钙钛矿锰氧化物(La_(1-x)Eu_x)_(4/3)Sr_(5/3)Mn_2O_7(x=0,0.15)的磁性和电性研究

通过传统固相反应法制备了钙钛矿锰氧化物(La1-xEux)4/3Sr5/3Mn2O7(x=0,0.15)多晶样品,并且对其磁性和电性进行了研究.磁性测量表明:随着温度的降低,样品经历了一个复杂的转变过程,在温度为T*时经历二维短程铁磁有序转变,在温度为TC时进入三维长程铁磁态.随着Eu的掺杂,T*和TC减小,并且样品(La0.85Eu0.15)4/3Sr5/3Mn2O7在低温区表现出自旋玻璃行为.电性质测量表明:在母体La4/3Sr5/3Mn2O7中La位掺杂Eu后电阻率明显变大,金属绝缘转变温度TMI降低,磁电阻峰值增大.这些影响归因于较小的Eu3+离子替代La3+离子导致平均离子半径减小,晶格发生畸变.此外,较小的Eu3+离子优先占据层间岩盐层的R-site,使La3+,Sr3+,Eu3+离子在(La0.85Eu0.15)4/3Sr5/3Mn2O7中的分布更加有序,所以x=0.15的样品的ρ-T曲线只有一个峰.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

Preparation and superconductivity of the co-doped superconductor Nd2−x−yCayCexCuO4 with T′ structure

The preparation and superconductivity of the co-doped superconductor Nd_2−x−yCa_yCe_xCuO₄ with T′ structure were studied by XRD and superconductivity measurements. The results indicate that the effect of the co-doping of Ca²⁺ and Ce⁴⁺ on T_O and the carrier type is not significant, but the effect on the range of the superconducting compositions in this system is obvious. The study of co-doped superconductors could be important for an understanding of the effect of co-doping on the carrier concentration and to explore new superconductors.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part I: F-NMR investigation

A ¹⁹F-NMR investigation of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is undertaken as a function of temperature. Several F⁻ ion groups become progressively mobile at the NMR time scale at increasing temperature, the first, (F_i)_pb and (F_n)_pb, are located in the surroundings of Pb²⁺ cations, the second ones, (F_rd)_AI and (F_ra)_Al, in that of Al³⁺ cations. Four types of fluoride ions are distinguished in the ¹⁹F-NMR spectra of rigid lattice at low temperature (T = 175 K) and the distribution of fluoride ions among the four sites is determined by deconvolution of the spectra registered. The sites occupied by the (F_n)_pb anions are identified with the normal anionic sites of the fluorite network, the others with different interstitial sites.     

Effect of Pr and Ca substitution on superconductivity in Y(1−x−yPrxCay)Ba2Cu3O7−δ

Pr substituted at constant Ca concentration for Y in (Y_1−x−yPr_xCa_y)Ba₂Cu₃O_7−δ superconductors have been prepared under identical conditions and the temperature dependence of the electrical resistivity of these samples are measured. The resistively determined values of T_c decrease linearly with increasing x (0 ≤ x ≤ 0.2) for constant y = 0.10 and 0.15 which provides convincing evidence that the suppression of superconductivity by Pr is mainly due to magnetic pair breaking. The suppression of superconductivity can also be correlated to the observed changes in oxygen content determined by iodometric analysis and to the average Cu-valences. However, it is found that the observed suppression of T_c cannot be compensated by appropriate hole doping with Ca.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

A new interpretation of the CO state in half-doped manganites: new results from neutron diffraction and synchrotron radiation experiments

