Effect of Y2O3 on microstructural characteristics and wear resistance of cobalt‐based composite coatings produced on TA15 titanium alloy surface by laser cladding

The effects of Y₂O₃ on the microstructure, phase composition of the coatings, microhardness and wear resistance of cobalt‐based composite coatings prepared by laser cladding were investigated. The TA15 titanium alloy was selected as substrate which the cobalt‐based composite powder with different content of Y₂O₃ was cladded on. The microstructure of the coatings was observed by scanning electron microscope (SEM) and metallurgical microscope. The phase structure of the coatings was determined by X‐ray diffraction (XRD), and the microhardness and wear resistance of the coatings were measured by hardness tester and wear testing machine. The results show that the rare earth oxide Y₂O₃ can refine and purify the microstructure of the coatings, reduce the porosities and cracks and improve compactness of the coatings. Moreover the addition of Y₂O₃ improves the microhardness of the coatings and reduces the friction coefficient, thus improving the wear property of the coatings. And the wear resistance of the coating with Y₂O₃ has improved about 50 times; the highest value of microhardness in the coating is HV1181.1. And 0.8 wt% content of Y₂O₃ in the coating is the best choice for improving the microhardness and wear resistance of the coating. It is feasible to improve the microstructure and tribological properties of laser cladding coatings by adding of Y₂O₃. Copyright © 2014 John Wiley & Sons, Ltd.