S型异质结光催化剂ZnFe2O4/WO3的构筑及光催化还原CO2性能

通过在WO₃纳米片表面负载ZnFe₂O₄纳米颗粒,构建了一系列S型异质结光催化剂ZnFe₂O₄/WO₃,并研究了其光催化CO₂还原性能。在没有助催化剂和牺牲剂的条件下,所制备的ZnFe₂O₄/WO₃复合材料可对CO₂与水蒸汽进行光催化反应。优化后的材料光照5 h后CO₂还原产物CO和CH₄的产量分别为7.87和4.88 μmol·g^-1。相对于单相组分,CO和CH₄的产量明显提高。光催化活性的提高,归因于ZnFe₂O₄和WO₃异质结的形成以及光生载流子的S型电荷传输模式。     

Sb2O3/BiVO4/WO3异质结构建及光电催化合成过氧化氢

采用溶剂热法-旋涂法构建了Sb₂O₃/BiVO₄/WO₃半导体异质结,并采用X射线衍射、扫描电子显微镜、X射线光电子能谱等手段表征了其物化性质。在1.23 V(vs RHE)电位下,BiVO₄/WO₃的光电流密度相对于BiVO₄提高了2倍。进一步复合Sb₂O₃之后,虽然Sb₂O₃/BiVO₄/WO₃薄膜的光电流密度有所下降,但其光电催化产H₂O₂的法拉第效率和产生速率得到明显提升。在1.89V(vs RHE)电位下,3c-Sb₂O₃/BiVO₄/WO₃薄膜产 H₂O₂的法拉第效率提高到约 19%;1c-Sb₂O₃/BiVO₄/WO₃薄膜 H₂O₂产生速率从约2.1 μmol·h^-1·cm^-2提高到约3.6 μmol·h^-1·cm^-2。此外,Sb₂O₃的复合显著提高了BiVO₄/WO₃电极材料的光电催化稳定性。     

Bi2WO6/TiO2纳米管异质结构复合材料的多模式下的光催化活性比较

以TiO₂纳米管为模板,采用多组分自组装结合水热法制备Bi₂WO₆/TiO₂纳米管异质结构复合材料。通过多种技术如X射线衍射（XRD）,X射线光电子能谱（XPS）,N₂吸附-脱附,扫描电镜（SEM）,高分辨透射电镜（HRTEM）和紫外可见漫反射吸收光谱（UV-Vis DRS）考察所制备样品的组成、结构、形貌、光吸收和电子性质。Bi₂WO₆纳米片或纳米粒子分布在TiO₂纳米管上,形成异质结构。随后,通过在紫外、可见和微波辅助光催化模式下降解染料罗丹明B（RhB）来评价复合催化剂的光催化活性。与TiO₂纳米管和Bi₂WO₆相比,Bi₂WO₆/TiO₂-35纳米管在多模式下表现出更优异的光催化活性。与紫外和可见降解模式相比,Bi₂WO₆/TiO₂-35纳米管在微波辅助光催化模式下对RhB的降解效率最高。这种增强的光催化活性源于适量Bi₂WO₆的引入、纳米管独特的形貌特征和降解模式所引起的增强的量子效率。降解过程中的活性物种被证明是h⁺,·OH和·O₂^-自由基。而且,在微波辅助光催化模式下,可产生更多的·OH和·O₂^-自由基。     

