Electrochemical performance of a nano SnO2-modified LiNi1/3Co1/3Mn1/3O2 cathode material

The nano SnO₂-modified LiNi_1/3Co_1/3Mn_1/3O₂ was successfully prepared by a carrier transfer method. The pristine and modified samples were characterized with various techniques such as XRD, SEM, XPS and EDS. The results showed that the SnO₂ particles did not enter the crystal structure of LiNi1/3Co1/ 3Mn1/3O₂, many nano SnO₂ particles were uniformly covered on the surface of LiNi_1/3Co_1/3Mn_1/3O₂ and the modified thin layer could inhibit the dissolution of transition metal oxides. The electrochemical tests indicated that the existence of nano SnO₂ could improve the discharge capacity and rate capability owing to the decreased interfacial polarization. The cycling stability was remarkably improved at room temperature and 55 ℃. The XRD patterns of the fresh NCM electrode and after 50 cycles proved that the structural change of NCM was not so effective on the capacity fade.