Preparation and Electrochemical Performance of V2O3-C Dual-Layer Coated LiFePO4 by Carbothermic Reduction of V2O5

The V₂O₃-C dual-layer coated LiFePO₄ cathode materials with excellent rate capability and cycling stability were prepared by carbothermic reduction of V₂O₅. X-ray powder diffraction, elemental analyzer, high resolution transmission electron microscopy and Raman spectra revealed that the V₂O₃ phase co-existed with carbon in the coating layer of LiFePO₄ particles and the carbon content reduced without graphitization degree changing after the carbothermic reduction of V₂O₅. The electrochemical measurement results indicated that small amounts of V₂O₃ improved rate capability and cycling stability at elevated temperature of LiFePO₄/C cathode materials. The V₂O₃-C dual-layer coated LiFePO₄ composite with 1wt% vanadium oxide delivered an initial specific capacity of 167 mAh/g at 0.2 C and 129 mAh/g at 5 C as well as excellent cycling stability. Even at elevated temperature of 55 oC, the specific capacity of 151 mAh/g was achieved at 1 C without capacity fading after 100 cycles.