Olefin bonding mechanism and growth to (1 0 0)(2 × 1):H diamond

The bonding and growth mechanism of photochemically attached olefin molecules to (1 0 0)(2 × 1):H diamond is characterized using atomic force (AFM) and scanning tunneling microscopy (STM) experiments in combination with molecular orbital calculations. To identify growth schemas, diamond surfaces after 10, 40 and 90 min of photo-chemically stimulated growth have been characterized. These data show clearly island formation which is discussed taking into account a growth model from silicon. The island growth shows no directional properties which are attributed to arrangement and geometrical properties of hydrogen terminated carbon bonds at the surface of (1 0 0) oriented (2 × 1) reconstructed diamond.     

Optical anisotropy of the In/Si(1 1 1)(4 × 1)/(8 × 2) nanowire array

Ab initio calculations of the reflectance anisotropy of Si(1 1 1)-In surfaces are presented. A very pronounced optical anisotropy around 2 eV is found that is related to In-chain states. The distortion of the indium chains characteristic for the (4 × 1) → (8 × 2) phase transition results in a splitting of the 2 eV peak, as observed experimentally. The splitting occurs irrespective wether the phase transition occurs according to the trimer or hexamer model.     

Electrochemical scanning tunneling microscopy examination of the structures of benzenethiol molecules adsorbed on Au(1 0 0) and Pt(1 0 0) electrodes

In situ electrochemical scanning tunneling microscopy (STM) has been used to examine the structures of benzenethiol adlayers on Au(1 0 0) and Pt(1 0 0) electrodes in 0.1 M HClO₄, revealing the formation of well-ordered adlattices of Au(1 0 0)-(√2 × √5) between 0.2 and 0.9 V and Pt(1 0 0)-(√2 × √2)R45° between 0 and 0.5 V (versus reversible hydrogen electrode), respectively. The coverage of Au(1 0 0)-(√2 × √5) is 0.33, which is identical to those observed for upright alkanethiol admolecules on Au(1 1 1). In comparison, the coverage of Pt(1 0 0)-(√2 × √2)R45° - benzenethiol is 0.5, much higher than those of thiol molecules on gold surfaces. This result suggests that benzenethiol admolecules on Pt(1 0 0) could stand even more upright than those on Au(1 0 0). All benzenethiol admolecules were imaged by the STM as protrusions with equal corrugation heights, suggesting identical molecular registries on Au(1 0 0) and Pt(1 0 0) electrodes, respectively. Modulation of the potential of a benzenethiol-coated Au(1 0 0) electrode resulted in irreversible desorption of admolecules at E ? 0.1 V (vs. reversible hydrogen electrode) and oxidation of admolecules at E ? 0.9 V. In contrast, benzenethiol admolecule was not desorbed from Pt(1 0 0) at potentials as negative as the onset of hydrogen evolution. Raising the potential rendered deposition of more benzenethiol molecules before oxidation of admolecules commenced at E > 0.9 V.     

Early stages of vanadium deposition on Si(1 1 1)-7 × 7

We investigate the low-coverage regime of vanadium deposition on the Si(1 1 1)-7 × 7 surface using a combination of scanning tunnelling microscopy (STM) and density-functional theory (DFT) adsorption energy calculations. We theoretically identify the most stable structures in this system: (i) substitutional vanadium atoms at silicon adatom positions; (ii) interstitial vanadium atoms between silicon adatoms and rest atoms; and (iii) interstitial vanadium - silicon adatom vacancy complexes. STM images reveal two simple vanadium-related features near the Si adatom positions: bright spots at both polarities (BB) and dark spots for empty and bright spots for filled states (DB). We relate the BB spots to the interstitial structures and the DB spots to substitutional structures.     

Perturbation of Ge(1 1 1) and Si(1 1 1)√3α-Sn surfaces by adsorption of dopants

We test the response of the √3 × √3α reconstructions formed by 1/3 monolayer of tin adatoms on silicon and germanium (1 1 1) surfaces upon doping with electrons or holes, using potassium or iodine as probes/perturbers of the initial electronic structures. From detailed synchrotron radiation photoelectron spectroscopy studies we show that doping with either electrons or holes plays a complimentary role on the Si and Ge surfaces and, especially, leads to complete conversion of the Sn 4d two-component spectra into single line shapes. We find that the low binding energy component of the Sn core level for both Si and Ge surfaces corresponds to Sn adatoms with higher electronic charge, than the Sn adatoms that contribute to the core level high binding energy signal. This could be analyzed as Sn adatoms with different valence state.     