In the R_1−xD_xMnO₃ (x0.5) manganites, the structural phase transition at T_CO is commonly interpreted as a concomitant charge and orbital ordering (CO/OO) process driven by a co-operative Jahn–Teller effect and Coulomb repulsion forces. The low-temperature phase is supposed to contain well-separated and ordered Mn³⁺ and Mn⁴⁺ ionic species in an NaCl-like pattern. Structure refinement, from a neutron diffraction experiment below T_CO on a Pr_0.6Ca_0.4MnO₃ single crystal, gives us a model for the displacement of atoms with respect to the high-temperature phase that invalidates the standard model based in the CO/OO picture. Our result is a non-centrosymmetric crystal structure with two non-equivalent MnO₆ octahedra, both being slightly elongated but displaying very similar average Mn–O distances (1.96 and 1.95 Å, respectively) and having off-centered Mn atoms. We argue that this is a proof of the absence of charge ordering in half-doped manganites in the sense of formation of separated Mn³⁺ and Mn⁴⁺ ionic species. A new qualitative interpretation of the CE-type spin ordering (SO) is proposed. The so-called CO transition is, in fact, a structural transition induced by the change in the mean free path of electrons that continue to be thermally activated below T_CO by forming ferromagnetic Mn–Mn pairs stabilized by a local double-exchange process. The CE SO pattern results from the ordering of these pairs formed at T_CO. High-resolution synchrotron powder diffraction shows a complex anisotropic/asymmetric strains appearing at the transition that can be phenomenologically fitted by additional phases. Complementary electron diffraction and microscopy have shown no trace of macroscopic phase separation.     

Non-Fermi liquid regimes in U1−xMxPd2Al3(M=Y,Th)

The temperature-composition (T–x) phase diagram and NFL characteristics in the electrical resistivity ρ(T), specific heat C(T), and magnetic susceptibility χ(T) at low temperatures for the systems U_1−xM_xPd₂Al₃ (M=Y,Th) are described. The T–x phase diagram, the NFL characteristics, and the underlying mechanism for the NFL behavior are distinctly different for M=Y³⁺ and Th⁴⁺, apparently reflecting the difference in valence of the M atom substituents, and suggesting that U is tetravalent in these two systems.     

Ramans study of Y1−xPrxBa2Cu3O7−δ and YB2Cu3−xZnxO7−δ single crystals

Single crystals with known T_c values of Y_1−xPr_xBa₂Cu₃O_7−δ (Y---Pr1:2:3) and YBa₂Cu_3−xZn_3−xZn_xO_7−δ (Y---Zn1:2:3) systems are studied by Raman measurements. The Raman spectra for (Y---Pr1:2:3) single crystals show that the frequencies of Ba and O_z modes increase as the Pr content increases. The results are consistent with the hole-localization scheme proposed for the suppression of superconductivity in the polycrystalline Y---Pr1:2:3 systems. On the other hand, in the Y---Zn1:2:3 system, all the Raman modes do not change in frequencies. However, the FWHM of the Cu(2) mode increases with the decrease of T_c, indicating strong scattering of charge carriers by the substituted Zn ions in the CuO₂ planes. The induced disorder in the CuO₂ planes may be related with suppression of T_c in the Y---Zn1:2:3 system. Thus, the suppression mechanism in the Y---Zn1:2:3 systems seems to be different from that in the Y---Pr1:2:3 systems.     

Anomalous magnetotransport phenomena in θ-(BEDT-TTF)2I3

Anomalous magnetotransport phenomena have been observed in θ-(BEDT-TTF)₂I₃ crystals at temperatures below 15 K. The magnetoresistance M : (1) is a linear function of the magnetic field H, (2) is not affected by the angle between the electric current and the magnetic field, (3) but depends on the magnetic field orientation with respect to the crystal axis. Magnetoresistance is expressed as M = (aH²_a + bH²_b + cH²_c)₀^-3/2/H in terms of H = (H_a, H_b, H_c), the zero field resistivity ₀, and parameters a, b, and c which are independent of temperature and magnetic field. We have found that b a > c. Magnetoresistance up to 40 is observed for H = 7T along the b-axis at T = 1.5K.     

Tuning the multiferroic properties of Pb(Fe1/2Nb1/2)O3 by cationic substitution

A series of substituted lead iron niobate compounds with the general formula Pb²⁺_(1−x)A^Z_x(Fe_{{(1−(2−Z)x)/2}}Nb_{{(1+(2−Z)x)/2}})O₃ (0<x<0.6 and A=La³⁺, K⁺ or Sr²⁺) were prepared by a modified solid-state synthesis. The relative concentrations of Fe³⁺ and Nb⁵⁺ were adjusted to compensate the charge imbalance due to the aliovalent substitution. The dielectric constant and magnetic susceptibilities were studied as a function of temperature. The temperature of the dielectric maximum, T_M, of the substituted compounds decreased linearly with increasing concentration of the substituent ions. The magnetic measurements showed an antiferromagnetic transition at temperatures T_N1 due to the superexchange interactions mediated by Fe–O–Fe and an additional antiferromagnetic-type transition at T_N2. T_N1 linearly increased with the increasing concentration of Fe³⁺ ion at the B-site of ABO₃-type substituted compounds. T_M is shown to be directly dependent on the concentration of the ferroactive Nb⁵⁺ ions at the B-site and Pb²⁺ ions at the A-site.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Dy,Co共掺杂对BiFeO3陶瓷磁特性和磁相变温度Tc的影响

