ZnCuInS/ZnSe/ZnS量子点发光光谱特性的研究

ZnCuInS/ZnSe/ZnS量子点是一种无毒,无重金属的“绿色”半导体纳米材料。在研究中,制备了三种尺寸的ZnCuInS/ZnSe/ZnS核壳量子点,其直径分别为3.3,2.7,2.3 nm。通过测量不同尺寸的ZnCuInS/ZnSe/ZnS量子点的光致发光光谱,其发射峰值波长随尺寸的减小而蓝移。其吸收峰值波长和发射峰值波长分别是510,611(3.3 nm),483,583(2.7 nm)以及447,545 nm(2.3 nm)。ZnCuInS/ZnSe/ZnS量子点具有显著的尺寸依赖效应。ZnCuInS/ZnSe/ZnS量子点的斯托克斯位移分别为398 meV(3.3 nm),436 meV(2.7 nm)以及498 meV(2.3 nm),这样大的斯托克斯位移证明,ZnCuInS/ZnSe/ZnS量子点的发光机制与缺陷能级有关。同时,对直径为3.3 nm的ZnCuInS/ZnSe/ZnS量子点进行了温度依赖的光致发光光谱的测量,当温度为15～90 ℃时,该量子点发射峰值波长随温度的升高而红移,发光强度随温度的升高而降低,说明ZnCuInS/ZnSe/ZnS量子点是以导带能级与缺陷能级之间跃迁为主的复合发光。     

应变超晶格(ZnS)1/(ZnSe)1的光学性质

用linear mufin tin orbital能带方法，计算Si衬底上（ZnS）_n/（ZnSe）_n（001）超晶格的能带结构，计算中采用外加调整势进行带隙修正．在得到较准确的能带结构和波函数的基础上，计算该超晶格系统的光学介电函数虚部ε₂（ω）．结果表明，该超晶格系统的光学性质结合了ZnS和ZnSe体材料光学性质的特点，在相当宽的能量范围内有较好的光谱响应．并且该超晶格系统是直接带隙材料，在光电器件应用中有很大潜力． 关键词：     

用高分辨透射电镜对MOCVD生长的ZnSe1-xSx-ZnSe应变超晶格结构的研究

本文利用高分辨电子显微镜(TEM)从原子尺度对MOCVD生长的ZnSe_1-xS_x-Znse应变超晶格的精细结构进行了细致观察.通过对缺陷的种类、分布的分析提出缺陷的产生原因与过渡层质量有直接关系,通过改善过渡层的成份及各层间的厚度可制备出结构较完整以及较平整的超晶格薄层材料.     

Localized excitonic states in ZnS–ZnSe single quantum wells

We present low temperature photoluminescence spectra taken from an 11Å ZnSe quantum well in ZnS barriers. The samples are grown by the technique of photo-assisted vapour phase epitaxy (PAVPE) and the spectra show evidence for interface disorder. The observed dependences of the excitonic luminescence on excitation power and temperature are interpreted by a model involving excitonic localization below an exciton mobility edge. This mobility edge is measured for these samples to be 6 meV below the free exciton energy in the ideal quantum well.     

分子束外延生长ZnSe自组织量子点光、电行为研究

分别应用光致发光、电容电压和深能级瞬态傅里叶谱技术详细研究ZnSe自组织量子点样品的光学和电学行为.光致发光温度关系表明ZnSe量子点的光致发光热猝火过程机理.两步猝火过程的理论较好模拟和解释了相关的实验数据.电容电压测量表明样品表观载流子积累峰出现的深度(样品表面下约100nm处)大约是ZnSe量子点层的位置.深能级瞬态傅里叶谱获得的ZnSe量子点电子基态能级位置为ZnSe导带下的011eV,这与ZnSe量子点光致发光热猝火模型得到的结果一致.     

真空热处理对VPE ZnSxSe1-x外延膜发光的影响

本文测量了经真空热处理的VPE ZnSxSe1-x(X=0.055,0.22)外延膜液氮温度下的光致发光(PL)光谱,观察到一个新的蓝色发光带,并把这一谱带归结为导带中自由电子与束缚在深受主中心上空穴的复合.实验表明,深受主中心是在真空热处理时形成,并与真空热处理时在外延层中产生的Zn空位有关.     

Exciton dynamics in ZnSe/ZnS x Se1−x superlattices

Il Nuovo Cimento D - Time-resolved photoluminescence experiments in a wide carrier density range up to and beyond the threshold for stimulated emission in ZnSe/ZnS x Se1−x superlattices are...     