Bi2WO6/TiO2纳米管异质结构复合材料的多模式下的光催化活性比较

以TiO₂纳米管为模板,采用多组分自组装结合水热法制备Bi₂WO₆/TiO₂纳米管异质结构复合材料。通过多种技术如X射线衍射（XRD）,X射线光电子能谱（XPS）,N₂吸附脱附,扫描电镜（SEM）,高分辨透射电镜（HRTEM）和紫外可见漫反射吸收光谱（UV-Vis DRS）考察所制备样品的组成、结构、形貌、光吸收和电子性质。Bi₂WO₆纳米片或纳米粒子分布在TiO₂纳米管上,形成异质结构。随后,通过在紫外、可见和微波辅助光催化模式下降解染料罗丹明B（RhB）来评价复合催化剂的光催化活性。与TiO₂纳米管和Bi₂WO₆相比,Bi₂WO₆/TiO₂-35纳米管在多模式下表现出更优异的光催化活性。与紫外和可见降解模式相比,Bi₂WO₆/TiO₂-35纳米管在微波辅助光催化模式下对RhB的降解效率最高。这种增强的光催化活性源于适量Bi₂WO₆的引入、纳米管独特的形貌特征和降解模式所引起的增强的量子效率。降解过程中的活性物种被证明是h⁺,·OH和·O₂^-自由基。而且,在微波辅助光催化模式下,可产生更多的·OH和·O₂^-自由基。     

BiVO4/ZnFe2O4同型异质结光阳极的构筑及其光电催化分解水性能

光生电子-空穴对的复合被认为是限制BiVO₄材料光电催化转换效率的重要原因之一。基于此,通过简单的水热-煅烧方法构筑了 BiVO₄/ZnFe₂O₄同型异质结光阳极,BiVO₄/ZnFe₂O₄复合光阳极在 1.23 V(vs RHE)下的光电流密度为 3.33 mA·cm^-2,较纯BiVO₄提升了2倍 (1.20 mA·cm^-2)。相关的结构及性能测试表明,BiVO₄和ZnFe₂O₄形成了带隙错开的n-n异质结,使得光生载流子得到有效分离,更有效地参与水氧化过程,进而提高了BiVO₄的光电催化水分解性能。     

Z型Ag-Cu2O/BiVO4光催化剂的光催化还原CO2性能

利用简单的化学还原沉积法将 Cu₂O纳米球和 Ag纳米颗粒均匀包裹在十面体 BiVO₄表面,成功构建了一种具有高效电荷载流子分离/转移特性的Z型异质结光催化剂Ag-Cu₂O/BiVO₄。Ag-Cu₂O/BiVO₄在可见光下光催化CO₂还原为CO的产率可达5.37 μmol·g^-1·h^-1,分别是纯 BiVO₄和 Cu₂O的 35.80倍和 6.30倍。通过 X射线粉末衍射(XRD)、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、X射线能谱(EDS)、紫外可见漫反射光谱(UV-Vis DRS)、光致发光(PL)光谱、瞬态光电流响应(TPC)和电化学阻抗谱(EIS)对 Ag-Cu₂O/BiVO₄的晶体结构、形貌、组成、能带结构和吸光能力等进行了系统表征分析,并提出了其光催化体系还原CO₂的催化机理。     

Z型Ag-Cu2O/BiVO4光催化剂的光催化还原CO2性能

利用简单的化学还原沉积法将Cu₂O纳米球和Ag纳米颗粒均匀包裹在十面体BiVO₄表面,成功构建了一种具有高效电荷载流子分离/转移特性的Z型异质结光催化剂Ag-Cu₂O/BiVO₄。Ag-Cu₂O/BiVO₄在可见光下光催化CO₂还原为CO的产率可达5.37 μmol·g^-1·h^-1,分别是纯BiVO₄和Cu₂O的35.8倍和6.25倍。通过X射线粉末衍射(XRD)、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、X射线能谱(EDS)、紫外可见漫反射光谱(UV-Vis DRS)、光致发光(PL)光谱、瞬态光电流响应(TPC)和电化学阻抗谱(EIS)对Ag-Cu₂O/BiVO₄的晶体结构、形貌、组成、能带结构和吸光能力等进行了系统表征分析,并提出了其光催化体系还原CO₂的催化机理。     

