eu3+纳米材料的水热法制备及发光性能研究

采用水热法制备了Eu3+掺杂SrMgB6O11纳米发光材料.利用X射线粉末衍射仪(XRD)、场发射扫描电子显微镜(FESEM)和荧光光谱对SrMgB6O11:Eu3+样品进行表征.结果表明:采用水热法可以成功地合成粒度均匀、结晶完好的SrMgB6O11:Eu3+纳米发光粉.深入研究了反应温度和pH值对SrMgB6O11:Eu3+纳米材料的晶体结构及形貌的影响.结果表明,在120℃时形成了尖锐且强度最强的衍射峰,同时FESEM也表明此时所得材料为纳米棒组成的规则扇形形貌,此后随着温度的升高,XRD图中衍射峰的位置和强度发生变化,说明荧光粉的晶体结构发生变化,FESEM也表明该荧光粉已变为球形颗粒.归属了发射光谱和激发光谱中各激发峰所对应的能级跃迁.荧光光谱也显示:反应温度和pH值影响着Eu3+在晶格中的对称性,且反应温度为120℃及pH值为9时,Eu3+在晶格中的对称性较好.另外,还初步探讨了纳米粒子的生长机制.