ZnSe-ZnS超晶格的通光蚀孔及列阵研究

用MOCVD方法在GaAs衬底上生长ZnSe-ZnS超晶格.用化学腐蚀方法在GaAs衬底上开一个通光窗口,使该窗口上仅剩有1～1.8μm厚的生长层.室温下测量了蚀孔后由于化学腐蚀造成生长层表面差异的ZnSe-ZnS超晶格的吸收光谱.研究了带有生长过渡层和无过渡层的超晶格质量对其吸收光谱性能的影响.发现过渡层的存在保护了超晶格激子吸收性能.在此基础上首次采用新工艺在3×3mm2面积上把GaAs衬底金部腐蚀掉,剩下均匀、光滑的ZnSe-ZnS超晶格层,在其上做出了300×300μm2的列阵,为在ZnSe-ZnS超晶格上实现光学双稳的集成化提供了必要条件.     

Temperature-dependent photoluminescence of dimethylzinc-treated ZnSe/ZnS quantum dots

Temperature-dependent photoluminescence (PL) measurements were carried out ZnSe/ZnS quantum dots (QDs) grown with post-growth interruption under a dimethylzinc (DMZn) flow. The PL spectra showed sigmoidal peak shifts and V-shaped full width at half maximum (FWHM) variations with increasing temperature, which strongly suggest that the QD structure of ZnSe/ZnS is quite similar to that of other material systems grown in the Stranski–Krastanov mode. Apparent differences are revealed as a consequence of DMZn treatment: (i) the PL spectra of ZnSe/ZnS QDs showed peaks at higher energies and persisted up to 300 K, and(ii) the minimum points of the V-shaped FWHM appear at a higher temperature compared to H₂-purged ZnSe/ZnS QDs. Experimental results demonstrate the enhancement of localization energy.     

Optical properties and recombination processes in (Zn,Cd)Se Graded Index Separate Confinement Heterostructures

Graded Index Separate Confinement Heterostructures have been grown by MOVPE using (Zn,Cd)Se and ZnSe wide bandgap semiconductors. These structures are composed of a deep Zn_1-xCd_xSe (x<0.23%) central well embedded between two thick (Zn,Cd)Se graded layers within which the cadmium composition varies from 0 up to 10% on one side of the well, and from 10 down to 0% on the other side. Both carriers and photon confinement occur in such structures making them suitable for blue-green stimulated emission.Reflectance and photoreflectance data, taken at 2K on a series of samples of different designs allowed us to observe excitonic transitions up to the third quantum number. The structures exhibit a strong photoluminescence line due to the recombination of the carriers in the quantum well. The photoluminescence intensity is analyzed as a function of the temperature and displays a strong thermal quenching. This quenching is due to an increase of the non-radiative recombinations through defects at low temperature and to the thermal escape of the carriers above 40-60K. The value of the activation energy for thermal escape shows that this mechanism is unipolar and concerns the heavy holes.     

CdSe/ZnSe/ZnS多壳层结构量子点的制备与表征

展示了一种简捷的多壳层量子点合成路线。在含有过量Se源的CdSe体系中直接注入Zn源,"一步法"合成了CdSe/ZnSe量子点;进一步以CdSe/ZnSe为"核",表面外延生长ZnS壳层制备了核/壳/壳结构CdSe/ZnSe/ZnS量子点。相对于以往报道的多壳层结构量子点的制备方法,该方法通过减少壳层的生长步骤有效地简化了实验操作,缩短了实验周期,同时减少对原料的损耗。对量子点进行高温退火处理,能够大幅提高CdSe/ZnSe/ZnS量子点的发光量子产率。透射电镜、XRD以及光谱研究表明:所制备的量子点接近球形,核与壳层纳米晶均为闪锌矿结构,最终获得的CdSe/ZnSe/ZnS量子点的光致发光量子产率达到53％。为了实现量子点的表面生物功能化,通过巯基酸进行了表面配体交换修饰,使量子点表面具有水溶性的羧基功能团,并且能够维持较高的光致发光量子产率。     

Raman spectroscopic studies of ZnSe/GaAs interfaces

ZnSe/semi‐insulating GaAs interfaces were studied by observing photogenerated plasmon–LO (PPL) coupled modes by nonresonant micro‐Raman spectroscopy. The effect of the carriers generated by the focused laser beam was investigated for a series of different thicknesses of ZnSe epitaxial layers. The PPL mode in GaAs was observed in the micro‐Raman spectra for all samples, but with different magnitude. The plasma is believed to be an electron gas as a result of the negative nature of the interfacial region that contains predominantly hole traps. The free carrier concentration is estimated to be > 10¹⁸ cm⁻³ and their lifetime ∼0.1 ns. This relatively long lifetime suggests that the ZnSe/GaAs interface has to be of high structural quality leading to a low recombination velocity. ZnSe/GaAs heterostructures of less crystalline quality (as determined by resonant Raman measurements) shows the effect of photogenerated carriers only to lesser extent. Copyright © 2007 John Wiley & Sons, Ltd.     

