Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Solubility of (UO2)3(PO4)2?4H2O in H+-Na+-OH?-H2PO?4-HPO2?4-PO3?4-H2O and Its Comparison to the Analogous PuO2 +2 System

The objectives of this study were to address uncertainties in the solubility product of (UO₂)₃(PO₄)₂⋅4H₂O(c) and in the phosphate complexes of U(VI), and more importantly to develop needed thermodynamic data for the Pu(VI)-phosphate system in order to ascertain the extent to which U(VI) and Pu(VI) behave in an analogous fashion. Thus studies were conducted on (UO₂)₃(PO₄)₂⋅4H₂O(c) and (PuO₂)₃(PO₄)₂⋅4H₂O(am) solubilities for long-equilibration periods (up to 870 days) in a wide range of pH values (2.5 to 10.5) at fixed phosphate concentrations of 0.001 and 0.01 M, and in a range of phosphate concentrations (0.0001–1.0 M) at fixed pH values of about 3.5. A combination of techniques (XRD, DTA/TG, XAS, and thermodynamic analyses) was used to characterize the reaction products. The U(VI)-phosphate data for the most part agree closely with thermodynamic data presented in Guillaumont et al.,⁽¹⁾ although we cannot verify the existence of several U(VI) hydrolyses and phosphate species and we find the reported value for formation constant of UO₂PO⁻₄ is in error by more than two orders of magnitude. A comprehensive thermodynamic model for (PuO₂)₃(PO₄)₂⋅4H₂O(am) solubility in the H⁺-Na⁺-OH⁻-Cl⁻-H₂PO⁻₄-HPO²⁻₄-PO³⁻₄-H₂O system, previously unavailable, is presented and the data shows that the U(VI)-phosphate system is an excellent analog for the Pu(VI)-phosphate system.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

La2Ti6O15-CeTi21O38-PbTiO3 ceramics formed in gaseous penetration of La-Ce into PbTiO3 and their electric properties

The gaseous penetration of La-Ce into PbTiO₃ ceramics is reported. The compounds of La₂Ti₆O₁₅ and CeTi₂₁O₃₈ are formed and the new La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics are prepared by the penetration of La and Ce in the gaseous state. The new ceramic materials have a significant change in electric properties. The room temperature resistivity decreases from 2.0×10¹⁰ to 0.248 Ω. m, and the grain resistance exhibits an obvious PTCR effect with the change of temperature. However, the grain boundary resistance decreases rapidly with increase in temperature. The change rule of the total resistance is similar to that of the grain boundary, and the PTCR effect disappears and the tendency of transition to a conductive body is manifest. The XPS analysis suggests that the particles that are Pb, Ti, La and Ce in La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics all change their valence and lead to decreasing resistivity, and the bound energy peak values of elements in La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics are also reported. The La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃ ceramics have a better thermal stability in high temperatures through TG-DTA analysis.     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, R[F²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, R[F²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks [O-Hg-Hg-O] for the mercurous compound, and [O-Hg-Hg-O] and [O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.     

Investigation on double perovskite Ba4Ca2Ta2O11

The structure, conductivity and water uptake of the oxygen-deficient perovskite-type compound Ba₄Ca₂Ta₂O₁₁ have been investigated. Ba₄Ca₂Ta₂O₁₁ crystallizes in the cryolite structure (cubic, Fm3m SG) with a = 8.4508(2) Å, under dry air. The compound can be partially hydrated up to a maximum water content of approximately 0.52 mol H₂O per mol Ba₄Ca₂Ta₂O₁₁. In moist air, the structure symmetry becomes monoclinic (C2/m) and the temperature dependence of total conductivity shows a different behavior because of changes in transport mechanism. Three regions can be observed as a function of temperature. For the low temperature range 200–400 °C, the protonic conduction is prevailing with an activation energy E_A = 0.85 eV. In the intermediate temperature range (400–600 °C), O²⁻ anionic and protonic conductions are mixed with an activation energy E_A = 0.45 eV and in the third region, for temperatures above 600 °C, O²⁻conduction is prevailing with an activation energy E_A = 0.85 eV.     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.     

Raman scattering investigations on lanthanum-doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

The ferroelectric ceramics of Bi₄Ti₃O₁₂, SrBi₄Ti₄O₁₅, and lanthanum-doped Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅ were synthesized, and their Raman spectra were investigated. La-doping resulted in the enlargement of remnant polarization of Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The structure of the Bi₂O₂ layers and TiO₆ octahedra of the intergrowth was found to be different from those of Bi₄Ti₃O₁₂ and SrBi₄Ti₄O₁₅. La³⁺ ions exhibit pronounced selectivity for the occupation of A site as La content is lower than 0.50, and tend to be incorporated into Bi₂O₂ layers when the La content is higher than 0.50. Lanthanum substitution brings about the structural phase transition in Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The variation of ferroelectric property may be attributed to combined contribution from the decreasing of the oxygen vacancies, the relaxation of the lattice distortion, the destroying of the insulation and the space charge compensation effects of the Bi₂O₂ slabs.     

