Effect of interface layer on growth behavior of atomic-layer-deposited Ir thin film as novel Cu diffusion barrier

Growth and nucleation behavior of Ir films grown by atomic layer deposition (ALD) on different interfacial layers such as SiO₂, surface-treated TaN, and 3-nm-thick TaN were investigated. To grow Ir thin film by ALD, (1,5-cyclooctadiene) (ethylcyclopentadienyl) iridium (Ir(EtCp)(COD)) and oxygen were employed as the metalorganic precursor and reactant, respectively. To obtain optimal deposition conditions, the deposition temperature was varied from 240 to 420 °C and the number of deposition cycles was changed from 150 to 300. The Ir film grown on the 3-nm-thick TaN surface showed the smoothest and most uniform layer for all the deposition cycles, whereas poor nucleation and three-dimensional island-type growth of the Ir layer were observed on Si, SiO₂, and surface-treated TaN after fewer number of deposition cycles. The uniformity of the Ir film layer was maintained for all the different substrates up to 300 deposition cycles. Therefore we suggest that the growth behavior of the Ir layer on different interface layer is related to the chemical bonding pattern of the substrate film or interface layer, resulting in better understand the growth mechanism of Ir layer as a copper diffusion barrier. The ALD-grown Ir films show the preferential direction of (1 1 1) for all the reflections, which indicates the absence of IrO₂ in metallic Ir.     

Off-axis pulsed laser deposition system for epitaxial oxide growth on substrates up to 2 inches in diameter

A novel off-axis pulsed-laser deposition (PLD) system for ferroelectric oxide thin films has been developed. The substrates are mounted "upside-down" and are rotating. The maximum substrate size is 2 inches in diameter. The optical and structural properties of the grown BaTiO₃ films are compared to the films produced by an on-axis PLD system. The stoichiometry and thickness were checked with Rutherford backscattering spectrometry (RBS). The crystalline quality and orientation were investigated with X-ray diffraction (XRD) and Rutherford backscattering spectrometry in channeling configuration (RBS/C). Using atomic force microscopy, the rms surface roughness was measured. The BaTiO₃ films grown on MgO form a planar optical waveguide. The optical losses and the refractive indices of these waveguides were determined with a prism coupling setup. Films grown on 10᎒ mm² MgO (100) substrates in on-axis geometry show optical waveguide losses less than 3 dB/cm.     

Room-Temperature Ferromagnetism in Zn1-xMnxO Thin Films Deposited by Pulsed Laser Deposition

Zn1-xMnxO （x = O.Olq3.1） thin films with a Curie temperature above 300K are deposited on Al2O3 （0001） substrates by pulsed laser deposition. X-ray diffraction （XRD）, ultraviolet （UV）-visible transmission and Raman spectroscopy are employed to characterize the microstructural properties of these films. Room temperature ferromagnetism is observed by superconducting quantum interference device （SQUID）. The results indicate that Mn doping introduces the incorporation of Mn^2＋ ions into the ZnO host matrix and the insertion of Mn^2＋ ions increases the lattice defects, which is correlated with the ferromagnetism of the obtained films. The doping concentration is also proven to be a crucial factor for obtaining highly ferromagnetic Zn1-xMnxO films.     

Epitaxial Properties of Co-Doped ZnO Thin Films Grown by Plasma Assisted Molecular Beam Epitaxy

High quality Co-doped ZnO thin films are grown on single crystalline Al2O3（0001） and ZnO（0001） substrates by oxygen plasma assisted molecular beam epitaxy at a relatively lower substrate temperature of 450℃. The epitaxial conditions are examined with in-situ reflection high energy electron diffraction （RHEED） and ex-situ high resolution x-ray diffraction （HRXRD）. The epitaxial thin films are single crystal at film thickness smaller than 500nm and nominal concentration of Co dopant up to 20%. It is indicated that the Co cation is incorporated into the ZnO matrix as Co^2＋ substituting Zn^2＋ ions. Atomic force microscopy shows smooth surfaces with rms roughness of 1.9 nm. Room-temperature magnetization measurements reveal that the Co-doped ZnO thin films are ferromagnetic with Curie temperatures Tc above room temperature.     

Effects of Helium and Oxygen Common Implantation in Silicon Wafer

Defect engineering for SiO2 precipitation is investigated using He-ion implantation as the first stage of separation by implanted oxygen （SIMOX）. Cavities axe created in Si by implantation with helium ions. After thermal annealing at different temperatures, the sample is implanted with 120 keV 8.0 ×1016 cm 2 0 ions. The Q ion energy is chosen such that the peak of the concentration distribution is centred at the cavity band. For comparison, another sample is implanted with O ions alone. Cross-sectionM transmission electron microscopy （XTEM）, Fourier transform infrared absorbance spectrometry （FTIR） and atomic force microscopy （AFM） measurements are used to investigate the samples. The results show that a narrow nano-cavity layer is found to be excellent nucleation sites that effectively assisted SiO2 formation and released crystal lattice strain associated with silicon oxidation.     

