Luminescent Nitridophosphates CaP2N4:Eu2+, SrP2N4:Eu2+, BaP2N4:Eu2+, and BaSr2P6N12:Eu2+

Nitridophosphates MP₂N₄:Eu²⁺ (M=Ca, Sr, Ba) and BaSr₂P₆N₁₂:Eu²⁺ have been synthesized at elevated pressures and 1100–1300 °C starting from the corresponding azides and P₃N₅ with EuCl₂ as dopant. Addition of NH₄Cl as mineralizer allowed for the growth of single crystals. This led to the successful structure elucidation of a highly condensed nitridophosphate from single‐crystal X‐ray diffraction data (CaP₂N₄:Eu²⁺ (P6₃, no. 173), a=16.847(2), c=7.8592(16) Å, V=1931.7(6) ų, Z=24, 2033 observed reflections, 176 refined parameters, wR₂=0.096). Upon excitation by UV light, luminescence due to parity‐allowed 4f⁶(⁷F)5d¹→4f⁷(⁸S_7/2) transition was observed in the orange (CaP₂N₄:Eu²⁺, λ_max=575 nm), green (SrP₂N₄:Eu²⁺, λ_max=529 nm), and blue regions of the visible spectrum (BaSr₂P₆N₁₂:Eu²⁺ and BaP₂N₄:Eu²⁺, λ_max=450 and 460 nm, respectively). Thus, the emission wavelength decreases with increasing ionic radius of the alkaline‐earth ions. The corresponding full width at half maximum values (2240–2460 cm^?1) are comparable to those of other known Eu²⁺‐doped (oxo)nitrides emitting in the same region of the visible spectrum. Following recently described quaternary Ba₃P₅N₁₀Br:Eu²⁺, this investigation represents the first report on the luminescence of Eu²⁺‐doped ternary nitridophosphates. Similarly to nitridosilicates and related oxonitrides, Eu²⁺‐doped nitridophosphates may have the potential to be further developed into efficient light‐emitting diode phosphors.