Bi2WO6量子点(QDs)修饰Bi2MoO6-xF2x异质结的构筑及其催化活性增强机理

采用简单沉积-沉淀法合成了Bi₂WO₆@Bi₂MoO_6-xF_2x（BWO/BMO6-xF2x）异质结,借助XRD、XPS、TEM、SEM、EDS、UV-Vis-DRS、PC和EIS等测试技术对其组成、形貌、光吸收特性和光电化学性能等进行系统表征,并以模型污染物罗丹明B（RhB）的光催化降解作为探针反应来评价Bi₂WO₆@Bi₂MoO_6-xF_2x异质结的光催化活性增强机制。形貌分析表明,所得Bi₂MoO₆微球由大量厚度为20~50 nm的纳米片组成;FE-SEM和HR-TEM分析表明,尺寸约为10 nm的Bi₂WO₆量子点均匀沉积在Bi₂MoO_6-xF_2x微球表面,形成新颖的Bi₂WO₆@Bi₂MoO_6-xF_2x异质结;与纯Bi₂MoO₆或者Bi₂WO₆相比,1∶1Bi₂WO₆@Bi₂MoO_6-xF_2x异质结表现出更好的光催化活性和光电流性质,其对RhB光催化降解的表观速率常数分别为纯BMO和BWO的6.4和11.6倍。PC和EIS图谱分析表明,Bi₂WO₆量子点表面沉积显著提高Bi₂MoO_6-xF_2x光生电子/空穴的分离效率和迁移速率;活性物种捕获实验证明了·O₂^-和h⁺是主要的活性物种。根据实验结果,探讨了F^-掺杂和Bi₂WO₆量子点之间的协同效应对Bi₂MoO₆的光催化活性的影响机制。     

ZnFe2O4/Ag/TiO2复合材料的制备及其光催化性能

以硝酸银、钛酸四丁酯、无水氯化锌、六水氯化铁为原料,采用溶胶-凝胶法与溶剂热相结合的方法制备了ZnFe₂O₄/Ag/TiO₂复合材料,通过扫描电子显微镜、能谱分析仪、X射线粉末衍射仪、X射线光电子能谱仪、振动样品磁强计、紫外可见分光光度计对样品进行表征及测试。结果表明： ZnFe₂O₄/Ag/TiO₂-10具有最佳的光催化效果,在紫外和可见光下对染料的降解率都能达到90%以上,具有优异的紫外可见光光催化活性。ZnFe₂O₄/Ag/TiO₂具有独特的磁性,能在外部磁场作用下进行回收利用,这使其在实际应用中成为可能。通过磁分离技术重复回收利用5次后仍然保持优良的光催化性能,说明ZnFe₂O₄/Ag/TiO₂-10具有优异的磁性及较高的光催化循环稳定性。     

Bi2Ti2O7/TiO2/Bi4Ti3O12多异质结的构筑及其增强的可见光催化性能

以静电纺丝技术制备的TiO₂纳米纤维为基质,硝酸铋为铋源,KOH为矿化剂,成功制备了多异质结Bi₄Ti₃O₁₂/TiO₂/Bi₂Ti₂O₇复合纳米纤维光催化剂。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、紫外可见漫反射光谱(UV-Vis DRS)等一系列表征,对其物相组成、微观形貌和光学性质等进行分析。结果表明： TiO₂纳米纤维的介入,将Ⅰ型异质结Bi₂Ti₂O₇/Bi₄Ti₃O₁₂分离为2个Ⅱ型异质结Bi₂Ti₂O₇/TiO₂和Bi₄Ti₃O₁₂/TiO₂。Bi₂Ti₂O₇、Bi₄Ti₃O₁₂和TiO₂三者的协同作用,有效提高了可见光吸收能力,改变了光生载流子的传输路径,降低了光生电子与空穴的复合几率,从而获得高效的光催化降解CH₃CHO性能。可见光照8 h,Bi₄Ti₃O₁₂/TiO₂/Bi₂Ti₂O₇复合纳米纤维对CH₃CHO的降解率达到87.1%。     

