Mechanochemical synthesis and thermal stability of phases in the Y2O3–Yb2O3 system

Substitutional, continuous solid solution of the general formula Y_2–xYb_xO₃ was obtained from the mixture of Y₂O₃ and Yb₂O₃ oxides, for the first time by the mechanochemical method in a high-energy ball milling. The monophasic samples of nanocrystalline solid solution for x?>?0.00 and x?<?2.00 were examined by the methods: XRD, DTA, SEM, IR and UV–Vis–DR. As follows from the results, the solid solution crystallizes in cubic system and is isostructural with Y₂O₃ and Yb₂O₃. The solution is stable in the air atmosphere up to at least 900°C, and its decomposition temperature decreases with the increase in x, that is, with decreasing number of Yb³⁺ ions replacing Y³⁺ ions in the crystal lattice of Y₂O₃. The energy band gap estimated for the solid solution varies from?~?5.30 eV for x?=?0.50 to?~?4.90 eV for x?=?1.50, which means that it is an insulator.