Phase relationships of the lithium halide spinels Li2MCl4-Li2MBr4 with M = Mn,Fe, Cd

The sections Li₂MCl_4?4xBr_4x of the quaternary systems LiCl-LiBr-MCl₂-MBr₂ with M = Mn, Cd, and Fe were studied by high-temperature X-ray diffraction patterns and DTA and DSC measurements. In the quasibinary lithium manganese halide system complete series of solid solutions exist between the inverse spinels Li₂MnCl₄ and Li₂MnBr₄. Li₂MnBr₄ and solid solutions with x > 0.54 undergo phase transitions to tetragonal spinels at lower temperatures. In the nonquasibinary system with M = Cd, only at temperatures near 400°C a complete series of mixed crystals is formed. At lower temperatures the system is mainly two-phase with rock salt-type Li_1?yCd_0.5yCl_1?xBr_x and cadmium chloride-type Cd_1?yLi_2yCl_2?2xBr_2x solid solutions in equilibrium. The lithium iron halide system is similar to that of cadmium, but spinel-type Li₂FeBr₄ does not exist at any temperature. The manganese and cadmium halide spinels and spinel solid solutions undergo phase transitions to NaCl defect structures at elevated temperatures.