Thermal stability, Judd-Ofelt theory analysis and spectroscopic properties of a new Er3+/Yb3+-codoped germano-tellurite glass

The Er3+/Yb3+-codoped 70TeO2-5Li2O-10B2O3-15GeO2 glass was prepared. The thermal stability, absorption spectra, emission spectra and up-conversion spectra were measured and investigated. The Judd-Ofelt analysis based on absorption spectra was performed in order to determine the Judd-Ofelt intensity parameters Omega(t) (t = 2, 4, 6), spontaneous emission probability, radiative lifetime and branching ratios of several Er3+ transitions. It was found that this studied glass has good thermal stability, broad fluorescence full width at half maximum (FWHM), large stimulated emission cross-section and strong up-conversion emissions at about 532, 546 and 659 nm, corresponding to the 2H(11/2)-->4I(15/2), 4S(3/2)-->4I(15/2) and 4F(9/2)-->4I(15/2) transitions of Er3+, respectively under the excitation at 970 nm. The results suggest that this Er3+/Yb3+-codoped germano-tellurite glass may be a potentially useful material for developing potential amplifiers and up-conversion optical devices.