Energetics of copper diphosphates – Cu2P2O7 and Cu3(P2O6OH)2

Differential scanning calorimetry and high temperature oxide melt solution calorimetry are used to study enthalpy of phase transition and enthalpies of formation of Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂. α-Cu₂P₂O₇ is reversibly transformed to β-Cu₂P₂O₇ at 338–363 K with an enthalpy of phase transition of 0.15 ± 0.03 kJ mol⁻¹. Enthalpies of formation from oxides of α-Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂ are −279.0 ± 1.4 kJ mol⁻¹ and −538.8 ± 2.7 kJ mol⁻¹, and their standard enthalpies of formation (enthalpy of formation from elements) are −2096.1 ± 4.3 kJ mol⁻¹ and −4302.7 ± 6.7 kJ mol⁻¹, respectively. The presence of hydrogen in diphosphate groups changes the geometry of Cu(II) and decreases acid–base interaction between oxide components in Cu₃(P₂O₆OH)₂, thus decreasing its thermodynamic stability.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Crystal-chemistry of mullite-type aluminoborates Al18B4O33 and Al5BO9: A stoichiometry puzzle

Orthorhombic Al₂O₃-rich aluminoborate is an important ceramic material for which two slightly different compositions have been assumed: Al₅BO₉ (5Al₂O₃:B₂O₃) and Al₁₈B₄O₃₃ (9Al₂O₃:2B₂O₃). The formula Al₁₈B₄O₃₃ (=Al_4.91B_1.09O₉) was derived from results of chemical analyses when crystal structure data were not yet available. Subsequent structural investigations indicated Al₅BO₉ composition. Nevertheless, Al₁₈B₄O₃₃ was still accepted as the correct stoichiometry assuming that additional B replaces 9% Al.Powder samples of both compositions and ones with excess boron were prepared by solid state reactions between α-Al₂O₃ and B₂O₃/H₃BO₃ at temperatures above 1100 °C and single-crystals were grown from flux at 1100 and 1550 °C. Products were investigated by single-crystal and powder XRD, ¹¹B and ²⁷Al solid-state MAS-NMR, Raman and FTIR spectroscopy as well as Laser-ablation ICP-MS. No indication of the predicted 9% B→Al substitution was found. LA ICP-MS indicated 12.36(27) wt% B₂O₃ corresponding to Al_4.97B_1.03O₉. Hence, the suggested Al₁₈B₄O₃₃ stoichiometry can be excluded for all synthesized samples. A very low amount of Al vacancies at a five-fold coordinated site are likely, charge balanced by an additional nearby three-fold coordinated B site. All evidences indicate that the title compound should be reported as Al_5−xB_1+xO₉ with x<0.038(6), which is close to Al₅BO₉.     

Synthesis and structural study of a new NASICON-type solid solution: Li1−xLax/3Zr2(PO4)3

A new complete solid solution of NASICON-type compounds between LiZr₂(PO₄)₃ and La_1/3Zr₂(PO₄)₃ was evidenced with the general formula Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1). These phases were synthesized by a complex polymerizable method and structurally characterized from Rietveld treatment of their X-ray and neutron powder diffraction data. This solid solution results from the substitution mechanism Li⁺→1/3La³⁺+2/3□ leading to an increase of the vacancies number correlated to an increase of the La content. According to this substitution mechanism, the general formula can then be written Li_1−xLa_x/3□_2x/3Zr₂(PO₄)₃ (0?x?1) in order to underline the correlation between the La content and the vacancies rate. For all the compounds, the structure is clearly related to that of the NASICON family with three crystallographic domains evidenced. For 0?x?0.5, all the members adopt at high temperature the typical NASICON-type structure (s.g. R3¯c), while at lower temperature, their structure distorts to a triclinic form (s.g. C 1¯), as observed for LiZr₂(PO₄)₃ prepared above 1100 °C. Moreover, in this domain, the reversible transition is clearly soft and the transition temperature strongly depends of the x value. For 0.6?x?0.9, the compounds crystallize in a rhombohedral cell (s.g. R3¯), while for x=1, the phase La_1/3Zr₂(PO₄)₃ is obtained (s.g. P3¯, Z=6, a=8.7378(2) Å, c=23.2156(7) Å).This paper is devoted to the structure analysis of the series Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1), from X-ray and neutron powder thermo diffraction and transmission electron microscopy (TEM) studies.     

XRD and Si MAS-NMR spectroscopy across the β-Lu2Si2O7-β-Y2Si2O7 solid solution

Samples in the system Lu_2−xY_xSi₂O₇ (0?x?2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu₂Si₂O₇ and Y₂Si₂O₇. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y₂Si₂O₇ in β-Lu₂Si₂O₇ at 1300 °C. ²⁹Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the ²⁹Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict ²⁹Si chemical shifts in silicates is applied here to obtain the theoretical variation in ²⁹Si chemical shift values in the system Lu₂Si₂O₇-Y₂Si₂O₇ and the results compare favorably with the values obtained experimentally.     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

Direct dynamics studies for the reactions of CF3CHFCF3 and CF3CF2CHF2 with H atoms

The rate constants of the hydrogen abstraction reactions of CF₃CHFCF₃ + H (R1) and CF₃CF₂CHF₂ + H (R2) have been calculated by means of the dual-level direct dynamics method. Optimized geometries and frequencies of stationary points and extra points along the minimum-energy path (MEP) are obtained at the MPW1K/6-311+G(d,p) level, and the classical energetic information is further corrected with the interpolated single-point energy (ISPE) approach by the G3(MP2) level of theory. Using the canonical variational transition state theory (CVT) with small-curvature tunneling corrections (SCT), the rate constants are evaluated over a wide temperature range of 200-2000 K. The calculated CVT/SCT rate constants are in good agreement with available experimental values. It is found that the variational effect is very small and almost negligible over the whole temperature region. However, the small-curvature tunneling correction plays an important role in the lower temperature range. Furthermore, the heats of formation of species CF₃CF₂CHF₂ (SC₁ or SC₂) and CF₃CF₂CF₂ are studied using isodesmic reactions to further elucidate the thermodynamic properties.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.