Crystallization kinetics of the monoclinic modification of poly(3,3-dimethyl oxetane)

Poly(3,3-dimethyl oxetane) fractions ranging in number average molecular weights from 18500 to 130000 have been isothermally crystallized from the relaxed melt state in the temperature range from 12 to 44 °C, where only the monoclinic modification is formed. The influence of molecular weight and undercooling in crystallization kinetics has been analyzed. The level of crystallinity is very slightly dependent on molecular weight but the influence of this parameter on the time scale of the crystallization is relatively pronounced. The crystallization temperature coefficient was determined and it was found a constant value of the product of the interfacial energies in the range of molecular weights which has been analyzed. Growth rate measurements were carried out for fraction ¯M _n=130000 and it was found that the temperature coefficients for overall and growth rates are equal. Finally, the comparison of the experimental results for this polymer with those reported for poly(oxetane) shows two main differences: first, the crystallization rate is slower for poly(3,3-dimethyl oxetane) and second, the temperature coefficient is smaller for this polymer.