Y2O3/纳米碳管复合粒子的结构及其对高氯酸铵热分解性能的研究
引用本文:周龙梅,侯立权,刘宏英,李凤生.Y2O3/纳米碳管复合粒子的结构及其对高氯酸铵热分解性能的研究[J].化学学报,2006,64(15):1548-1552.
作者姓名:周龙梅  侯立权  刘宏英  李凤生
作者单位:扬州技师学院 扬州225003(周龙梅),北京新东方扬州外国语学院 扬州225003(侯立权),南京理工大学国家特种超细粉体工程技术研究中心 南京210094(刘宏英,李凤生)
摘    要:采用溶胶-凝胶法制备了Y2O3/纳米碳管复合粒子, 并用SEM, XPS, FT-IR和XRD对Y2O3/纳米碳管复合粒子的形貌和微观结构进行了表征. 结果表明, 纳米碳管有效承载了Y2O3, Y2O3连续均匀地负载在纳米碳管的表面, 负载量为19.53%. FT-IR 和XPS证明了Y2O3粒子和纳米碳管表面之间发生了化学键合. 用三种方法将相同比例的Y2O3/纳米碳管复合粒子与高氯酸胺(AP)进行混合, 采用差热分析(DTA)研究了三种混合样品中Y2O3/纳米碳管复合粒子对高氯酸铵热分解的催化性能. 结果表明, 三种混合样品中的Y2O3/纳米碳管复合粒子都能催化高氯酸铵的热分解, 其中通过水溶剂混合的样品中Y2O3/纳米碳管复合粒子的催化效果优于另外两种. 与纯高氯酸铵相比, 其样品中高氯酸铵的高温分解峰温降低了168.5 ℃, 表观分解热由371 J•g-1提高到1410 J•g-1. 并用不同样品中高氯酸铵热分解动力学参数对所得结果进行了理论分析.

关 键 词:溶胶-凝胶法  纳米碳管  Y2O3  Y2O3/纳米碳管复合粒子  高氯酸铵
收稿时间:12 9 2005 12:00AM
修稿时间:2005-12-092006-04-10

Y2O3/Carbon Nanotube Composite Particles: Microstrcture and Catalytic Performance for Decomposition of Ammonium Perchlorate
ZHOU,Long-Mei,HOU,Li-Quan,LIU,Hong-Ying,LI,Feng-Sheng.Y2O3/Carbon Nanotube Composite Particles: Microstrcture and Catalytic Performance for Decomposition of Ammonium Perchlorate[J].Acta Chimica Sinica,2006,64(15):1548-1552.
Authors:ZHOU  Long-Mei  HOU  Li-Quan  LIU  Hong-Ying  LI  Feng-Sheng
Institution:(Yangzhou Technician College, Yangzhou 225003)
( Beijing New Oriental Forign Language School at Yangzhou, Yangzhou 225003)
(National Special Superfine Powder Engineering Research Center, Nanjing University of Science and Technology, Nanjing 210094)
Abstract:Y2O3/carbon nanotube composite particles were prepared by a sol-gel method. The microstrcture and looks of the composite particles obtained were characterized by SEM, XPS, FT-IR and XRD methods. The results indicate that Y2O3 are supported well on the surface of carbon nanotube. The Y2O3 particles coating on carbon naotube appear even and continous. This points to high nucleation density and big binding energy. FT-IR and XPS reveal that Y2O3 particles are coated with carbon nanotube through chemical bond. Three comparison samples mixing Y2O3/carbon nanoube composite particles with ammonia perchlorate (AP) by three mixing methods were prepared. And DTA experiments were used to characterize their catalytic performance. The results imply that the catalytic performance of Y2O3/carbon nanotube composite particles in the sample mixing by water phase is superior to that of the other. Compared with the pure ammonia perchlorate, the peak temperature of high temperature decomposition of AP in this mixing sample decreases 168.5 ℃, and the total heat release improves from 371 to 1410 J•g-1. The kinetics parameters of the thermal decomposition of AP in different samples were investigated to explain the above results.
Keywords:sol-gel method  carbon nanotube  Y2O3  Y2O3/carbon nanotube composite particle  ammonia p erchlorate