TiO2/SnO2复合光催化剂的耦合效应

采用改进的sol gel技术制备TiO2/SnO2耦合型半导体光催化剂,利用XRD、气相色谱 仪、粒度仪和表面光电压装置等研究了耦合型半导体光催化机理和光催化效率的影响因素, 并通过降解甲醛探讨其在空气污染治理中的作用.实验结果表明,添加20 ％(mol) SnO2的复 合半导体光催化剂,其光催化效率比纯TiO2高一倍以上.据实验结果和粒子紧密堆积原理,提 出强耦合效应和弱耦合效应的光催化反应模型,并用此模型较好地解释了TiO2/SnO2复合型半 导体光催化剂的光催化效率随SnO2含量变化规律.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Conversion of NO in NO/N2, NO/O2/N2, NO/C2H4/N2 and NO/C2H4/O2/N2 Systems by Dielectric Barrier Discharge Plasmas

An experimental study on the conversion of NO in the NO/N₂, NO/O₂/N₂, NO/C₂H₄/N₂ and NO/C₂H₄/O₂/N₂ systems has been carried out using dielectric barrier discharge (DBD) plasmas at atmospheric pressure. In the NO/N₂ system, NO decomposition to N₂ and O₂ is the dominating reaction; NO conversion to NO₂ is less significant. O₂ produced from NO decomposition was detected by an on-line mass spectrometer. With the increase of NO initial concentration, the concentration of O₂ produced decreases at 298 K, but slightly increases at 523 K. In the NO/O₂/N₂ system, NO is mainly oxidized to NO₂, but NO conversion becomes very low at 523 K and over 1.6% of O₂. In the NO/C₂H₄/N₂ system, NO is reduced to N₂ with about the same NO conversion as that in the NO/N₂ system but without NO₂ formation. In the NO/C₂H₄/O₂/N₂ system, the oxidation of NO to NO₂ is dramatically promoted. At 523 K, with the increase of the energy density, NO conversion increases rapidly first, and then almost stabilizes at 93–91% of NO conversion with 61–55% of NO₂ selectivity in the energy density range of 317–550 J L⁻¹. It finally decreases gradually at high energy density. A negligible amount of N₂O is formed in the above four systems. Of the four systems studied, NO conversion and NO₂ selectivity of the NO/C₂H₄/O₂/N₂ system are the highest, and NO/O₂/C₂H₄/N₂ system has the lowest electrical energy consumption per NO molecule converted.     

Energetics of copper diphosphates – Cu2P2O7 and Cu3(P2O6OH)2

Differential scanning calorimetry and high temperature oxide melt solution calorimetry are used to study enthalpy of phase transition and enthalpies of formation of Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂. α-Cu₂P₂O₇ is reversibly transformed to β-Cu₂P₂O₇ at 338–363 K with an enthalpy of phase transition of 0.15 ± 0.03 kJ mol⁻¹. Enthalpies of formation from oxides of α-Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂ are −279.0 ± 1.4 kJ mol⁻¹ and −538.8 ± 2.7 kJ mol⁻¹, and their standard enthalpies of formation (enthalpy of formation from elements) are −2096.1 ± 4.3 kJ mol⁻¹ and −4302.7 ± 6.7 kJ mol⁻¹, respectively. The presence of hydrogen in diphosphate groups changes the geometry of Cu(II) and decreases acid–base interaction between oxide components in Cu₃(P₂O₆OH)₂, thus decreasing its thermodynamic stability.     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

