The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, RF²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, RF²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks O-Hg-Hg-O] for the mercurous compound, and O-Hg-Hg-O] and O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.