Preparation of TiO2 Thin Film Photocatalysts by Dip Coating Using a Highly Viscous Solvent

TiO₂ thin film photocatalysts coated onto soda lime glass were prepared by a dip coating process using a highly viscous solvent. The source of the TiO₂ was tetraisopropyl orthotitanate, and -terpineol was used as the solvent. Two types of thin film preparation procedures based on dip coating (a sol-gel system and thermal decomposition system) were used to prepare the samples. TiO₂ thin films were obtained after calcination at 450°C for 1 hour. The film thickness obtained with a single dipping was proportional to the viscosity of the dip coating solutions. The obtained thin films were transparent with a thickness of 1 m. The crystal form of the obtained photocatalyst films was anatase alone. The thin films were formed with aggregated nano-sized TiO₂ single crystals (7–15 nm). The photocatalytic activity of the TiO₂ thin films, as evaluated by the photooxidation of NO (1 ppm) in dry air, was as high as our previous TiO₂ thin films prepared by the sol-gel method.