A novel boron-rich quaternary scandium borocarbosilicide Sc3.67−xB41.4−y−zC0.67+zSi0.33−w

A novel quaternary scandium borocarbosilicide Sc_3.67−xB_41.4−y−zC_0.67+zSi_0.33−w was found. Single crystallites were obtained as an intergrowth phase in the float-zoned single crystal of Sc_0.83−xB_10.0−yC_0.17+ySi_0.083−z that has a face-centered cubic crystal structure. Single crystal structure analysis revealed that the compound has a hexagonal structure with lattice constants a = b = 1.43055(8) nm and c = 2.37477(13) nm and space group (No. 187). The crystal composition calculated from the structure analysis for the crystal with x = 0.52, y = 1.42, z = 1.17, and w = 0.02 was ScB_12.3C_0.58Si_0.10 and that agreed rather well with the composition of ScB_11.5C_0.61Si_0.04 measured by EPMA. In the crystal structure that is a new structure type of boron-rich borides, there are 79 structurally independent atomic sites, 69 boron and/or carbon sites, two silicon sites and eight scandium sites. Boron and carbon form seven structurally independent B₁₂ icosahedra, one B₉ polyhedron, one B₁₀ polyhedron, one irregularly shaped B₁₆ polyhedron in which only 10.7 boron atoms are available because of partial occupancies and 10 bridging sites. All polyhedron units and bridging site atoms interconnect each other forming a three-dimensional boron framework structure. Sc atoms reside in the open spaces in the boron framework structure.