Structural and electrochemical properties of a porous nanostructured SnO2 film electrode for lithium-ion batteries

A B₂O₃-doped SnO₂ thin film was prepared by a novel experimental procedure combining the electrodeposition and the hydrothermal treatment, and its structure and electrochemical properties were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) analysis, energy dispersive X-ray (EDX) spectroscopy and galvanostatic charge–discharge tests. It was found that the as-prepared modified SnO₂ film shows a porous network structure with large specific surface area and high crystallinity. The results of electrochemical tests showed that the modified SnO₂ electrode presents the largest reversible capacity of 676 mAh g^?1 at the fourth cycle, close to the theoretical capacity of SnO₂ (790 mAh g^?1); and it still delivers a reversible Li storage capacity of 524 mAh g^?1 after 50 cycles. The reasons that the modified SnO₂ film electrode shows excellent electrochemical properties were also discussed.