g-C3N4/Bi2O2CO32D纳米片复合材料的制备及可见光催化性能研究

采用自组装和化学沉淀法分别制得两种可见光驱动复合材料石墨相氮化碳/碳酸氧铋(g-C_3N_4/Bi_2O_2CO_3).采用X射线衍射光谱(XRD),紫外可见光谱、扫描电镜(SEM)、N_2吸附、电化学阻抗谱(EIS)和X射线光电子能谱(XPS)等分析手段对制备的催化剂进行了表征.结果表明,制备方法对纳米复合材料的晶相、形态及光学性能没有影响,但是影响g-C_3N_4和Bi_2O_2CO_3之间的相互作用力,导致光生电子-空穴对的分离速率存在显著差异.以可见光驱动苯酚和罗丹明B的降解实验为探针反应检测催化剂的光催化性能.实验结果表明自组装法得到的异质结催化剂中相互作用力更强,催化效果最高.O_2-是罗丹明B降解反应的主要活性物种,染料的光敏化、Bi_2O_2CO_3与g-C_3N_4综合效应,导致光生载流子电荷分离效率更高.     

Spectroscopic properties of guanidinium zinc sulphate [C(NH2)3]2Zn(SO4)2 and ab initio calculations of [C(NH2)3]2 and HC(NH2)3

Raman and FTIR spectra of guanidinium zinc sulphate [C(NH₂)₃]₂Zn(SO₄)₂ are recorded and the spectral bands assignment is carried out in terms of the fundamental modes of vibration of the guanidinium cations and sulphate anions. The analysis of the spectrum reveals distorted SO₄²⁻ tetrahedra with distinct S–O bonds. The distortion of the sulphate tetrahedra is attributed to Zn–O–S–O–Zn bridging in the structure as well as hydrogen bonding. The CN₃ group is planar which is expressed in the twofold symmetry along the C–N (1) vector. Spectral studies also reveal the presence of hydrogen bonds in the sample. The vibrational frequencies of [C(NH₂)₃]₂ and HC(NH₂)₃ are computed using Gaussian 03 with HF/6-31G* as basis set.     

EuZn2Si2 and EuZn2Ge2 Grown from Zn or Ga(ln)/Zn Flux

Single crystals of the novel ternary compounds EuZn₂Si₂ and EuZn₂Ge₂ were grown from pure gallium, indium, or zinc metal used as a flux solvent. Crystal properties were characterized using X-ray single-crystal analyses via Gandolfi and Weissenberg film techniques and by four-circle X-ray single-crystal diffractometry. The new compounds crystallize with ternary derivative structures of BaAl₄, i.e., EuZn₂Si₂ with ThCr₂Si₂-type (a=0.42607(2) nm, c=1.03956(5) nm, I4/mmm, R₁=0.038) and EuZn₂Ge₂ with CaBe₂Ge₂-type (a=0.43095(2) nm, c=1.07926(6) nm, P4/nmm, R₁=0.067). XAS and magnetic measurements on EuZn₂Si₂ and EuZn₂Ge₂ revealed in both compounds the presence of Eu²⁺ ions carrying large magnetic moments, which order magnetically at low temperatures. The magnetic phase transition occurs at T_N=16 and 7.5 K for the silicide and the germanide, respectively. In EuZn₂Si₂ there occurs a spin reorientation at 13 K and furthermore some canting of antiferromagnetically ordered moments below about 10 K. In EuZn₂Ge₂ a canted antiferromagnetic structure is formed just at T_N.     

Mn-Na2WO4/SiO2催化剂表面活性中心结构的DFT研究

Mn Na2WO4/SiO2 is one of the best catalysts for oxidative coupling of methane.To investigate the nature of active centers and the reaction mechanism,the structure of possible metal sites formed by tungsten and manganese over the silica surface were studied using molecular simulation method and ab initio DFT calculations.Silica support exists in the catalyst as 岐瞔ristobalite and its (111) face exposes preferentially to the surface.The calculated results show that tungsten interacts with the silica surface by three or one bridge oxygen atoms to form tetrahedral [WO4],and manganese interacts with single bridge oxygen to form dispersed [MnO4] or exists as oxide clusters.The nature of the molecular orbitals and the electronic structure suggest that the tetrahedral [WO4] site with single bridge oxygen is the most probable active center responsible for methane activation.