A ‘grafting‐from’ approach to synthesize microparticle‐supported conjugated polyelectrolyte brushes is presented. Poly(3‐bromohexylthiophene) is selectively grown from monodisperse organosilica microparticles by surface‐initiated Kumada catalyst‐transfer polycondensation (SI‐KCTP) and then ionizable amino groups are introduced by a two‐step polymer analogous transformation. Optical properties of the resulting microparticle‐supported conjugated polyelectrolyte brushes were found to be dependent on the surrounding chemical environment and thus the particles are promising materials for sensor applications.
A dextran‐based dual‐sensitive polymer is employed to endow gold nanoparticles with stability and pH‐ and temperature‐sensitivity. The dual‐sensitive polymer is prepared by RAFT polymerization of N‐isopropylacrylamide from trithiocarbonate groups linked to dextran and succinoylation of dextran after polymerization. The functionalized nanoparticles show excellent stability under various conditions and can be stored in powder‐form. UV and DLS measurements confirm that the temperature‐induced optical changes and aggregation behaviors of the particles are strongly dependent on pH.
The monomer 3‐ethyl‐1‐vinyl‐2‐pyrrolidone ( 3 ) and the homopolymer poly(3‐ethyl‐1‐vinyl‐2‐pyrrolidone) ( 5 ) have been synthesized. Polymer 5 is soluble in water and shows a critical temperature (Tc) of 27 °C. The presence of cyclodextrin causes a slight shift of the Tc. The lower critical solution temperature (LCST) could be varied between 27 and 40 °C by copolymerization with N‐vinyl‐2‐pyrrolidone. A linear correlation between the Tc and the copolymer composition is observed.
A high molecular weight ladder polymer based on 5,5′,6,6′‐tetrahydroxy‐3,3,3′,3′‐tetramethylspirobisindane and 1,4‐dicyanotetraflurobenzene has been synthesized by polycondensation under high‐intensity mixing conditions at about 155 °C and cyclic‐free products were obtained in high yield with low molecular weight distribution (1.7–2.3). The reaction could be completed within a few minutes. The polymer properties were characterized by GPC, 1H NMR, 13C NMR, F NMR, FT‐IR, and MALDI‐TOF MS. In addition, the mechanical properties, apparent surface areas and gas permeability are also reported. This procedure can also be used for the synthesis of other ladder polymers by irreversible polycondensations of tetraphenols with activated tetrafluoro aromatics.
Commercially available 1,2‐PB was transformed into a well‐defined reactive intermediate by quantitative bromination. The brominated polymer was used as a polyfunctional macroinitiator for the cationic ring‐opening polymerization of 2‐ethyl‐2‐oxazoline to yield a water‐soluble brush polymer. Nucleophilic substitution of bromide by 1‐methyl imidazole resulted in the formation of polyelectrolyte copolymers consisting of mixed units of imidazolium, bromo, and double bond. These copolymers, which were soluble in water without forming aggregates, were used as stabilizers in the heterophase polymerization of styrene and were also studied for their ionic conducting properties.
Sixteen parallel polymerization reactions of 2‐ethyl‐2‐oxazoline have been performed at different temperatures in an automated synthesizer that allowed individual heating of each reactor. During the reactions samples were taken automatically, which were characterized by means of both online GPC and offline GC, in order to optimize the reaction temperature and to determine the activation energy of the polymerization.