Effects of electronic confinement and substrate on the low-temperature growth of Pb islands on Si(1 0 0)-2 × 1 surfaces

The growth of Pb films on the Si(1 0 0)-2 × 1 surface has been investigated at low temperature using scanning tunneling microscopy. Although the orientation of the substrate is (1 0 0), flat-top Pb islands with (1 1 1) surface can be observed. The island thickness is confined within four to nine atomic layers at low coverage. Among these islands, those with a thickness of six layers are most abundant. Quantum-well states in Pb(1 1 1) islands of different thickness are acquired by scanning tunneling spectroscopy. They are found to be identical to those taken on the Pb(1 1 1) islands grown on the Si(1 1 1)7 × 7 surface. Besides Pb(1 1 1) islands, two additional types of Pb islands are formed: rectangular flat-top Pb(1 0 0) islands and rectangular three-dimensional (3D) Pb islands, and both their orientations rotate by 90° from a terrace to the adjacent one. This phenomenon implies that the structures of Pb(1 0 0) and 3D islands are influenced by the Si(1 0 0)-2 × 1 substrate.     

Core-level photoelectron study of indium chains on Si(1 1 1) at 10 K

High-resolution core-level data from the prototypical In/Si(1 1 1) system have been acquired at 10 K. An asymmetric tail in the In 4d spectra reveals a metallic character of the low temperature Si(1 1 1)8 × 2 phase confined to the inner indium rows. The decoupling of the one-dimensional inner indium chains from any metallic environment at ∼10 K suggests a possible Luttinger liquid behavior. At room temperature essentially a broadening of the spectral features is noticed, which appears compatible with a fluctuation scenario.     

A study of Ga layers on Si(1 0 0)-(2 × 1) by SR-PES: Influence of adsorbed water

Results for deposition and thermal annealing of gallium on the Si(1 0 0)-(2 × 1) surface achieved by synchrotron radiation photoelectron spectroscopy (SR-PES) and low energy electron diffraction (LEED) are presented. In addition to deposition of Ga on a clean surface, the influence of water adsorption on the arrangement of gallium atoms was also studied. The results on Ga deposition at a higher temperature (490 °C) are consistent with a Ga ad-dimer model showing equivalent bond arrangement of all Ga atoms for coverages up to 0.5 ML. The deposition onto a surface with adsorbed water at room temperature led to a disordered gallium growth. In this case gallium atoms bind to silicon dimers already binding fragments of adsorbed water. A subsequent annealing of these layers leads to a surface structure similar to the Ga-(2 × 2), however, it is less ordered, probably due to the presence of silicon oxides formed from water fragments.     

Scanning tunneling microscopy luminescence from nanoscale surface of GaAs(1 1 0)

Scanning tunneling microscopy luminescence (STML) was induced from the nanometer scale surfaces of cleaved n-type and p-type GaAs(1 1 0) wafers by using of an ITO-coated optical fiber probe in an ultrahigh-vacuum chamber. The STML from n-type GaAs(1 1 0) surface was induced under negative sample bias when the applied bias exceeds a threshold voltage around −1.5 V. Whereas the STML from p-type GaAs(1 1 0) surface was induced under positive sample bias when the applied bias exceeds a threshold voltage around +1.5 V. The excitation energies at the threshold voltages are consistent with the band gap of GaAs (1.42 eV) at 295 K. The typical quantum efficiencies for n-type and p-type GaAs are about 3 × 10⁻⁵ and 2 × 10⁻⁴ photons/electron, respectively. The observed STML from are attributed to a radiative recombination of electron-hole pairs generated by a hole injection for n-type GaAs under negative sample bias and an electron injection for p-type GaAs under positive sample bias, respectively.     

Structural study of Si(1 1 1)-6 × 1-Ag surface using surface X-ray diffraction

The surface structure of Si(1 1 1)-6 × 1-Ag was investigated using surface X-ray diffraction techniques. By analyzing the CTR scattering intensities along 00 rod, the positions of the Ag and reconstructed Si atoms perpendicular to the surface were determined. The results agreed well with the HCC model proposed for a 3 × 1 structure induced by alkali-metals on a Si(1 1 1) substrate. The heights of the surface Ag and Si atoms did not move when the surface structure changed from Si(1 1 1)-√3 × √3-Ag to Si(1 1 1)-6 × 1-Ag by the desorption of the Ag atoms. From the GIXD measurement, the in-plane arrangement of the surface Ag atoms was determined. The results indicate that the Ag atoms move large distances at the phase transition between the 6 × 1 and 3 × 1 structures.     