Room-Temperature Ferromagnetic ZnMnO Thin Films Synthesized by Plasma Enhanced Chemical Vapour Deposition Method

Room-temperature ferromagnetic Mn-doped ZnO films are grown on Si （001） substrates by plasma enhanced chemical vapour deposition （PECVD）. X-ray diffraction measurements reveal that the Znl-xMn.O films have the single-phase wurtzite structure. X-ray photoelectron spectroscopy indicates the existence of Mn^2＋ ions in Mndoped ZnO films. Furthermore, the decreasing additional Raman peak with increasing Mn-doping is considered to relate to the substitution of Mn ions for the Zn ions in ZnO lattice. Superconducting quantum interference device （SQUID） measurements demonstrate that Mn-doped ZnO films have ferromagnetic behaviour at room temperature.     

Multilayer Au/TiO2Composite Films with Ultrafast Third-Order Nonlinear Optical Properties

We report on the ultrafast third-order optical nonlinearity in multilayer Au/TiO2 composite films fabricated on quartz substrates by pulsed laser deposition technique. The linear optical properties of the films are determined and optical absorption peaks due to surface plasmon resonance of Au particles are observed at about 590hm. The third-order optical nonlinearities of the films are investigated by z-scan method using a femtosecond laser （50 fs） at the wavelength of 800 nm. The sample showed fast nonlinear optical responses with nonlinear absorption coefficient and nonlinear refractive index being -3.66 × 10^-10 m/W and -2.95 × 10^-17 m^2/W, respectively. The results also show that the nonlinear optical effects increase with the increasing Au concentration in the composite films.     

Growth and Characterization of InN Thin Films on Sapphire by MOCVD

Indium nitride thin films are grown on sapphire substrates by metal-organic chemical vapour deposition （MOCVD） By employing three-step layer buffers, the mirror-like layers on two-inch sapphire wafers have been obtained. The structural, optical and electrical characteristics of InN are investigated by x-ray diffraction, scanning electron microscopy, atomic force microscopy, photoluminescence and infrared optical absorption. The photoluminescence and the absorption studies of the materials reveal a marked energy bandgap structure around 0.70eV at room temperature. The room-temperature Hall mobility and carrier concentration of the film are typically 939 cm^2 /Vs, and 3.9 × 1018cm^-3, respectively.     

Structural and electrical properties of La0.5Sr0.5CoO3 films on SrTiO3 and porous a-Al2O3 substrates

Films of La_0.5Sr_0.5CoO₃ (LSCO) have been deposited on specially treated TiO₂-terminated (001) SrTiO₃ substrate surfaces and on macroporous polycrystalline !-Al₂O₃ substrates, having a mean pore diameter of 80 nm, by pulsed laser deposition. The films deposited on SrTiO₃ are good conducting, (001) textured, and exceptionally smooth (1-2 Å for 100 nm thick films). LSCO films deposited on porous !-Al₂O₃ are polycrystalline and exhibit good crystallographic and electrical properties despite the large substrate roughness and the differences in lattice parameters and crystal structure between the film and the substrate. Different growth modes have been observed on the porous !-Al₂O₃ substrates depending on the oxygen pressure during film deposition. Films grown at an oxygen pressure of 10^-1 mbar are macroporous, whereas films grown at 10^-2 mbar completely cover the substrate pores. In the latter case, strain effects lead to film cracking.     

Ruthenium oxide and strontium ruthenate electrodes for ferroelectric thin-films capacitors

Metallic ruthenium and ruthenium oxides, such as SrRuO₃ and RuO₂, are potential electrode materials for ferroelectric capacitors. The electrical properties (e.g. leakage currents) of such thin film devices are dependent on the electronic properties of the electrode/ferroelectric junctions and therefore also on the electrode work functions. During growth and processing of film-electrode layer structures the formation of sub-oxides within the electrode is possible, with their work functions being unknown. In order to obtain information for predicting device properties, we have systematically analysed the valence bands and work functions of RuO_x and SrRuO_y thin films with different oxidation states by using photoelectron spectroscopy techniques. The results suggest that Ru⁰ and Ru⁴⁺ ions are present in co-existence at the surfaces of oxygen-deficient polycrystalline films (inhomogeneous oxidation). For both oxygen-deficient materials the work function coincides with that of metallic ruthenium (4.6ǂ.1 eV). Only for fully oxidised ruthenium oxide and strontium ruthenate films (no Ru⁰ present at the surface) is the work function increased to 5.0 or 4.9 eV, respectively. As an example of importance for new dynamic random access memory applications, the junctions of Ba_1-xSr_xTiO₃ with SrRuO_y and RuO_x are discussed.     

