| Li_(3.22)Na_(0.569)Mn_(5.78)O_(12.0)的电化学性能 |
| |
| 引用本文： | 童庆松,杨勇,连锦明. Li_(3.22)Na_(0.569)Mn_(5.78)O_(12.0)的电化学性能[J]. 电化学, 2005, 11(4): 435-439 |
| |
| 作者姓名： | 童庆松 杨勇 连锦明 |
| |
| 作者单位： | 福建师范大学化学与材料学院,厦门大学固体表面物理化学国家重点实验室,福建师范大学化学与材料学院 福建福州350007,厦门大学固体表面物理化学国家重点实验室,福建厦门361005,福建厦门361005,福建福州350007 |
| |
| 基金项目： | 全国教育科学规划项目;福建省自然科学基金 |
| |
| 摘 要： | 以L iOH.H2O和Mn(CH3COO)2.2H2O作原料,应用微波-固相两段烧结法合成具有L i4Mn5O12结构特征,组成为L i3.22Na0.569Mn5.78O12.0的锂离子电池正极材料.XRD分析表明,在380℃的后处理温度下,微波烧结前处理有利于生成纯L i4Mn5O12尖晶石相.充放电实验表明,在4.5~2.5V电压区间,新制样品的初始放电容量为132 mAh.g-1,100循环的容量衰减率为6.8%;4个月存放样的初始放电容量为122 mAh.g-1,100循环的容量衰减率为17.4%.表现出较好的充放电性能和循环寿命.微波烧结使样品的Mn-O键被加强.
|
| 关 键 词： | Li4Mn5O12 微波 可充性 |
| 文章编号： | 1006-3471（2005）04-0435-05 |
| 收稿时间： | 2005-06-06 |
| 修稿时间： | 2005-08-06 |
Electrochemical Performance of Li3.22Na0.569Mn5.78O12.0 |
| |
| TONG Qing-song,YANG Yong,LIAN Jin-ming. Electrochemical Performance of Li3.22Na0.569Mn5.78O12.0[J]. Electrochemistry, 2005, 11(4): 435-439 |
| |
| Authors: | TONG Qing-song YANG Yong LIAN Jin-ming |
| |
| Abstract: | By selecting LiOH·H_(2)O and Mn(CH_(3)COO)_(2)2H_(2)O as starting-materials,the positive materials with the structure characterization of Li_(4)Mn_(5)O_(12)and composition of Li_(3.22)Na_(0.569)Mn_(5.78)O_(12.0)were prepared by two-phase sintering method consisted of microwave and solid-state sintering processes.XRD patterns data showed that a pure Li_(4)Mn_(5)O_(12)phase was obtained by the fore-treatment of microwave sintering and the post-treatment of the solid-state sintering at 380℃.The charge-discharge tests showed that the newly prepared sample exhibited an initial capacity of 132 mAh·g~(-1)and its capacity faded after 100 cycles was 6.8% lower as compared with 1st cycle capacity in the voltage range of 4.5 to 2.5 V.The sample stored for 4 months exhibited an initial capacity of 122 mAh·g~(-1)and its capacity faded after 100 cycles was 17.4% lower than its 1st cycle capacity in the same voltage range.The Mn-O bond of the sample strengthened by microwave sintering process. |
| |
| Keywords: | Li4Mn5O12 |