用微波技术制备NiW/TiO2-Al2O3加氢脱硫催化剂
引用本文:刘百军,查显俊,孟庆民,侯辉娟,高山松,张金霞,盛世善,杨维慎.用微波技术制备NiW/TiO2-Al2O3加氢脱硫催化剂[J].催化学报,2005,26(6):458-462.
作者姓名:刘百军  查显俊  孟庆民  侯辉娟  高山松  张金霞  盛世善  杨维慎
作者单位:1. 石油大学,北京,中国石油天然气集团公司催化重点实验室,北京,102249
2. 中国科学院大连化学物理研究所催化基础国家重点实验室,辽宁大连,116023
基金项目:国家重点基础研究发展计划(973计划);国家重点实验室基金
摘    要: 采用微波技术制备了NiW/TiO2-Al2O3加氢脱硫催化剂,并用NH3-TPD,Py-FT-IR,TPR和TPS(程序升温硫化)对催化剂进行了表征; 以噻吩为模型化合物,在中压固定床微反装置上考察了催化剂的加氢脱硫性能. 结果表明,在w(TiO2)=15%的催化剂样品中,微波处理的催化剂的活性比常规催化剂高. 微波处理改变了载体和催化剂表面的酸性质,催化剂样品表面的强酸酸量减少,弱酸和中强酸酸量增加. 微波处理的催化剂的还原性能和硫化性能均好于常规法制备的催化剂. 这可能是微波技术制备的催化剂具有较高加氢脱硫活性的原因.

关 键 词:微波  氧化镍  氧化钨  氧化钛  氧化铝  负载型催化剂  噻吩  加氢脱硫
文章编号:0253-9837(2005)06-0458-05
收稿时间:2005-06-25

Preparation of NiW/TiO2-Al2O3 Hydrodesulfurization Catalyst with Microwave Technique
LIU Baijun,ZHA Xianjun,MENG Qingmin,HOU Huijuan,GAO Shansong,Zhang Jinxia,SHENG Shishan,YANG Weishen.Preparation of NiW/TiO2-Al2O3 Hydrodesulfurization Catalyst with Microwave Technique[J].Chinese Journal of Catalysis,2005,26(6):458-462.
Authors:LIU Baijun  ZHA Xianjun  MENG Qingmin  HOU Huijuan  GAO Shansong  Zhang Jinxia  SHENG Shishan  YANG Weishen
Abstract:The NiW/TiO_2-Al_2O_3 catalyst samples were prepared by conventional drying method (CON-Cat) and by microwave irradiation method (MW-Cat and MW-Cat1). The catalyst samples were characterized with NH_3-temperature-programmed desorption, Py-FT-IR, temperature-programmed reduction, and temperature-programmed sulfurization techniques. The hydrodesulfurization (HDS) reactivity of thiophene over them was studied in a fixed-bed microreactor. The thiophene conversion over MW-Cat increased from 70.9% at 16 h to 71.8% at 19 h, while the thiophene conversion over MW-Cat1 kept to 71% after 17 h and then increased very slowly. The HDS reactivity over CON-Cat increased slowly after 15 h and the thiophene conversion increased from 63.3% at 15 h to 69.4% at 19 h. The activity difference between CON-Cat and MW-Cat was due to the different sulfidation performance. MW-Cat or MW-Cat1 could be sulfided to some extent by using shorter time than CON-Cat. The surface acidic properties of MW-Cat and MW-Cat1 were changed with microwave irradiation power and time. The amounts of weak and medium acid sites in MW-Cat and MW-Cat1 increased, while that of strong acid sites decreased. The strength order of weak and medium acids was MW-Cat
Keywords:microwave  nickel oxide  tungsten oxide  titania  alumina  supported catalyst  thiophene  hydrodesulfurization