Pulsed laser deposition of photosensitive a-Si thin films

Si films have been fabricated by pulsed KrF excimer laser deposition (PLD) through the use of various Si targets and deposition conditions. The deposits consisted of droplets and homogeneous films, which were assigned to be crystalline and amorphous silicon, respectively, by the micro Raman scattering measurements. Not only the crystalline but also the amorphous Si part scarcely (<1 atomic %) contained hydrogen regardless of whether or not the films are prepared in the presence of H₂ gas. Conditions were explored to reduce the droplet formation and to produce photosensitive films. Amorphous Si films with photosensitivity (C_ph/C_d) exceeding 10³ were obtained, and they exhibited high stability against light soaking. Thus, PLD is a promising method to fabricate photosensitive and photostable a-Si films.     

A laser-ablation system for deposition of high-temperature superconducting thin films for device applications

We present a compact-size laser-ablation system to produce high-temperature superconducting (HTS) YBa₂Cu₃O_7-' (YBCO) thin films for component applications. The system has been designed for deposition of multilayer structures on 5-cm-diameter substrates and for reliable operation with reduced need for maintenance. The performance of the system has been studied by depositing YBCO films on small LaAlO₃ substrates. The films have critical temperatures of 88-90 K and critical current densities of 0.9-4.5 MA/cm² as measured with an inductive technique.     

Microstructure and electrical properties of textured Sr0.51Ba0.48La0.01Nb2O6 thin films

Sr_0.51Ba_0.48La_0.01Nb₂O₆ (SBLN) thin films were prepared on platinized silicon substrates by pulsed laser deposition (PLD) combined with annealing technique. The preferred orientation, surface morphology, composition, and interfacial properties of the SBLN thin films were characterized by X-ray diffraction, atomic force microscopy, transmission electron microscopy, X-ray energy dispersive spectroscopy, and automatic spreading resistance measurement. The ferroelectric properties were confirmed by P - E hysteresis loops. The frequency variation of the dielectric constant was measured as well.     

Atomic Diffusion in Cu/Si （111） and Cu/SiO2/Si （111） Systems by Neutral Cluster Beam Deposition

The Cu films are deposited on two kinds of p-type Si （111） substrates by ionized duster beam （ICB） technique. The interface reaction and atomic diffusion of Cu/Si （111） and Cu/SiO2/Si （111） systems are studied at different annealing temperatures by x-ray diffraction （XRD） and Rutherford backscattering spectrometry （RBS）. Some significant results are obtained： For the Cu/Si （111） samples prepared by neutral dusters, the interdiffusion of Cu and Si atoms occurs when annealed at 230℃. The diffusion coefficients of the samples annealed at 230℃ and 500℃ are 8.5 ×10^-15 cm^2.s^-1 and 3.0 ×10^-14 cm^2.s^-1, respectively. The formation of the copper-silicide phase is observed by XRD, and its intensity becomes stronger with the increase of annealing temperature. For the Cu/SiO2//Si （111） samples prepared by neutral dusters, the interdiffusion of Cu and Si atoms occurs and copper silicides are formed when annealed at 450℃. The diffusion coefficients of Cu in Si are calculated to be 6.0 ×10^-16 cm^2.s^-1 at 450℃, due to the fact that the existence of the SiO2 layer suppresses the interdiffusion of Cu and Si.     

Electrical and optical properties of indium tin oxide thin films grown by pulsed laser deposition

Indium tin oxide (ITO) thin films (200-400 nm in thickness) have been grown by pulsed laser deposition (PLD) on glass substrates without a post-deposition anneal. The electrical and optical properties of these films have been investigated as a function of substrate temperature and oxygen partial pressure during deposition. Films were deposited at substrate temperatures ranging from room temperature to 300 °C in O₂ partial pressures ranging from 0.1 to 100 mTorr. For 300 nm thick ITO films grown at room temperature in oxygen pressure of 10 mTorr, the electrical conductivity was 2.6᎒^-3 Q^-1cm^-1 and the average optical transmittance was 83% in the visible range (400-700 nm). For 300 nm thick ITO films deposited at 300 °C in 10 mTorr of oxygen, the conductivity was 5.2᎒^-3 Q^-1cm^-1 and the average transmittance in the visible range was 87%. Atomic force microscopy (AFM) measurements showed that the RMS surface roughness for the ITO films grown at room temperature was ~7 Å, which is the lowest reported value for the ITO films grown by any film growth technique at room temperature.     

