Intramolecular cyclization of styrene–p-divinylbenzene copolymers

Styrene has been copolymerized at low conversion with minor quantities of p-divinyl-benzene (p-DVB) in (10–15%) solution in toluene and cyclohexane. Under these conditions the molecular weight of the polystyrene formed in the absence of p-DVB was controlled by chain transfer, and the copolymerization coefficients of the styrene and the p-DVB agreed with previous work. Polymer molecular weights were studied as a function of conversion. At very low conversions the number-average (2.2 × 10⁵) and the weight-average (4.4 × 10⁵) molecular weights were unaffected by substituting some of the styrene by p-DVB, but as the reaction continued M?_n increased slowly and M?_w much faster. On the other hand, even at the lowest conversions the intrinsic viscosity was drastically reduced by the introduction of p-DVB, and the radius of gyration, as measured by light scattering, fell. Infrared studies on the polymer show that the concentration of pendent double bonds in low-conversion copolymers is about half of the doubly substituted phenyl groups. It is concluded that the first polymer chains formed are extensively cyclized with the formation of a relatively large number of small rings.