Electronic structure study of reconstructed Au-SiC(0 0 0 1) surfaces

A study of surface and interface properties of reconstructed Au-SiC(0 0 0 1) surfaces is reported. Two reconstructions were prepared on SiC(0 0 0 1), a √3 × √3R30° and a Si-rich 3 × 3, before Au deposition and subsequent annealing at different temperatures. For the Si-rich 3 × 3 surface the existence of three stable reconstructions 2√3 × 2√3R30°, 3 × 3 and 5 × 5 are revealed after deposition of Au layers, 4-8 Å thick, and annealing at progressively higher temperatures between 500 and 950 °C. For the 2√3 surface two surface shifted Si 2p components are revealed and the Au 4f spectra clearly indicate silicide formation. The variation in relative intensity for the different core level components with photon energy suggests formation of an ordered silicide layer with some excess Si on top. Similar core level spectra and variations in relative intensity with photon energy are obtained for the 3 × 3 and 5 × 5 phases but the amount of excess Si on top is observed to be smaller and an additional weak Si 2p component becomes discernable.For the √3 surface the evolution of the core level spectra after Au deposition and annealing is shown to be distinctly different than for the Si-rich 3 × 3 surface and only one stable reconstruction, a 3 × 3 phase, is observed at similar annealing temperatures.     

Configuration of pentacene (C22H14) films on Si(1 0 0)-2 × 1 studied by NEXAFS

Pentacene films on Si(1 0 0)-(2 × 1) surface at 300 K were investigated using near edge X-ray absorption fine structure (NEXAFS) at the carbon K-edge. NEXAFS spectra show that pentacene molecules are chemisorbed on the Si(1 0 0)-(2 × 1) surface for monolayer with flat-laying and predominantly physisorbed on the Si(1 0 0)-(2 × 1) surface for multilayer films with an upright molecular orientation. Absorption angle of pentacene molecules were measured through π^∗ transition. The angles between the double bond and the silicon surface were 35-55°, 65° and 76° at monolayer, 24 and 48 nm pentacene deposited on the Si(1 0 0) surface, respectively. We observed that the intermediate flat-laying phase is favored for monolayer coverage, while the films of molecules standing perpendicular to the Si(1 0 0) surface are favored for multilayer coverage.     

Characteristic energy band values and electron attenuation length of a chemical-vapor-deposition diamond (0 0 1)2 × 1 surface

The characteristic energy band values such as the Fermi-level position with respect to valence band top for a boron-doped p-type hydrogen-terminated chemical-vapor-deposition (CVD) diamond (0 0 1)2 × 1 surface and for a clean CVD diamond (0 0 1)2 × 1 surface have been determined by a new method with an accuracy of ±0.02 eV. The electron attenuation length for the clean diamond (0 0 1)2 × 1 surface for the electron kinetic energy of C 1s X-ray photoemission peak by Mg Kα excitation is experimentally determined to be 2.1-2.2 nm. These values are compared and discussed with the previously reported experimental and simulation values.     

Growth of (√3 × √3)-Ag and (1 1 1) oriented Ag islands on Ge/Si(1 1 1) surfaces

We have studied the growth of Ag on Ge/Si(1 1 1) substrates. The Ge/Si(1 1 1) substrates were prepared by depositing one monolayer (ML) of Ge on Si(1 1 1)-(7 × 7) surfaces. Following Ge deposition the reflection high energy electron diffraction (RHEED) pattern changed to a (1 × 1) pattern. Ge as well as Ag deposition was carried out at 550 °C. Ag deposition on Ge/Si(1 1 1) substrates up to 10 ML has shown a prominent (√3 × √3)-R30° RHEED pattern along with a streak structure from Ag(1 1 1) surface. Scanning electron microscopy (SEM) shows the formation of Ag islands along with a large fraction of open area, which presumably has the Ag-induced (√3 × √3)-R30° structure on the Ge/Si(1 1 1) surface. X-ray diffraction (XRD) experiments show the presence of only (1 1 1) peak of Ag indicating epitaxial growth of Ag on Ge/Si(1 1 1) surfaces. The possibility of growing a strain-tuned (tensile to compressive) Ag(1 1 1) layer on Ge/Si(1 1 1) substrates is discussed.     

