单分散SiO2的焙烧温度对Rh基催化剂上CO加氢反应性能的影响
引用本文:俞俊,毛东森,郭强胜,韩璐蓬,卢冠忠.单分散SiO2的焙烧温度对Rh基催化剂上CO加氢反应性能的影响[J].物理化学学报,2012,28(3):667-673.
作者姓名:俞俊  毛东森  郭强胜  韩璐蓬  卢冠忠
作者单位:1. Research Institute of Industrial Catalysis, East China University of Science and Technology, Shanghai 200237, P. R. China; 2. Research Institute of Applied Catalysis, Shanghai Institute of Technology, Shanghai 201418, P. R. China
基金项目:上海市科委(08520513600);上海市教委重点学科建设(J51503);上海市优秀青年教师专项基金(yyy10083)资助项目~~
摘    要:在比较了分别以商业SiO2和采用Sto?ber法制备的单分散SiO2为载体的Rh-Mn-Li/SiO2催化剂催化CO加氢反应性能的基础上,进一步调变了Stober法制备SiO2时的焙烧温度,并考察了其对Rh-Mn-Li/SiO2催化CO加氢性能的影响.利用N2吸附-脱附、傅里叶变换红外(FTIR)光谱、H2程序升温还原(H2-TPR)、程序升温表面反应(TPSR)等方法对载体及催化剂的物理化学性能进行了表征.结果表明:不同温度焙烧的载体表面具有不同的Si―OH数量,从而影响金属的分散状态及Rh和Mn之间的相互作用.载体表面较多的羟基有利于Rh的分散和CO的吸附,从而增强催化剂的反应活性.载体表面适当数量的羟基能够得到适中的Rh与Mn之间的相互作用,使催化剂具有合适的CO解离能力,有利于CHx的CO插入反应,从而提高了C2含氧化合物的选择性.

关 键 词:Rh-Mn-Li/SiO2  CO加氢  C2含氧化合物  焙烧温度  
收稿时间:2011-10-11
修稿时间:2011-12-22

Effect of Calcination Temperature of Monodispersed SiO2 on the Performance of Rh-Based Catalysts for CO Hydrogenation
YU Jun,MAO Dong-Sen,GUO Qiang-Sheng,HAN Lu-Peng,LU Guan-Zhong.Effect of Calcination Temperature of Monodispersed SiO2 on the Performance of Rh-Based Catalysts for CO Hydrogenation[J].Acta Physico-Chimica Sinica,2012,28(3):667-673.
Authors:YU Jun  MAO Dong-Sen  GUO Qiang-Sheng  HAN Lu-Peng  LU Guan-Zhong
Institution:1. Research Institute of Industrial Catalysis, East China University of Science and Technology, Shanghai 200237, P. R. China; 2. Research Institute of Applied Catalysis, Shanghai Institute of Technology, Shanghai 201418, P. R. China
Abstract:Based on a comparison of catalytic performances of Rh-Mn-Li/SiO 2 catalysts,in which commercial SiO 2 and monodispersed SiO 2 synthesized by the Stober method were used as the support, respectively,the effect of the calcination temperature of the synthesized SiO 2 on the catalytic performance of Rh-Mn-Li/SiO 2 for CO hydrogenation to C 2 oxygenates was investigated.Fourier transform infrared spectroscopy,N 2 adsorption-desorption,temperature-programmed reduction with hydrogen(H 2 -TPR),and temperature-programmed surface reaction(TPSR)were used to characterize the physico-chemical properties of the SiO 2 supports and the corresponding catalysts.The results showed that the number of surface Si―OH groups on the SiO 2 supports affected the dispersion of metal and the interaction between Rh and Mn.Large amount of surface Si―OH groups was favorable for the dispersion of Rh particles and CO adsorption,and enhanced the activity of the catalyst.An appropriate amount of Si―OH groups can gain moderate interaction between the Rh and Mn.This interaction is conducive to achieve the right CO dissociation ability,which is favorable for the insertion of CO to CH x ,and ultimately increases the selectivity of C 2 oxygenates.
Keywords:Rh-Mn-Li/SiO 2  CO hydrogenation  C 2 oxygenate  Calcination temperature