| 不同电解质溶液对聚吡咯修饰膜性质的影响 |
| |
| 引用本文： | 田颖,李浙齐,徐洪峰,吴艳波,杨凤林.不同电解质溶液对聚吡咯修饰膜性质的影响[J].物理化学学报,2008,24(4):612-618. |
| |
| 作者姓名： | 田颖 李浙齐 徐洪峰 吴艳波 杨凤林 |
| |
| 作者单位： | College of Environmental and Chemical Engineering, Dalian Jiaotong University, Dalian 116028, Liaoning Province, P. R. China; Department of Environmental Science and Technology, Dalian University of Technology, Dalian 116024, Liaoning Province, P. R. China |
| |
| 摘 要： | 以对甲基苯磺酸钠(p-TSNa)为掺杂剂在不锈钢电极表面恒电位合成聚吡咯(PPy)修饰膜, 采用循环伏安法在-1.6 - 0.8 V大范围扫描研究了修饰膜在H2SO4、Na2SO4、NaOH电解质溶液中的氧化还原行为. 结果表明, 在H2SO4溶液中, 以H+的脱出(氧化)/嵌入(还原)为特征, 并发现聚吡咯在酸性溶液中所特有的质子还原峰. 在Na2SO4和NaOH溶液中, 以Na+的脱出(氧化)/嵌入(还原)峰为特征. FT-IR吸收光谱显示, 经NaOH处理后, 聚吡咯膜的长共轭结构被完全破坏, 而经H2SO4和Na2SO4处后, 膜的共轭结构未发生变化.
|
| 关 键 词： | 聚吡咯 氧化还原行为 电解质溶液 FT-IR |
| 收稿时间： | 2007-11-28 |
| 修稿时间： | 2007年11月28 |
Effects of Different Electrolyte Solutions on Characteristics of Polypyrrole-Modified Films |
| |
| TIAN Ying,LI Zhe-Qi,XU Hong-Feng,WU Yan-Bo,YANG Feng-Lin.Effects of Different Electrolyte Solutions on Characteristics of Polypyrrole-Modified Films[J].Acta Physico-Chimica Sinica,2008,24(4):612-618. |
| |
| Authors: | TIAN Ying LI Zhe-Qi XU Hong-Feng WU Yan-Bo YANG Feng-Lin |
| |
| Institution: | College of Environmental and Chemical Engineering, Dalian Jiaotong University, Dalian 116028, Liaoning Province, P. R. China; Department of Environmental Science and Technology, Dalian University of Technology, Dalian 116024, Liaoning Province, P. R. China |
| |
| Abstract: | Polypyrrole (PPy) films were synthesized by potentiolstatic method froma para-toluenesulfonic sodium (p-TSNa) solution on stainless steel. Cyclic voltammetry of PPy-modified electrodes in the wide potential range from -1.6 to 0.8 V was conducted in H2SO4, Na2SO4, and NaOH solutions, respectively. The results showed that cyclic voltammogramin H2SO4 solution was featured by H+ insertion during reduction process and H+ expulsion during oxidation process. A unique peak associated to H+ reduction was first discovered. In Na2SO4 and NaOH solutions, cyclic voltammograms are featured by Na+ insertion during reduction process and Na+ expulsion during oxidation process. The data of FT-IR absorption spectra demonstrated that NaOH treatment had made extensive structure degradation, but Na2SO4 and H2SO4 treatments had not made conjugated structure changes on PPy films. |
| |
| Keywords: | Polypyrrole Redox behavior Electrolyte solutions FT-IR |