| In-situ study of precipitates in Al–Zn–Mg–Cu alloys using anomalous small-angle x-ray scattering |
| |
| 引用本文： | 杨春明,边风刚,熊柏青,刘冬梅,李怡雯,滑文强,王劼. In-situ study of precipitates in Al–Zn–Mg–Cu alloys using anomalous small-angle x-ray scattering[J]. 中国物理 B, 2016, 25(6): 66101-066101. DOI: 10.1088/1674-1056/25/6/066101 |
| |
| 作者姓名： | 杨春明 边风刚 熊柏青 刘冬梅 李怡雯 滑文强 王劼 |
| |
| 作者单位： | 1.Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204, China;2.State Key Laboratory of Nonferrous Metals and Processes, General Research Institute for Nonferrous Metals, Beijing 100088, China |
| |
| 基金项目： | Project supported by the National Natural Science Foundation of China (Grant Nos. 11005143, 11405259, and 51274046) and the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry of China (Grant No. [2014]1685). |
| |
| 摘 要： | In the present work,the precipitate compositions and precipitate amounts of these elements(including the size distribution,volume fraction,and inter-precipitate distance) on the Cu-containing 7000 series aluminum alloys(7150 and 7085 Al alloys),are investigated by anomalous small-angle x-ray scattering(ASAXS) at various energies.The scattering intensity of 7150 alloy with T6 aging treatment decreases as the incident x-ray energy approaches the Zn absorption edge from the lower energy side,while scattering intensity does not show a noticeable energy dependence near the Cu absorption edge.Similar results are observed in the 7085 alloy in an aging process(120℃) by employing in-situ ASAXS measurements,indicating that the precipitate compositions should include Zn element and should not be strongly related to Cu element at the early stage after 10 min.In the aging process,the precipitate particles with an initial average size of ~ 8 ?A increase with aging time at an energy of 9.60 ke V,while the increase with a slower rate is observed at an energy of 9.65 ke V as near the Zn absorption edge.
|
| 收稿时间： | 2015-11-27 |
In-situ study of precipitates in Al-Zn-Mg-Cu alloys using anomalous small-angle x-ray scattering |
| |
| Affiliation: | 1.Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204, China;2.State Key Laboratory of Nonferrous Metals and Processes, General Research Institute for Nonferrous Metals, Beijing 100088, China |
| |
| Abstract: | In the present work, the precipitate compositions and precipitate amounts of these elements (including the size distribution, volume fraction, and inter-precipitate distance) on the Cu-containing 7000 series aluminum alloys (7150 and 7085 Al alloys), are investigated by anomalous small-angle x-ray scattering (ASAXS) at various energies. The scattering intensity of 7150 alloy with T6 aging treatment decreases as the incident x-ray energy approaches the Zn absorption edge from the lower energy side, while scattering intensity does not show a noticeable energy dependence near the Cu absorption edge. Similar results are observed in the 7085 alloy in an aging process (120℃) by employing in-situ ASAXS measurements, indicating that the precipitate compositions should include Zn element and should not be strongly related to Cu element at the early stage after 10 min. In the aging process, the precipitate particles with an initial average size of ～8Å increase with aging time at an energy of 9.60 keV, while the increase with a slower rate is observed at an energy of 9.65 keV as near the Zn absorption edge. |
| |
| Keywords: | anomalous small-angle x-ray scattering alloy precipitates |