Fast Li-Ion Conduction in Spinel-Structured Solids

Spinel-structured solids were studied to understand if fast Li⁺ ion conduction can be achieved with Li occupying multiple crystallographic sites of the structure to form a “Li-stuffed” spinel, and if the concept is applicable to prepare a high mixed electronic-ionic conductive, electrochemically active solid solution of the Li⁺ stuffed spinel with spinel-structured Li-ion battery electrodes. This could enable a single-phase fully solid electrode eliminating multi-phase interface incompatibility and impedance commonly observed in multi-phase solid electrolyte–cathode composites. Materials of composition Li_1.25M(III)_0.25TiO₄, M(III) = Cr or Al were prepared through solid-state methods. The room-temperature bulk Li⁺-ion conductivity is 1.63 × 10⁻⁴ S cm⁻¹ for the composition Li_1.25Cr_0.25Ti_1.5O₄. Addition of Li₃BO₃ (LBO) increases ionic and electronic conductivity reaching a bulk Li⁺ ion conductivity averaging 6.8 × 10⁻⁴ S cm⁻¹, a total Li-ion conductivity averaging 4.2 × 10⁻⁴ S cm⁻¹, and electronic conductivity averaging 3.8 × 10⁻⁴ S cm⁻¹ for the composition Li_1.25Cr_0.25Ti_1.5O₄ with 1 wt. % LBO. An electrochemically active solid solution of Li_1.25Cr_0.25Mn_1.5O₄ and LiNi_0.5Mn_1.5O₄ was prepared. This work proves that Li-stuffed spinels can achieve fast Li-ion conduction and that the concept is potentially useful to enable a single-phase fully solid electrode without interphase impedance.