Growth of oriented Pb(ZrxTi1-x)O3 thin films on glass substrates by pulsed laser deposition

Oriented crystalline Pb(Zr_xTi_1-x)O₃ (x=0.53) (PZT) thin films were deposited on metallized glass substrates by pulsed laser deposition (1060-nm wavelength Nd:YAG laser light, 10-ns pulse duration, 10-Hz repetition rate, 0.35-J/pulse and 25-J/cm² laser fluence), from a commercial target at substrate temperatures in the range 380-400 °C. Thin films of 1-3 7m were grown on Au(111)/ Pt/NiCr/glass substrates with a rate of about 1 Å/pulse on an area of 1 cm². The deposited PZT films with perovskite structure were oriented along the (111) direction, as was revealed from X-ray diffraction spectra. Fourier transform infrared spectroscopy (FTIR) was performed on different PZT films so that their vibrational modes could be determined. Piezoelectric d₃₃ coefficients up to 30 pC/N were obtained on as-deposited films. Ferroelectric hysteresis loops at 100 Hz revealed a remanent polarization of 20 7C/cm² and a coercive field of 100 kV/cm.     

Structure Stability of LaAlO3 Thin Films on Si Substrates

A series of amorphous and single-crystalline LaAlO3 （LAO） thin films are fabricated by laser molecular-beam epitaxy technique on Si substrates under various conditions of deposition. The structure stability of the LAO films annealed in high temperature and various ambients is studied by x-ray diffraction as well as high-resolution transmission electron microscopy. The results show that the epitaxial LAO films have very good stability, and the structures of amorphous LAO thin films depend strongly on the conditions of deposition and post-annealing. The results reveal that the formation of LAO composition during the deposition is very important for the structure stability of LAO thin films.     

Surface Erosion of GaN Bombarded by Highly Charged 208Pbq+-Ions

Surface change of gallium nitride specimens after bombardment by highly charged Pbq^＋-ions （q = 25, 35） at room temperature is studied by means of atomic force microscopy. The experimental results reveal that the surface of GaN specimens is significantly etched and erased. An unambiguous step-up is observed. The erosion depth not only strongly depends on the charge state of ions, but also is related to the incident angle of Pbq^＋-ions and the ion dose. The erosion depth of the specimens in 60° incidence （tilted incidence） is significantly deeper than that of the normal incidence. The erosion behaviour of specimens has little dependence on the kinetic energy of ion （Ek = 360, 700 keV）. On the other hand, surface roughness of the irradiated area is obviously decreased due to erosion compared with the un-irradiated area. A fiat terrace is formed.     

Evolution of Structural Defects in SiOx Films Fabricated by Electron Cyclotron Resonance Plasma Chemical Vapour Deposition upon Annealing Treatment

We study the structural defects in the SiO, film prepared by electron cyclotron resonance plasma chemical vapour deposition and annealing recovery evolution. The photoluminescence property is observed in the as-deposited and annealed samples. [-SiO3]^2- defects are the luminescence centres of the ultraviolet photoluminescence （PL） from the Fourier transform infrared spectroscopy and PL measurements. [-SiO3]^2- is observed by positron annihilation spectroscopy, and this defect can make the S parameters increase. After 1000℃ annealing, [-SiO3]^2- defects still exist in the films.     

Flexible Cu（In,Ga）Se2 Thin-Film Solar Cells on Polyimide Substrate by Low-Temperature Deposition Process

The electrical and structural properties of polycrystalline Cu（In, Ga）Se2 films grown on polyimide （PI） substrates below 400℃ via one-stage and three-stage co-evaporation process have been investigated by x-ray diffraction spectra （XRD）, scanning electron microscopy （SEM） and Hall effect measurement. As shown by XRD spectra, the stoichiometric CIGS films obtained by one-stage process exhibit the characteristic diffraction peaks of the （In0.68Ga0.32）2Se3 and Cu（In0.7Ga0.3）2Se. It is also found that the film structures indicate more columnar and compact than the three-stage process films from SEM images. The stoichiometric CIGS films obtained by three-stage process exhibit the coexistence of the secondary phase of （In0.68Ga0.32）2Se3, Cu2-xSe and Cu（In0.7Ga0.3）2Se. High net carrier concentration and sheet conductivity are also observed for this kind of film, related to the presence of Cu2-xSe phase. As a result, when the CIGS film growth temperature is below 400℃, the three-stage process is inefficient for solar cells. By using the one-stage co-evaporation process, the flexible CIGS solar cell on a PI substrate with the best conversion efficiency of 6.38% is demonstrated （active area 0.16cm^2）.