采用快速液相烧结法制备BiFeO₃和Bi_0.95Dy_0.05Fe_1-xCo_xO₃ (x=0, 0.05, 0.1, 0.15)陶瓷样品. 实验结果表明: 所有样品的主衍射峰与纯相BiFeO₃相符合且具有良好的晶体结构, 随着Co³⁺掺杂量的增大, Bi_0.95Dy_0.05Fe_1-xCo_xO₃样品的主 衍射峰由双峰(104)与(110)逐渐重叠为单峰(110), 当掺杂量x>0.05时, 样品呈现正方晶系结构; SEM形貌分析可知: Dy³⁺, Co³⁺共掺杂使BiFeO₃晶粒尺度由原来的3—5 μ减小到约1 μ. 室温下, BiFeO₃样品表现出较弱的铁磁性, 随着Dy³⁺和Co³⁺掺杂, BiFeO₃样品的铁磁性显著提高. 在外加磁场为30 kOe的作用下, Bi_0.95Dy_0.05Fe_1-xCo_xO₃ (x=0.05, 0.1, 0.15)的M_r分别为0.43, 0.489, 0.973 emu/g; M_S分别为0.77, 1.65, 3.08 emu/g. BiFeO₃和Bi_0.95Dy_0.05Fe_1-xCo_xO₃样品磁矩M随着温度T的升高而逐渐减小, Dy掺杂使BiFeO₃样品的T_N由644 K升高到648 K, 而T_C基本没有变化. Dy和Co共掺杂导致BiFeO₃样品磁相变温度T_C由870 K降低到780 K, 其T_C变化主要取决于Fe-O-Fe反铁磁超交换作用的强弱和磁结构的相对稳定性. 关键词： 铁磁电材料 磁滞回线 磁相变温度     

Ising spin glass on a D = 3 hierarchical lattice: Effects of tailed coupling distributions

Within a real-space renormalization-group framework, we approach the cubic lattice through a D = 3 diamond-like hierarchical lattice. The model is a standard, nearest-neighbor, Ising spin glass with coupling constants {J_ij} distributed according to the family of continuous probability distributions P_q(J_ij) ∝ 1/[1 + (q − 1)J_ij²/2J²]^{1/(q − 1)} (if 1 + (q − 1) J_ij²/2J² > 0, and zero otherwise; q ). Such distributions, which arise naturally in the treatment, within the recently proposed nonextensive thermostatistics, of anomalous diffusion, reproduce the usual, Gaussian case, for q → 1. Moreover, they present a second moment J_ij² proportional to (5 − 3q)⁻¹ for q < 5/3, diverging for q ≥ 5/3, but keeping a finite width at midheight. In the limit q → 3, P_q(J_ij) collapses with the abscissa, and so the width at midheight diverges. We compute the q-dependence of the spin-glass critical temperature T_c. We show numerically that T_c does not scale with J_ij^21/2 (contrary to the usual belief), but rather with the width at midheight of P_q(J_ij). Our results suggest that T_c vanishes as −1/q when q → −∞; furthermore, we verified that T_c diverges exponentially when q approaches 3 from below.     

Influence of the Tl- and Hg-content on magnetic and transport properties of the Pb, Sr-doped Tl-1223 and Hg-1223 superconductors

The effects of the thallium and mercury content x on the as-sintered and post annealed samples of M_xPb_0.4Sr_1.6Ba_0.4Ca₂Cu₃O_8+δ {M: Tl (0.32≤x≤0.74) or Hg (0.18≤x≤0.68)} have been studied by magnetization and transport measurements. For Tl-1223 we have found the optimum Tl doping level to be x=0.53 regarding the grain properties, the content of superconducting phase, the first penetration field H_pl^wl, the transport (J_c^tr), magnetic intergrain (J_c^M) and intragrain (J_c^g) critical current densities. The critical temperature T_c of the as-sintered Tl-1223 sample decreased with increasing Tl content. Post-annealing in oxygen improved the T_c for Tl contents of x≥0.53 and had generally positive effects on the critical current densities. The intergrain properties of the Hg-1223 samples were much worse than those of the Tl-based superconductors.     

