Barium Sodium Niobate Powders and Thin Films: Preparation and Ferroelectric Behavior

Powders and thin films of barium sodium niobate, Ba₄Na₂Nb₁₀O₃₀, of filled tungsten bronze type ferroelectric were processed by a sol-gel route using barium metal, niobium ethoxide and sodium methoxide as precursors. Polycrystalline powder resulted after heat treating the gel powder at or above 650°C. Thin films of Ba₄Na₂Nb₁₀O₃₀ showed no preferred orientation on Si(100), Pt/Si(100) and sapphire substrates. Hysteresis measurements at 1 kHz for the thin films annealed at 750°C, obtained using a prehydrolyzed precursor solution, and gave remanent polarization of 17.34 µC/cm² and coercive field of 62.5 kV/cm. Microstructural investigation of surface morphology of these films revealed grains about 0.3 µm in size. Prehydrolysis of the precursor solution was found to be necessary to achieve dense films with ferroelectric properties.