VPE ZnSxSe1-x外延膜中的自发和受激辐射

本文首次报道了VPE ZnSxSe1-x外延膜在77K时起因于激子和激子(Ex-Ex)散射的自发辐射和受激辐射,研究了Ex-Ex散射发光的位置和强度与激发密度的关系,分析了受激辐射的光子能量比自发辐射稍低的原因.     

Zn1—xMnx／ZnSe应变超晶格分子束外延生长及光学特性研究

用分子束外延方法在ＧａＡｓ（１００）衬底上成功生长了高质量的Ｚｎ１－ｘＭｎｘＳｅ／ＺｎＳｅ（ｘ＝０．１６），超晶格结构，用Ｘ射线衍射和低温光致发光（ＰＬ）对其结构，应变分布以及光学性能进行了研究，结果表明，２Ｋ温度下，Ｚｎ１－ｘＭｎｘＳｅ／ＺｎＳｅ超晶格的光致发光中主发光峰对应于ＺｎＳｅ阱中基态电子和基态轻空穴之间的自由激子跃迁，而且其峰位相对于ＺｎＳｅ薄膜材料的自由激子峰有明显移动。其中，当超晶     

Photoluminescence and magneto-optical properties of multilayered type-II ZnTe/ZnSe quantum dots

Multilayered Zn–Se–Te structures grown by migration enhanced epitaxy are studied by temperature- and excitation-dependent photoluminescence (PL) as well as magneto-PL. The PL consists of two bands: a blue band, overlaid with band edge sharp lines, dominant at low temperatures and high excitation, and a green band, which appears at elevated temperature and low excitation. Upon varying excitation intensity by four orders of magnitude, the green band peak energy shifts by ∼60 meV, indicating recombination of excitons in type-II quantum dots (QDs); no significant shift is observed for the blue band. Therefore, the green emission is attributed to ZnTe/ZnSe type-II QDs, which co-exist with isoelectronic centers, responsible for the blue and band edge emissions. The existence of type-II ZnTe/ZnSe QDs is further confirmed by magneto-PL, for which the observed oscillations in the PL intensity as a function of magnetic field is explained in terms of the optical Aharonov–Bohm effect.     

ZnSe／ZnS多量子阱激子光学双稳性

用MOCVD在CaF_2衬底上生长的ZnSe/ZnS多量子阱材料,在77K下用N_2激光泵浦染料获得的宽带光脉冲进行了非线性光学测量,首次观察到ZnSe/ZnS多量子阱的激子光学双稳性,据分析这是由激子的能带增宽效应引起的增强吸收光学双稳性.     

Optical properties of core/multishell CdSe/Zn(S,Se) nanocrystals

CdSe nanocrystals are now known as highly efficient fluorescent light sources. Their efficiency is however strongly dependent on the quality of the passivation layers. We show here that using a ZnSe/ZnS bi-layer shell leads to a larger photoluminescence yield than both ZnSe and ZnS simple shells. The intermediate ZnSe layer acts as a lattice parameter adaptation layer to improve on the core/shell interface quality, while the ZnS outer shell maximizes the exciton confinement.     

The 2s exciton in intermediate dimensionality structures

We report the observation of the 1s and 2s ground state excitons in small-offset superlattices with alternating layers of non-magnetic (ZnSe) and diluted magnetic (Zn_xMn_1 − xSe) semiconductors. Due to the large Zeeman splitting of the electron states in ZnMnSe, valence and conduction band offsets in these structures can be tuned by external magnetic field over the scale of tens of meV. Two series of superlattices were investigated, with Mn concentrations close to 10 and 15 atomic percent, respectively. Each series consisted of five superlattices with different layer thicknesses. The 2s exciton of the ground state is observed in all samples, and exhibits a diamagnetic shift that is consistent with earlier studies. The ability to determine the energy separation between the 1s and 2s exciton states allows us to analyze our results in the framework of thefractional dimension analysis , and to extract the values of exciton binding energies for the superlattices from the analysis.     

气相外延ZnSe单晶膜的自由激子发光

本文在77K和N2激光器3371谱线高密度激发的VPE ZnSe单晶膜上,首次得到了起因于自由激子与自由激子(Ex-Ex)散射的发光谱带(P带),理论拟合了该谱带的形状并讨论了它的发光特性。文中把在选择的VPE ZnSe外延单晶膜中得到P带的起因归结为这些ZnSe外延单晶膜的质量较高。     

Computerized setup for double-monochromator photoreflectance spectroscopy

An experimental setup for studying semiconductor structures by photoreflectance spectroscopy is designed. The double-monochromator-based optical scheme of the setup makes it possible to depress uncontrolled heating of the sample and diminishes a bending of the energy bands due to charge carrier photogeneration. Accordingly, the photoreflectance spectra are detected with a minimal influence of the modulating and probe radiations on the sample. With this setup, the room-temperature photoreflectance spectra from GaAs/GaAsP superlattices are taken and the interband transition energies, as well as a potential step in the conduction band of these superlattices, are measured.