Time‐Resolved Phase Transitions of the Nanocrystalline Cubic to Submicron Monoclinic Phase in Zirconia

The nanocrystalline cubic, tetragonal, and submicron monoclinic phases of pure zirconia were prepared by thermal decomposition of carbonate and hydroxide precursors. The crystallization and isothermal phase transformations of the oxide were studied using high temperature X‐ray diffraction, X‐ray diffraction and Raman spectra of quenched samples. Cubic zirconia formed first, and then progressively transformed to tetragonal and monoclinic phases at temperatures as low as 320°C. The cubic, tetragonal, and monoclinic phases for ZrO₂ were found to be distinct functions of crystallite size, indicating the nanocrystalline nature of these phases. They were found to exist within critical size ranges of 50 to 140 Å, 100 to 220 Å and 190 to 420 Å (±5 Å), respectively. Thus, as the crystallites grow during annealing, they first transform from cubic to tetragonal and then from tetragonal to monoclinic at critical sizes. The classical Avrami equation for nucleation and growth was applied to the tetragonal to monoclinic phase transition.