| MCM-22和ITQ-2分子筛负载型催化剂加氢裂化性能的对比研究 |
| |
| 引用本文： | 刘百军,冯乐刚,侯辉娟,高山松,查显俊.MCM-22和ITQ-2分子筛负载型催化剂加氢裂化性能的对比研究[J].催化学报,2007,28(1):34-38. |
| |
| 作者姓名： | 刘百军 冯乐刚 侯辉娟 高山松 查显俊 |
| |
| 作者单位： | 1. 中国石油大学(北京)中国石油天然气集团公司催化重点实验室,北京,102249
2. 中国石油兰州石化公司思达公司精化厂,甘肃兰州,730060 |
| |
| 基金项目： | 国家重点基础研究发展计划(973计划,2004CB217805)，国家自然科学基金(20576077) |
| |
| 摘 要： | 以MCM-22和ITQ-2分子筛为载体, WNi为活性组分,制得两种负载型催化剂,考察了两种催化剂的加氢裂化性能,并通过N2吸附、氨程序升温脱附和原位红外光谱对催化剂进行了表征. 减压瓦斯油加氢裂化反应结果表明, WNi/ITQ-2的加氢裂化活性高于WNi/MCM-22, 并且前者的反应温度相对较低. WNi/ITQ-2具有高催化活性是因为ITQ-2分子筛具有空旷的次级结构和较多的可接近的酸性位; 中油选择性高是因为空旷的次级结构使裂化产物快速离开酸性位而避免了二次裂化.
|
| 关 键 词： | MCM-22分子筛 ITQ-2分子筛 钨 镍 减压瓦斯油 加氢裂化 次级结构 |
| 文章编号： | 0253-9837（2007）01-0034-05 |
| 收稿时间： | 2007-01-25 |
| 修稿时间： | 2006-07-04 |
Comparative Study on Hydrocracking over MCM-22 and ITQ-2 Zeolite-Supported Catalysts |
| |
| LIU Baijun,FENG Legang,HOU Huijuan,GAO Shansong,ZHA Xianjun.Comparative Study on Hydrocracking over MCM-22 and ITQ-2 Zeolite-Supported Catalysts[J].Chinese Journal of Catalysis,2007,28(1):34-38. |
| |
| Authors: | LIU Baijun FENG Legang HOU Huijuan GAO Shansong ZHA Xianjun |
| |
| Institution: | 1 Key Laboratory of Catalysis of CNPC, China University of Petroleum, Beijing 102249, China ; 2 Sida Refine Chemical Plant of Lanzhou Petrochemical Company, PetroChina, Lanzhou 730060, Gansu, China |
| |
| Abstract: | A series of supported WNi catalysts for hydrocracking of vacuum gas oil (VGO) were prepared using ITQ-2 and MCM-22 zeolites as supports. The catalysts were characterized by temperature-programmed desorption of ammonia, infrared spectroscopy of pyridine adsorption, and nitrogen adsorption. The acidities of WNi/MCM-22 and WNi/ITQ-2 catalysts were similar; but the surface area and pore volume of WNi/ITQ-2 were larger than those of WNi/MCM-22. The results of VGO hydrocracking indicated that WNi/ITQ-2 catalysts had higher catalytic activity and selectivity for middle distillates. The higher activity was due to the large secondary pore structure of the ITQ-2 zeolite and its rich accessible acidic centers. The reason for the higher selectivity was that products left acid centers rapidly and secondary cracking was avoided because of the large secondary structure. |
| |
| Keywords: | MCM-22 ITQ-2 tungsten nickel vaccum gas oil hydrocracking secondary structure |