Cathodic carboxylation of gold in thick {Au-CO2}n layers. A model for reversible electrochemical sequestration of CO2

Catalytic reduction of CO₂ (saturated in organic polar solvents, e.g. N,N-dimethylfomamide, containing Me₄NX or NaBF₄) was achieved at smooth gold electrodes and at glassy carbon electrodes galvanostatically capped with a thin layer of gold. Under these quite explicit conditions, very sharp reduction steps were observed near − 1.5 V vs. Ag/AgCl. With small cations listed above, an unexpected behavior was observed, a progressive electrode inhibition occurring upon several scans or after a fixed-potential electrolysis at E < − 1.7 V. This phenomenon could be attributed to the insertion of CO₂ into gold, leading to the formation of a thick iono-metallic multi-strata layer (less conducting than pure metal) that grows with the electrode charge. The formation of this new interface is due to the concur of three elements: transient CO₂ anion radical, the metal, and rather small-sized cations (M⁺ = Na⁺ or TMA⁺), the three possibly associated in a form {Au-CO₂⁻,M⁺} apparently very reactive with oxygen, moisture, and with some organic π-acceptors. Upon multi-scans up to − 2.2 V, the thickness of formed layer progressively increases reaching more than 10^− 7 to 10^− 6 mol cm^− 2. Such multi-layers undergo decomposition in the anodic domain at about + 1.7 V liberating CO₂ beforehand trapped in Au. Coulometric analyses demonstrated that insertion (cathodic) and release (anodic) steps are quite equivalent, which permits to consider this process as chemically reversible sequestration of carbon dioxide.