Study of superconducting state parameters of alkali–alkali binary alloys by a pseudopotential

A detailed study of the superconducting state parameters (SSP) viz. electron–phonon coupling strength λ, Coulomb pseudopotential μ^*, transition temperature T_C, isotope effect exponent and effective interaction strength N_OV of ten alkali–alkali binary alloys i.e. Li_1−xNa_x, Li_1−xK_x, Li_1−xRb_x, Li_1−xCs_x, Na_1−xK_x, Na_1−xRb_x, Na_1−xCs_x, K_1−xRb_x, K_1−xCs_x and Rb_1−xCs_x are made within the framework of the model potential formalism and employing the pseudo-alloy-atom (PAA) model for the first time. We use the Ashcroft’s empty core (EMC) model potential for evaluating the superconducting properties of alkali alloys. Five different forms of local field correction functions viz. Hartree (H), Taylor (T), Ichimaru–Utsumi (IU), Farid et al. (F) and Sarkar et al. (S) are used to incorporate the exchange and correlation effects. A considerable influence of various exchange and correlation functions on λ and μ^* is found from the present study. Reasonable agreement with the theoretical values of the SSP of pure components is found (corresponding to the concentration x = 0 or 1). It is also concluded that nature of the SSP strongly depends on the value of the atomic volume Ω₀ of alkali–alkali binary alloys.     

Superconductivity and crystallographic properties of La2 − xMxCuO4 − δ (M = Na, K)

Superconductivity and crystallographic properties of La_{2 − x}M_xCuO_{4 − δ} (M = Na, K) are studied. In the La_{2 − x}M_xCuO_{4 − δ} system, superconductivity is detected for x 0.2. Oxygen content analysis shows that the system has more oxygen vacancies than the La_{2 − x}Sr_xCuO_{4 − δ} system. These oxygen vacancies may reduce the hole concentration, and high Na-doping is needed to produce superconductivity. In the La_{2 − x}K_xCuO_{4 − δ} system, superconductivity is observed for the first time. Resistivity and magnetic susceptibility measurements show that T_c(onset) is 40 K and the Meissner volume fraction is about 4% for x = 0.7. The system changes from orthorhombic to a tetragonal K₂NiF₄ structure at x ≈ 0.3 and only tetragonal samples show superconductivity.     

Effect of Hg addition on synthesis of Bi-based superconductors

We have investigated the effect of Hg addition on the superconducting properties of BiSrCaCuO system. Polycrystalline samples with nominal composition Bi₂Sr_2−xHg_xCa₁Cu₂O_y and Bi₂Sr_2−xHg_xCa₂Cu₃O_y (x=0.3) were synthesized and used to investigate the phase evolution by XRD, superconducting behaviour by R–T measurement and the structural grain boundary effects by SEM. From these measurements, it has been noticed that the phases obtained with both types of compositions are the same as Bi2212 but the T_c values are different. With additional annealing, T_{c zero} values were raised from 60 to 72 K in Bi₂Sr_2−xHg_xCa₁Cu₂O_y and 64 to 92 K in Bi₂Sr_2−xHg_xCa₂Cu₃O_y. Also, an improved grain boundary linkage has been observed by SEM for the 92 K sample.     

CoFe2O4纳米颗粒的结构、磁性以及离子迁移

聚乙烯醇(PVA)溶胶凝胶法制备出CoFe₂O₄纳米微粉，用X射线衍射研究了铁氧体纳米颗粒的结构.测量了CoFe₂O₄纳米颗粒80—873 K的变温穆斯堡尔谱，发现纳米颗粒的磁转变温度范围为793—813 K，比块体材料的磁性转变温度要低.CoFe₂O₄纳米颗粒的德拜温度θ_A=674 K，θ_B=243 K，比块体材料要小.CoFe₂O₄纳米颗粒超精细场H_f随温度的变化符合T^3/2+T^5/2定理.当温度较高时，平均同质异能移IS随温度的升高而减小，并呈线性关系. 关键词： 纳米颗粒 磁性 穆斯堡尔谱