| MgO/Al_2O_3吸附剂对CO_2动态吸附性能的研究 | |
| 引用本文： | 闻霞,孙楠楠,李碧,李军平,王峰,赵宁,肖福魁,魏伟,孙予罕,任泽厚,郭金刚,王志杰,李庆,吴志斌.MgO/Al_2O_3吸附剂对CO_2动态吸附性能的研究[J].燃料化学学报,2010,38(2). |
| 作者姓名： | 闻霞 孙楠楠 李碧 李军平 王峰 赵宁 肖福魁 魏伟 孙予罕 任泽厚 郭金刚 王志杰 李庆 吴志斌 |
| 作者单位： | 1. 中国科学院,山西煤炭化学研究所,山西,太原,030001;中国科学院研究生院,北京,100049 2. 中国科学院,山西煤炭化学研究所,山西,太原,030001 3. 山西潞安矿业(集团)有限责任公司,山西,长治,046204 |
| 基金项目： | 中国科学院山西煤炭化学研究所知识创新工程领域前沿项目，山西潞安矿业(集团)有限责任公司 |
| 摘 要： | 以γ-Al2O3为载体,采用等体积浸渍法制取MgO/Al2O3吸附剂,利用BET、XRD等表征手段对吸附剂进行表征;并通过固定床测量穿透曲线的方法研究其对CO2动态吸附性能的影响,考察了MgO负载量、吸附温度、气体流量等因素对吸附剂吸附CO2性能的影响,同时还通过多次吸脱附实验考察MgO/Al2O3吸附剂的稳定性和再生能力。结果表明,MgO负载量为10%的吸附剂,吸附温度在50℃左右,流量为45 mL/min动态吸附量最大;经数次循环后材料的结构性质和吸附性能未见明显变化,可再生性能比较优异,是一种潜在的可工业化应用的CO2吸附剂。 |
| 关 键 词： | 固定床 吸附量 穿透曲线 |
Dynamic adsorption study of CO_2 adsorption by MgO/Al_2O_3 |
|
| WEN Xia,SUN Nan-nan,LI Bi,LI Jun-ping,WANG Feng,ZHAO Ning,XIAO Fu-kui,WEI Wei,SUN Yun-han,REN Ze-hou,GUO Jin-gang,WANG Zhi-jie,LI Qing,WU Zhi-bin.Dynamic adsorption study of CO_2 adsorption by MgO/Al_2O_3[J].Journal of Fuel Chemistry and Technology,2010,38(2). | |
| Authors: | WEN Xia SUN Nan-nan LI Bi LI Jun-ping WANG Feng ZHAO Ning XIAO Fu-kui WEI Wei SUN Yun-han REN Ze-hou GUO Jin-gang WANG Zhi-jie LI Qing WU Zhi-bin |
| Institution: | WEN Xia1,2,SUN Nan-nan1,LI Bi1,LI Jun-ping1,WANG Feng1,ZHAO Ning1,XIAO Fu-kui1,WEI Wei1,SUN Yun-han1,REN Ze-hou3,GUO Jin-gang3,WANG Zhi-jie3,LI Qing3,WU Zhi-bin3(1.Institute of Coal Chemistry,Chinese Academy of Sciences,Taiyuan 030001,China,2.Graduate University of Chinese Academy of Sciences,Beijing 100049,3.Lu\'an Mining Industry Group Co.Ltd.,Changzhi 046204,China) |
| Abstract: | A MgO/Al2O3 adsorbent prepared with impregnation method was characterized by using N2-adsorption and XRD,and its CO2 kinetic sorption properties were studied by means of breakthrough analysis in a fixed bed flow adsorber.The effects of MgO loadings,adsorption temperatures and gas flow rates were investigated.The stability and regenerative abilities were studied by cyclic experiment.The results indicated that the optimal loading of MgO was 10%,the maximal adsorption capacities were achieved when the temperat... |
| Keywords: | CO_2 MgO/Al_2O_3 carbon dioxide fixed-bed adsorption capacities breakthrough curves MgO/Al_2O_3 |