Synthesis, crystal structure and magnetic properties of the Sr2Al0.78Mn1.22O5.2 anion-deficient layered perovskite

A new layered perovskite Sr₂Al_0.78Mn_1.22O_5.2 has been synthesized by solid state reaction in a sealed evacuated silica tube. The crystal structure has been determined using electron diffraction, high-resolution electron microscopy, and high-angle annular dark field imaging and refined from X-ray powder diffraction data (space group P4/mmm, a=3.89023(5) Å, c=7.8034(1) Å, R_I=0.023, R_P=0.015). The structure is characterized by an alternation of MnO₂ and (Al_0.78Mn_0.22)O_1.2 layers. Oxygen atoms and vacancies, as well as the Al and Mn atoms in the (Al_0.78Mn_0.22)O_1.2 layers are disordered. The local atomic arrangement in these layers is suggested to consist of short fragments of brownmillerite-type tetrahedral chains of corner-sharing AlO₄ tetrahedra interrupted by MnO₆ octahedra, at which the chain fragments rotate over 90°. This results in an averaged tetragonal symmetry. This is confirmed by the valence state of Mn measured by EELS. The relationship between the Sr₂Al_0.78Mn_1.22O_5.2 tetragonal perovskite and the parent Sr₂Al_1.07Mn_0.93O₅ brownmillerite is discussed. Magnetic susceptibility measurements indicate spin glass behavior of Sr₂Al_0.78Mn_1.22O_5.2. The lack of long-range magnetic ordering contrasts with Mn-containing brownmillerites and is likely caused by the frustration of interlayer interactions due to presence of the Mn atoms in the (Al_0.78Mn_0.22)O_1.2 layers.