Die Perthioborate RbBS3, TIBS3 und TI3B3S10

The Perthioborates RbBS₃, TIBS₃, and Tl₃B₃S₁₀ . RbBS₃ (P2₁/c, a=7.082(2) Å, b=11.863(4) Å, c=5.794(2) Å, β=106.54(2)°) was prepared as colourless, plate-shaped crystals by reaction of stoichiometric amounts of rubidium sulfide, boron, and sulfur at 600°C and subsequent annealing. TlBS₃ (P2₁/c, a=6.874(3) Å, b=11.739(3) Å, c=5.775(2) Å, β=113.08(2)°) which is isotypic with RbBS₃ was synthesized from a sample of the composition Tl₂S · 2 B₂S₃. The glassy product which was obtained after 7 h at 850°C was annealed in a two zone furnace for 400 h at 400→350°C. Yellow crystals of TlBS₃ formed at the warmer side of the furnace. Tl₃B₃S₁₀ (P1 , a=6.828(2) Å, b=7.713(2) Å, c=13.769(5) Å, α=104.32(2)°, β=94.03(3)°, γ=94.69(2)°) was prepared as yellow plates from stoichiometric amounts of thallium sulfide, boron, and sulfur at 850°C and subsequent annealing. All compounds contain tetrahedrally coordinated boron. The crystal structures consist of polymeric anion chains. In the case of RbBS₃ and TlBS₃ nonplanar five-membered B₂S₃ rings are spirocyclically connected via the boron atoms. To obtain the anionic structure of Tl₃B₃S₁₀ every third B₂S₃ ring of the polymeric chains of MBS₃ is to be substituted by a six-membered B(S₂)₂B ring.