Electron-stimulated desorption from an unexpected source: Internal hot electrons for Br-Si(1 0 0)-(2 × 1)

The desorption of Br adatoms from Br-saturated Si(1 0 0)-(2 × 1) was studied with scanning tunneling microscopy as a function of dopant type, dopant concentration, and temperature for 620-775 K. Analysis yields the activation energies and prefactors for desorption, and the former correspond to the energy separation between the Fermi level and Si-Br antibonding states. Thus, electron capture in long-lived states results in Br expulsion via a Franck-Condon transition. Analysis of the prefactors reveals that optical phonons provide the energy needed for the electronic excitation. These results show that desorption induced by an electronic transition can occur in closed system without external stimulus, and they indicate that thermally-excited charge carriers may play a general role in surface reactions.     

Intramolecular structures of C60 and C84 molecules on Si(1 1 1)-7 × 7 surfaces by scanning tunneling microscopy

The intramolecular features of carbon 60 and carbon 84 molecules on Si(1 1 1)-7 × 7 surfaces were studied under a UHV-scanning tunneling microscope. Carbon molecules preferentially appear in faulted halves, rather than in unfaulted halves and corner holes; they are embedded in silicon substrates. The orientation and details of the structure of carbon molecules are determined by applying various sample biases to the silicon substrate. As compared with other fullerenes, a bright pentagonal ring with nebulous clusters which represents the cage structure is clearly observed on top of carbon 60 molecules. The bright stripes associated with partitioned curves which depict eight features of asymmetrical C₈₄ molecules are also investigated on Si(1 1 1)-7 × 7 surfaces. The orientations and possible configurations of C₆₀ and C₈₄ are considered in this work. The energy differences for various features of C₆₀ and C₈₄ molecules are estimated and discussed. The corresponding models with respect to each intramolecular feature are proposed and compared with recent theoretical calculation.     

STM image visualization of Si(1 1 1) 7 × 7 surface (graphic simulation and implementation)

The possibilities of graphic STM image simulation of a clean Si(1 1 1) 7 × 7 surface at atomic level are indicated. The presented procedure takes into account various types of deformation on the surface near the Fermi level in order to classify them and explain their origin. It also gives a clear hint to insert relevant physical phenomena in a suggested analysis. This goal is achieved exploiting the results of DAS (dimmer adatom stacing fault) model by means of standard mathematical programmes. A clean Si(1 1 1) 7 × 7 surface is considered as the representative example, but similar evaluation is possible for another non-metal and metal surfaces.     

Study of vacancy on diamond (1 0 0) (2 × 1) surface from first-principles

Structure and energy related properties of neutral and charged vacancies on relaxed diamond (1 0 0) (2 × 1) surface were investigated by means of density functional theory. Calculations indicate that the diffusion of a single vacancy from the top surface layer to the second layer is not energetically favored. Analysis of energies in charged system shows that neutral state is most stable on diamond (1 0 0) (2 × 1) surface. The multiplicity of possible states can exist on diamond (1 0 0) surface in dependence on the surface Fermi level, which supports that surface diffusion of a vacancy is mediated by the change of vacancy charge states. Analysis of density of states shows surface vacancy can be effectively measured by photoelectricity technology.     

Growth and morphology of the epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) Trilayers

Growth and surface morphology of epitaxial Fe(1 1 0)/MgO(1 1 1)/Fe(1 1 0) trilayers constituting a magnetic tunnel junction were investigated by low-energy electron diffraction (LEED) and scanning tunneling microscopy (STM). STM reveals a grain-like growth mode of MgO on Fe(1 1 0) resulting in dense MgO(1 1 1) films at room temperature as well as at 250 °C. As observed by STM, initial deposition of MgO leads to a partial oxidation of the Fe(1 1 0) surface which is confirmed by Auger electron spectroscopy. The top Fe layer deposited on MgO(1 1 1) at room temperature is relatively rough consisting of clusters which can be transformed by annealing to an atomically flat epitaxial Fe(1 1 0) film.     

Mechanisms of preferential adsorption on the Si(1 1 1)7 × 7 surface

The surface relaxation mechanisms governing the preferential adsorption of metal atoms onto the faulted half-cells of a 7 × 7 reconstructed Si(1 1 1) surface are studied by rate equations and kinetic Monte Carlo simulations. The versatility of these mechanisms to control the formation of quasi-perfect 2D arrays of metal clusters is revealed via the optimization of the deposition/annealing conditions as a function of operating mechanisms, the Si(1 1 1)7 × 7 energy landscape, and the thermal stability of the created clusters. The influence on the formation process of such nanoarrays of the balance between kinetic limitations, which are especially relevant on Si(1 1 1)7 × 7, and thermodynamic tendencies is discussed.